Low Cost, High Volume, Carbon Fiber Precursor for Plasma Oxidation
Light weighting with carbon fiber is critical to improving the energy efficiency of wind turbines, airplanes, and automobiles, but the high cost of carbon fiber continues to limit market growth and applications. Half of this cost is in the raw materials. For the carbon fiber market to reach the next level of adoption, the cost of both the raw materials and conversion must be reduced. This project considered the combination of low-cost, textile-grade precursors combined with the increased efficiency of plasma oxidation to greatly reduce the cost of carbon fiber. The primary objective of this project was to make industrial-grade carbon fiber (550 ksi tensile strength, 35 Msi tensile modulus) from textile-grade PAN precursors, something that cannot be achieved with conventional oxidation and to date has not been achieved with any technology. To accomplish this, the project team iteratively optimized the process conditions in the plasma oxidation and carbonization stages to maximize the tensile properties of the resultant carbon fibers. This involved implementing experimental designs for both stages, whereby process conditions (e.g. temperature) were varied and correlated to fiber properties. Samples of oxidized PAN fibers (OPFs) were prepared using a small pilot-scale plasma oxidation oven at 4XTechnologies (4XT). The thermal, chemical, and physical properties of OPF samples were analyzed by the University of Tennessee (UTK) and Oak Ridge National Laboratory (ORNL). The OPF samples were then converted to carbon fiber by subsequent low- and high-temperature carbonization using a lab-scale furnace at ORNL. The resultant carbon fibers were tested for tensile strength also at ORNL, and the results were fed back into the experimental design. Of the hundreds of carbon fiber samples produced over the course of the project, the best sample had an average break strength of 479 ksi and modulus of 33 Msi. While the best tensile properties achieved fell short of the final project targets of 550 ksi for break strength and 35 Msi for modulus, the team demonstrated the potential to produce industrial-grade carbon fiber using textile-grade precursors. The best performing fiber samples had tensile properties that are 87% of the goal for tensile strength and 94% of the goal for tensile modulus. With additional optimization work, it is likely that the targets could be achieved, since only a fraction of the process parameter space was explored during this project. 4XT and its affiliate (4M) have already secured funding through private equity, and there is a CRADA (Cooperative Research and Development Agreement) project currently underway with the Carbon Fiber Technology Center (CFTF) at ORNL to continue this research. Additionally, while not an original goal of the project, the carbon fibers for most samples had diameters >8.5μm. This is considerably larger than commercially available carbon fiber products, which can impart unique properties to the composites (e.g. increased compressive strength) and decrease manufacturing costs even further. Moreover, these fibers were oxidized with plasma oxidation using residence times ranging <60mins, which would be considered fast for normal diameter fibers, but it is as much as 5x faster when factoring in the diameter of the fibers.