DOE OSTI2021

High speed manufacturing of aluminum alloy 7075 tubing by Shear Assisted Processing and Extrusion (ShAPE)

Shear assisted processing and extrusion (ShAPE) was used to extrude aluminum alloy 7075 tubing at speeds up to 12.2 m/min. This is in comparison to 2.0 m/min which is generally the limit for conventionally extruded 7075. The increased speed is primarily attributed to more extensive shear deformation, compared to conventional extrusion, which results in a high density of low angle grain boundaries that facilitate continued deformation and delay the onset of surface tearing. Mechanical testing after heat treating to the T6 condition gave an ultimate tensile strength of 565.3 ± 4.6 MPa, yield strength of 495.7 ± 8.7 MPa, and elongation of 16.8 ± 0.8%. Strength values exceed the ASTM minimum standard and are on par with ASM typical values, while elongation was substantially improved compared to 7 and 11% for the ASTM and ASM values respectively. Finally, it was observed that low temperature extrusion at 341 °C and 40 rpm gave superior material properties in the T6 condition compared to high temperature extrusion at 441 °C and 120 rpm due to variances in nanoscale second phase size and distribution.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Scaled-Up Fabrication of Thin-Walled ZK60 Tubing using Shear Assisted Processing and Extrusion (ShAPE)

Shear Assisted Processing and Extrusion (ShAPE) has been scaled-up and applied to direct extrusion of thin-walled magnesium tubing. Using ShAPE, billets of ZK60A-T5 were directly extruded into round tubes having an outer diameter of 50.8 mm and wall thickness of 1.52 mm. The severe shearing conditions inherent to ShAPE resulted in microstructural refinement with an average grain size of 3.8μm measured at the midpoint of the tube wall. Tensile testing per ATSM E-8 on specimens oriented parallel to the extrusion direction gave an ultimate tensile strength of 254.4 MPa and elongation of 20.1%. Specimens tested perpendicular to the extrusion direction had an ultimate tensile strength of 297.2 MPa and elongation of 25.0%. Due to material flow effects resulting from the simultaneous linear and rotational shear intrinsic to ShAPE, ram force and electrical power consumption during extrusion were just 40 kN and 11.5 kW respectively. This represents a significant reduction in ram force and power consumption compared to conventional extrusion. As such, there is potential for ShAPE to offer a scalable, lower cost extrusion option with potentially improved bulk mechanical properties.

Direct Extrusion↗
DOE OSTI2021

Shear Assisted Processing and Extrusion (ShAPE) of Aluminum Alloy 7075, 2024, and Al-12.4TM

The most common aluminum alloys utilized in the aerospace industry are 7075 and 2024 due to their high strength-to-weight ratio compared to advanced high strength steels and other aluminum alloys. Despite excellent performance, these aluminum alloys have seen limited use outside of the aerospace industry due in part to high cost. If high-performance aluminum extrusions could be made more cost effectively by eliminating energy intensive process steps typical of conventional extrusion, then numerous opportunities exist for more widespread adoption. A key reason for the high cost of 7075 and 2024 extrusions (25-75% higher than 6061) is their slow extrusion speed. 7075 and 2024 are limited to 2 m/min and 3.5 m/min respectively, in contrast to 6061 which can be extruded at 20–80 m/min. In addition to slow speed, aluminum alloys require numerous thermal treatments throughout the extrusion process including homogenization and pre-heating prior to extrusion, and solution heat treating and artificial aging after extrusion. Each of these steps contribute to the total energy consumed during manufacturing of extruded components. This project investigates the use of ShAPE to improve extrusion speed and reduce, or even eliminate, the typical thermal treatments for high strength aluminum alloys, all while improving material performance. The overarching goal of this project was to demonstrate that Shear Assisted Processing and Extrusion (ShAPE) can manufacture high-performance aluminum alloy tubing with lower manufacturing energy and improved mechanical properties compared to conventional extrusion. Unlike conventional extrusion where the billet is rammed against a stationary die using a strictly linear motion, the ShAPE process superimposes a rotational shear force by spinning the die while the billet is plunged. Compared to conventional linear extrusion, the ShAPE process imparts significantly more strain into the feedstock material, which enables the formation of novel microstructures. These microstructures manifest an array of property and process improvements for extrusion of high-performance aluminum alloys. The following accomplishments were achieved for this project: Extrusion of 7075 at 12.2 meters/min compared to 2 meters/min for conventional extrusion; Elimination of 7075 billet homogenization (430 °C for 20 hours) which is required prior to conventional extrusion; Elimination of 7075 billet pre-heating (400 °C for 1 hour) in a separate furnace which is required prior to conventional extrusion; Achieved 7075-T6with yield strength = 595 MPa, ultimate tensile strength = 531MPa, and elongation = 17.4% for extrusions made from unhomogenized billets. Exceeds the ASTM and ASM standard, and typical industry values; Achieved 7075-T5 (i.e., no solution heat treatment) with yield strength = 588 MPa, ultimate tensile strength = 535 MPa, and elongation = 14.8% for extrusions made from homogenized billets; Extrusion of 2024 at 7.4 meters/min compared to 3.5 meters/min for conventional extrusion; Achieved 2024-T8510 yield strength = 522 MPa, ultimate strength = 510MPa, and elongation = 7.1% for extrusions made from wrought billets. Exceeds the ASTM and ASM standard, and typical industry values; Extrusion of Al-12.4TM high-performance aluminum powder directly into tubing, in a single step, which eliminates process steps typical of powder metallurgy extrusion.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Shear Assisted Processing and Extrusion (ShAPE) of Plastics: Recycling and Remolding

Polyethylene (PE) and polypropylene (PP) are often disposed as mixed plastic wastes. The challenges in recycling and upcycling these mixed polyolefin wastes lie in the difficulty in separating individual constituents in a cost-effective and scalable manner. Direct recycling the mixed PE and PP wastes in conventional melt-phase extruders typically result in a product with poor properties and low added value, because of immiscibility, phase separation, and lack of crystallinity. Friction extrusion (FE), a solid phase processing technique that has successfully extruded metal matrix composites with desired end products, has never been utilized to address the issue of recycling mixed plastic wastes. In this study, FE was performed on single-stream low-density polyethylene (LDPE), single-stream PP and mixed-stream LDPE+PP. Consolidated filaments of 2.5 mm diameter were extruded from different precursors. The thermal, infrared, and microscopic properties of extruded filaments were measured to evaluate the effects of FE process on the structure of recycled polymers. Meanwhile, the energy efficiency of FE was estimated based on extrusion rates and compared with conventional melt extrusion processes.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
DOE OSTI2022

Co-extrusion of dissimilar Al alloys via shear assisted processing and extrusion

Cladded tubes are generally used where two distinct properties are required at the outer and inner part of a tube, for instance, strength and corrosion resistance. In this investigation, shear assisted processing and extrusion (ShAPE) was employed to fabricate bi-metallic tubes from 1100 and 7075, and 1100 and 2024 dissimilar Al alloy combinations. Surface defect-free bi-metallic tubes were fabricated via the ShAPE process. Detailed microstructural characterization of the interface and various locations of the cladded tubes were carried out using light and scanning electron microscopy techniques. A defect-free, metallurgically bonded interface between the cladded layer and high strength Al (7075 and 2024 Al) was observed. Furthermore, hardness and tensile properties of the cladded ShAPE tubes were examined in the as-extruded conditions.

Komarasamy, Mageshwari↗
DOE OSTI2023

Co-Extrusion of Dissimilar Aluminum Alloys via Shear-Assisted Processing and Extrusion

Bimetallic tubes are used when a component requires more than one performance requirement, for instance, strength/creep resistance and oxidation/corrosion resistance. Shear-assisted processing and extrusion (ShAPE) can be used to fabricate extrudates that are comparable or superior in performance relative to conventionally manufactured extrudates. For the first time, ShAPE has been successfully employed in producing bimetallic Al tubing consisting of 6061 and 7075 Al alloys. Both light and electron microscopy techniques were used to investigate the integrity of the tubes, especially the interface between the core and cladding of the bimetallic tubes. Void-free bimetallic tubes were produced using ShAPE. Quantification of tube integrity was carried out with tensile testing under as-extruded and post-aged conditions. All the bimetallic tubes in the as-extruded samples exhibited uniform elongation above 5% with good tensile strength. Key insights such as material flow during bimetallic tube extrusion were obtained from the characterization of remnant billet and simulation results from a smoothed particle hydrodynamics model.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of various post-extrusion tempering on performance of AA2024 tubes fabricated by shear assisted processing and extrusion

In this report aluminum alloy 2024 (AA2024) tubes were extruded using the shear assisted processing and extrusion (ShAPE) method. As a ubiquitous aerospace alloy, AA2024 has reached a high degree of maturity with respect to manufacturing processes, alloy chemistry and heat treatment to maximize material strength. Therefore, over the eight decades since the introduction of this alloy, the mechanical properties have plateaued, and the extrusion speed has reached a 3.5 m/min ceiling using conventional extrusion. The ShAPE technique enabled an extrusion speed of AA2024 up to 7.4 m/min at 480 °C which is surpassing the extrudability chart of this alloy. Variation of the standard T3510 and T8510 post extrusion heat treatments were applied to improve the mechanical performance of the ShAPE extruded AA2024 tube. The ultimate tensile strength and yield strength of AA2024-T8510 ShAPE extruded tube are 522.0 ± 3.3 MPa and 510.7 ± 3.3 MPa, which are respectively 18% and 32% higher than ASM-typical and ASTM minimum values. The elongation at break of ShAPE extruded AA2024-T8510 tubes is two times higher than the ASM-typical and ASTM-minimum values. This improved ductility is attributed to the refinement of grain size and secondary phases as well as due to the uniform dispersion of sub-micron strengthening precipitates formed during the ShAPE process.

42 ENGINEERING↗
DOE OSTI2021

Hot rolling of ZK60 magnesium sheet with isotropic tensile properties from tubing made by Shear Assisted Processing and Extrusion (ShAPE)

In order to evaluate the viability of ShAPE processed Mg alloys as a feedstock for fabricating lightweight sheet material, tubes consisting of ShAPE-extruded Mg alloy ZK60 were flattened into plates and hot rolled at 450 °C to reductions of 37%, 68%, and 93%. The mechanical properties and microstructure of the rolled material were characterized through tensile testing and electron backscattered diffraction (EBSD). ZK60 specimens rolled to 68% reduction had tensile properties similar to published properties of rolled ZK60 sheets fabricated using conventional processes, and exhibited negligible tensile anisotropy referenced to the rolling direction. Additional rolling from 68% to 93% reduced the ultimate tensile stress in the rolling direction from 341.74±5.96 MPa to 260.76±22.4MPa. The yield stress and elongation to failure of the material also decreased from 292.16±1.11 MPa to 256.93±18.4 MPa and 6.95±1.94% to 3.38±0.51%, respectively, but negligible little anisotropy was observed with respect to loading direction. EBSD mapping indicated that the as-extruded ZK60 had texture rotated away from the basal direction which developed into a strong basal texture over numerous hot rolling steps. This evolution in texture has been observed after rolling for hot-rolled ZK60 fabricated through conventional extrusion processes. The initial grain structure was found to have experienced noticeable twinning from flattening the tube into plate. After hot rolling, the grain structure became more equiaxed, but the average grain diameter did not change appreciably from 5.15 ± 3.39 µm in the ShAPE extruded material, to 5.27 ± 12.44 µm in the 93% hot rolled sheet. This response to hot rolling is similar to the response of ZK60 fabricated using other methods such as Equal Channel Angular Processing (ECAP). Therefore, this work demonstrates ShAPE has the potential as an alternative method to producing feedstock for Mg alloy sheets. Modifications to the experimental procedure which could lead to improvements in observed properties are briefly discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Analysis of contact conditions and microstructure evolution in shear assisted processing and extrusion using smoothed particle hydrodynamics method

Shear assisted processing and extrusion (ShAPE) is a solid-phase processing technique that adds an additional shear force as compared with a conventional extrusion approach. Recently, ShAPE has demonstrated the capability of extruding high-performance aluminum alloy 7075 (AA7075) tubes at speeds up to 12.2 m/min without surface tearing. However, the relationship among the ShAPE processing parameters, thermomechanical conditions, contact conditions, heat generation, and microstructure evolution remains primarily empirical because an insightful understanding of the associated physics is still lacking. To help elucidate these relationships, this work proposes a thermomechanical meshfree model for the first time for ShAPE processing of AA7075 using the smoothed particle hydrodynamics (SPH) method. The meshfree model is first validated thoroughly by experimental data in terms of material flow, die face temperature, and extrusion force with various processing parameters. The validated model is then used to analyze the steady-state contact conditions and heat generation rates during ShAPE processing. Distributions of the average grain size of AA7075 being extruded are calculated using the SPH model output. The meshfree model results reveal that extrusions conducted at lower temperatures and higher strain rates yield more refined grains and possibly higher material strength, which is also consistent with the experimental observations.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Two-sided friction stir riveting by extrusion: A process for joining dissimilar materials

Two-sided friction stir riveting (FSR) by extrusion is an innovative process developed to rapidly, efficiently, and securely join dissimilar materials. This process extends a previously developed one sided friction stir extrusion process to create a strong and robust joint by producing a continuous, rivet-like structure through a preformed hole in one of the materials with a simultaneous, two-sided friction stir spot weld. The two-sided FSR by extrusion process securely joins the dissimilar materials together and effectively locks them in place without the use of any separate materials or fasteners. Lastly, in this paper we demonstrate the process by joining aluminum to steel and illustrate its potential application to automotive and aerospace manufacturing processes.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of post-extrusion heat treatment on mechanical property of aluminum alloy 2024 tube produced using Shear Assisted Processing and Extrusion (ShAPE)

The present work deals with the Shear Assisted Processing and Extrusion (ShAPE) of aluminum alloy 2024 tubes and mechanical property optimization via post extrusion heat treatments (T3510 and T8510). The ShAPE process enables extruding AA2024 at an extrusion speed of 7.4 m/min and extrusion temperature of 480 °C, which is otherwise beyond the extrudability limit of this alloy using conventional extrusion techniques. The ultimate tensile strength reaches 466 MPa for ShAPE+T3510 condition and 503 MPa for ShAPE+T8510 condition, both of which exceed the corresponding ASTM/ASM (minimum/typical) values for the studied tube geometry. The yield strength reaches 382 MPa for ShAPE+T3510 condition and 481 MPa for ShAPE+T8510 condition, both of which surpass any reported values in the literature or the highest industrial values. In addition, the ductility of AA2024 tube fabricated from ShAPE+T3510 or ShAPE+T8510 are evidently improved by the grain size refinement, second phase refinement, and enhanced uniformity in second phase distribution due to the severe plastic deformation of ShAPE process.

Shear Assisted Processing and Extrusions (ShAPE), ↗
DOE OSTI2023

Hot Rolling of ZK60 Magnesium Alloy with Isotropic Tensile Properties from Tubing Made by Shear Assisted Processing and Extrusion (ShAPE)

In the present work, we utilized Shear Assisted Processing and Extrusion (ShAPE), a solid-phase processing technique, to extrude hollow tubes of ZK60 Mg alloy. Hot rolling was performed on these as-extruded tubes (after slitting them longitudinally) to thickness reductions of 37%, 68%, and 93% to investigate their viability as rolling feedstock material. EBSD analysis showed the formation of twinned grains in the ShAPE processed material and a gradual re-orientation of the basal texture parallel to the extrusion direction with each rolling step. Moreover, an equiaxed grain size of 5.15 ± 3.39 μm was obtained in the ShAPE extruded material, and the microstructure was retained even after 93% rolling reduction. The rolled sheets also showed excellent tensile strengths and no mechanical anisotropy, a critical characteristic for formability. The unique microstructures developed and their excellent mechanical properties, combined with the ease of scalability of the process, make ShAPE a promising alternative to existing methods for producing rolling feedstock material.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Microstructure characterization of LAE442 magnesium alloy processed by extrusion and ECAP

The magnesium alloy LAE442 was processed by extrusion and equal channel angular pressing (ECAP) to achieve ultrafine grained microstructure. Detailed characterization of the microstructure was performed by scanning electron microscope, electron back scattered diffraction (EBSD) and transmission electron microscope. The initial, as-cast, microstructure consisted of large grains of ~ 1 mm. The grain refinement due to the processing by severe plastic deformation led to a decrease of the average grain size to ~ 1.7 μm after the final step of ECAP. A detailed characterization of secondary phases showed the precipitation of Al{sub 11}RE{sub 3}, Al{sub 2}Ca and Al{sub 10}RE{sub 2}Mn{sub 7} intermetallic phases. X-ray diffraction measurements proved that Li is dissolved within the magnesium matrix in the as-cast condition. Newly formed Al{sub 3}Li phase was observed after ECAP. The texture formation due to the extrusion and ECAP was different from that in the other magnesium alloys due to the activation of non-basal slip systems as a result of the decrease of the c/a ratio. - Highlights: • Combined extrusion and equal channel angular pressing results in significant grain refinement by factor 1000 approximately. • Al{sub 11}RE{sub 3}, Al{sub 2}Ca and Al{sub 10}RE{sub 2}Mn{sub 7} secondary phases are present in the as-cast material while Li was dissolved in the Mg matrix. • Extrusion and ECAP have no effect on the composition of the secondary phases but they influence strongly their distribution. • Texture evolution is affected by decrease of c/a ratio due to the presence of Li and resulting activation of non-basal slip.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Shear Assisted Processing and Extrusion of Unhomogenized Aluminum Alloy 6063 Castings with High Iron Content

Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate aluminum 6063 tubing directly from secondary scrap. Trimmings from an automotive manufacturing facility were cast into billets spiked with iron (0.3 wt% Fe) to explore the tolerance of ShAPE to Fe contamination. Billets were extruded in the unhomogenized condition to form tubing with an outer diameter of 12 mm and wall thickness of 2 mm. Tensile properties reached 0.2% YS = 206 MPa, UTS = 238 MPa, and U.E. = 16.3% in the T6 temper. Performance exceeds the ASTM minimum standard and is on par with ASM typical values for conventional extrusion of primary aluminum billets in the fully homogenized condition. Microstructural characterization shows extensive refinement of grain size along with dispersion and refinement of Fe-Al-Si intermetallic phases. This study suggests that ShAPE extrusion may offer a lower carbon manufacturing pathway through direct recycling of secondary aluminum scrap and elimination of the billet homogenization step.

solid phase processing, AA 6063, extrusion, Shear ↗
DOE OSTI2023

Shear Assisted Processing and Extrusion (ShAPE) of Lightweight Automotive Components (CRADA 418)

Shear Assisted Processing and Extrusion (ShAPE) was developed to manufacture non-circular multicell profiles from secondary aluminum. This was accomplished by integrating a porthole die approach within the rotating ShAPE process. Complexity of the profile geometry was deliberately advanced over the course of the project from round to square, to asymmetric trapezoidal, to two-cell asymmetric trapezoidal. Aluminum alloy 6063 in the form of briquettes (compacted shreddings and engineered machining chips) and castings from pre-consumer industrial scrap were utilized as the feedstock. Tensile properties were shown to exceed the ASTM minimum standard and ASM typical values with the best results reaching yield strength = 247 ± 10 MPa, ultimate tensile strength = 271 ± 10 MPa, and uniform elongation = 16.5 ± 2.4%. These values were achieved for porthole extrusion using unhomogenized castings made from 100% aluminum 6063 industrial scrap. The ability to extrude unhomogenized billet was made possible by in situ conversion of plate-like β-type Fe-rich intermetallics to more extrudable needle-like α-type which is not possible with conventional extrusion. By eliminating the need to dilute iron with primary aluminum during the recycling process, savings of >90% on lifecycle carbon footprint and >50% on embedded energy could ultimately result in lower cost, more environmentally friendly, automotive components.

42 ENGINEERING↗
DOE OSTI2021

Shear Assisted Processing and Extrusion of Thin-Walled AA6063 Tubing

Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate thin-walled AA6063 tubing with improved mechanical properties compared to conventional extrusion. Namely, tensile properties for ShAPE extrusions after T5 heat treating far exceed conventional T5 properties and are on par with T6 tensile properties. Die rotational speed did not affect tensile properties, although increased extrusion speed did lead to moderate increases in elongation.

Friction Extrusion, ShAPE, AA 6063, friction stir ↗
DOE OSTI2017

A novel freeform extrusion fabrication process for producing solid ceramic components with uniform layered radiation drying

An extrusion-based additive manufacturing process, called the Ceramic On-Demand Extrusion (CODE) process, for producing three-dimensional ceramic components with near theoretical density is introduced in this paper. Heere in this process, an aqueous paste of ceramic particles with a very low binder content (<1 vol%) is extruded through a moving nozzle at room temperature. After a layer is deposited, it is surrounded by oil (to a level just below the top surface of most recent layer) to preclude non-uniform evaporation from the sides. Infrared radiation is then used to partially, and uniformly, dry the just-deposited layer so that the yield stress of the paste increases and the part maintains its shape. The same procedure is repeated for every layer until part fabrication is completed. Several sample parts for various applications were produced using this process and their properties were obtained. The results indicate that the proposed method enables fabrication of large, dense ceramic parts with complex geometries.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Strength Variation in Processing Multiport Extrusion Tubes of A1100 and A3102 Alloys

The manufacturing process of multiport extrusion tubes generally includes homogenization, extrusion, roll leveling and heat treatment. In order to investigate the influence of the manufacturing procedures on strength variation of multiport extrusion tubes made of A1100 and A3102 alloys, the tube fabrication experiments and following materials characterization are carried out. The alloys’ stress–strain curves after every processing procedure are measured, and pressure-bearing capacity of the tubes is tested. The tubes’ strength and pressure-bearing capacity reach the peak values after straightening process and drop to the minimum after annealing. The contributions of solid solution hardening, grain boundary hardening and constituent particle strengthening to yield strength are evaluated. It is deduced that cluster hardening is the dominant strengthening mechanism for the as-homogenized and as-extruded samples; the contribution of clusters is second to work hardening after straightening process; slight cold work in conjunction with high-temperature annealing accelerates abnormal grain growth. The loss of strength increment from clusters can be interpreted by the remarkable reduction of high-angle grain boundaries after abnormal grain growth.

36 MATERIALS SCIENCE↗