Material flow visualization during friction stir welding using high-speed X-ray imaging
Not Available
Agiwal, Hemant (ORCID:0000000180516389)↗
SEARCH · Search NASA
Results for “Friction stir welding”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Processing-microstructure-property correlations for temperature-controlled friction stir welding of 304L SS plates
Not Available
Bhattacharyya, Madhumanti↗
Complete the initial testing on friction stir welding machine to evaluate the hardware issues that caused inconsistent weld quality
Explore the source record for details and available documents.
Chen, Jian [ORNL] (ORCID:0000000165321081)↗
In Situ Study on Fracture Behavior of Thick-Section Friction Stir-Welded AA 5083 Alloy
Friction stir welding (FSW) produces a gradient microstructure with distinct metallurgical zones. Here, the present study focuses on characterizing the fracture behavior during uniaxial loading across thick-section FSW joint in nonheat-treatable 5083 aluminum alloy. The hardness variation is linked to microstructural features across the weld zones through correlative microscopy. Notably, the heat-affected zone (HAZ) exhibits a lower hardness of 75 HV, while the thermomechanically affected zone (TMAZ) and stir zones (SZ) display a hardness of around 79HV. A marginal difference in hardness in HAZ prompts strain localization in HAZ on the advancing side of the weld, resulting in offset in fracture from the SZ, which is captured through in situ monitoring of the tensile test. Further, the postdeformation analysis reveals crack propagation along the maximum shear stress plane due to the coalescence of microvoids resulting from the fracturing and debonding of second-phase particles. Overall, this study provides valuable insight for optimizing the FSW process of AA 5083 alloy for thick-section applications.
36 MATERIALS SCIENCE↗
Additive Friction Stir Deposition of a Tantalum–Tungsten Refractory Alloy
Additive friction stir deposition (AFSD) is a solid-state metal additive manufacturing technique, which utilizes frictional heating and plastic deformation to create large deposits and parts. Much like its cousin processes, friction stir welding and friction stir processing, AFSD has seen the most compatibility and use with lower-temperature metals, such as aluminum; however, there is growing interest in higher-temperature materials, such as titanium and steel alloys. In this work, we explore the deposition of an ultrahigh-temperature refractory material, specifically, a tantalum–tungsten (TaW) alloy. The solid-state nature of AFSD means refractory process temperatures are significantly lower than those for melt-based additive manufacturing techniques; however, they still pose difficult challenges, especially in regards to AFSD tooling. In this study, we perform initial deposition trials of TaW using twin-rod-style AFSD with a high-temperature tungsten–rhenium-based tool. Many challenges arise because of the high temperatures of the process and high mechanical demand on AFSD machine hardware to process the strong refractory alloy. Despite these challenges, successful deposits of the material were produced and characterized. Mechanical testing of the deposited material shows improved yield strength over that of the annealed reference material, and this strengthening is mostly attributed to the refined recrystallized microstructure typical of AFSD. These findings highlight the opportunities and challenges associated with ultrahigh-temperature AFSD, as well as provide some of the first published insights into twin-rod-style AFSD process behaviors.
36 MATERIALS SCIENCE↗
Chloride-Induced Stress Corrosion Cracking of Friction Stir-Welded 304L Stainless Steel: Effect of Microstructure and Temperature
Dry storage canisters of used nuclear fuels are fabricated using SUS 304L stainless steel. Chloride-induced stress corrosion cracking (CISCC) is one of the major failure modes of dry storage canisters. The cracked canisters can be repaired by friction stir welding (FSW), a low-heat input ‘solid-phase’ welding process. It is important to evaluate the ClSCC resistance of the friction stir welded material. Stress corrosion cracking (SCC) studies were carried out on mill-annealed base materials and friction stir welded 304L stainless U-bend specimens in 3.5% NaCl + 5 N H2SO4 solution at room temperature and boiling MgCl2 solution at 155 °C. The engineering stress on the outer fiber of the FSW U-bend specimen was ~60% higher than that of the base metal (BM). In spite of the higher stress level of the FSW, both materials (FSW and BM) showed almost similar SCC failure times in the two different test solutions. The SCC occurred in the thermo-mechanically affected zone (TMAZ) of the FSW specimens in the 3.5% NaCl + 5 N H2SO4 solution at room temperature, while the stirred zone (SZ) was relatively crack-free. The failure occurred at the stirred zone when tested in the boiling MgCl2 solution. Hydrogen reduction was the cathodic reaction in the boiling MgCl2 solution, which promoted hydrogen-assisted cracking of the heavily deformed stirred zone. The emergence of the slip step followed by passive film rupture and dissolution of the slip step could be the SCC events in the 3.5% NaCl + 5 N H2SO4 solution at room temperature. However, the slip step height was not sufficient to cause passivity breakdown in the fine-grained SZ. Therefore, the SCC occurred in the partially recrystallized softer TMAZ. Overall, the friction-stirred 304L showed higher tolerance to ClSCC than the 304L base metal.
304L austenitic stainless steel↗
High-speed friction stir butt welding of 25.4 mm thick 7175-T79 aluminum alloy
This presents the first experimental demonstration of friction stir butt welding of 25.4 mm thick high-strength, precipitate-strengthened 7XXX aluminum alloy at a welding speed above 500 mm/min and penetration depth greater than 10 mm. Tool pin threads that terminate away from the shoulder region, helped mitigate nearby stress concentration during tool traversing, enabling a higher welding speed while avoiding pin fracture near shoulder. Two kinds of welds—one-sided with full penetration of the plate thickness and double-sided with partial penetration of the plate thickness—were conducted. Significant grain refinement (grain size 1.3 ± 0.8 µm) was evident at the junction of double-sided friction stir welding (FSW) compared to other regions of weld-nugget or base material. Cross-weld tensile testing with digital image correlation revealed high local strains at the junction of double-sided FSW before macro-yield. This strain concentration impeded the typical early necking on advancing/retreating sides of FSW joints, improving the yield strength of as-welded double-sided FSW by 20–24% over slow- to medium-speed one-sided FSW. In conclusion, the joint efficiency of as-welded, double-sided high-speed FSW was about 76% with respect to the base material’s ultimate tensile strength.
36 MATERIALS SCIENCE↗
Microstructure and texture evolution of friction stir lap welded dissimilar multi-aluminum stack
Here this work investigates the microstructural evolution of a dissimilar multiple-aluminum alloy stack (AA7055, AA7055, AA6022) produced by friction stir lap welding (FSLW). A through-thickness analyses of grain orientation map, grain size and distribution, strain distribution, and texture evolution by electron backscattered diffraction-based characterization technique were performed. Two different welding parameters (combination of tool rotation and traverse speed) were used to study the effects of the welding parameters on these microstructural characteristics. The study shows that higher welding speed and higher rotation speed of the FSLW tool yield finer grains. FSLW resulted in shear texture formation in the weld regions due to high welding speeds. This texture development in the nugget zone is consistent with shear deformation, and (111) pole figures show ideal shear texture components. The Stir Zone (SZ) exhibits shear texture (A/A ̅ and B/B ̅ components), consistent with other shear-assisted processes. Recrystallization mechanisms observed are CDRX in SZ and DDRX in TMAZ (Thermo-Mechanically Affected Zone). Interface analysis reveals the presence of oxide layers between different aluminum sheets, affecting joint mechanical performance. The mechanical property of the lap welded joints was presented in terms of microhardness distribution across the weld cross section. Slightly higher hardness in higher speed welding setup was observed throughout the SZ and AA6022 layer, indicating greater grain refinement and uniform grain structure distribution.
36 MATERIALS SCIENCE↗
Numerical Simulation and Experimental Validation of Joint Performance in Aluminum-Steel Lap Welds Formed by Friction Stir Dovetailing
Friction stir dovetailing (FSD) is a new dissimilar material joining process that simultaneously forms a mechanical interlock and metallurgical bond at the dissimilar material interface. This work presents development of a modeling and simulation approach to predict mechanical performance of FSD thick section aluminum to steel joints. A finite element analysis (FEA) was carried out in order to predict the load-carrying capacity and failure location for aluminum thicknesses between 12.7 mm and 50.8 mm with different numbers of dovetails. The numerical results and corresponding experimental investigation are in agreement and suggest that the developed methods can be used effectively for design and analysis of FSD joints using standard FEA tools.
Friction stir dovetailing, Friction stir welding, ↗
System and method for light assisted friction stir processing and welding of metallic and non-metallic materials
An apparatus for use in a friction stir operation, such as friction stir welding (FSW) or friction stir processing (FSP). The apparatus may have a rotating tool adapted to be plunged into a material, where the material is susceptible to being softened by heating. The rotating tool may further be adapted to be advanced along a surface of the material. An optical energy generating subsystem may be used to heat a portion of the material using optical energy as the tool is advanced along the material.
42 ENGINEERING↗
Interfacial reaction during friction stir assisted scribe welding of immiscible Fe and Mg alloy system
We report on interfacial characteristics and chemistry of bonded Mg-Fe interfaces welded using friction stir assisted scribe technique (FaST). Two pairs of dissimilar joints: (AZ31-DP590) and (Pure Mg-DP590) were studied to shed light on joining mechanisms responsible for bonding of “immiscible” pairs of Mg and Fe. We present first direct experimental evidence of presence of oxide layer, Al segregation by atom probe tomography and nano steel grains close to interface by transmission electron microscopy study.
36 MATERIALS SCIENCE↗
Hydrogen-assisted fracture resistance of pipeline welds in gaseous hydrogen
Fracture resistance of pipeline welds from a range of strength grades and welding techniques was measured in air and 21 MPa hydrogen gas, including electric resistance weld of X52, friction stir weld of X100 and gas metal arc welds (GMAW) of X52, X65 and X100. Welds exhibited a decrease in fracture resistance in hydrogen compared to complementary tests in air. A general trend was observed that fracture resistance in 21 MPa hydrogen gas decreased with increasing yield strength. To accommodate material constraints, two different fracture coupon geometries were used in this study, which were shown to yield similar fracture resistance values in air and 21 MPa hydrogen gas; values using different coupons resulted in less than 15% difference. In addition, fracture coupons were removed from controlled locations in select welds to examine the potential influence of orientation and residual stress. The two orientations examined in the X100 GMAW exhibited negligible differences in fracture resistance in air and, similarly, negligible differences in hydrogen. Residual stress exhibited a modest influence on fracture resistance; however, a consistent trend was not observed between tests in air and hydrogen, suggesting further studies are necessary to better understand the influence of residual stress. A comparison of welds and base metals tested in hydrogen gas showed similar susceptibility to hydrogen-assisted fracture. The overall dominant factor in determining the susceptibility to fracture resistance in hydrogen is the yield strength.
08 HYDROGEN↗
NuMI/LBNF Horn and Stripline Welding
Focusing horns for secondary particles are critical components for creating a stable beam of neutrinos. These components need to survive in a harsh environment and withstand high stresses. Extending the lifetime of the horns is critical as spare fabrication takes approximately two years and has many subcomponents with strict quality control. Two key aspects of the fabrication process include the inner conductor CNC TIG welding and the friction stir welding of the stripline pieces. The process for welding requires steps such as sample welding, x-ray imaging, and tensile pull tests. Having a perfect weld retains as much of the original strength of the base metal and reduces the risk of failure. As FNAL ramps up in power to 2.4MW, the lifetime of the horn and stripline will more heavily rely on continuing to have high quality welding procedures and thorough quality assurance.
Orea, Adrian↗
Abnormal grain growth suppression in Al alloys
The present invention provides a process for suppressing abnormal grain growth in friction stir welded aluminum alloys by inserting an intermediate annealing treatment (“IAT”) after the welding step on the article. The IAT may be followed by a solution heat treatment (SHT) on the article under effectively high solution heat treatment conditions. In at least some embodiments, a deformation step is conducted on the article under effective spin-forming deformation conditions or under effective superplastic deformation conditions. The invention further provides a welded article having suppressed abnormal grain growth, prepared by the process above. Preferably the article is characterized with greater than about 90% reduction in area fraction abnormal grain growth in any friction-stir-welded nugget.
Hales, Stephen J.↗
Joining AA7099 to Ni-Cr-Mo Steel Using Single Pass Friction Stir Dovetailing and AA6061 Butter Layer
A novel single pass friction stir dovetailing (FSD) was developed to join thick plate AA7099 to Ni-Cr-Mo steel in a lap configuration through the use of an AA6061 butter layer. The butter layer approach can be shown to significantly reduce interfacial failures by inhibiting the formation of brittle Fe–Al intermetallic compounds (IMCs) which are typically formed during conventional friction stir welding (FSW) of AA7099 directly to steel. This study evaluates the strength and microstructural evolution of the aluminum/steel joint interface between single pass FSD of AA7099/AA6061(butter)/steel fabricated using three different FSD tool configurations. The butter layer was achieved by placement of a free-floating strip of AA6061 within the dovetail groove that was pre-machined in the steel substrate. Friction stir welding was then used to simultaneously join the thick plate AA7099, the AA6061 strip and the AA7099 in a single weld pass. To optimize the joining process, three different pin geometries (full thread, half smooth/half thread, no thread) were evaluated; it was demonstrated that the half smooth/half thread tool produced the strongest weld joint due to the absence of a Zn rich layer at the Al/steel interface. The efficacy of this unique processing technique was tested using lap shear tensile testing as well as high resolution transmission electron microscopy (TEM). A discussion of the new FSD technique, joint configurations, and process parameters are provided along with joint microstructural analyses and mechanical performance.
Olszta, Matthew J.↗
Pitting behavior of friction stir repair-welded 304L stainless steel in 3.5% NaCl solution at room temperature: role of grain and defect structures
Stainless steel (SS) canisters used for storing spent nuclear waste are prone to chloride-induced stress corrosion cracking. Friction stir welding (FSW), being a low heat input process, can be used for repair welding of these canisters. In this study, an artificial crack was introduced on the 304L SS coupons by an electric discharge machining process. The artificial crack was repair-welded by FSW by maintaining the tool temperature a constant at two levels (725 and 825 °C). Friction stirring significantly reduced the grain size of the stirred zone (SZ) from about 47 to 2–4 μm. The fraction of low-angle grain boundaries increased in the SZ from 2 to 37–43%. Here, on the other hand, the fraction of special grain boundaries (Σ3 and Σ9) that was ~ 50% in the base metal reduced to < 10% in the SZ. During friction stirring, the oxide layer of artificial crack was broken and aligned to form a spiral defect called lazy-S structure. All these microstructural changes affected the corrosion behavior of the FSW specimens when tested in 3.5% NaCl at room temperature using cyclic polarization, chronoamperometry, and electrochemical impedance spectroscopy. The FSW specimens showed lower polarization resistance and lower transpassive potential than those of the base metal specimens. However, the pitting protection potentials of the FSW specimens were higher than that of the base metal. The pitting behavior of the FSW specimens was influenced more by the preferential attack on the lazy-S region than by passive film breakdown. The flat band potentials of the passive film formed on the FSW specimens were more positive than that of base metal. The charge carrier density of passive film formed on the FSW specimens was higher than that of the base metal. The higher fraction of low-angle grain boundaries present in the FSW specimens could supply more number of misorientation dislocations at the metal/film interface which could form anion vacancies by a climb process leading to formation of oxide at these locations without stressing the substrate. Therefore, low-angle boundaries are considered helpful for formation of stress-free passive films that will be highly stable and enhance both pitting and stress corrosion cracking resistance.
Dry storage canister↗
Investigating microstructural evolution in SolidStir™ extruded oxide dispersion strengthened 14YWT alloy fuel cladding tube
Structural components for extreme environments require advanced materials and manufacturing processes. One such advanced material is oxide dispersion strengthened (ODS) Fe–14 wt.%Cr–3W–0.4Ti–0.3Y 2 O 3 (14YWT), which is developed for components to be used in Gen IV and fusion nuclear reactors. However, the conventional manufacturing processes to produce components, such as fuel cladding tubes, either do not retain the desired microstructural attributes or are costly and less efficient. As a result, a more attractive option is a novel manufacturing process developed on the principle of friction stir welding or processing (FSW/P) and commercially referred to as SolidStir™ Extrusion (SSE). Here this study used the SSE technique to study the manufacturing and microstructural evolution of a fuel cladding tube made of ODS 14YWT alloy. The cladding extrusion by the SSE technique involved the use of ball-milled 14YWT powders with Y, Ti, and O in the solid solution and the use of a specially designed W-25Re-Hf tool for consolidation and extrusion of the powders. A scanning electron microscope (SEM), electron backscattered diffraction (EBSD), and transmission electron microscope (TEM) were utilized for microstructural characterization. A Keyence microscope captured macrostructural photographs of the extruded tube. EBSD examination of the extruded tube on both transverse and longitudinal cross-sections showed the presence of dynamically recrystallized grains and revealed that the average grain size of the transverse cross-section was smaller than that of the longitudinal cross-section. The texture was weak and consisted of some amount of shear texture. The presence of nano-oxide clusters or precipitates of Y, Ti, and O (pyrochlores) in the extruded tube was determined by TEM. Aging heat treatment caused the average precipitate size to decrease and the density to increase compared to the as-processed condition. The results indicated that SSE is a viable tool for manufacturing fuel cladding tubes with the desired microstructural attributes.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Report on Thermal Cycling Testing and Bimaterial Weld Development for a Passively Actuated Materials Surveillance Test Article
This report describes the continuation and conclusion of a thermal cycling test program designed to evaluate a family of passively actuated material surveillance test articles. Additionally, the report details a preliminary study of bimetallic welding between 316 stainless steel and TZM (tungsten-zirconium-molybdenum) alloy. The test program was ultimately successful in demonstrating the basic viability of the passively actuated test article concept as well as specifically validating the procedures developed to size specimens to mimic the mechanical response of operating components. The report discusses and summarizes the results of the complete test program which tested samples for more than 1,000 controlled thermal cycles. The weld development program included both stir friction and electron beam joining. The stir friction welding was ultimately successful, while the electron beam welding would require additional development. Ultimately, these test programs pave the way for implementing a materials surveillance program in future molten salt reactors (MSRs). The report conclusions outline a plan for transforming the research and developed described here into a definite set of practices and procedures for a surveillance program at a future operating reactor.
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗