Analytical systems for biological study of mars. the role of electron microscopy and electron optical techniques in exobiology
Electron microscopy and electron optical techniques in exobiology
OPTICAL METHOD↗
SEARCH · Search NASA
Results for “Optical Microscopy”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Analyses of Contaminated Solar Array Handrail Samples Retrieved from Mir
In January 1998 during, the STS-89 mission, an eight section Russian solar array panel was retrieved after more than ten years exposure to the orbital space environment on the Russian space station Mir. Two darkened handrail samples from the Russian solar array have been evaluated for contamination: a section of a white paint covered rigid handrail and a section of woven fabric over-wrapped around a flexible handhold. The handrail samples were evaluated using optical microscopy (OM), field emission scanning electron microscopy (FESEM) and energy dispersive spectroscopy (EDS). Optical properties were also obtained. Microscopy has shown the discolored areas to have thick layers of contaminant that has crazed and spalled off in regions. Energy dispersive spectroscopy revealed that the brown contaminant is composed of oxidized silicon. No silicon was present on the unexposed fabric over-wrap, and very small amounts were present in the white paint. Therefore, the contaminant layer on both samples is attributed to silicone contamination from other spacecraft materials that have been oxidized by atomic oxygen while in orbit. A significant source of the silicone contamination appears to be from the solar array itself.
deGroh, Kim K.↗
A Deuterium NMR Study of Bent-Core Liquid Crystals: Synthesis and Characterization of Deuterium-Labeled Oxadiazole-Containing Liquid Crystals - 1
We have synthesized two deuterated boomerang-shaped liquid crystals based on 2,5-bis(4-hydroxyphenyl)-1,3,4-oxadiazole (ODBP). Deuterium was introduced in the rigid 2,5-diphenyl-1,3,4-oxadiazole core and in the aromatic ring of the terminal 4-dodecyloxyphenyl moiety using standard acid catalyzed deuterium exchange conditions. Both compounds, ([4,4'(1,3,4-oxadiazole-2,5-diyl-d4)] di-4-dodecyloxybenzoate: ODBP-d4-Ph-O-C12) and ([4,4'(1,3,4-oxadiazole-2,5-diyl)] di-4-dodecyloxy-benzoate-d4; ODBP-Ph-d4-O-C12) were investigated by nuclear magnetic resonance, optical microscopy and differential scanning calorimetry. The optical textures and thermal behavior of both compounds were found to be identical to the non-deuterated analog [4,4(1,3,4-oxadiazole-2,5-diyl)] di-4-dodecyloxybenzoate (ODBP-Ph-O-C12) which we reported earlier. These compounds exhibit behavior indicative of a biaxial nematic liquid crystal phase, which we hope to confirm using deuterium NMR spectroscopy in the next phase of this study.
Dingemans, Theo J.↗
Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherents
Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.
bondline thickness↗
Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherends
Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.
X-ray computed tomography↗
Two-Photon Fluorescence Microscopy Developed for Microgravity Fluid Physics
Recent research efforts within the Microgravity Fluid Physics Branch of the NASA Glenn Research Center have necessitated the development of a microscope capable of high-resolution, three-dimensional imaging of intracellular structure and tissue morphology. Standard optical microscopy works well for thin samples, but it does not allow the imaging of thick samples because of severe degradation caused by out-of-focus object structure. Confocal microscopy, which is a laser-based scanning microscopy, provides improved three-dimensional imaging and true optical sectioning by excluding the out-of-focus light. However, in confocal microscopy, out-of-focus object structure is still illuminated by the incoming beam, which can lead to substantial photo-bleaching. In addition, confocal microscopy is plagued by limited penetration depth, signal loss due to the presence of a confocal pinhole, and the possibility of live-cell damage. Two-photon microscopy is a novel form of laser-based scanning microscopy that allows three-dimensional imaging without many of the problems inherent in confocal microscopy. Unlike one-photon microscopy, it utilizes the nonlinear absorption of two near-infrared photons. However, the efficiency of two-photon absorption is much lower than that of one-photon absorption because of the nonlinear (i.e., quadratic) electric field dependence, so an ultrafast pulsed laser source must typically be employed. On the other hand, this stringent energy density requirement effectively localizes fluorophore excitation to the focal volume. Consequently, two-photon microscopy provides optical sectioning and confocal performance without the need for a signal-limiting pinhole. In addition, there is a reduction in photo-damage because of the longer excitation wavelength, a reduction in background fluorescence, and a 4 increase in penetration depth over confocal methods because of the reduction in Rayleigh scattering.
Fischer, David G.↗
Melt Pool Imaging using a Configurable Architecture Additive Testbed System
This paper describes the inline (coaxial to laser) near infrared (NIR) camera sensor on the Configurable Architecture Additive Testbed (CAAT). The CAAT is an instrument that provides the capability to investigate laser based additive manufacturing (AM) processes and is configured for the metal powder bed fusion process. A low cost NIR camera is radiometrically calibrated to obtain coaxial, inline, imagery of laser generated melt pools. The camera capabilities, system optical path, and the uncertainty in the temperature measurement from NIR surface area scans on a bare titanium alloy plate are presented and discussed. The surface radiance measurements are compared to optical microscopy images of the melt pool width and depth. A metallic additive manufacturing process thermal model is developed in order to predict thermal distributions during laser scanning. The predicted thermal distributions by the model for different configurations are compared to the coaxial NIR measurements and discussed.
Additive manufacturing↗
The impact of LDEF results on the space application of metal matrix composites
Over 200 graphite/aluminum and graphite/magnesium composites were flown on the leading and trailing edges of LDEF on the Advanced Composites Experiment. The performance of these composites was evaluated by performing scanning electron microscopy and x-ray photoelectron spectroscopy of exposed surfaces, optical microscopy of cross sections, and on-orbit and postflight thermal expansion measurements. Graphite/aluminum and graphite/magnesium were found to be superior to graphite/polymer matrix composites in that they are inherently resistant to atomic oxygen and are less susceptible to thermal cycling induced microcracking. The surface foils on graphite/aluminum and graphite/magnesium protect the graphite fibers from atomic oxygen and from impact damage from small micrometeoroid or space debris particles. However, the surface foils were found to be susceptible to thermal fatigue cracking arising from contamination embrittlement, surface oxidation, or stress risers. Thus, the experiment reinforced requirements for carefully protecting these composites from prelaunch oxidation or corrosion, avoiding spacecraft contamination, and designing composite structures to minimize stress concentrations. On-orbit strain measurements demonstrated the importance of through-thickness thermal conductivity in composites to minimize thermal distortions arising from thermal gradients. Because of the high thermal conductivity of aluminum, thermal distortions were greatly reduced in the LDEF thermal environment for graphite/aluminum as compared to graphite/magnesium and graphite/polymer composites. The thermal expansion behavior of graphite/aluminum and graphite/magnesium was stabilized by on-orbit thermal cycling in the same manner as observed in laboratory tests.
Steckel, Gary L.↗
NASA Tech Briefs, January 2010
Topics covered include: Cryogenic Flow Sensor; Multi-Sensor Mud Detection; Gas Flow Detection System; Mapping Capacitive Coupling Among Pixels in a Sensor Array; Fiber-Based Laser Transmitter for Oxygen A-Band Spectroscopy and Remote Sensing; Low-Profile, Dual-Wavelength, Dual-Polarized Antenna; Time-Separating Heating and Sensor Functions of Thermistors in Precision Thermal Control Applications; Cellular Reflectarray Antenna; A One-Dimensional Synthetic-Aperture Microwave Radiometer; Electrical Switching of Perovskite Thin-Film Resistors; Two-Dimensional Synthetic-Aperture Radiometer; Ethernet-Enabled Power and Communication Module for Embedded Processors; Electrically Variable Resistive Memory Devices; Improved Attachment in a Hybrid Inflatable Pressure Vessel; Electrostatic Separator for Beneficiation of Lunar Soil; Amorphous Rover; Space-Frame Antenna; Gear-Driven Turnbuckle Actuator; In-Situ Focusing Inside a Thermal Vacuum Chamber; Space-Frame Lunar Lander; Wider-Opening Dewar Flasks for Cryogenic Storage; Silicon Oxycarbide Aerogels for High-Temperature Thermal Insulation; Supercapacitor Electrolyte Solvents with Liquid Range Below -80 C; Designs and Materials for Better Coronagraph Occulting Masks; Fuel-Cell-Powered Vehicle with Hybrid Power Management; Fine-Water-Mist Multiple-Orientation-Discharge Fire Extinguisher; Fuel-Cell Water Separator; Turbulence and the Stabilization Principle; Improved Cloud Condensation Nucleus Spectrometer; Better Modeling of Electrostatic Discharge in an Insulator; Sub-Aperture Interferometers; Terahertz Mapping of Microstructure and Thickness Variations; Multiparallel Three-Dimensional Optical Microscopy; Stabilization of Phase of a Sinusoidal Signal Transmitted Over Optical Fiber; Vacuum-Compatible Wideband White Light and Laser Combiner Source System; Optical Tapers as White-Light WGM Resonators; EPR Imaging at a Few Megahertz Using SQUID Detectors; Reducing Field Distortion in Magnetic Resonance Imaging; Fluorogenic Cell-Based Biosensors for Monitoring Microbes; A Constant-Force Resistive Exercise Unit; GUI to Facilitate Research on Biological Damage from Radiation; On-Demand Urine Analyzer; More-Realistic Digital Modeling of a Human Body; and Advanced Liquid-Cooling Garment Using Highly Thermally Conductive Sheets.
Source record↗
Soil microstructure and electron microscopy
As part of the process of comparing Martian soils with terrestial soils, high resolution electron microscopy and associated techniques should be used to examine the finer soil particles, and various techniques of electron and optical microscopy should be used to examine the undisturbed structure of Martian soils. To examine the structure of fine grained portions of the soil, transmission electron microscopy may be required. A striking feature of many Martian soils is their red color. Although the present-day Martian climate appears to be cold, this color is reminiscent of terrestial tropical red clays. Their chemical contents are broadly similar.
Smart, P.↗
MAB Phase Ceramics for Lunar Applications
During the ten-week internship my work focused on designing characterization protocol for 3D printed MAB phase ceramics on steel and Tiplates. I was mentored by Dr. Samuel Hocker of NASA and advised by Dr. Gupta from University of North Dakota. I also collaborated with Mackenzie Short from the University of North Dakota. The characterization protocol was divided into following steps; initially, we performed visual inspection of the plates. During this process, the coatings which spalled or delaminated were discarded for further evaluation. During the next step, we performed optical microscopy to discern and document surface features and porosities of the samples. We also noted some decomposition under the optical microscope as well. Thereafter, profilometry analysis was performed to understand the effect of power density on the surface roughness. Due to the deposited powder over the samples, the profilometry was inconclusive. We then cleaned the samples on the steel plate using ethanol and cotton swabs to wipe up the loose powder covering the samples. Detailed SEM analysis was then performed on the cleaned specimens. In parallel, the 3D printed samples on the Tiplate were cleaned by using an ultrasonic bath for 1h. Optical imaging showed that this cleaning process was more effective for cleaning except that small cracks propagated through the layered ceramics. The profilometry data gathered on the titanium plate after cleaning was more conclusive. The SEM data on the steel plate showed that there is decomposition at all wattages although at 100 W the extent of decomposition was lower. We are planning to characterize the steel samples after cleaning in ultrasonic bath for 5-10 min to minimize cracking during the cleaning process. In addition, we are also planning to study the fractured surface by SEM analysis.
Additive Manufacturing, Laser Powder Bed Fusion, S↗
Contamination, Transportation or Transmutation in LENR Material Analyses
LENR experiments using various loading and triggering mechanisms rely on a variety of elemental and isotopic assays to determine LENR effects. These assays include optical microscopy, Scanning Electron Microscopy with Energy Dispersive X-Ray Analysis (SEM/EDX), X-Ray Photoelectron Spectroscopy (XPS) and Transmission Electron Microscopy (TEM). All of these methods observe the surface of a material. By dissolving or vaporizing the sample, Inductively Coupled Plasma Optical Element Spectroscopy (ICP-OES) can determine elemental composition (ppb) or with mass spectroscopy, isotopes (ICP/MS). One can use a focused ion beam (FIB) to cut open a sample and observe the “cut” with either SEM/EDX, or Time-of-Flight Secondary Ion Mass Spectroscopy (TOF-SIMS). High Purity Gamma Ray Spectroscopy (HPGe) and alpha/ beta Liquid Scintillator spectroscopy can be used. We’ve employed these assay methods in our NASA GRC research under both the Advanced Energy Conversion and Lattice Confinement Fusion Projects. However, there are limitations associated with each of these methods ranging from handling contamination, instrumental limitations including sensitivity and field of view, and sample preparation.
Low Energy Nuclear Reactions↗
Analysis of Phase Separation in Czochralski Grown Single Crystal Ilmenite
Ilmenite (FeTiOs) is a wide bandgap semiconductor with an energy gap of 2.58 eV. Ilmenite has properties suited for radiation tolerant applications, as well as a variety of other electronic applications. Single crystal ilmenite has been grown from the melt using the Czochralski method. Growth conditions have a profound effect on the microstructure of the samples. Here we present data from a variety of analytical techniques which indicate that some grown crystals exhibit distinct phase separation during growth. This phase separation is apparent for both post-growth annealed and unannealed samples. Under optical microscopy, there appear two distinct areas forming a matrix with an array of dots on order of 5 pm diameter. While appearing bright in the optical micrograph, atomic force microscope (AFM) shows the dots to be shallow pits on the surface. Magnetic force microscope (MFM) shows the dots to be magnetic. Phase identification via electron microprobe analysis (EMPA) indicates two major phases in the unannealed samples and four in the annealed samples, where the dots appear to be almost pure iron. This is consistent with micrographs taken with a scanning probe microscope used in the magnetic force mode. Samples that do not exhibit the phase separation have little or no discernible magnetic structure detectable by the MFM.
Wilkins, R.↗
Vapor transport growth of organic solids in microgravity and unit gravity: some comparisons and results to date
Thin films of an organic nonlinear optical (NLO) material, N, N-dimethyl-p-(2,2-dicyanovinyl) aniline (DCVA), have been grown in space and on the ground by physical vapor transport in an effusive ampoule arrangement. The thin film growth technique developed on the ground is a direct result of information gleaned from experiments in microgravity. This paper covers the results of our experimental investigations for establishing "ideal" terrestrial conditions for deposition of a DCVA film. The active control during the deposition process was exercised by three deposition variables: the material source temperature, the background pressure external to the growth ampoule and the substrate temperature. Successful growth occurred when the difference in temperature between the source material and the copper substrate was 14 degrees C and the background nitrogen pressure was such that the transport was either diffusive or convective. A qualitative diffusion limited boundary was estimated to occur at a pressure of approximately 20 torr. We have probed the DCVA thin films with visible-near infrared reflection absorption spectroscopy, polarized Fourier transform infrared spectrometry, differential interference contrast optical microscopy, and stylus profilometry.
short duration↗
Effects of Ambient High Temperature Exposure on Alumina-Titania High Emittance Surfaces for Solar Dynamic Systems
Solar dynamic (SD) space power systems require durable, high emittance surfaces on a number of critical components, such as heat receiver interior surfaces and parasitic load radiator (PLR) elements. To enhance surface characteristics, an alumina-titania coating has been applied to 500 heat receiver thermal energy containment canisters and the PLR of NASA Lewis Research Center's (LeRC) 2 kW SD ground test demonstrator (GTD). The alumina-titania coating was chosen because it had been found to maintain its high emittance under vacuum (less than or equal to 10(exp -6) torr) at high temperatures (1457 F (827 C)) for an extended period (approximately 2,700 hours). However, preflight verification of SD systems components, such as the PLR require operation at ambient pressure and high temperatures. Therefore, the purpose of this research was to evaluate the durability of the alumina-titania coating at high temperature in air. Fifteen of sixteen alumina-titania coated Incoloy samples were exposed to high temperatures (600 F (316 C) to l500 F (816 C)) for various durations (2 to 32 hours). Samples, were characterized prior to and after heat treatment for reflectance, solar absorptance, room temperature emittance and emittance at 1,200 F (649 C). Samples were also examined to detect physical defects and to determine surface chemistry using optical microscopy, scanning electron microscopy operated with an energy dispersive spectroscopy (EDS) system, and x ray photoelectron spectroscopy (XPS). Visual examination of the heat-treated samples showed a whitening of samples exposed to temperatures of 1,000 F (538 C) and above. Correspondingly, the optical properties of these samples had degraded. A sample exposed to 1,500 F (816 C) for 24 hours had whitened and the thermal emittance at 1,200 F (649 C) had decreased from the non-heat treated value of 0.94 to 0.62. The coating on this sample had become embrittled with spalling off the substrate noticeable at several locations. Based on this research it is recommended that preflight testing of SD components with alumina-titania coatings be restricted to temperatures no greater than 600 F (316 C) in air to avoid optical degradation. Moreover, components with the alumina-titania coating are likely to experience optical property degradation with direct atomic oxygen exposure in space.
deGroh, Kim K.↗
Tutorial for Collecting and Processing Images of Composite Structures to Determine the Fiber Volume Fraction
Fiber-reinforced composite structures have become more common in aerospace components due to their light weight and structural efficiency. In general, the strength and stiffness of a composite structure are directly related to the fiber volume fraction, which is defined as the fraction of fiber volume to total volume of the composite. The most common method to measure the fiber volume fraction is acid digestion, which is a useful method when the total weight of the composite, the fiber weight, and the total weight can easily be obtained. However, acid digestion is a destructive test, so the material will no longer be available for additional characterization. Acid digestion can also be difficult to machine out specific components of a composite structure with complex geometries. These disadvantages of acid digestion led the author to develop a method to calculate the fiber volume fraction. The developed method uses optical microscopy to calculate the fiber area fraction based on images of the cross section of the composite. The fiber area fraction and fiber volume fraction are understood to be the same, based on the assumption that the shape and size of the fibers are consistent in the depth of the composite. This tutorial explains the developed method for optically determining fiber area fraction performed at NASA Langley Research Center.
Conklin, Lindsey↗
Toughening mechanisms in elastomer-modified epoxies. I - Mechanical studies. II - Microscopy studies
Tensile dilatometry at constant displacement rates is presently used to ascertain whether voiding, crazing or shear banding are the deformation mechanisms at work in the toughening of brittle epoxies through the addition of an elastomeric phase. The results obtained for epoxies toughened by various levels of several types of carbonyl-terminated butadiene nitrile liquid rubber indicate that, at low strain rates, the rubber particles simply enhance shear deformation; at sufficiently high strain rates, the particles cavitate and promote further shear deformation. Examinations of these materials are conducted by means of SEM, TEM, and optical microscopy in the second part of this study. Toughening is hypothesized to involve cavitation's relieving of triaxial tension at the crack tip, as well as shear band formation, which creates a plastic zone.
Yee, A. F.↗
Electron Backscatter Diffraction (EBSD) Analysis and U-Pb Geochronology of the Oldest Lunar Zircon: Constraining Early Lunar Differentiation and Dating Impact-Related Deformation
The evolution of the early moon was dominated by two processes (i) crystallization of the Lunar Magma Ocean (LMO) and differentiation of potassium-rare earth element-phosphorous-rich residual magma reservoir referred to as KREEP, and (ii) an intense meteorite bombardment referred to as lunar cataclysm . The exact timing of these processes is disputed, and resolution relies on collection and interpretation of precise age data. This study examines the microstructure and geochronology of zircon from lunar impact breccias collected during the Apollo 17 mission. A large zircon clast within lunar breccia 72215,195 shows sector zoning in optical microscopy, cathodoluminescence (CL) imaging and Raman mapping, and indicates that it was a relict fragment of a much larger magmatic grain. Sensitive high resolution ion microprobe (SHRIMP) U-Pb analysis of the zircon shows that U and Th concentration correlate with sector zoning, with darkest CL domains corresponding with high-U and Th (approx.150 and approx.100 ppm respectively), and the brightest-CL sectors containing approx.30-50 ppm U and approx.10-20 ppm Th. This indicates that variations in optical CL and Raman properties correspond to differential accumulation of alpha-radiation damage in each sector. Electron backscatter diffraction (EBSD) mapping shows that the quality of electron backscatter patterns (band contrast) varies with sector zoning, with the poorest quality patterns obtained from high-U and Th, dark-CL zones. EBSD mapping also reveals a deformation microstructure that is cryptic in optical, CL and Raman imaging. Two orthogonal sets of straight discrete and gradational low-angle boundaries accommodate approx.12 misorientation across the grain. The deformation bands are parallel to the crystallographic {a}-planes of the zircon, have misorientation axes parallel to the c-axis, and are geometrically consistent with formation by dislocation creep associated with <100>{010} slip. The deformation bands are unlike curved morphology of crystal-plastic microstructures in tectonically deformed terrestrial zircon, and geometrically similar to dislocation microstructures reported in experimentally shocked zircon. We interpret these crystal-plastic deformation microstructures to have resulted from a significant impact, either directly from impact shock, or during ductile flow directly following the impact. The deformation bands appear to continue undeflected through the non-indexed, radiation-damaged areas of the grain, which suggests that the orientation variation predates any significant mechanical weakening from radiation damage in the grain, and therefore occurred early in its history.
Timms, Nick↗