DOE OSTI2022

Compatibility of Fe-Cr-Al and Fe-Cr-Al-Mo oxide dispersion strengthened steels with static liquid sodium at 700 °C

We report the corrosion behavior and tensile properties of oxide dispersion strengthened (ODS) FeCr, FeCrAl, FeCrAlMo steels and 316H stainless steel were evaluated after 1000 h at 700 °C in static sodium with and without an oxygen getter (Zr foil). Without Zr foil to getter the dissolved oxygen in the liquid sodium, combined oxidation (formation of Cr, Fe-rich or Al-rich oxides) and dissolution of the studied materials was observed. For the ODS FeCr, Cr- and Fe-rich oxide formation and dissolution induced Cr depletion in the underlying alloy and led to the formation of laves phases that were observed to be detrimental to the room temperature tensile properties. For ODS FeCrAlMo and FeCrAl Al-rich oxide formation and dissolution resulted in Al depletion in the underlying alloys but did not impact tensile properties at room temperature. For 316H temperature induced sensitization combined with oxidation decreased room temperature tensile properties. With Zr foil added as oxygen getter, roughened surfaces and Al depletion profiles suggested the dissolution of ODS FeCr and FeCrAl into the liquid sodium while limited dissolution was observed for ODS FeCrAlMo and 316H. For the 316H and ODS FeCrAlMo steels, precipitates were formed at the grain boundaries after exposure. Tensile properties of ODS FeCr, FeCrAl and FeCrAlMo were not affected by the 1000 h corrosion exposure with Zr foil added to the sodium but for 316H temperature-induced grain boundary sensitization negatively affected the tensile properties.

36 MATERIALS SCIENCE↗
NASA NTRS1979

Transverse and longitudinal tensile properties at 760 C of several oxide dispersion strengthened nickel-base alloys

The transverse and longitudinal tensile properties of the oxide dispersion strengthened nickel-base alloys were determined at 760 C. The alloys with small amounts of gamma prime have strength levels suitable for turbine vane applications, while other highly alloyed, gamma prime strengthened superalloys have strengths typical of turbine blade materials. These alloys were produced by mechanical alloying and extrusion and the turbine blade alloys were also directionally recrystallized. Resultant grain aspect ratios varied from 1:1 to over 20:1. Longitudinal tensile strengths ranged from 285 to 1175 MPa, while longitudinal elongations were in excess of 4 percent for all alloys. Transverse tensile strengths were comparable to longitudinal strengths, but transverse ductility levels were generally less than 2 percent elongation. Tensile and yield strengths increased with increasing strain rate over the range 0.001 to 0.05 per second. Ductility in both orientations was not strain rate sensitive but could be related to grain size and grain aspect ratio.

Anglin, A. E., Jr.↗
DOE OSTI2024

Characteristics of oxide-dispersion strengthened alloys produced by high-temperature severe deformation

This study is to explore an economically attractive and technically feasible processing method for oxide-nanoparticle strengthened alloys for fusion reactor application. Despite many scientific merits of the advanced oxide-dispersion strengthened (ODS) alloys, such as the nanostructured ferritic alloy (NFA) 14YWT, the only viable production path for a high-quality NFA is the high-power mechanical alloying process. This process is often a multi-day high-speed ball milling of alloy powder with a small quantity of yttria (Y 2 O 3 ) powder, followed by the milled-powder consolidation using extrusion or other methods and additional thermomechanical processing (TMP) for property control. This complex production path, including the low-temperature mechanical alloying in particular, has limited technical advancement toward the cost-effective and scale-up production of ODS alloy components. To overcome such a practical limitation, we proposed to explore alternative low-cost processing routes using traditional thermomechanical processing (TMP) method only. Further, a series of continuous TMP cycles, which were designed to impose high-temperature severe plastic deformation (HT-SPD) conditions to the consolidated powder mixtures, were applied to achieve the effective distribution of oxide particles in nanograin structure and thus desirable mechanical properties. Since the reduced-activation ferritic-martensitic (RAFM) alloy powders (Fe-10Cr and Fe-14Cr alloys with various Y contents) are available in our inventory, we focused to utilize the new solid-state synthesis approach for controlling oxide (oxygen source) dissolution and nanoscale clustering in nanograin structure in those alloys. A combination of powder consolidation at 900 °C and continuous thermomechanical activation at 600 °C yielded two essential ODS alloy microstructure contents–nanograin structure and nanoparticle distribution–and thus demonstrated a good combination of strength and ductility.

36 MATERIALS SCIENCE↗
NASA NTRS1998

Elevated Temperature Compressive Strength Properties of Oxide Dispersion Strengthened NiAl After Cryo-milling and Roasting in Nitrogen

In an effort to superimpose two different elevated temperature strengthening mechanisms in NiAl, several lots of oxide dispersion strengthened (ODS) NiAl powder have been cryo-milled in liquid nitrogen to introduce AlN particles at the grain boundaries. As an alternative to cryo-milling, one lot of ODS NiAl was roasted in nitrogen to produce AlN. Both techniques resulted in hot extruded AlN-strengthened, ODS NiAl alloys which were stronger than the base ODS NiAl between 1200 and 1400 K. However, neither the cryo-milled nor the N2-roasted ODS NiAl alloys were as strong as cryo-milled binary NiAl containing like amounts of AlN. The reason(s) for the relative weakness of cryo-milled ODS NiAl is not certain; however the lack of superior strength in N2-roasted ODS NiAl is probably due to its relatively large AlN particles.

Whittenberger, J. Daniel↗
NASA NTRS1984

Elevated temperature compressive steady state deformation and failure in the oxide dispersion strengthened alloy MA 6000E

The compressive flow strength-strain rate behavior of the oxide-dispersion-strengthened alloy MA 6000E has been studied in the temperature range 1144-1366 K, with strain rates ranging from 2.1 x 10 to the -5th to 2.1 x 10 to the -7th per s. It is found that the inherent strength of the alloy is essentially the same in all test directions and that the low strength observed in tensile tests results from the inability of grain boundaries to support high tensile stresses. The failure of MA 6000E under high-temperature, slow plastic flow conditions is shown to be the result of concentrated slip. Slow plastic deformation in MA 6000E can be described by a threshold stress model of creep where threshold stresses are calculated from relatively fast testing procedures and the effective stress exponent for creep is assumed to be 3.5.

Whittenberger, J. D.↗
NASA NTRS2023

Superior Tensile Creep Behavior of A Novel Oxide Dispersion Strengthened Crconi Multi-Principal Element Alloy

The creep behavior of an additively manufactured (AM) yttrium oxide dispersion strengthened (ODS) CrCoNi multi-principal element alloy (MPEA) is investigated in this study. Tests were conducted over a constant tensile stress range of 40–200 MPa and a temperature range of 973–1173 K. A stress exponent of 6.5 ± 0.1 and activation energies in the range of 335–367 kJ/mol were measured. Compared to its non-ODS counterpart and its parent alloy (CrMnFeCoNi), AM ODS CrCoNi has superior creep resistance at all tested stresses and temperatures. The mechanism contributing to the excellent creep resistance of AM ODS CrCoNi is attributed to the interaction of mixed character dislocations with oxide particles. The creep ductility of AM ODS CrCoNi is higher than its nonODS counterpart due to a large percentage of low angle grain boundaries associated with its columnar grain structure. It was also found that creep ductility is significantly greater at the highest applied stress of 200 MPa compared to lower stresses. The steady state dislocation structure of AM ODS CrCoNi consists of long arrays of dislocations, which is different from that observed in non-ODS CrCoNi which consists of individual curved dislocations.

Seyed Gianmarco Sahragard-Monfared↗
NASA NTRS1978

Creep of oxide dispersion strengthened materials (with special reference to TD nichrome)

It was shown that the creep behavior of oxide dispersion strengthened (ODS) alloys is controlled principally by the creep properties of the matrix of the alloy devoid of particles. Thus, diffusion controlled slip process determine the rate controlling step in such materials. The role of the particles is to stabilize a fine substructure which is invariant with the creep stress over a wide range of stress. This characteristic leads to negligible strain hardening during creep and suggests that creep relations developed for pure metals and many solid solution alloys at constant structure should be used to describe the creep of ODS alloys. A second characteristics of the ODS alloys is that a stress may exist below which creep will not occur (threshold stress).

Lin, J.↗
DOE OSTI2022

Cold spray manufacturing of oxide-dispersion strengthened (ODS) steels using gas-atomized and ball-milled 14YWT powders

The cold spray deposition process has been investigated for the manufacture of 14YWT oxide-dispersion strengthened (ODS) steel, a nanostructured ferritic alloy (NFA), using gas-atomized and ball-milled feedstock powders. Cold spraying of the gas-atomized powder resulted in a thick dense deposit, but annealing them above 900 °C induced grain growth and heterogeneous precipitation of nanoparticles, thus resulting in lower hardness (~ 170 HV) compared to 14YWT ODS steel manufactured by the conventional method. The ball-milled powder (Fe-14Cr-3W-0.4Ti-0.2Y-0.125O) was cryomilled in liquid N 2 to achieve small particle sizes followed by annealing in a H 2 /Ar environment at 1000 °C and 1100 °C to reduce the hardness from ~ 8 GPa to ~ 5 GPa. Both smaller particle sizes and lower hardness of annealed powders made them amenable to the cold spray deposition process, resulting in thick and dense deposits, while retaining the favorable fully solutionized microstructure of the ball-milled powders. The microstructure of the as-deposited ODS exhibited very fine grain sizes (50–250 nm) with a uniform dispersion of Y-Ti-O nanoprecipitates in the ferritic steel matrix. The hardness values of the cold spray deposits using the powders annealed at 1000 °C and 1100 °C was 770 HV and 496 HV, respectively. Post-heat treatment of the as-deposited material up to 1100 °C showed a high-density microstructure with uniformly dispersed nanoscale oxide particles. The hardness of the annealed deposits up to 1000 °C had a notably higher hardness than bulk 14YWT ODS steel manufactured by conventional methods. The study demonstrates that cold spray deposition of the microstructurally-tailored feedstock powders can be used to successfully manufacture ODS steel with microstructure and properties comparable to those produced by the conventional methods, while providing for an attractive option for the more rapid and cost-effective manufacturing of ODS steel cladding tubes.

14YWT↗
NASA NTRS1977

Effect of prior creep at 1365 K on the room temperature tensile properties of several oxide dispersion strengthened alloys

An experimental study was conducted to determine whether oxide dispersion-strengthened (ODS) Ni-base alloys in wrought bar form are subject to creep degradation effects similar to those found in thin-gage sheet. The bar products evaluated included ODS-Ni, ODS-NiCr, and advanced ODS-NiCrAl types; the alloys included microstructures ranging from an essentially perfect single crystal to a structure consisting of very small elongated grains. Tensile test specimens were exposed to creep at various stress levels at 1365 K and then tensile tested at room temperature. Low residual tensile properties, change in fracture mode, appearance of dispersoid free bands, grain boundary cavitation, and/or internal oxidation are interpreted as creep degradation effects. The amount of degradation depends on creep strain, and degradation appears to be due to diffusional creep which produces dispersoid free bands around grain boundaries acting as vacancy sources.

Whittenberger, J. D.↗
NASA NTRS1975

The elastic modulus correction term in creep activation energies Applied to oxide dispersion strengthened superalloy

The effect of elastic modulus and the temperature dependence of elastic modulus on creep activation energies for an oxide dispersion strengthened nickel-base superalloy are investigated. This superalloy is commercially known as Inconel Alloy MA 753, strengthened both by gamma-prime precipitates and by yttria particles. It is shown that at intermediate temperatures, say below 1500 F, where elastic modulus is weakly dependent on temperature, the modulus correction term to creep activation energy is small. Accordingly, modulus corrections are insignificant for the superalloy considered, which shows high apparent creep activation energies at this temperature. On the contrary, at very high temperatures, the elastic modulus correction term can be significant, thus reducing the creep activation energy to that of vacancy self-diffusion. In order to obtain high-temperature creep resistance, a high-value elastic modulus with a weak dependence on temperature is required.

Malu, M.↗
NASA NTRS1981

Advanced oxide dispersion strengthened sheet alloys for improved combustor durability

Burner design modifications that will take advantage of the improved creep and cyclic oxidation resistance of oxide dispersion strengthened (ODS) alloys while accommodating the reduced fatigue properties of these materials were evaluated based on preliminary analysis and life predictions, on construction and repair feasibility, and on maintenance and direct operating costs. Two designs - the film cooled, segmented louver and the transpiration cooled, segmented twin Wall - were selected for low cycle fatigue (LCF) component testing. Detailed thermal and structural analysis of these designs established the strain range and temprature at critical locations resulting in predicted lives of 10,000 cycles for MA 956 alloy. The ODs alloys, MA 956 and HDA 8077, demonstrated a 167 C (300 F) temperature advantage over Hastelloy X alloy in creep strength and oxidation resistance. The MA 956 alloy was selected for mechanical property and component test evaluations. The MA 956 alloy was superior to Hastelloy X in LCF component testing of the film cooled, segmented louver design.

Henricks, R. J.↗
DOE OSTI2023

Investigating microstructural evolution in SolidStir™ extruded oxide dispersion strengthened 14YWT alloy fuel cladding tube

Structural components for extreme environments require advanced materials and manufacturing processes. One such advanced material is oxide dispersion strengthened (ODS) Fe–14 wt.%Cr–3W–0.4Ti–0.3Y 2 O 3 (14YWT), which is developed for components to be used in Gen IV and fusion nuclear reactors. However, the conventional manufacturing processes to produce components, such as fuel cladding tubes, either do not retain the desired microstructural attributes or are costly and less efficient. As a result, a more attractive option is a novel manufacturing process developed on the principle of friction stir welding or processing (FSW/P) and commercially referred to as SolidStir™ Extrusion (SSE). Here this study used the SSE technique to study the manufacturing and microstructural evolution of a fuel cladding tube made of ODS 14YWT alloy. The cladding extrusion by the SSE technique involved the use of ball-milled 14YWT powders with Y, Ti, and O in the solid solution and the use of a specially designed W-25Re-Hf tool for consolidation and extrusion of the powders. A scanning electron microscope (SEM), electron backscattered diffraction (EBSD), and transmission electron microscope (TEM) were utilized for microstructural characterization. A Keyence microscope captured macrostructural photographs of the extruded tube. EBSD examination of the extruded tube on both transverse and longitudinal cross-sections showed the presence of dynamically recrystallized grains and revealed that the average grain size of the transverse cross-section was smaller than that of the longitudinal cross-section. The texture was weak and consisted of some amount of shear texture. The presence of nano-oxide clusters or precipitates of Y, Ti, and O (pyrochlores) in the extruded tube was determined by TEM. Aging heat treatment caused the average precipitate size to decrease and the density to increase compared to the as-processed condition. The results indicated that SSE is a viable tool for manufacturing fuel cladding tubes with the desired microstructural attributes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
NASA NTRS1977

Development of oxide dispersion strengthened turbine blade alloy by mechanical alloying

There were three nickel-base alloys containing up to 18 wt. % of refractory metal examined initially for oxide dispersion strengthening. To provide greater processing freedom, however, a leaner alloy was finally selected. This base alloy, alloy D, contained 0.05C/15Cr / 2Mo/4W/2Ta/4.5Al/2.Ti/015Zr/0.01-B/Bal. Ni. Following alloy selection, the effect of extrusion, heat treatment, and oxide volume fraction and size on microstructure and properties were examined. The optimum structure was achieved in zone annealed alloy D which contained 2.5 vol. % of 35 mm Y2O3 and which was extruded 16:1 at 1038 C.

Merrick, H. F.↗
NASA NTRS1981

Creep and residual mechanical properties of cast superalloys and oxide dispersion strengthened alloys

Tensile, stress-rupture, creep, and residual tensile properties after creep testing were determined for two typical cast superalloys and four advanced oxide dispersion strengthened (ODS) alloys. The superalloys examined included the nickel-base alloy B-1900 and the cobalt-base alloy MAR-M509. The nickel-base ODS MA-757 (Ni-16CR-4Al-0.6Y2O3 and the iron-base ODS alloy MA-956 (Fe-20Cr-5Al-0.8Y2O3) were extensively studied, while limited testing was conducted on the ODS nickel-base alloys STCA (Ni-16Cr-4.5Al-2Y2O3) with a without Ta and YD-NiCrAl (Ni-16Cr-5Al-2Y2O3). Elevated temperature testing was conducted from 114 to 1477 K except for STCA and YD-NiCrAl alloys, which were only tested at 1366 K. The residual tensile properties of B-1900 and MAR-M509 are not reduced by prior creep testing (strains at least up to 1 percent), while the room temperature tensile properties of ODS nickel-base alloys can be reduced by small amounts of prior creep strain (less than 0.5 percent). The iron-base ODS alloy MA-956 does not appear to be susceptible to creep degradation at least up to strains of about 0.25 percent. However, MA-956 exhibits unusual creep behavior which apparently involves crack nucleation and growth.

Whittenberger, J. D.↗
DOE OSTI2020

Oxide dispersion strengthened 304 L stainless steel produced by ink jetting and laser powder bed fusion

This paper discusses the fundamentals of a novel hybrid method to synthesize oxide dispersion strengthened (ODS) 304 L stainless steel (SS) alloy using a modified laser powder bed fusion (LPBF) machine. Previously, ODS metal matrix composites have been produced by LPBF via ball-milling, which is expensive to scale. Here, we selectively dope yttria nanoparticles into a SS matrix by jetting a precursor chemistry onto the SS substrate prior to laser conversion and consolidation. Here, the new alloy shows good room temperature mechanical properties. Microstructures are studied using electron microscopy, energy dispersive spectroscopy and electron backscatter diffraction.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Selective laser melting of oxide dispersion strengthened MA956 alloy and its surface finishing by magnetic field assisted finishing

Selective laser melting (SLM) is a prominent metal additive manufacturing (AM) capable of processing a myriad of engineering materials with high precision and design freedom. However, similar to other AM processes, poor surface finishing has been an omnipresent problem in SLM technology. In this study, magnetic field assisted finishing (MAF) was used to finish SLM fabricated oxide dispersion strengthened (ODS) MA956, an iron-chromium-aluminum alloy. The effect of laser processing parameters on part density and surface roughness was first studied. Using a multi-objective optimization technique, the optimal parameters to obtain the highest density and lowest surface roughness were determined. Finally, MAF was applied to the parts built with the obtained optimal SLM parameters, but without significant improvement on the surfaces of as-printed samples. Hence, the surfaces of as-printed samples were post-processed (ground) to yield better initial surface conditions prior to MAF. The effect of initial roughness, iron particles size, and abrasive size on MAF performance was studied. Initial roughness had the most dominant effect followed by abrasive size. The underlying mechanism behind the dependency on initial roughness on final surface quality was analyzed by studying the change on the surface profiles with different starting initial roughness. The initial roughness required for MAF to be effective was determined. In conclusion, using the optimal processing conditions, MAF was applied to the post-processed samples to attain the final average surface roughness (R a ) as little as 0.36 μm starting from initial average roughness (R a ) of 1.53 μm.

36 MATERIALS SCIENCE↗
NASA NTRS1978

Tensile and creep properties of the experimental oxide dispersion strengthened iron-base sheet alloy MA-956E at 1365 K

A study of the 1365 K tensile properties, creep characteristics and residual room temperature properties after creep testing of the experimental oxide dispersion strengthened iron-base alloy MA-956E (Fe-20Cr-4.5Al-0.5Ti-0.5Y2O3) was conducted. The 1365 K tensile properties, particularly ductility, are strongly dependent on strain rate. It appears that MA-956E does not easily undergo slow plastic deformation. Rather than deform under creep loading conditions, the alloy apparently fails by a crack nucleation and growth mechanism. Fortunately, there appears to be a threshold stress below which crack nucleation and/or growth does not occur.

Whittenberger, J. D.↗
DOE OSTI2023

Oxide Dispersion Strengthened Ferritic Steel Wire Feedstock Development for Large Format Additive Manufacturing - CRADA 620 (Abstract)

This CRADA project funded through DOE’s INFUSE program seeks to demonstrate the viability of fabricating large, complex parts from oxide dispersion strengthened (ODS) steel with advanced manufacturing. Exhibiting excellent radiation tolerance and high mechanical performance at elevated temperatures, ODS steel is a promising structural material candidate for near-plasma components in fusion energy systems. Its use, however, has been limited by a lack of manufacturability. This project will seek to produce ODS steel wire through a solid-state shear assisted extrusion process and then demonstrate that the wire can undergo controlled local melting while being welded with the final part sufficiently retaining the beneficial properties of ODS steel. This would allow the use of wire-arc additive manufacturing (WAAM) to manufacture large-scale ODS parts, even though ODS is currently only available as a powder. WAAM is a promising technique for producing components like the replaceable ARC vacuum vessel in CFS’ fusion reactor design. Meanwhile, this project will also expand PNNL’s capability in producing custom wire feedstock with friction extrusion, enabling downstream large-scale manufacturing with WAAM and solid-state based additive manufacturing.

36 MATERIALS SCIENCE↗