DOE OSTI2025

Damage progression and failure of SiC/SiC composite tubes under hard-contact radial expansion

The response of silicon carbide (SiC) fiber-reinforced SiC matrix (SiC/SiC) composite cladding to mechanical interaction with fissile fuel is a knowledge gap that must be overcome to design and assess SiC-based cladding systems for advanced nuclear applications. This study developed the relevant mechanical testing capability and identified the failure behavior and the critical microstructural features and processing defects. Sections of SiC composite tube were subjected to a modified expansion-due-to-compression (EDC) test in an X-ray computed tomography microscope: a polyurethane plug pressed surrogate Al 2 O 3 into the inner walls of the SiC/SiC composite tubes to achieve hard contact. A pure EDC test with just a polyurethane plug was also performed as a reference. Through the use of displacement fields, digital volume correlation revealed inhomogeneous deformation fields in the tubes, even for pure EDC, which was related to the inherent defects in the structure. Deep learning–aided segmentation and systematic data analysis revealed that the presence of inhomogeneous deformation applied by the hard contact was exaggerated by the presence of inner surface imperfections left behind from the matrix densification process. In conclusion, the findings provide insights into the applications, highlighting the necessity for improvements in inner surface roughness and the incorporation of localized contacts in pellet–cladding mechanical interaction computational models.

Composites↗

DOE OSTI2022

Failure evaluation of neutron-irradiated SiC/SiC composites by underwater acoustic emission

Here, understanding the statistical properties of mechanical properties of non-irradiated and neutron-irradiated SiC/SiC composites is essential for component design. This study aims to evaluate the detailed damage accumulation behavior of composites focusing on two fracture parameters: proportional limit stress (PLS) and acoustic emission (AE) onset stress. The developmental underwater AE technique, which is benefit in non-contact in-situ failure monitoring method during mechanical testing and in handle of the irradiated material, was first applied to evaluate damage accumulation behavior. Two types of chemical vapor infiltration SiC/SiC composites were used: one reinforced with Hi-Nicalon Type-S SiC fiber and one reinforced with Tyranno-SA3 SiC fiber in the form of satin-woven 2D fabrics with pyrolytic carbon interface. Neutron irradiation in the High Flux Isotope Reactor at Oak Ridge National Laboratory reached a fluence of 30 dpa at a temperature of 620–670°C. Four-point flexural tests were conducted to evaluate post-irradiation strength. Weibull statistics did not suggest marked degradation of composite strength. Detailed failure behavior evaluated by AE demonstrated no irradiation-induced change of the AE onset stress (i.e., crack initiation equivalent stress). Failure probability analysis suggests that increasing the reliability of composites (i.e., the Weibull modulus rather than strength itself) is essential to expanding the design margin and benefiting from a probabilistic design approach.

36 MATERIALS SCIENCE↗

DOE OSTI2026

Long-Length SiC/SiC Tube Irradiation Experiment at LWR Temperatures Inserted into HFIR

This report describes the pre-irradiation characterization and successful assembly of a High Flux Isotope Reactor (HFIR) irradiation experiment designed to assess radiation-induced lateral bowing of silicon carbide fiber–reinforced, silicon carbide matrix composite (SiC/SiC) components under a radial fast neutron flux gradient at representative light-water reactor (LWR) temperatures of approximately 300 °C. The over-arching goal of this work is to validate thermomechanical models of SiC/SiC composite fuel assembly distortion used to predict the extent of lateral bowing and dose at which bowing reaches a maximum value. Ultimately, these models are used to ensure that fuel assembly distortion does not block coolant channels, interfere with control rod/blade movements, and/or impact local reactivity. The experiment contains six cladding tube specimens that are approximately 558.5 mm long with representative pressurized water reactor (PWR) outer and inner diameters of 9.5 mm and 7.5 mm, respectively. The specimens were thoroughly characterized prior to irradiation using traditional dimensional inspection and surface profilometry so that these measurements can later be compared with similar measurements that will be made post-irradiation to determine radiation-induced deformations. Furthermore, fine engraving markers were inscribed along the outer surfaces of the specimen and mapped using analytic photography and a three-dimensional stage. This technique allowed for accurate measurements of the marker spacings, which can be compared with similar measurements that will be made post-irradiation to provide local radiation-induced strain mapping. A light curtain optical micrometer was also employed to measure the pre-irradiation bowing of each specimen. The experiment was successfully assembled and inserted into position VXF-19 for HFIR cycle 516, which began May 12, 2026. The experiment will be removed after cycle 519, which is currently scheduled to end in December 2026.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

NASA NTRS1998

Mechanical Behavior and Analytical Modeling of Melt-Infiltrated SiC/SiC Woven Composite

The desirable properties in ceramic matrix composites (CMCs), such as high temperature strength, corrosion resistance, high toughness, low density, or good creep resistance have led to increased use of CMCs in high-speed engine structural components and structures that operate in extreme temperature and hostile aero-thermo-chemical environments. Ceramic matrix composites have been chosen for turbine material in the design of 21st century civil propulsion systems to achieve high fuel economy, improved reliability, extended life, and reduced cost. Most commercial CMCs are manufactured using a chemical vapor infiltration (CVI) process. However, a lower cost fabrication known as melt-infiltration process is also providing CMCs marked for use in hot sections of high-speed civil transports. Limited samples of a SiC/SiC melt-infiltrated woven composites are being investigated at room and elevated temperature below and above matrix cracking. These samples show graceful failure and toughness at room temperature with a reduction in strength and modulus at elevated temperatures. A generic finite element model is also being developed to predict monotonic and cyclic loading behavior of the woven composite. Use of the initial test data from the woven composite is being used for the development of the analytical model. This model is the first of a iterative process leading towards the development the model's capability to predict behavior at room and elevated temperature for monotonic and cyclic loading. The purpose of this paper is to report on the material and mechanical findings of the SiC/SiC melt-infiltrated woven composite and progress on the development of the finite element model.

Lang, J.↗

NASA NTRS2000

Silicon Effects on Properties of Melt Infiltrated SiC/SiC Composites

Silicon effects on tensile and creep properties, and thermal conductivity of Hi-Nicalon SiC/SiC composites have been investigated. The composites consist of 8 layers of 5HS 2-D woven preforms of BN/SiC coated Hi-Nicalon fiber mats and a silicon matrix, or a mixture of silicon matrix and SiC particles. The Hi-Nicalon SiC/silicon and Hi-Nicalon SiC/SiC composites contained about 24 and 13 vol% silicon, respectively. Results indicate residual silicon up to 24 vol% has no significant effect on creep and thermal conductivity, but does decrease the primary elastic modulus and stress corresponding to deviation from linear stress-strain behavior.

Bhatt, Ramakrishna T.↗

NASA NTRS2002

Fracture Mechanisms For SiC Fibers And SiC/SiC Composites Under Stress-Rupture Conditions at High Temperatures

The successful application of SiC/SiC ceramic matrix composites as high-temperature structural materials depends strongly on maximizing the fracture or rupture life of the load-bearing fiber and matrix constituents. Using high-temperature data measured under stress-rupture test conditions, this study examines in a mechanistic manner the effects of various intrinsic and extrinsic factors on the creep and fracture behavior of a variety of SiC fiber types. It is shown that although some fiber types fracture during a large primary creep stage, the fiber creep rate just prior to fracture plays a key role in determining fiber rupture time (Monkman-Grant theory). If it is assumed that SiC matrices rupture in a similar manner as fibers with the same microstructures, one can develop simple mechanistic models to analyze and optimize the stress-rupture behavior of SiC/SiC composites for applied stresses that are initially below matrix cracking.

DiCarlo, James A.↗

NASA NTRS2003

Modeling the Thermostructural Stability of Melt-infiltrated Sic/sic Composites

SiC/SiC composites developed by NASA with Sylramic-iBN fibers and melt-infiltrated (MI) SiC-Si matrices have demonstrated 1000-hour rupture life in air at 100 MPa and 1315OC. Recently it has been determined that a major factor controlling the long-term rupture life of these composites is not environment or stress, but an intrinsic microstructural and strength instability caused by a thermally-induced silicon attack of the Sic fibers. The objective of this paper is to present a simple diffusion-based analytical model which predicts well the observed effects of stress-free thermal exposure on the residual tensile strength of Sylramic-iBN/SiC-Si composites. The practical implications of the model for SiC/SiC composites with MI matrices are discussed.

DiCarlo, James A.↗

NASA NTRS2004

Foreign Object Damage Behavior of a SiC/SiC Composite at Ambient and Elevated Temperatures

Foreign object damage (FOD) behavior of a gas-turbine grade SiC/SiC ceramic matrix composite (CMC) was determined at 25 and 1316 C, employing impact velocities from 115 to 440 meters per second by 1.59-mm diameter stell-ball projectiles. Two different types of specimen support were used at each temperature: fully supported and partially supported. For a given temperature, the degree of post-impact strength degradation increased with increasing impact velocity, and was greater in a partially supported configuration than in a fully supported one. The elevated-temperature FOD resistance of the composite, particularly under partially supported loading at higher impact velocities greater than or equal to 350 meters per second, was significantly less than the ambient-temperature counterpart, attributed to a weakening effect of the composite. For fully supported loading, frontal contact stress played a major role in generating composite damage; whereas, for partially supported loading, both frontal contact and backside bending stresses were combined sources of damage generation. The SiC/SiC composite was able to survive higher energy impacts without complete structural failure but suffered more strength affecting damage from low energy impacts than AS800 and SN282 silicon nitrides.

Bhatt, Ramakrishna T.↗

NASA NTRS2004

Probabilistic Analysis of a SiC/SiC Ceramic Matrix Composite Turbine Vane

To demonstrate the advanced composite materials technology under development within the Ultra-Efficient Engine Technology (UEET) Program, it was planned to fabricate, test, and analyze a turbine vane made entirely of silicon carbide-fiber-reinforced silicon carbide matrix composite (SiC/SiC CMC) material. The objective was to utilize a five-harness satin weave melt-infiltrated (MI) SiC/SiC composite material developed under this program to design and fabricate a stator vane that can endure 1000 hours of engine service conditions. The vane was designed such that the expected maximum stresses were kept within the proportional limit strength of the material. Any violation of this design requirement was considered as the failure. This report presents results of a probabilistic analysis and reliability assessment of the vane. Probability of failure to meet the design requirements was computed. In the analysis, material properties, strength, and pressure loading were considered as random variables. The pressure loads were considered normally distributed with a nominal variation. A temperature profile on the vane was obtained by performing a computational fluid dynamics (CFD) analysis and was assumed to be deterministic. The results suggest that for the current vane design, the chance of not meeting design requirements is about 1.6 percent.

Murthy, Pappu L. N.↗

NASA NTRS2004

Advanced SiC/SiC Ceramic Composites For Gas-Turbine Engine Components

NASA Glenn Research Center (GRC) is developing a variety of advanced SiC/SiC ceramic composite (ASC) systems that allow these materials to operate for hundreds of hours under stress in air at temperatures approaching 2700 F. These SiC/SiC composite systems are lightweight (approximately 30% metal density) and, in comparison to monolithic ceramics and carbon fiber-reinforced ceramic composites, are able to reliably retain their structural properties for long times under aggressive gas-turbine engine environments. The key for the ASC systems is related first to the NASA development of the Sylramic-iBN Sic fiber, which displays higher thermal stability than any other SiC- based ceramic fibers and possesses an in-situ grown BN surface layer for higher environmental durability. This fiber is simply derived from Sylramic Sic fiber type that is currently produced at ATK COI Ceramics (COIC). Further capability is then derived by using chemical vapor infiltration (CVI) and/or polymer infiltration and pyrolysis (PIP) to form a Sic-based matrix with high creep and rupture resistance as well as high thermal conductivity. The objectives of this study were (1) to optimize the constituents and processing parameters for a Sylramic-iBN fiber reinforced ceramic composite system in which the Sic-based matrix is formed at COIC almost entirely by PIP (full PIP approach), (2) to evaluate the properties of this system in comparison to other 2700 F Sylramic-iBN systems in which the matrix is formed by full CVI and CVI + PIP, and (3) to examine the pros and cons of the full PIP approach for fabricating hot-section engine components. A key goal is the development of a composite system with low porosity, thereby providing high modulus, high matrix cracking strength, high interlaminar strength, and high thermal conductivity, a major property requirement for engine components that will experience high thermal gradients during service. Other key composite property goals are demonstration at high temperatures of high environmental resistance and high creep resistance, which in turn will result in long component life. Data are presented from a variety of laboratory tests on simple two-dimensional panels that examine these properties and compare the performance of the optimized full PIP system with those of the full CVI and CVI + PIP hybrid systems. Underlying mechanisms for performance differences in the various systems are discussed. Remaining issues for further property enhancement and for application of the full PIP approach for engine components are also discussed, as well as on-going approaches at NASA to solve these issues.

H. M. Yun↗

NASA NTRS2004

Thermo-Mechanical Properties of SiC/SiC Composites with Hybrid CVI-PIP Matrices

For long term structural service, the upper temperature capability for slurry-cast melt infiltrated (MI) SiC/SiC composites is limited to approx. 1315 C because of silicon reaction with the SiC fibers. For applications requiring material temperatures in excess of 1315 C, alternate methods of manufacturing the SiC matrices without silicon are being investigated, such as a hybrid combination of CVI and PIP. In this study, stacked fabric plies of Sylramic i-BN SiC fibers were coated with a CVI BN interface layer followed by a partial CVI SiC matrix. The remaining porosity in the SiC/SiC preforms was then infiltrated with silicon carbide matrix by PIP. Thermo-mechanical property measurements indicate that these composites are stable to 1700 C in inert environments under no load conditions for 100 h and under load conditions to 1450 C in air for 300 h. The advantages, disadvantages, and potential of this composite system for high temperature applications will be discussed.

Bhatt, R. T.↗

NASA NTRS2007

In-Plane Cracking Behavior and Ultimate Strength for 2D Woven and Braided Melt-Infiltrated SiC/SiC Composites Tensile Loaded in Off-Axis Fiber Directions

The tensile mechanical properties of ceramic matrix composites (CMC) in directions off the primary axes of the reinforcing fibers are important for architectural design of CMC components that are subjected to multi-axial stress states. In this study, 2D-woven melt-infiltrated (MI) SiC/SiC composite panels with balanced fiber content in the 0 degree and 90 degree directions were tensile loaded in-plane in the 0 degree direction and at 45 degree to this direction. In addition, a 2D triaxially-braided MI composite panel with balanced fiber content in the plus or minus 67 degree bias directions and reduced fiber content in the axial direction was tensile loaded perpendicular to the axial direction tows (i.e., 23 degrees from the bias fibers). Stress-strain behavior, acoustic emission, and optical microscopy were used to quantify stress-dependent matrix cracking and ultimate strength in the panels. It was observed that both off-axis loaded panels displayed higher composite onset stresses for through-thickness matrix cracking than the 2D-woven 0/90 panels loaded in the primary 0 degree direction. These improvements for off-axis cracking strength can in part be attributed to higher effective fiber fractions in the loading direction, which in turn reduces internal stresses on critical matrix flaws for a given composite stress. Also for the 0/90 panel loaded in the 45 degree direction, an improved distribution of matrix flaws existed due to the absence of fiber tows perpendicular to the loading direction. In addition, for the +67/0/-67 braided panel, the axial tows perpendicular to the loading direction were not only low in volume fraction, but were also were well separated from one another. Both off-axis oriented panels also showed relatively good ultimate tensile strength when compared to other off-axis oriented composites in the literature, both on an absolute strength basis as well as when normalized by the average fiber strength within the composites. Initial implications are discussed for constituent and architecture design to improve the directional cracking of SiC/SiC CMC components with MI matrices.

Morscher, Gregory N.↗

NASA NTRS2008

Impact Resistance of EBC Coated SiC/SiC Composites

Impact performance of 2-D woven SiC/SiC composites coated with 225 and 525 m thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59-mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s. Both microscopy and nondestructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s, no detectable damage was noticed in the MI SiC/SiC composites coated with 525 m EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 m EBC showed less damage than the composite coated with 225 m EBC. Both types of EBC coated composites retained a large fraction of the baseline properties of as-fabricated composites and exhibited non-brittle failure after impact testing at projectile velocities up to 375 m/s. Exposure of impact tested specimens in a moisture environment at 1316 C for 500 hr indicated that the through-the-thickness cracks in the EBC coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Fox, Dennis S.↗

NASA NTRS2008

Impact Resistance of Environmental Barrier Coated SiC/SiC Composites

Impact performance of 2D woven SiC/SiC composites coated with 225 and 525 microns thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59 mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s . Both microscopy and non-destructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s , no detectable internal damage was noticed in the MI SiC/SiC composites coated with 525 microns EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 microns EBC showed less damage than those coated with 225 microns EBC. Both types of coated composites retained a large fraction of the baseline properties of the as-fabricated composites and exhibited non-brittle failure after impact testing. Furnace exposure of impacted specimens in a moisture environment at 1316 C for 500 h indicated that the through-the-thickness cracks in the coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Bhatt, Ramakrishna T.↗

NASA NTRS2008

Electrical Resistance as a NDE Technique to Monitor Processing and Damage Accumulation in SiC/SiC Composites

Ceramic matrix composites are suitable for high temperature structural applications such as turbine airfoils and hypersonic thermal protection systems. The employment of these materials in such applications is limited by the ability to process components reliable and to accurately monitor and predict damage evolution that leads to failure under stressed-oxidation conditions. Current nondestructive methods such as ultrasound, x-ray, and thermal imaging are limited in their ability to quantify small scale, transverse, in-plane, matrix cracks developed over long-time creep and fatigue conditions. Electrical resistance of SiC/SiC composites is one technique that shows special promise towards this end. Since both the matrix and the fibers are conductive, changes in matrix or fiber properties should relate to changes in electrical conductivity along the length of a specimen or part. Initial efforts to quantify the electrical resistance of different fiber and different matrix SiC/SiC composites will be presented. Also, the effect of matrix cracking on electrical resistivity for several composite systems will be presented. The implications towards electrical resistance as a technique applied to composite processing, damage detection, and life-modeling will be discussed.

Smith, Craig↗

NASA NTRS2008

SiC/SiC Composites: The Effect of Fiber Type and Fiber Architecture on Mechanical Properties

Woven SiC/SiC composites represent a broad family of composites with a broad range of properties which are of interest for many energy-based and aero-based applications. Two important features of SiC/SiC composites which one must consider are the reinforcing fibers themselves and the fiber-architecture they are formed into. The range of choices for these two features can result in a wide range of elastic, mechanical, thermal, and electrical properties. In this presentation, it will be demonstrated how the effect of fiber-type and fiber architecture effects the important property of "matrix cracking stress" for slurry-cast melt-infiltrated SiC matrix composites, which is often considered to be a critical design parameter for this system of composites.

Morscher, Gregory N.↗

NASA NTRS2006

Advances in SiC/SiC Composites for Aerospace Applications

In recent years, supported by a variety of materials development programs, NASA Glenn Research Center has significantly increased the thermostructural capability of SiC/SiC composite materials for high-temperature aerospace applications. These state-of-the-art advances have occurred in every key constituent of the composite: fiber, fiber coating, matrix, and environmental barrier coating, as well as processes for forming the fiber architectures needed for complex-shaped components such as turbine vanes for gas turbine engines. This presentation will briefly elaborate on the nature of these advances in terms of performance data and underlying mechanisms. Based on a list of first-order property goals for typical high-temperature applications, key data from a variety of laboratory tests are presented which demonstrate that the NASA-developed constituent materials and processes do indeed result in SiC/SiC systems with the desired thermal and structural capabilities. Remaining process and microstructural issues for further property enhancement are discussed, as well as on-going approaches at NASA to solve these issues. NASA efforts to develop physics-based property models that can be used not only for component design and life modeling, but also for constituent material and process improvement will also be discussed.

DiCarlo, James A.↗

NASA NTRS2006

Modeling Creep Effects in Advanced SiC/SiC Composites

Because advanced SiC/SiC composites are projected to be used for aerospace components with large thermal gradients at high temperatures, efforts are on-going at NASA Glenn to develop approaches for modeling the anticipated creep behavior of these materials and its subsequent effects on such key composite properties as internal residual stress, proportional limit stress, ultimate tensile strength, and rupture life. Based primarily on in-plane creep data for 2D panels, this presentation describes initial modeling progress at applied composite stresses below matrix cracking for some high performance SiC/SiC composite systems recently developed at NASA. Studies are described to develop creep and rupture models using empirical, mechanical analog, and mechanistic approaches, and to implement them into finite element codes for improved component design and life modeling

Lang, Jerry↗