NASA NTRS1998

Degradation of Teflon(tm) FEP Following Charged Particle Radiation and Rapid Thermal Cycling

During the Second Servicing Mission (SM2) of the Hubble Space Telescope (HST) severe degradation was observed on the outer layer of the thermal control blankets. Astronaut observations and photographs revealed large cracks in the metallized Teflon FEP (fluorinated ethylene propylene), the outer layer of the multi-layer insulation (MLI), in many locations around the telescope. In an effort to understand what elements of the space environment might cause such damage, pristine Teflon' FEP was tested for durability to radiation and thermal cycling. Specimens were subjected to electron and proton fluences comparable to those experienced by HST and were subsequently thermal cycled in a custom-built rapid thermal cycle chamber. Tensile tests of the specimens showed that radiation followed by thermal cycling significantly reduced the ultimate strength and elongation of Teflon FEP.

Townsend, Jacqueline A.↗
NASA NTRS1998

Degradation of Teflon(tm) FEP Following Charged Particle Radiation and Rapid Thermal Cycling

During the Second Servicing Mission (SM2) of the Hubble Space Telescope (HST) severe degradation was observed on the outer layer of the thermal control blankets. Astronaut observations and photographs revealed large cracks in the metallized Teflon' FEP (fluorinated ethylene propylene), the outer layer of the multi-layer insulation (MLI), in many locations around the telescope. In an effort to understand what elements of the space environment might cause such damage, pristine Teflon(registered trademark) FEP was tested for durability to radiation and thermal cycling. Specimens were subjected to electron and proton fluences comparable to those experienced by HST and were subsequently thermal cycled in a custom-built rapid thermal cycle chamber. Tensile tests of the specimens showed that radiation followed by thermal cycling significantly reduced the ultimate strength and elongation of Teflon(registered trademark) FEP.

Townsend, Jacqueline A.↗
NASA NTRS1998

Degradation of Teflon(tm) FEP Following Charged Particle Radiation and Rapid Thermal Cycling

During the Second Servicing Mission (SM2) of the Hubble Space Telescope (HST) severe degradation was observed on the outer layer of the thermal control blankets. Astronaut observations and photographs revealed large cracks in the metallized Teflon(R) FEP (fluorinated ethylene propylene), the outer layer of the multi-layer insulation (MLI), in many locations around the telescope. In an effort to understand what elements of the space environment might cause such damage, pristine Teflon(R) FEP was tested for durability to radiation and thermal cycling. Specimens were subjected to electron and proton fluences comparable to those experienced by HST and were subsequently thermal cycled in a custom-built rapid thermal cycle chamber. Tensile tests of the specimens showed that radiation followed by thermal cycling significantly reduced the ultimate strength and elongation of Teflon(R) FEP.

Townsend, Jacqueline↗
NASA NTRS1999

Degradation of Teflon(trademark) FEP Following Charged Particle Radiation and Rapid Thermal Cycling

During the Second Servicing Mission (SM2) of the Hubble Space Telescope (HST) severe degradation was observed on the outer layer of the thermal control blankets. Astronaut observations and photographs revealed large cracks in the metallized Teflon(trademark) FEP (fluorinated ethylene propylene), the outer layer of the multi-layer insulation (MLI), in many locations around the telescope. In an effort to understand what elements of the space environment might cause such damage, pristine Teflon(trademark) FEP was tested for durability to radiation and thermal cycling. Specimens were subjected to electron and proton fluences comparable to those experienced by HST and were subsequently thermal cycled in a custom-built rapid thermal cycle chamber. Tensile tests of the specimens showed that radiation followed by thermal cycling significantly reduced the ultimate strength and elongation of Teflon(trademark) FEP.

Townsend, Jacqueline↗
NASA NTRS2003

Thermal Contributions to the Degradation of Ground Laboratory and Space Irradiated Teflon

The aluminized Teflon fluorinated ethylene propylene outer most layer of the multilayer insulation blankets on the Hubble Space Telescope has become embrittled resulting in severe on-orbit cracking. During the second servicing mission, a piece of aluminized fluorinated ethylene propylene was retrieved that had curled, exposing the back-surface aluminum to space. This extremely embrittled piece reached 200 C on-orbit, 150 C higher than the nominal temperature extreme. Therefore, experiments have been conducted to determine the effect of heating on the degradation of fluorinated ethylene propylene that has been irradiated in a ground laboratory facility or in space on Hubble Space Telescope. Samples of pristine, x-ray irradiated and Hubble Space Telescope retrieved fluorinated ethylene propylene were heat treated from 50 to 200 C at 25 C intervals in a high vacuum facility and tensile tested. Density measurements were also obtained. Results indicate that heating does not embrittle non-irradiated Teflon. However, there is a significant dependence of the embrittlement of irradiated Teflon on heating temperature, with near complete loss of elongation at 100 C and higher. Rate of degradation changes, which were consistent with the glass transition temperature for fluorinated ethylene propylene, were present in the data. The results support chain scission as the primary mechanism of degradation of fluorinated ethylene propylene on Hubble Space Telescope, and indicate the significance of the on-orbit temperature of fluorinated ethylene propylene with respect to its degradation in the space environment.

deGroh, Kim K.↗
NASA NTRS2004

Effects of Various Wavelength Ranges of Vacuum Ultraviolet Radiation on Teflon FEP Film Investigated

Teflon Fluorinated Ethylene Propylene (FTP) films (DuPont) have been widely used for spacecraft thermal control and have been observed to become embrittled and cracked upon exposure to the space environment. This degradation has been attributed to a synergistic combination of radiation and thermal effects. A research study was undertaken at the NASA Glenn Research Center to examine the effects of different wavelength ranges of vacuum ultraviolet (VUV) radiation on the degradation of the mechanical properties of FEP. This will contribute to an overall understanding of space radiation effects on Teflon FEP, and will provide information necessary to determine appropriate techniques for using laboratory tests to estimate space VUV degradation. Research was conducted using inhouse facilities at Glenn and was carried out, in part, through a grant with the Cleveland State University. Samples of Teflon FEP film of 50.8 microns thickness were exposed to radiation from a VUV lamp from beneath different cover windows to provide different exposure wavelength ranges: MgF2 (115 to 400 nm), crystalline quartz (140 to 400 nm), and fused silica (FS, 155 to 400 nm). Following exposure, FEP film specimens were tensile tested to determine the ultimate tensile strength and elongation at failure as a function of the exposure duration for each wavelength range. The graphs show the effect of ultraviolet exposure on the mechanical properties of the FEP samples.

Dever, Joyce A.↗
NASA NTRS1967

Technique for stripping Teflon insulated wire

Cryogenic stripping of Teflon insulated wire leaves no residue and produces no physical damage. After the wire is immersed in liquid nitrogen, bent slightly, and returned to room temperature, the Teflon is removed by fingernails or flat-nosed pliers.

Babb, B. D.↗
NASA NTRS1978

Silver-Teflon contamination UV radiation study

Silver-Teflon (Ag/FEP) is planned to be used as the thermal control material covering the radiator surfaces on the shuttle orbiter payload bay doors. These radiators require the use of materials that have a very low solar absorptance and a high emittance for heat rejection. However, operationally, materials used on these critical radiator surfaces, such as silver-Teflon, will be exposed to a variety of conditions which include both the natural as well as the induced environments from the Shuttle Orbiter. A complete test facility was assembled, and detailed test procedures and a test matrix were developed. Measurements of low solar absorptance were taken before and after contamination, at intervals during irradiation, and after sample cleaning to fulfill all the requirements.

Muscari, J. A.↗
NASA NTRS1980

Characteristics of edge breakdowns on Teflon samples

The characteristics of electrical discharges induced on silverbacked Teflon samples irradiated by a monoenergetic electron beam have been studied under controlled laboratory conditions. Measurements of breakdown threshold voltages indicate a marked anisotropy in the electrical breakdown properties of Teflon: differences of up to 10 kV in breakdown threshold voltage are observed depending on the sample orientation. The material anisotropy can be utilized in spacecraft construction to reduce the magnitude of discharge currents.

Yadlowsky, E. J.↗
NASA NTRS1981

Charging and discharging Teflon

The charging and discharging characteristics of several common satellite materials exposed to 0-30KV electrons are measured. Teflon is discussed because the charging characteristics are radically altered immediately after a spontaneous discharge. The exterior geometry of the test structure is shown. In all cases dielectric samples were 82 cm in diameter mounted on the front of a 120 cm diameter cylinder supported on an 85 cm, 0.95 cm thick plexiglass disc. Dielectric materials investigated were: back surface aluminized Kapton, back surface silvered Teflon, silicon alkyd white thermal control paint, and 50 cm by 50 cm array of 0.030 cm thick MgF2 coated fused silica solar cell cover slips.

Passenheim, B. C.↗
NASA NTRS1981

Experimental validation of a numerical model predicting the charging characteristics of Teflon and Kapton under electron beam irradiation

The effect differential charging of spacecraft thermal control surfaces is assessed by studying the dynamics of the charging process. A program to experimentally validate a computer model of the charging process was established. Time resolved measurements of the surface potential were obtained for samples of Kapton and Teflon irradiated with a monoenergetic electron beam. Results indicate that the computer model and experimental measurements agree well and that for Teflon, secondary emission is the governing factor. Experimental data indicate that bulk conductivities play a significant role in the charging of Kapton.

Hazelton, R. C.↗
NASA NTRS1982

Bonding procedure for Teflon seals

Material and bonding procedures designed for use as seals at the National Transonic Facility at the NASA Langley Research Center are presented. Teflon TFE was chosen for its ability to withstand pressures of up to 130 psi and temperatures ranging from -320 to 150 F, in addition to tolerances of 0.074 in. and having a movement allowance of 0.75 in. during transient cycles. Since some of the seals are 14 in. in diameter, Teflon sheets had to be sliced and bonded together after machining to size, resulting in seals with circular, oval, straight, and rectangular cross sections. Step-by-step preparation procedures are provided, and it is noted that the scarf joints performed as predicted during tests.

Barringer, S. R.↗
NASA NTRS1985

Degradation studies of SMRM Teflon

A working group was organized to study materials and components of the Solar Max Satellite (SMS) that was returned by the STS 41C. These materials were exposed in space for 50 months and represent the only real time long term exposure data available to date. In the molecular modeling of material and energetic oxygen atom interaction, it is pointed out that the importance of developing correlation between accelerated exposure data from STS and some real time data. In particular, it was predicted that Teflon which showed no detectable degradation on various STS flights may be susceptible to atomic oxygen degradation under real time conditions. Initial inspection of returned SMS samples showed that Teflon suffered visual damage such as cracking and yellowing. The results of examination of these samples are given.

Liang, R. H.↗
NASA NTRS1991

Evaluation of Surlyn 8920 as PHE Visor Material and Evaluations of New Adhesives for Improving Bonding Between Teflon and Stainless Steel at Cryogenic Temperature

Two studies are presented, and in the first study, Surlyn 8920 (an ionic and amorphous low density polyethylene made by Dupont) was evaluated as a possible replacement of Plexyglass G as PHE visor material. Four formulations of the polymer were made by adding different amounts of UV stabilizer, energy quencher, and antioxident in a Brabender Plasticorder. The formulated polymers were molded in the form of sheets in a compression molder. Cut samples from the molded sheets were exposed in a weatherometer and tested on Instron Tensile Tester for strength and elongation. Specially molded samples of the formulated polymers were subjected to Charpy Impact Tests. In the second study, preliminary evaluations of adhesives for improvement of bonding between Teflon and stainless steel (SS) were performed. Kapton, a high temperature polyimide made by Dupont, and a rubber based adhesive made by Potter Paint Co., were evaluated against industrial quality epoxy, the current material used to bond Teflon and SS. The degreased surfaces of the SS discs were etched mechanically, with a few of these etched chemically. The surfaces of the SS discs were etched mechanically, with a few of these etched chemically. Bonding strengths were evaluated using lap shear tests on the Instron Tensile Tester for the samples bonded by Kapton and industrial quality epoxy. Bond strengths were also evaluated using a pull test on the Instron for the samples bonded by Potter adhesive (CWL-152) and industrial quality epoxy. Based on limited lap shear data, Kapton gave bond strength favorable compared to that of industrial epoxy. Based on limited pull test data, Kapton bonded and CWL-152 bonded samples showed poor strength compared to epoxy bonded sample.

Ray, Asit K.↗
NASA NTRS1992

Silver Teflon blanket: LDEF tray C-08

A study of the Teflon blanket surface at the edge of tray C-08 illustrates the complexity of the microenvironments on the Long Duration Exposure Facility (LDEF). The distribution of particulate contaminants varied dramatically over a distance of half a centimeter (quarter of an inch) near the edge of the blanket. The geometry and optical effects of the atomic oxygen erosion varied significantly over the few centimeters where the blanket folded over the edge of the tray resulting in a variety of orientations to the atomic oxygen flux. A very complex region of combined mechanical and atomic oxygen damage occurred where the blanket contacted the edge of the tray. A brown film deposit apparently fixed by ultraviolet light traveling by reflection through the Teflon film was conspicuous beyond the tray contract zone. Chemical and structural analysis of the surface of the brown film and beyond toward the protected edge of the blanket indicated some penetration of energetic atomic oxygen at least five millimeters past the blanket-tray contact interface.

Crutcher, E. Russ↗
NASA NTRS1993

Performance of silvered Teflon (trademark) thermal control blankets on spacecraft

Silverized Teflon (Ag/FEP) is a widely used passive thermal control material for space applications. The material has a very low alpha/e ratio (less than 0.1) for low operating temperatures and is fabricated with various FEP thicknesses (as the Teflon thickness increases, the emittance increases). It is low outgassing and, because of its flexibility, can be applied around complex, curved shapes. Ag/FEP has achieved multiyear lifetimes under a variety of exposure conditions. This has been demonstrated by the Long Duration Exposure Facility (LDEF), Solar Max, Spacecraft Charging at High Altitudes (SCATHA), and other flight experiments. Ag/FEP material has been held in place on spacecraft by a variety of methods: mechanical clamping, direct adhesive bonding of tapes and sheets, and by Velcro(TM) tape adhesively bonded to back surfaces. On LDEF, for example, 5-mil blankets held by Velcro(TM) and clamping were used for thermal control over 3- by 4-ft areas on each of 17 trays. Adhesively bonded 2- and 5-mil sheets were used on other LDEF experiments, both for thermal control and as tape to hold other thermal control blankets in place. Performance data over extended time periods are available from a number of flights. The observed effects on optical properties, mechanical properties, and surface chemistry will be summarized in this paper. This leads to a discussion of performance life estimates and other design lessons for Ag/FEP thermal control material.

Pippin, Gary↗
NASA NTRS1994

Experimental impacts into Teflon targets and LDEF thermal blankets

The Long Duration Exposure Facility (LDEF) exposed approximately 20 sq m of identical thermal protective blankets, predominantly on the Ultra-Heavy Cosmic Ray Experiment (UHCRE). Approximately 700 penetration holes greater than 300 micron in diameter were individually documented, while thousands of smaller penetrations and craters occurred in these blankets. As a result of their 5.7 year exposure and because they pointed into a variety of different directions relative to the orbital motion of the nonspinning LDEF platform, these blankets can reveal important dynamic aspects of the hypervelocity particle environment in near-earth orbit. The blankets were composed of an outer teflon layer (approximately 125 micron thick), followed by a vapor-deposited rear mirror of silver (less than 1000 A thick) that was backed with an organic binder and a thermal protective paint (approximately 50 to 75 micron thick), resulting in a cumulative thickness (T) of approximately 175 to 200 microns for the entire blanket. Many penetrations resulted in highly variable delaminations of the teflon/metal or metal/organic binder interfaces that manifest themselves as 'dark' halos or rings, because of subsequent oxidation of the exposed silver mirror. The variety of these dark albedo features is bewildering, ranging from totally absent, to broad halos, to sharp single or multiple rings. Over the past year experiments were conducted over a wide range of velocities (i.e., 1 to 7 km/s) to address velocity dependent aspects of cratering and penetrations of teflon targets. In addition, experiments were performed with real LDEF thermal blankets to duplicate the LDEF delaminations and to investigate a possible relationship of initial impact conditions on the wide variety of dark halo and ring features.

Hoerz, F.↗