NASA NTRS2003

Damage Assessment of Stress-Thermal Cycled High Temperature

We report on the characterization of bismaleimide and polyimide carbon fiber composite, microcrack development under stress thermal cycling loading. Such cycle range from cryogenic temperatures associated with cryogenic fuel (LN, LOX) containment to high temperatures of 300 degrees associated with future hypervelocity aeropropulsion systems. Microcrack development thresholds as a function of temperature range of the thermal cycle, the number of cycles, and the applied stress level imposed on the composite are reported. We have conducted stress-thermal cycles on thin bismaleimide-woven carbon fiber foils for three temperature range cycles. The principle findings are that the full cycles from -196 degree celsius up to 250 degree celsius cause the most significant microcrack development. These observations indicate that the high temperature portion of the cycle under load causes fiber-matrix interface failure and subsequent exposure to higher stresses at the cryogenic, low temperature region results in composite matrix microcracking as a result of the additional stresses associated with the fiber-matrix thermal expansion mismatch. Our initial studies for 12 ply PMR-II-50 polyimide/M6OJB carbon fabric [0f, 90f, 90f, 0f, 0f, 90f] composites will be presented. The stress-thermal cycle test procedure for these will be described. Moisture absorption characteristics between cycles will be used to monitor interconnected microcrack development. The applied stress level will be 75 percent of the composite cryogenic -196 degree celsius ultimate strength.

Ju, Jach-Yung↗
NASA NTRS2004

Ultrasonic Guided-Wave Scan System Used to Characterize Microstructure and Defects in Ceramic Composites

Ceramic matrix composites (CMCs) are being developed for advanced aerospace propulsion applications to save weight, improve reuse capability, and increase performance. However, mechanical and environmental loads applied to CMCs can cause discrete flaws and distributed microdamage, significantly reducing desirable physical properties. Such microdamage includes fiber/matrix debonding (interface failure), matrix microcracking, fiber fracture and buckling, oxidation, and second phase formation. A recent study (ref. 1) of the durability of a C/SiC CMC discussed the requirement for improved nondestructive evaluation (NDE) methods for monitoring degradation in these materials. Distributed microdamage in CMCs has proven difficult to characterize nondestructively because of the complex microstructure and macrostructure of these materials. This year, an ultrasonic guided-wave scan system developed at the NASA Glenn Research Center was used to characterize various microstructural and flaw conditions in SiC/SiC (silicon carbide fiber in silicon carbide matrix) and C/SiC (carbon fiber in silicon carbide matrix) CMC samples.

Roth, Don J.↗
NASA NTRS2004

Damage Assessment of Stress-Thermal Cycled high temperature

We report on the characterization of bismaleimide and polyimide carbon fiber composite, microcrack development under stress thermal cycling loading. Such cycles range from cryogenic temperatures associated with cryogenic fuel (LN, LOX) containment to high temperatures of 300 degrees Celsius associated with future hypervelocity aeropropulsion systems. Microcrack development thresholds as a function of temperature range of the thermal cycle; the number of cycles; the applied stress level imposed on the composite are reported. We have conducted stress-thermal cycles on thin bismaleimide-woven carbon fiber foils for three temperature range cycles: 1. Ambient temperature - -196 degrees celsius. 2. Ambient temperature - 150 degrees Celsius; 200 degrees Celsius; 250 degrees Celsius. 3. -196 degrees Celsius - 250 degrees Celsius. The Principle findings are that the full cycles from -196 degrees Celsius to to 250 degrees Celsius cause the most significant microcrack of development. These observations indicate that the high temperature portion of the cycle under load causes fiber-matrix interface failure and subsequent exposure to higher stresses at the cryogenic, low temperature region results in composite matrix microcracking as a result of the additional stresses associate with the fiber-matrix thermal expansion mismatch. Our initial studies for 12 ply PMR-II-50 polyimide/M60JB carbon fabric [0f,90f,90f,0f,0f,90f]ls composites will be presented. The stress-thermal cycle test procedure for these will be described. Moisture absorption characteristics between cycles will be used to monitor interconnected microcrack development. The applied stress level will be 75% of the composite cryogenic (-196 degrees Celsius) ultimate strength.

Ju, Jae-Hyung↗
NASA NTRS2003

High-Performance Acousto-Ultrasonic Scan System Being Developed

Acousto-ultrasonic (AU) interrogation is a single-sided nondestructive evaluation (NDE) technique employing separated sending and receiving transducers. It is used for assessing the microstructural condition and distributed damage state of the material between the transducers. AU is complementary to more traditional NDE methods, such as ultrasonic cscan, x-ray radiography, and thermographic inspection, which tend to be used primarily for discrete flaw detection. Throughout its history, AU has been used to inspect polymer matrix composites, metal matrix composites, ceramic matrix composites, and even monolithic metallic materials. The development of a high-performance automated AU scan system for characterizing within-sample microstructural and property homogeneity is currently in a prototype stage at NASA. This year, essential AU technology was reviewed. In addition, the basic hardware and software configuration for the scanner was developed, and preliminary results with the system were described. Mechanical and environmental loads applied to composite materials can cause distributed damage (as well as discrete defects) that plays a significant role in the degradation of physical properties. Such damage includes fiber/matrix debonding (interface failure), matrix microcracking, and fiber fracture and buckling. Investigations at the NASA Glenn Research Center have shown that traditional NDE scan inspection methods such as ultrasonic c-scan, x-ray imaging, and thermographic imaging tend to be more suited to discrete defect detection rather than the characterization of accumulated distributed micro-damage in composites. Since AU is focused on assessing the distributed micro-damage state of the material in between the sending and receiving transducers, it has proven to be quite suitable for assessing the relative composite material state. One major success story at Glenn with AU measurements has been the correlation between the ultrasonic decay rate obtained during AU inspection and the mechanical modulus (stiffness) seen during fatigue experiments with silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite samples. As shown in the figure, ultrasonic decay increased as the modulus decreased for the ceramic matrix composite tensile fatigue samples. The likely microstructural reason for the decrease in modulus (and increase in ultrasonic decay) is the matrix microcracking that commonly occurs during fatigue testing of these materials. Ultrasonic decay has shown the capability to track the pattern of transverse cracking and fiber breakage in these composites.

Roth, Don J.↗
NASA NTRS2003

High-Performance Acousto-Ultrasonic Scan System Being Developed

Acousto-ultrasonic (AU) interrogation is a single-sided nondestructive evaluation (NDE) technique employing separated sending and receiving transducers. It is used for assessing the microstructural condition and distributed damage state of the material between the transducers. AU is complementary to more traditional NDE methods, such as ultrasonic cscan, x-ray radiography, and thermographic inspection, which tend to be used primarily for discrete flaw detection. Throughout its history, AU has been used to inspect polymer matrix composites, metal matrix composites, ceramic matrix composites, and even monolithic metallic materials. The development of a high-performance automated AU scan system for characterizing within-sample microstructural and property homogeneity is currently in a prototype stage at NASA. This year, essential AU technology was reviewed. In addition, the basic hardware and software configuration for the scanner was developed, and preliminary results with the system were described. Mechanical and environmental loads applied to composite materials can cause distributed damage (as well as discrete defects) that plays a significant role in the degradation of physical properties. Such damage includes fiber/matrix debonding (interface failure), matrix microcracking, and fiber fracture and buckling. Investigations at the NASA Glenn Research Center have shown that traditional NDE scan inspection methods such as ultrasonic c-scan, x-ray imaging, and thermographic imaging tend to be more suited to discrete defect detection rather than the characterization of accumulated distributed microdamage in composites. Since AU is focused on assessing the distributed microdamage state of the material in between the sending and receiving transducers, it has proven to be quite suitable for assessing the relative composite material state. One major success story at Glenn with AU measurements has been the correlation between the ultrasonic decay rate obtained during AU inspection and the mechanical modulus (stiffness) seen during fatigue experiments with silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite samples. As shown in the figure, ultrasonic decay increased as the modulus decreased for the ceramic matrix composite tensile fatigue samples. The likely microstructural reason for the decrease in modulus (and increase in ultrasonic decay) is the matrix microcracking that commonly occurs during fatigue testing of these materials. Ultrasonic decay has shown the capability to track the pattern of transverse cracking and fiber breakage in these composites.

Roth, Don J.↗
NASA NTRS2005

Ultrasonic Guided-Wave-Scan System Used to Characterize C-Enhanced Silicon Carbide Composite During Creep- Rupture Tests

Ceramic matrix composites (CMCs) are being developed for advanced aerospace propulsion applications in order to save weight, improve reuse capability, and increase performance. However, mechanical and environmental loads applied to CMCs can cause degradation in the form of discrete flaws and distributed microdamage that can play a significant role in reducing desirable physical properties. Categories of microdamage include fiber/matrix debonding (interface failure), matrix microcracking, fiber fracture and buckling, oxidation, and second-phase formation. Distributed microdamage in CMCs has proven difficult to characterize nondestructively because of the complex microstructure and macrostructure of these materials, and a recent study regarding the durability of a ceramic matrix composite discussed the requirement for improved nondestructive evaluation (NDE) methods for monitoring degradation in these materials.

Roth, Don J.↗
NASA NTRS2011

Moisture-Induced TBC Spallation on Turbine Blade Samples

Delayed failure of TBCs is a widely observed laboratory phenomenon, although many of the early observations went unreported. "The weekend effect" or "DeskTop Spallation" (DTS) is characterized by initial survival of a TBC after accelerated laboratory thermal cycling, then failure by exposure to ambient humidity or water. Once initiated, failure can occur quite dramatically in less than a second. To this end, the water drop test and digital video recordings have become useful techniques in studies at NASA (Smialek, Zhu, Cuy), DECHMA (Rudolphi, Renusch, Schuetze), and CNRS Toulouse/SNECMA (Deneux, Cadoret, Hervier, Monceau). In the present study the results for a commercial turbine blade, with a standard EB-PVD 7YSZ TBC top coat and Pt-aluminide diffusion bond monitored by weight change and visual appearance. Failures were distributed widely over a 5-100 hr time range, depending on temperature. At some opportune times, failure was captured by video recording, documenting the appearance and speed of the moisture-induced spallation process. Failure interfaces exhibited alumina scale grains, decorated with Ta-rich oxide particles, and alumina inclusions as islands and streamers. The phenomenon is thus rooted in moisture-induced delayed spallation (MIDS) of the alumina scale formed on the bond coat. In that regard, many studies show the susceptibility of alumina scales to moisture, as long as high strain energy and a partially exposed interface exist. The latter conditions result from severe cyclic oxidation conditions, which produce a highly stressed and partially damaged scale. In one model, it has been proposed that moisture reacts with aluminum in the bond coat to release hydrogen atoms that 'embrittle' the interface. A negative synergistic effect with interfacial sulfur is also invoked.

Smialek, James L.↗
NASA NTRS2011

Moisture-Induced TBC Spallation on Turbine Blade Samples

Delayed failure of TBCs is a widely observed laboratory phenomenon, although many of the early observations went unreported. The weekend effect or DeskTop Spallation (DTS) is characterized by initial survival of a TBC after accelerated laboratory thermal cycling, then failure by exposure to ambient humidity or water. Once initiated, failure can occur quite dramatically in less than a second. To this end, the water drop test and digital video recordings have become useful techniques in studies at NASA (Smialek, Zhu, Cuy), DECHMA (Rudolphi, Renusch, Schuetze), and CNRS Toulouse/SNECMA (Deneux, Cadoret, Hervier, Monceau). In the present study the results for a commercial turbine blade, with a standard EB-PVD 7YSZ TBC top coat and Pt-aluminide diffusion bond coat are reported. Cut sections were intermittently oxidized at 1100, 1150, and 1200 C and monitored by weight change and visual appearance. Failures were distributed widely over a 5-100 hr time range, depending on temperature. At some opportune times, failure was captured by video recording, documenting the appearance and speed of the moisture-induced spallation process. Failure interfaces exhibited alumina scale grains, decorated with Ta-rich oxide particles, and alumina inclusions as islands and streamers. The phenomenon is thus rooted in moisture-induced delayed spallation (MIDS) of the alumina scale formed on the bond coat. In that regard, many studies show the susceptibility of alumina scales to moisture, as long as high strain energy and a partially exposed interface exist. The latter conditions result from severe cyclic oxidation conditions, which produce a highly stressed and partially damaged scale. In one model, it has been proposed that moisture reacts with aluminum in the bond coat to release hydrogen atoms that embrittle the interface. A negative synergistic effect with interfacial sulfur is also invoked.

Smialek, James↗
NASA NTRS2002

Application of Interface Technology in Progressive Failure Analysis of Composite Panels

A progressive failure analysis capability using interface technology is presented. The capability has been implemented in the COMET-AR finite element analysis code developed at the NASA Langley Research Center and is demonstrated on composite panels. The composite panels are analyzed for damage initiation and propagation from initial loading to final failure using a progressive failure analysis capability that includes both geometric and material nonlinearities. Progressive failure analyses are performed on conventional models and interface technology models of the composite panels. Analytical results and the computational effort of the analyses are compared for the conventional models and interface technology models. The analytical results predicted with the interface technology models are in good correlation with the analytical results using the conventional models, while significantly reducing the computational effort.

Sleight, D. W.↗
NASA NTRS2010

Modeling Geometry and Progressive Failure of Material Interfaces in Plain Weave Composites

A procedure combining a geometrically nonlinear, explicit-dynamics contact analysis, computer aided design techniques, and elasticity-based mesh adjustment is proposed to efficiently generate realistic finite element models for meso-mechanical analysis of progressive failure in textile composites. In the procedure, the geometry of fiber tows is obtained by imposing a fictitious expansion on the tows. Meshes resulting from the procedure are conformal with the computed tow-tow and tow-matrix interfaces but are incongruent at the interfaces. The mesh interfaces are treated as cohesive contact surfaces not only to resolve the incongruence but also to simulate progressive failure. The method is employed to simulate debonding at the material interfaces in a ceramic-matrix plain weave composite with matrix porosity and in a polymeric matrix plain weave composite without matrix porosity, both subject to uniaxial cyclic loading. The numerical results indicate progression of the interfacial damage during every loading and reverse loading event in a constant strain amplitude cyclic process. However, the composites show different patterns of damage advancement.

Hsu, Su-Yuen↗
NASA NTRS2002

NESTEM-QRAS: A Tool for Estimating Probability of Failure

An interface between two NASA GRC specialty codes, NESTEM and QRAS has been developed. This interface enables users to estimate, in advance, the risk of failure of a component, a subsystem, and/or a system under given operating conditions. This capability would be able to provide a needed input for estimating the success rate for any mission. NESTEM code, under development for the last 15 years at NASA Glenn Research Center, has the capability of estimating probability of failure of components under varying loading and environmental conditions. This code performs sensitivity analysis of all the input variables and provides their influence on the response variables in the form of cumulative distribution functions. QRAS, also developed by NASA, assesses risk of failure of a system or a mission based on the quantitative information provided by NESTEM or other similar codes, and user provided fault tree and modes of failure. This paper will describe briefly, the capabilities of the NESTEM, QRAS and the interface. Also, in this presentation we will describe stepwise process the interface uses using an example.

Patel, Bhogilal M.↗
NASA NTRS1990

Surface Cracking and Interface Reaction Associated Delamination Failure of Thermal and Environmental Barrier

In this paper, surface cracking and interface reactions of a ZrO2-8wt%Y2O3 and mullite/BSAS/Si thermal and environmental barrier coating system on SiC/SiC ceramic matrix composites were characterized after long-term combined laser thermal gradient and furnace cyclic tests in a water vapor containing environment. The surface cracking was analyzed based on the coating thermal gradient sintering behavior and thermal expansion mismatch stress characteristics under the thermal cyclic conditions. The interface reactions that were largely enhanced by the coating surface cracking in the water vapor environment were investigated in detail, and the reaction phases were identified for the coating system after the long-term exposure. The accelerated coating delamination failure was attributed to the increased delamination driving force under the thermal gradient cyclic loading and the reduced interface adhesion due to the detrimental interface reactions. The coating design issues will also be discussed based on the observed failure mechanisms under the high-heat-flux test conditions.

Zhu, Dongming↗
NASA NTRS2003

Surface Cracking and Interface Reaction Associated Delamination Failure of Thermal and Environmental Barrier Coatings

In this paper, surface cracking and interface reactions of a BSAS coating and a multi-layer ZTO2-8wt%Y2O3 and mullite/BSAS/Si thermal and environmental barrier coating system on SiC/SiC ceramic matrix composites were characterized after long-term combined laser thermal gradient and furnace cyclic tests in a water vapor containing environment. The surface cracking was analyzed based on the coating thermal gradient sintering behavior and thermal expansion mismatch stress characteristics under the thermal cyclic conditions. The interface reactions, which were largely enhanced by the coating surface cracking in the water vapor environment, were investigated in detail, and the reaction phases were identified for the coating system after the long- term exposure. The accelerated coating delamination failure was attributed to the increased delamination driving force under the thermal gradient cyclic loading and the reduced interface adhesion due to the detrimental interface reactions.

Zhu, Dongming↗
NASA NTRS2003

Surface Cracking and Interface Reaction Associated Delamination Failure of Thermal and Environmental Barrier Coatings

In this paper, surface cracking and interface reactions of a BSAS coating and a multi-layer ZrO2-8wt%Y2O3 and mullite/BSAS/Si thermal and environmental barrier coating system on SiC/SiC ceramic matrix composites were characterized after long-term combined laser thermal gradient and furnace cyclic tests in a water vapor containing environment. The surface cracking was analyzed based on the coating thermal gradient sintering behavior and thermal expansion mismatch stress characteristics under the thermal cyclic conditions. The interface reactions, which were largely enhanced by the coating surface cracking in the water vapor environment, were investigated in detail, and the reaction phases were identified for the coating system after the long-term exposure. The accelerated coating delamination failure was attributed to the increased delamination driving force under the thermal gradient cyclic loading and the reduced interface adhesion due to the detrimental interface reactions.

Zhu, Dong-Ming↗
NASA NTRS2013

Nickel-Graphite Composite Compliant Interface and/or Hot Shoe Material

Next-generation high-temperature thermoelectric-power-generating devices will employ segmented architectures and will have to reliably withstand thermally induced mechanical stresses produced during component fabrication, device assembly, and operation. Thermoelectric materials have typically poor mechanical strength, exhibit brittle behavior, and possess a wide range of coefficient of thermal expansion (CTE) values. As a result, the direct bonding at elevated temperatures of these materials to each other to produce segmented leg components is difficult, and often results in localized microcracking at interfaces and mec hanical failure due to the stresses that arise from the CTE mismatch between the various materials. Even in the absence of full mechanical failure, degraded interfaces can lead to increased electrical and thermal resistances, which adversely impact conversion efficiency and power output. The proposed solution is the insertion of a mechanically compliant layer, with high electrical and thermal conductivity, between the low- and high-temperature segments to relieve thermomechanical stresses during device fabrication and operation. This composite material can be used as a stress-relieving layer between the thermoelectric segments and/or between a thermoelectric segment and a hot- or cold-side interconnect material. The material also can be used as a compliant hot shoe. Nickel-coated graphite powders were hot-pressed to form a nickel-graphite composite material. A freestanding thermoelectric segmented leg was fabricated by brazing the compliant pad layer between the high-temperature p- Zintl and low-temperature p-SKD TE segments using Cu-Ag braze foils. The segmented leg stack was heated in vacuum under a compressive load to achieve bonding. The novelty of the innovation is the use of composite material that re duces the thermomechanical stresses en - countered in the construction of high-efficiency, high-temperature therm - o-electric devices. The compliant pad enables the bonding of dissimilar thermoelectric materials while maintaining the desired electrical and thermal properties essential for efficient device operation. The modulus, CTE, electrical, and thermal conductances of the composite can be controlled by varying the ratio of nickel to graphite.

Firdosy, Samad A.↗
DOE OSTI2025

Investigation of the Mechanical Degradation of Zinc-Based Cold Spray Coatings for Steel Pipelines

Internal corrosion in wet natural gas is a big challenge in the oil and gas industry due to corrosive constituents such as carbon dioxide (CO2), hydrogen sulfide (H2S), other forms of sulfur, and water in the gas stream. To mitigate internal corrosion, zinc-based cold spray coatings were designed for use in natural gas pipelines to increase the lifespan of the pipeline network. However, one of the requirements in designing internal coatings is the resistance of the coatings to mechanical forces applied on the pipeline's internal wall during pigging operations. These forces are primarily compressive and shear/friction forces. This study examines material properties that must be considered when evaluating mechanical considerations. To determine the viability of the developed coatings with respect to the shear/friction forces, the shear adhesion and wear resistance of the materials have been evaluated. Shear adhesion testing was performed with modified clevises to determine the shear stress required to cause adhesion failure at the coating/substrate interface. Scanning electron microscopy was utilized to characterize the interfaces after failure. Wear testing was performed on coatings and pipeline materials utilizing pin-on-drum testing. These tests display the stress limitations and wear that the coatings can tolerate from pigging.

mechanical degradation↗
DOE OSTI2023

Interface microstructure effects on dynamic failure behavior of layered Cu/Ta microstructures

Abstract Structural metallic materials with interfaces of immiscible materials provide opportunities to design and tailor the microstructures for desired mechanical behavior. Metallic microstructures with plasticity contributors of the FCC and BCC phases show significant promise for damage-tolerant applications due to their enhanced strengths and thermal stability. A fundamental understanding of the dynamic failure behavior is needed to design and tailor these microstructures with desired mechanical responses under extreme environments. This study uses molecular dynamics (MD) simulations to characterize plasticity contributors for various interface microstructures and the damage evolution behavior of FCC/BCC laminate microstructures. This study uses six model Cu/Ta interface systems with different orientation relationships that are as- created, and pre-deformed to understand the modifications in the plasticity contributions and the void nucleation/evolution behavior. The results suggest that pre-existing misfit dislocations and loading orientations (perpendicular to and parallel to the interface) affect the activation of primary and secondary slip systems. The dynamic strengths are observed to correlate with the energy of the interfaces, with the strengths being highest for low-energy interfaces and lowest for high-energy interfaces. However, the presence of pre-deformation of these interface microstructures affects not only the dynamic strength of the microstructures but also the correlation with interface energy.

42 ENGINEERING↗