DOE OSTI2024

Characterization of Stress-Corrosion-Cracking in Plutonium-Bearing Storage Containers

Introduction • The Integrated Surveillance Program, under the Department of Energy, is responsible for the periodic surveillance of storage containers containing plutonium-bearing materials. • The container-packages are designed to isolate the materials for 50 to 100 years with minimal surveillance. • During monitoring, corrosion-pitting and stress-corrosion-cracking (SCC) has been identified in some of the inner-cans near the weld regions. • SCC through wall penetration would result in an undesired increased risk of leakage. • An investigation is in progress to identify and characterize corrosion events to determine the prevalence of corrosion features and the likelihood of a throughwall breach. • Here, we discuss the characterization efforts carried out by Scanning Electron Microscopy (SEM), including 3D-tomography by Focused Ion Beam (FIB) methods.

Perez, Emmanuel E.↗
DOE OSTI2020

Progress on Advancing the Robotic Air-slot Volumetric Inspection System (RAVIS) for Hanford Under-tank Inspection - 20519

The 27 in-service double-shell tank (DST) systems at Hanford provide interim storage for nearly 56 million gallons of nuclear and hazardous chemical legacy waste. The safe and reliable storage of the waste is critical to the site's extended cleanup mission. While in service, the leak integrity of the DSTs must be demonstrated to satisfy the Washington Administrative Code, inform decisions on tank management, and gauge fitness for continued service beyond originally intended design lives. The carbon steel plates and welds that comprise DST primary tank sidewalls and lower knuckles are routinely 'sampled' for volumetric non-destructive testing using ultrasonic inspection technology to determine whether corrosion pitting, cracking, or general corrosion are occurring that could compromise tank leak integrity. However, the carbon steel plates and welds that comprise the bottoms of primary tanks have not been thoroughly inspected since the DSTs were constructed (i.e., since 1968-1986) due to limited physical access to the exterior tank bottoms. The Robotic Air-slot Volumetric Inspection System, or 'RAVIS,' is being engineered to overcome the challenge of tank bottom in-service inspection. The system will be deployed under primary tanks within the small cooling channels/air-slots in the refractory pads upon which the tanks rest and will use ultrasonic guided wave inspection technology to volumetrically inspect physically inaccessible regions that make up ∼90% of a tank bottom, as well as regions that are physically accessible from the air-slots but comprise only ∼10% of a tank bottom. This paper describes the air-slot sensor and robotic deployment system and focuses on the testing approach and methods that are being applied to support (1) design feedback and performance acceptance (requirement verification) and (2) performance repeatability/reliability assessments (qualification) to ensure the RAVIS is prepared for successful inservice inspections of primary tank bottoms. Test progress made against the test plan, the results of 2019 testing, and the future outlook are included. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2020

Augmented Monitoring and Condition Assessment Program for SNF Wet Storage Life Extension - 20489

Approximately 27 MTHM of spent nuclear fuel (SNF) owned and managed by the U.S. Department of Energy, Office of Environmental Management is stored in the L Basin at the Savannah River Site (SRS). This 'DOE SNF' is comprised of approximately 12,000 aluminum-clad, aluminum-based fuel assemblies (∼7 MTHM), and approximately 2000 non-aluminum fuel assemblies (∼20 MTHM). A program is in progress to perform Non-Destructive Examination (NDE) of the fuel and their storage containers to characterize the materials' condition, and to evaluate the effects of service to enable continued safe wet storage of the SNF. The Augmented Monitoring and Condition Assessment Program (AMCAP), a two-part program to develop and implement remote underwater Non-Destructive Examination of the aluminum SNF, and of the containers of the non-aluminum SNF, respectively, is aimed at the characterization and evaluation of corrosion degradation of aluminum fuel and container materials. The predominant design of the aluminum SNF (ASNF) stored in L Basin is the Materials Test Reactor (MTR) equivalent design, a plate fuel design. These SNF are stored in 5'' diameter tubes or 5'' x 5'' squares (called bundles) that are nominally 12' or up to 14' long. The SNF is de-bundled and inspected using a custom-designed MTR Fuel Inspection Table. The inspection table provides for indexed fuel positioning for a video camera examination with controlled lighting. A total of 10 of the SNF originating from foreign research and test reactors were selected for examination based on burnup, enrichment, and prior damage caused by service/storage history. A special inspection campaign of these 10 assemblies is in progress. The observed corrosion damage included minor to moderate attack from general corrosion, pitting, crevice, end grain and galvanic corrosion. Example results from the completed inspections are shown and discussed. The focus is a comparison of the as-received condition versus the as-found current storage condition that will serve to validate Water Chemistry and Corrosion Monitoring Programs. The non-aluminum SNF (NASNF) stored in L Basin are of diverse design that includes various geometries with claddings of stainless steel, Zircaloy, and Hastelloy. The fuel core materials include uranium alloys, oxides/mixed oxides, and carbides. These SNF materials, originating from early experimental and test reactors, are in various physical forms including single fuel elements and cut pieces. The fuel is stored in L Basin in various configurations including in direct bundled storage in aluminum tubes and in isolation cans that are in the bundles or in a larger over-size storage container (OSC). Concern with inside-out corrosion and the potential loss of configuration control and ability to handle the storage containers prompted the development of remote NDE methods that include visual and UT technologies to assess the condition of the containers. Candidate stored materials were selected for a special inspection campaign; the development of the NDE methods for the inspection for galvanic, crevice and sediment-induced corrosion (inside-out) are discussed. A summary of the SNF storage in L Basin at the SRS, and an overview of the AMCAP to enable continued safe storage of DOE SNF are described. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2022

Effect of thermal aging on corrosion behavior of duplex stainless steels

Abstract Despite their exceptional mechanical and corrosion properties, duplex stainless steels (DSS) have not found widespread use in high-temperature applications due to concerns over thermal aging and embrittlement at elevated operational temperatures (> 300 °C). The present study investigated the effect of thermal aging time on the electrochemical properties of lean and standard grade DSS that are exposed to a range of pressurized water reactors containing LiOH and H 3 BO 3 . The results indicated that the electrolyte chemistry plays a significant role in the corrosion behavior of the DSS alloys. Corrosion resistance decreased with thermal aging time for all DSS alloys; however, standard grade DSS (2205 and 2209-w) alloys showed better corrosion resistance than lean grades (2003, 2101, 2101-w). The presence of dissolved oxygen in the electrolytes resulted in a significant increase in corrosion rate for the DSS alloys, but it did not affect the general trend of corrosion rates with aging time. All DSS alloys became vulnerable to pitting corrosion due to chloride addition, but the pitting resistance decreased with increasing thermal aging time. Increased boron B content resulted in degradation of corrosion resistance of the DSS alloys, while minor changes in pH did not show a significant change in corrosion resistance. Mechanical and metallurgical characterization coupled with electrochemical characterization of the DSS alloys gave a comprehensive insight into the effects of thermal aging on the electrochemical response of the DSS. Graphical abstract

Murkute, Pratik (ORCID:0000000278636346)↗
DOE OSTI2024

Effect of Minor Ce Additions on Corrosion Behavior of Experimental Pipeline Steel

Minor additions of rare earth elements (REEs) have been shown to improve various steel properties. In particular, Cerium (Ce), as a relatively abundant and inexpensive element, has received attention as a potentially beneficial minor alloying addition for a variety of steel applications, including pipelines materials. The objective of this work is to investigate the effect of Ce on corrosion performance of experimental high-strength pipeline steel. Electrochemical corrosion experiments were carried out on steel without and with 0.006, 0.018, and 0.03 wt.% of Ce in 3.5 wt.% NaCl saturated with CO2 at 20 oC. For comparison purposes, X100 carbon steel specimens machined from an experimental pipe with a yield strength of 731 MPa were tested under the same conditions. The electrochemical techniques employed included: potentiodynamic polarization (PDP), linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS). In addition, post-corrosion surface characterization was performed using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS), while crystalline phases were determined by X-ray diffraction (XRD). The corrosion of base metal without Ce was lower (0.15 mm/y) compared to carbon steel X100 (0.9 mm/yr). The electrochemical results showed that adding Ce accelerates corrosion rates compared to base metal without Ce. No pitting corrosion of tested steel was detected.

Belarbi, Zineb↗
DOE OSTI2023

Directly monitoring the shift in corrosion mechanisms of a model FeCrNi alloy driven by electric potential

Abstract Stainless steels are used in a myriad of engineering applications, including construction, automobiles, and nuclear reactors. Developing accurate, predictive mechanistic models for corrosion and electrochemical corrosion kinetics of stainless steels has been a topic of research studies over many decades. Herein, we quantified the aqueous corrosion kinetics of a model austenitic Fe–18Cr–14Ni (wt%) alloy in the presence and absence of applied potential using systematic in situ electrochemical atomic force microscopy (EC-AFM) and transmission electron microscopy (TEM). Without an applied bias, vertical dissolution of corrosion pits is controlled by the surface kinetics/diffusion hybrid mechanism, whereas lateral dissolution is diffusion controlled. When an electric bias is applied, the increase in corrosion rate is dominated by the nucleation of new pits. These insights gained by the in situ EC-AFM will allow applications of this method for a quantitative understanding of corrosion of a wider class of materials.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Determining Drying Conditions to Mitigate Hanford Transfer Line Corrosion

Radioactive waste is stored in underground, carbon-steel double-shell tanks at the Department of Energy Hanford site.1,2,3 The underground transfer lines are used to transfer the waste between the tanks and other assets at the Hanford tank farm facilities. The transfer lines constructed before 1990 are pipe-in-pipe design with most of the lines having carbon steel carrier pipe and carbon steel encasements. The lines constructed after 1990 have a stainless-steel carrier with a carbon steel encasement. The carrier lines, which are in contact with the waste, provide a critical confinement function, while the encasements provide secondary containment to reduce the risk of a release and contamination to the environment. In 2022, a visual inspection of the annulus between the encasement and the carrier for one of the pre-1990 transfer lines revealed standing liquid in contact with the carrier pipe. Additionally, a significant build-up of corrosion products on the exterior of the carrier pipe and the interior of the encasement pipe was observed. To assess the extent of condition, borescope inspections were performed in the encasement space of additional transfer lines in the facility to provide a baseline. The inspection revealed that of the lines inspected, 29 had either moisture present or evidence that moisture had been present in the past (e.g., waterline corrosion where the pipe had been exposed to standing water). Additional inspections indicated several instances of pitting corrosion on the interior of the encasement and exterior the carrier transfer lines. An image of the carrier pipe with several pits is presented in Figure 1(a) and the profiled image of the transfer line section along with the pit depths are presented Figure 1(b). As seen in the figure, the deepest pit was 73 mils on the pipe section. These lines were designated as “do-not-use” until further compensatory actions are implemented to return the lines to service.

Shukla, Pavan K. [Savannah River National Laborato↗
DOE OSTI2023

Surface Film Formation on Al-V Alloys with Far-From-Equilibrium Microstructure

Nanocrystalline supersaturated Al-V alloys produced by high-energy ball milling have been reported to exhibit enhanced corrosion resistance and mechanical properties compared to commercial Al alloys. Corrosion of passive alloys such as Al-V alloy relies on the characteristics of the surface film, which is studied using scanning/transmission electron microscopy and time-of-flight secondary ion mass spectrometry. The effect of microstructure and composition on the surface film has been investigated after different immersion periods (30 min, 2 h, and 1 day) in 0.1 M NaCl. The surface film was complex and composed of oxidized Al and V. The heterogeneous surface film was observed due to the presence of secondary phases and initiation of localized corrosion. The void formation was observed beneath the surface film that would potentially cause pitting corrosion. The generation of nano-sized voids was dependent on grain orientation. Compared to pure Al, the chloride penetration is suppressed in Al-V alloys. The effect of composition and microstructure on surface film formation and attendant corrosion behavior is discussed herein.

36 MATERIALS SCIENCE↗
DOE OSTI2025

From Micro-environments to Macroscopic Effects: How the Alkaline Hydrogen Evolution Reaction Drives Cu Cathodic Corrosion

Cathodic corrosion of copper (Cu) has posed a significant challenge for over a century, impeding various technological progresses such as electrochemical conversion of CO 2 (eCO 2 RR) into fuels and other value-added carbon products. Here, in this study, employing a combined Density Functional Theory (DFT) and kinetic Monte Carlo (kMC) simulation approach, we delve into the atomistic level mechanism driving this phenomenon in Cu. Our hypothesis posits the pivotal role of alkaline hydrogen evolution reaction (HER) in facilitating cathodic corrosion in Cu. We rigorously develop a pH-dependent hydroxide (OH) adsorption mechanism and calculate the equilibrium OH coverage (𝜃 OH ) at varying pH levels, the thermodynamic stability of subsurface oxygen (O sub ), as well as the Cu-vacancy mediated diffusion of subsurface oxygens (O sub ). Through comprehensive analysis, we establish correlation among various microenvironments, including oxygen diffusion in subsurface layers, pH-dependent OH adsorption, and Cu dissolution into the electrolyte as (Cu-OH) complexes. Furthermore, our investigation explores the correlation between surface coordination environment of active sites and cathodic corrosion of Cu. Finally, by integrating DFT-derived thermodynamic data into a kMC model, we successfully predict the formation of experimentally observed corrosion pits on Cu-surfaces. This combined approach not only advances our fundamental understanding of Cu cathodic corrosion but also offers insights crucial for developing effective corrosion mitigation strategies.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

The Center for Performance and Design of Nuclear Waste Forms and Containers (WastePD) Energy Frontier Research Center (Final Report)

The DOE Office of Environmental Management is responsible for high level nuclear waste that must be safely isolated from humans and the environment for extremely long periods. The waste forms and containers are made of glass, ceramics, and metals. Verified safe disposal requires understanding the fundamental mechanisms of waste form degradation and the design of new waste forms with improved performance, which comprise the goals of the Energy Frontier Research Center known as the Center for the Performance and Design of Nuclear Waste Forms and Containers, WastePD. WastePD was constructed to develop innovative approaches and solutions to those goals through the synergistic interactions of individuals who are experts in the degradation behavior, modeling, and design of glasses, ceramics and metal alloys. WastePD is the first center ever created to address this diverse group of materials in a comprehensive and coordinated manner. The science goals are grouped into three common topics: corrosion mechanisms via advanced characterization, environmental impacts, and materials design. Synergistic interactions in these areas were a key component of WastePD. The fundamental understanding of the degradation mechanisms of the waste forms and containers as well as the development of new materials with improved properties will allow DOE to prevent environmental contamination and to explore totally new repository concepts. WastePD was operational from August 2016 through July 2022, but the DOE support was drastically reduced for the last two years. This final technical report covers the full period of performance. However, much of what was accomplished in the first four years is nicely summarized in a review paper published in 2021, which is appended to this report. Therefore, this final report focuses on the technical findings from the last two years of WastePD activities. Considerable progress was made in the areas of a) the environmental and compositional impacts on the corrosion of borosilicate and aluminosilicate glasses, b) the mechanism of glass corrosion and the structure and evolution of the surface alteration layer, c) the effects of environment and composition on the corrosion of pyrochlore, perovskite, hollandite, and other oxide ceramics, d) the corrosion mechanism of multi-principal element metallic alloys, and e) a new framework for understanding the pitting corrosion of metals.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2025

Slow Strain Rate Testing of A537 Tank Wall Material

At Savannah River Site (SRS), High-Level Waste is stored in below-grade carbon steel tanks. This waste in part consists of sludge, salt cake, and/or supernate. Preparation of this waste for future processing involves dissolution of the salt cake layer. The salt dissolution process can create conditions that leave the carbon steel tanks susceptible to localized corrosion. The salt to be dissolved contains high concentrations of nitrate, that once released, create an environment that may be conducive to pitting corrosion and/or stress corrosion cracking (SCC) of carbon steel. The salt dissolution process also liberates interstitial liquid trapped between the salt crystals. This liquid is initially high in nitrite and hydroxide concentration. High pH and greater ratios of nitrite to nitrate act as inhibitors to minimize corrosion of carbon steel in high nitrate environments. However, as dissolution proceeds, the concentration of nitrate will increase, while the hydroxide and nitrite concentration of the interstitial liquid will deplete and become insufficient to prevent the onset of corrosion attack. Tank blending and the addition of inhibitors are used to ensure adequate concentrations of hydroxide and nitrite. However, this is not desirable during salt dissolution as it can reduce process efficiency and increase the amount of waste that needs processing. This testing program was designed to examine the risk of SCC associated with utilizing the pitting factor (PF) and nitrite/nitrate (NO 2 - /NO 3 - ) ratio limits for handling dissolved salt solutions at an elevated temperature in the carbon steel waste tanks. The previously identified limits are a PF of 1.2 and an NO 2 - /NO 3 - ratio of 0.15. The results indicate that as long as the NO 2 - /NO 3 - ratio exceeds 0.1 and the PF is above approximately 0.8, there is a discernible safety margin between the open circuit potential (OCP) and the critical cracking potential (CCP) observed during applied potential testing. However, this margin, defined by the difference between the OCP and CCP, is relatively narrow, ranging from 0.1 to 0.25 volts. This small margin raises concerns about potential shifts in OCP during waste retrieval operations, which could inadvertently increase the risk of SCC if the OCP approaches or exceeds the CCP. These results confirm that dissolved salt solutions provide a potent chemistry that, under certain conditions, makes carbon steel susceptible to SCC. The next question to consider is the influence these results have on decisions for storage and retrieval of waste from the tanks. For Type III/IIIA waste tanks, the risk of SCC remains very low. First, and most importantly, the post-weld stress relief of the tanks has reduced the residual stress near the welds. Thus, without the stress component, SCC risk is minimized. The material of construction (A537 Carbon steel) for the Type III/IIIA tanks is superior to the steel in its resistance to SCC than the steel that was utilized for the Type I, II, and IV tanks (A285 carbon steel). From a chemistry control standpoint for a Type III/IIIA tank directly involved with handling dissolved salt solutions, the PF and NO 2 - /NO 3 - ratio limits may be utilized wherein chemistry control provides an extra layer of defense against SCC. Chemistry control for a Type III/IIIA tank minimizes the risk for a tank that may receive the dissolved salt solution, particularly if that tank is a Type I, II, or IV waste tank. On the other hand, if the dissolved salt solution is handled by a Type I, II, or IV waste tank the risk of SCC is real. The potent chemistry, absence of stress relief, and inferior material result in a condition that is conducive to cracking. Efforts should be made to either avoid transferring waste that may not meet the PF and NO 2 - /NO 3 - ratio criteria to one of these tanks or if it is unavoidable, take measures to minimize the consequences of a leak. As shown by these tests, even if the PF and NO 2 - /NO 3 - ratio criteria are met, there is a risk that the tank potential may be disturbed in the positive direction and the risk of SCC increase.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2021

Marine Atmospheric Corrosion of Additively Manufactured Stainless Steels

Additively manufactured (AM) stainless steels exhibit numerous microstructural differences compared to their wrought counterparts, such as Cr enriched dislocation cell structures. The influence these unique features have on a SSs corrosion resistance are still under investigation with most current works limited to laboratory experiments. The work herein shows the first documented study of AM 304L and 316L exposed to a severe marine environment on the eastern coast of Florida with comparisons made to wrought counterparts. Coupons were exposed for 21 months and resulted in significant pitting corrosion to initiate after 1 month of exposure for all conditions. At all times, the AM coupons exhibited lower average and maximum pit depths than their wrought counterparts. After 21 months, pits on average were 4 μm deep for AM 316L specimen and 8 μm deep for wrought specimen. Pits on the wrought samples tended to be nearly hemispherical and polished with some pits showing crystallographic attack while pits on AM coupons exhibited preferential attack at melt pool boundaries and the cellular microstructure.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Refinement of Salt Dissolution Inhibitor Requirements (Interim Report)

At Savannah River Site, High-Level Waste is stored in below-grade carbon steel tanks. This waste in part consists of sludge, salt cake, and/or supernate. Preparation of this waste for future processing involves dissolution of the salt cake layer. The salt dissolution process can create conditions that leave the carbon steel tanks susceptible to localized corrosion. The salt to be dissolved contains high concentrations of nitrate, that once released, create an environment that may be conducive to pitting corrosion or stress corrosion cracking (SCC) of carbon steel. The salt dissolution process also liberates interstitial liquid trapped between the salt crystals. This liquid is initially high in nitrite and hydroxide concentration. High pH and greater ratios of nitrite to nitrate act as inhibitors to minimize corrosion of carbon steel in high nitrate environments. However, as dissolution proceeds, the concentration of nitrate increases while the hydroxide and nitrite concentration of the interstitial liquid depletes and becomes insufficient to prevent the onset of corrosion attack. While tank blending and the addition of inhibitors are used to ensure adequate concentrations of hydroxide and nitrite during normal operation, this is not desirable during salt dissolution as it can reduce process efficiency and increase the amount of waste that needs processed.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2020

Failure modes of protection layers produced by atomic layer deposition of amorphous TiO 2 on GaAs anodes

Amorphous titanium dioxide (a-TiO 2 ) films formed by atomic layer deposition can serve as protective coatings for semiconducting photoanodes in water-splitting cells using strongly alkaline aqueous electrolytes. Herein, we experimentally examine the mechanisms of failure for p + -GaAs anodes coated with a-TiO 2 films (GaAs/a-TiO 2 ). Galvanic displacement of exposed GaAs by Au allowed imaging of pinholes in the a-TiO 2 coatings, and enabled collection of quantitative and statistical data associated with pinhole defects. A combination of imaging, electrochemical measurements, and quantitative analyses of corrosion products indicated that extrinsic pinholes were present in the a-TiO 2 films before electrochemical operation. During electrochemical operation these pinholes led to pitting corrosion of the underlying GaAs substrate. The dominant source of pinholes was the presence of atmospheric particulate matter on the GaAs surface during deposition of the a-TiO 2 layer. The pinhole density decreased substantially when the thickness of the a-TiO 2 coating increased beyond 45 nm, and approached zero when the thickness of the film exceeded 112 nm. The density of pinholes in films thinner than 45 nm decreased when the a-TiO 2 coating was deposited in an environmentally controlled cleanroom. Pinhole-free GaAs/a-TiO 2 devices were also tested via chronoamperometry to quantify the rate of pinhole formation during electrochemistry. The time-to-failure increased with thickness, suggesting that the failure mechanism may involve diffusion or migration through the film. However, other mechanisms may also contribute to the degradation of thicker films (>112 nm). Nevertheless, as previously hypothesized, extrinsic pinhole defects formed during deposition and testing control the short-term protective performance of the a-TiO 2 film for GaAs anodes evolving O 2 from water.

25 ENERGY STORAGE↗
DOE OSTI2025

Laser Confocal Microscopy Uncertainty Quantification Study

At Los Alamos National Laboratory (LANL), the Storage Safety and Engineering (SSE) team completes annual surveillance on a subset of in-use interim nuclear material storage containers in fulfilment of requirements outlined in DOE Manual M 441.1-1. The containers are selected through several methods, such as subject matter expert judgement, random selection, and trending items. Following these selections, the SSE team has the capacity to complete surveillance on 15-20 containers each fiscal year, composed of a combination of SAVY-4000 and Hagan storage containers. Through previous work, the stainless-steel components of the containers have been identified as life limiting components, with an emphasis on the thin-walled bodies. The team is focused on understanding the extent of general and pitting corrosion, due to observations of extensive corrosion from stored contents and bag-out-bag degradation. Quantifying corrosion effects on the thin-walled stainless steel container bodies, and understanding potential impacts to the respective design release rates and design qualification release rates is paramount to the team. To date, destructive examination (DE) has proven to be the most insightful method for developing an understanding on the extent of corrosion on used containers. To standardize this process, the SSE team developed a destructive examination guide for analyzing stainless steel components of the containers. Corroded containers of interest are identified during surveillance activities and set aside for sectioning and characterization. Following sectioning, a major step in the DE workflow is the utilization of laser confocal microscopy for scanning corroded samples of interest and extracting data on pits, such as count, depth, and equivalent diameter. Adhering to the techniques outlined in the DE guide, analysis has been completed on two Hagans and one SAVY-4000 container, with the maximum pit depth recorded as 139.1 ± 22.82 μm on a 17.5 year old Hagan. The findings from the completed destructive examinations will be utilized to support lifetime extension efforts of the SAVY-4000 as the team can better estimate corrosion rates and effects over time based on stored contents and age. Due to the implications of observing extreme pit depths that approach the nominal container body thickness of .0299 inches (0.759 mm) or minimum container thickness of 0.236” (0.6 mm), high confidence in the LCM measurements is desired. Through testing outlined in, it was concluded that the total error ascribed to the 20x objective when conducting large image mapping on the Keyence VK-X3050 laser confocal microscope (LCM) relative to a 50x objective (reference) is 16.4% (± 8.73%). For shallow features on the order of pristine SAVY surface defects (i.e. 5 μm), this uncertainty is appropriate. However, this conservative estimate of total error poses a fundamental concern for pit depths that approach the thickness of the measured samples. That is, with the measurement uncertainty currently employed on all measurements, the LCM would be unable to resolve if a pit with a depth of 515 μm is through wall. Standard step height samples were procured and used in the present study to assess the resolution and repeatability of height measurements. Understanding the resolution and repeatability of height measurements was the first focus of the team as it relates directly to pit depth, which is of primary concern. Calibration gratings were procured to evaluate the resolution and repeatability of measurements in the X and Y axes of the LCM stage. The results of the depth uncertainty study were conducted first and presented in the subsequent sections. The planar uncertainty study is appended to the depth study with conclusions from both summarized at the end of the report.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of Drying on Corrosion Mitigation of Hanford Transfer Lines

Radioactive waste is stored in underground, carbon-steel double-shell tanks at the Department of Energy Hanford site. The waste is transferred between the tanks and other assets using the transfer lines spanning throughout the various tank farms at Hanford. The transfer lines consist of a pipe-in-pipe design, small diameter pipes, and are not piggable. Recent inspection data of the transfer lines have shown areas with corrosion on both interior of the encasements and exterior of the primary pipes, with nearly 50 percent wall loss on the primary pipes and nearly 25% wall loss on the encasement pipes due to pitting corrosion. The visual inspections of the transfer lines have shown presence of corrosion products near the pipeline risers and beyond. It has been hypothesized that the corrosion is predominantly due to the high humidity conditions and in some cases is driven by the presence of residual hydrotest water in the encasement and the associated contact with the safety significant primary pipe. Therefore, drying of the transfer lines could lead to corrosion mitigation. Experimental studies are being conducted to understand the effect of environmental conditions, especially, relative humidity and temperature, on transfer line grade carbon steel corrosion and on mitigating corrosion. The experimental conditions are selected based on the seasonal temperature changes, and relative humidity conditions ranging from 30 to 100 percent. The experimental data will be used as guidance for maintaining a dry environment that will help mitigate the transfer-line corrosion caused by the high humidity conditions.

Shukla, Pavan K.↗