Results for “yttria stabilized”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 55 records · Page 3

All sources NASA NTRS DOE OSTI

NASA NTRS1976

Durability of zirconia thermal-barrier ceramic coatings on air-cooled turbine blades in cyclic jet engine operation

Thermal barrier ceramic coatings of stabilized zirconia over a bond coat of Ni Cr Al Y were tested for durability on air cooled turbine rotor blades in a research turbojet engine. Zirconia stabilized with either yttria, magnesia, or calcia was investigated. On the basis of durability and processing cost, the yttria stabilized zirconia was considered the best of the three coatings investigated.

Liebert, C. H.↗

NASA NTRS1976

Ceramic thermal-barrier coatings for cooled turbines

Ceramic thermal-barrier coatings on hot engine parts have the potential to reduce metal temperatures, coolant requirements, cost, and complexity of the cooling configuration, and to increase life, turbine efficiency and gas temperature. Coating systems consisting of a plasma-sprayed layer of zirconia stabilized with either yttria, magnesia or calcia over a thin alloy bond coat have been developed, their potential analyzed and their durability and benefits evaluated in a turbojet engine. The coatings on air-cooled rotating blades were in good condition after completing as many as 500 two-minute cycles of engine operation between full power at a gas temperature of 1644 K and flameout, or as much as 150 hours of steady-state operation on cooled vanes and blades at gas temperatures as high as 1644 K witn 35 start and stop cycles. On the basis of durability and processing cost, the yttria-stabilized zirconia was considered the best of the three coatings investigated.

Liebert, C. H.↗

NASA NTRS1999

Thermal-Mechanical Stability of Single Crystal Oxide Refractive Concentrators for High-Temperature Solar Thermal Propulsion

Single crystal oxides such as yttria-stabilized zirconia (Y2O3-ZrO2), yttrium aluminum garnet (Y3Al5O12, or YAG), magnesium oxide (MgO) and sapphire (Al2O3) are candidate refractive secondary concentrator materials for high temperature solar propulsion applications. However, thermo-mechanical reliability of these components in severe thermal environments during the space mission sun/shade transition is of great concern. Simulated mission tests are important for evaluating these candidate oxide materials under a variety of transient and steady-state heat flux conditions, and thus provide vital information for the component design. In this paper, a controlled heat flux thermal shock test approach is established for the single crystal oxide materials using a 3.0 kW continuous wave CO2 laser, with a wavelength 10.6 micron. Thermal fracture behavior and failure mechanisms of these oxide materials are investigated and critical temperature gradients are determined under various temperature and heating conditions. The test results show that single crystal sapphire is able to sustain the highest temperature gradient and heating-cooling rate, and thus exhibit the best thermal shock resistance, as compared to the yttria-stabilized zirconia, yttrium aluminum garnet, and magnesium oxide.

Zhu, Dongming↗

NASA NTRS1999

Thermal-Mechanical Stability of Single Crystal Oxide Refractive Concentrators for High-Temperature Solar Thermal Propulsion

Zhu, Dongming↗

NASA NTRS2001

Environmental Barrier Coatings for Silicon-Based Ceramics

Silicon-based ceramics, such as SiC fiber-reinforced SiC (SiC/SiC ceramic matrix composites (CMC) and monolithic silicon nitride (Si3N4), are prime candidates for hot section structural components of next generation gas turbine engines. Silicon-based ceramics, however, suffer from rapid surface recession in combustion environments due to volatilization of the silica scale via reaction with water vapor, a major product of combustion. Therefore, application of silicon-based ceramic components in the hot section of advanced gas turbine engines requires development of a reliable method to protect the ceramic from environmental attack. An external environmental barrier coating (EBC) is considered a logical approach to achieve protection and CP long-term stability. The first generation EBC consisted of two layers, mullite (3Al2O3-2SiO2) bond coat and yttria-stabilized zirconia (YSZ, ZrO2-8 Wt.% Y2O3) top coat. Second generation EBCs, with substantially improved performance compared with the first generation EBC, were developed in the NASA High Speed Research-Enabling Propulsion Materials (HSR-EPM) Program. The first generation EBC consisted of two layers, mullite (3Al2O3-2SiO2) bond coat and yttria-stabilized zirconia (YSZ, ZrO2-8 wt.% Y2O3) top coat. Second generation EBCs, with substantially improved performance compared with the first generation EBC, were developed in the NASA High Speed Research-Enabling Propulsion Materials (HSR-EPM) Program (5). They consist of three layers, a silicon first bond coat, a mullite or a mullite + BSAS (BaO(1-x)-SrO(x)-Al2O3-2SiO2) second bond coat, and a BSAS top coat. The EPM EBCs were applied on SiC/SiC CMC combustor liners in three Solar Turbines (San Diego, CA) Centaur 50s gas turbine engines. The combined operation of the three engines has accumulated over 24,000 hours without failure (approximately 1,250 C maximum combustor liner temperature), with the engine in Texaco, Bakersfield, CA, accumulating about 14,000 hours. As the commercialization of Si-based ceramic components in gas turbines is on the horizon, a major emphasis is placed on EBCs for two reasons. First, they are absolute necessity for the protection of Si-based ceramics from water vapor. Second, they can enable a major enhancement in the performance of gas turbines by creating temperature gradients with the incorporation of a low thermal conductivity layer. Thorough understanding of current state-of-the-art EBCs will provide the foundation upon which development of future EBCs will be based. Phase stability and thermal conductivity of EPM EBCs are published elsewhere. This paper will discuss the chemical/environmental durability and silica volatility of EPM EBCs and their impact on the coating's upper temperature limit.

Lee, Kang N.↗

NASA NTRS1981

Thermal barrier coatings for thermal insulation and corrosion resistance in industrial gas turbine engines

Four thermal barrier coatings were subjected to a 500-hour gas turbine engine test. The coatings were two yttria stabilized zirconias, calcium ortho silicate and calcium meta titanate. The calcium silicate coating exhibited significant spalling. Yttria stabilized zirconia and calcium titanate coatings showed little degradation except in blade leading edge areas. Post-test examination showed variations in the coating due to manual application techniques. Improved process control is required if engineering quality coatings are to be developed. The results indicate that some leading edge loss of the coating can be expected near the tip.

Vogan, J. W.↗

NASA NTRS1985

Long-term stability and properties of zirconia ceramics for heavy duty diesel engine components

Physical, mechanical, and thermal properties of commercially available transformation-toughened zirconia are measured. Behavior is related to the material microstructure and phase assemblage. The stability of the materials is assessed after long-term exposure appropriate for diesel engine application. Properties measured included flexure strength, elastic modulus, fracture toughness, creep, thermal shock, thermal expansion, internal friction, and thermal diffusivity. Stability is assessed by measuring the residual property after 1000 hr/1000C static exposure. Additionally static fatigue and thermal fatigue testing is performed. Both yttria-stabilized and magnesia-stabilized materials are compared and contrasted. The major limitations of these materials are short term loss of properties with increasing temperature as the metastable tetragonal phase becomes more stable. Fine grain yttria-stabilized material (TZP) is higher strength and has a more stable microstructure with respect to overaging phenomena. The long-term limitation of Y-TZP is excessive creep deformation. Magnesia-stabilized PSZ has relatively poor stability at elevated temperature. Overaging, decomposition, and/or destabilization effects are observed. The major limitation of Mg-PSZ is controlling unwanted phase changes at elevated temperature.

Larsen, D. C.↗

NASA NTRS2007

Glass/Ceramic Composites for Sealing Solid Oxide Fuel Cells

A family of glass/ceramic composite materials has been investigated for use as sealants in planar solid oxide fuel cells. These materials are modified versions of a barium calcium aluminosilicate glass developed previously for the same purpose. The composition of the glass in mole percentages is 35BaO + 15CaO + 5Al2O3 + 10B2O3 + 35SiO2. The glass seal was found to be susceptible to cracking during thermal cycling of the fuel cells. The goal in formulating the glass/ ceramic composite materials was to (1) retain the physical and chemical advantages that led to the prior selection of the barium calcium aluminosilicate glass as the sealant while (2) increasing strength and fracture toughness so as to reduce the tendency toward cracking. Each of the composite formulations consists of the glass plus either of two ceramic reinforcements in a proportion between 0 and 30 mole percent. One of the ceramic reinforcements consists of alumina platelets; the other one consists of particles of yttria-stabilized zirconia wherein the yttria content is 3 mole percent (3YSZ). In preparation for experiments, panels of the glass/ceramic composites were hot-pressed and machined into test bars.

Bansal, Narottam P.↗

NASA NTRS2015

Thermal Conductivity and Erosion Durability of Composite Two-Phase Air Plasma Sprayed Thermal Barrier Coatings

To enhance efficiency of gas turbines, new thermal barrier coatings (TBCs) must be designed which improve upon the thermal stability limit of 7 wt% yttria stabilized zirconia (7YSZ), approximately 1200 C. This tenant has led to the development of new TBC materials and microstructures capable of improved high temperature performance. This study focused on increasing the erosion durability of cubic zirconia based TBCs, traditionally less durable than the metastable t' zirconia based TBCs. Composite TBC microstructures composed of a low thermal conductivity/high temperature stable cubic Low-k matrix phase and a durable t' Low-k secondary phase were deposited via APS. Monolithic coatings composed of cubic Low-k and t' Low-k were also deposited, in addition to a 7YSZ benchmark. The thermal conductivity and erosion durability were then measured and it was found that both of the Low-k materials have significantly reduced thermal conductivities, with monolithic t' Low-k and cubic Low-k improving upon 7YSZ by approximately 13 and approximately 25%, respectively. The 40 wt% t' Low-k composite (40 wt% t' Low-k - 60 wt% cubic Low-k) showed a approximately 22% reduction in thermal conductivity over 7YSZ, indicating even at high levels, the t' Low-k secondary phase had a minimal impact on thermal in the composite coating. It was observed that a mere 20 wt% t' Low-k phase addition can reduce the erosion of a cubic Low-k matrix phase composite coating by over 37%. Various mixing rules were then investigated to assess this non-linear composite behavior and suggestions were made to further improve erosion durability.

Rare earth zirconia↗

NASA NTRSDate not supplied

Enhanced Thermal Stability of High Yttria Concentration YSZ Aerogels

Aerogels demonstrate extraordinarily low thermal conductivity and low density, presenting a promising form of lightweight insulation for aerospace applications. The primary challenge is stabilization of the highly porous structure at temperatures to 1200 °C. Upon collapse of the pore structure, the favorable thermal properties and low density are diminished. Yttria-stabilized zirconia (YSZ) aerogels are synthesized to investigate the effect of composition on morphology, phase behavior, and thermal stability (specific surface area, pore size distribution). This work demonstrates the improvement in thermal stability of zirconia aerogels with increased yttria content. Furthermore, changes in structure and surface chemistry of YSZ aerogels are studied in both oxidizing and inert atmospheres. With an improved understanding of aerogel structure and performance, metal oxide aerogels can be developed to withstand the extreme environments of space exploration.

Nathaniel Olson↗

NASA NTRS2020

Durability of YSZ coated Ti2AlC in 1300°C high velocity burner rig tests

A thermal barrier coating system survived 500 h in cyclic burner rig tests at 1300°C, exceeding the life of all previous systems. An yttria stabilized zirconia (7YSZ) thermal barrier coating (TBC) was plasma sprayed on the oxidation resistant Ti2AlC MAX phase and tested in a jet fuel burner. No coating spallation or recession was observed, only a 2.4 mg/sq.cm mass gain due to typical cubic Al2O3 oxidation kinetics. The modest weight gain contrasted with large TBC spallation or oxide volatility losses that might occur under cyclic, high velocity (~100 m/s) burner conditions. The coating surface exhibited colonies of [111]flourite fiber-textured columns separated by craze crack patterns, but with no visible moisture attack. The thickness of the alumina scale under the YSZ face was >20 μm, more than twice that formed on TBC/superalloy systems at failure. TiO2 nodules, initially formed on the uncoated backside, were then removed as volatile hydroxides formed in high temperature, high velocity water vapor (~10%). Overall, the test indicated the exceptional stability of the YSZ/Ti2AlC system under turbine conditions, due in large part to good thermal expansion matching.

alumina, MAX phases, thermal barrier coatings (TBC↗

NASA NTRS1991

Multilayer ceramic oxide solid electrolyte for fuel cells and electrolysis cells

A unitary layered ceramic structure is disclosed which comprises co-sintered layers. The co-sintered structure comprises a sintered central layer of yttria stabilized zirconia (YSZ) which is about 8 mole percent yttria and having a density of at least about 95% of theoretical, and sintered outer layers of strontium lanthanum manganite (LSM) having the approximate molecular composition La.sub.0.8 Sr.sub.0.2 MnO.sub.3, having a density from about 50 to about 60% of theoretical, and having interconnected porosity from about 40 to 50% with an interconnected pore diameter from about one micron to about five microns. The sintered central layer is sandwiched by and bonded and sintered to the outer layers and is essentially free of significant amounts of manganese. A process for making the unitary composition-of-matter is also disclosed which involves tape casting a LSM tape and then on top thereof casting a YSZ tape. The process comprises presintering LSM powder at 1250.degree. F., crushing the presintered commercially available LSM powder, forming a slurry with the crushed LSM, a binder and solvent, tape casting the slurry and allowing the slurry to air dry. A mixture of commercially available submicron size particle YSZ powder is milled with a dispersant and solvent to disperse the YSZ particles thereby forming a dispersed YSZ slurry. The YSZ slurry is then tape cast on the dried LSM tape. If desired, a third layer of LSM can be cast on top of the dried YSZ layer. After drying the composite LSM/YSZ and LSM/YSZ/LSM tapes are fired at 1300.degree. C. No migration of manganese into the YSZ layer was observed with scanning electron microscope/edax in the sintered multilayer tape.

Schroeder, James E.↗

NASA NTRS1990

Multilayer ceramic oxide solid electrolyte for fuel cells and electrolysis cells and method for fabrication thereof

An unitary layered ceramic structure is disclosed which comprises co-sintered layers. The co-sintered structure comprises a sintered central layer of yttria stabilized zirconia (YSZ) which is about 8 mole percent yttria and having a density of at least about 95% of theoretical, and sintered outer layers of strontium lanthanum manganite (LSM) having the approximate molecular composition La.sub.0.8 Sr.sub.0.2 MnO.sub.3, having a density from about 50 to about 60% of theoretical, and having interconnected porosity from about 40 to 50% with an interconnected pore diameter from about one micron to about five microns. The sintered central layer is sandwiched by and bonded and sintered to the outer layers and is essentially free of significant amounts of manganese. A process for making the unitary composition-of-matter is also disclosed which involves tape casting a LSM tape and then on top thereof casting a YSZ tape. The process comprises presintering LSM powder at 1250.degree. F., crushing the presintered commercially available LSM powder, forming a slurry with the crushed LSM, a binder and solvent, tape casting the slurry and allowing the slurry to air dry. A mixture of commercially available submicron size particle YSZ powder is milled with a dispersant and solvent to disperse the YSZ particles thereby forming a dispersed YSZ slurry. The YSZ slurry is then tape cast on the dried LSM tape. If desired, a third layer of LSM can be cast on top of the dried YSZ layer. After drying the composite LSM/YSZ and LSM/YSZ/LSM tapes are fired at 1300.degree. C. No migration of manganese into the YSZ layer was observed with scanning electron microscope/edax in the sintered multilayer tape.

Schroeder, James E.↗

NASA NTRS1985

Advanced thermal barrier coating systems

Current state-of-the-art thermal barrier coating (TBC) systems consist of partially stabilized zirconia coatings plasma sprayed over a MCrAlY bond coat. Although these systems have excellent thermal shock properties, they have shown themselves to be deficient for a number of diesel and aircraft applications. Two ternary ceramic plasma coatings are discussed with respect to their possible use in TBC systems. Zirconia-ceria-yttria (ZCY) coatings were developed with low thermal conductivities, good thermal shock resistance and improved resistance to vanadium containing environments, when compared to the baseline yttria stabilized zirconia (YSZ) coatings. In addition, dense zirconia-titania-yttria (ZTY) coatings were developed with particle erosion resistance exceeding conventional stabilized zirconia coatings. Both coatings were evaluated in conjunction with a NiCr-Al-Co-Y2O3 bond coat. Also, multilayer or hybrid coatings consisting of the bond coat with subsequent coatings of zirconia-ceria-yttria and zirconia-titania-yttria were evaluated. These coatings combine the enhanced performance characteristics of ZCY with the improved erosion resistance of ZTY coatings. Improvement in the erosion resistance of the TBC system should result in a more consistent delta T gradient during service. Economically, this may also translate into increased component life simply because the coating lasts longer.

Dorfman, M. R.↗

NASA NTRS1978

Effects of compositional changes on the performance of a thermal barrier coating system

Currently proposed thermal barrier systems for aircraft gas turbine engines consist of NiCrAlY bond coating covered with an insulating oxide layer of yttria-stabilized zirconia. The effect of yttrium concentration (from 0.15 to 1.08 w/o) in the bond coating and the yttria concentration (4 to 24.4 w/o) in the oxide layer were evaluated. Furnace, natural gas-oxygen torch, and Mach 1.0 burner rig cyclic tests on solid specimens and air-cooled blades were used to identify trends in coating behavior. Results indicate that the combinations of yttrium levels between 0.15 - 0.35 w/o in the bond coating and the yttria concentration between 6 - 8 w/o in the zirconium oxide layer were the most adherent and resistant to high temperature cyclic exposure.

Stecura, S.↗

NASA NTRSDate not supplied

Optimization of Aerogels for High Temperature Applications

Aerogels can be used in spaceflight applications as thermal insulators due to their low density, low thermal conductivity, and tortuous path for solid conduction. However, the aerogel formulation must be optimized to increase the thermal stability of the aerogels as drastic densification and decrease in surface area is often exhibited after high-temperature exposure. Current research investigates yttria-stabilized zirconia (YSZ) aerogels, which have low thermal conductivity and are expected to be used between 600°C and 1000°C. We anticipate that new sol-gel chemistries and processing will yield YSZ aerogels that display retained mesoporous structure, increased surface area, and minimized shrinkage upon exposure to higher temperatures in the projected use range. This work investigates the cationic surfactant, cetrimonium bromide (CTAB), as a templating agent to prevent the collapse of the aerogel pore structure upon gelation and drying. It was determined that adding one-half times the critical micelle concentration (CMC) of CTAB increased the surface area and pore volume of the aerogels, as compared to aerogels without CTAB or with twice the CMC of CTAB, following high-temperature exposure. By optimizing CTAB, the thermal stability of YSZ aerogels can be enhanced to make these materials more efficient when used as thermal management systems.

Rebecca C Walker↗

NASA NTRS1999

Thermal Mechanical Stability of Single-Crystal-Oxide Refractive Concentrators Evaluated for High-Temperature Solar-Thermal Propulsion

Recently, refractive secondary solar concentrator systems were developed for solar thermal power and propulsion (ref. 1). Single-crystal oxides-such as yttria-stabilized zirconia (Y2O3-ZrO2), yttrium aluminum garnet (Y3Al5O12, or YAG), magnesium oxide (MgO), and sapphire (Al2O3)-are candidate refractive secondary concentrator materials. However, the refractive concentrator system will experience high-temperature thermal cycling in the solar thermal engine during the sun/shade transition of a space mission. The thermal mechanical reliability of these components in severe thermal environments is of great concern. Simulated mission tests are important for evaluating these candidate oxide materials under a variety of transient and steady-state heat flux conditions. In this research at the NASA Lewis Research Center, a controlled heat flux test approach was developed for investigating the thermal mechanical stability of the candidate oxide. This approach used a 3.0-kW continuous-wave (wavelength, 10.6 mm) carbon dioxide (CO2) laser (ref. 2). The CO2 laser is especially well-suited for single-crystal thermal shock tests because it can directly deliver well-characterized heat energy to the oxide surfaces. Since the oxides are opaque at the 10.6-mm wavelength of the laser beam, the light energy is absorbed at the surfaces rather than transmitting into the crystals, and thus generates the required temperature gradients within the specimens. The following figure is a schematic diagram of the test rig.

Jacobson, Nathan S.↗

NASA NTRS2005

Depth-Penetrating Luminescence Thermography of Thermal- Barrier Coatings

A thermographic method has been developed for measuring temperatures at predetermined depths within dielectric material layers . especially thermal-barrier coatings. This method will help satisfy a need for noncontact measurement of through-the-thickness temperature gradients for evaluating the effectiveness of thermal- barrier coatings designed to prevent overheating of turbine blades, combustor liners, and other engine parts. Heretofore, thermography has been limited to measurement of surface and near-surface temperatures. In the thermographic method that is the immediate predecessor of the present method, a thermographic phosphor is applied to the outer surface of a thermal barrier coating, luminescence in the phosphor is excited by illuminating the phosphor at a suitable wavelength, and either the time dependence of the intensity of luminescence or the intensities of luminescence spectral lines is measured. Then an emissivity-independent surface-temperature value is computed by use of either the known temperature dependence of the luminescence decay time or the known temperature dependence of ratios between intensities of selected luminescence spectral lines. Until now, depth-penetrating measurements have not been possible because light of the wavelengths needed to excite phosphors could not penetrate thermal-barrier coating materials to useful depths. In the present method as in the method described above, one exploits the temperature dependence of luminescence decay time. In this case, the phosphor is incorporated into the thermal-barrier coat at the depth at which temperature is to be measured. To be suitable for use in this method, a phosphor must (1) exhibit a temperature dependence of luminescence decay time in the desired range, (2) be thermochemically compatible with the thermal-barrier coating, and (3) exhibit at least a minor excitation spectral peak and an emission spectral peak, both peaks being at wavelengths at which the thermal-barrier coating is transparent or at least translucent. Conventional thermographic phosphors are not suitable because they are most efficiently excited by ultraviolet light, which does not penetrate thermal- barrier coating materials. (Typical thermal-barrier coating materials include or consist of various formulations of yttria-stabilized zirconia.) Only a small fraction of phosphor candidates have significant excitation at wavelengths long enough (>500 nm) for sufficient penetration of thermal-barrier coatings. One suitable phosphor material . yttria doped with europium (Y2O3:Eu) . has a minor excitation peak at 532 nm and an emission peak at 611 nm. In experiments, this material was incorporated beneath a 100-microns-thick thermal-barrier coating and subjected to excitation and measurement by the luminescence-decay-time technique. These experiments were found to yield reliable temperature values up to 1,100 C. At the time of reporting the information for this article, a search for suitable phosphors other than (Y2O3:Eu) was continuing.

Eldridge, Jeffrey↗