NASA NTRS1974

Stress-rupture strength and microstructural stability of W-HF-C wire-reinforced superalloy composites

W-Hf-C superalloy composites were found to be potentially useful for turbine-blade applications on the basis of stress-rupture strength. The 100- and 1000-hour rupture strengths obtained for 70 volume percent fiber composites tested at 1090 C were 420 and 280 MN/sq m. The investigation indicated that with better quality fibers, composites having 100- and 1000-hour rupture strengths of 570 and 370 MN/sq m may be obtained. Metallographic studies indicated sufficient fiber-matrix compatibility for long-term applications at 1090 C for 1000 hours or more.

Petrasek, D. W.↗
NASA NTRS1977

Correlation of creep rate with microstructural changes during high temperature creep

Creep tests were conducted on Haynes 188 cobalt-base alloy and alpha titanium. The tests on Haynes 188 were conducted at 1600 F and 1800 F for stresses from 3 to 20 ksi, and the as-received, mill-annealed results were compared to specimens given 5%, 10%, and 15% room temperature prestrains and then annealed one hour at 1800 F. The tests on alpha titanium were performed at 7,250 and 10,000 psi at 500 C. One creep test was done at 527 C and 10,000 psi to provide information on kinetics. Results for annealed titanium were compared to specimens given 10% and 20% room temperature prestrains followed by 100 hours recovery at 550 C. Electron microscopy was used to relate dislocation and precipitate structure to the creep behavior of the two materials. The results on Haynes 188 alloy reveal that the time to reach 0.5% creep strain at 1600 F increases with increasing prestrain for exposure times less than 1,000 hours, the increase at 15% prestrain being more than a factor of ten.

Young, C. T.↗
NASA NTRS1977

Microstructure and composition of InSb-GaSb ingots directionally solidified aboard Skylab

InSb-GaSb solid solution ingots prepared by directional solidification aboard Skylab and on earth consist of twins with (111) twin planes parallel to the direction of solidification and growth directions that lie along 211, 110, or 321 crystallographic directions. Significant fractions of several ingots prepared aboard Skylab were solidified from melts that were not in contact with container walls, resulting in convection driven by surface tension gradients in the melt and corresponding radially-symmetric composition variations in the ingot. In these regions, adjacent twins exhibit marked differences in indium content, indicating a substantial dependence of composition on crystallographic orientation.

Lefever, R. A.↗
NASA NTRS1977

Effects of C and Hf concentration on phase relations and microstructure of a wrought powder-metallurgy superalloy

NASA IIB-11, a candidate alloy for advanced temperature turbine engine disks, and four modifications with varying C and Hf concentrations were produced from prealloyed powders. Several notable effects of C and Hf concentration in the alloys were observed. Both the amount of the gamma-prime phase and its solvus temperature increased with decreasing C, but only the gamma-prime solvus was affected by Hf, increasing with increasing Hf. Hf also promoted a cellular gamma-prime precipitation. Hf was, however, about equally distributed between gamma-prime and gamma. Hf and C both affected the carbides formed. Increasing both promoted formation of an MC relative to that of an M6C.

Miner, R. V., Jr.↗
NASA NTRS1977

Effects of long-term aging on ductility and microstructure of Cb and Mo alloys

A program was conducted to determine if aging embrittlement occurs in columbium-base alloys C-103, Cb-1Zr, and Cb-752 or in a molybdenum alloy, Mo-TZM. Results showed that aging embrittlement does not occur in C-103, Cb-1Zr, or Mo-TZM during long-term (1000 hour) aging at temperatures in the range of 700-1025 C. In comparison, aging embrittlement occurred in the Cb-752 alloy after similar aging at 900 C. A critical combination of the solute additions W and Zr led to Zr segregation at grain boundaries during long-term aging which subsequently resulted in embrittlement as indicated by an increase in the ductile-brittle transition temperature from below -196 C to about -150 C.

Stephens, J. R.↗
NASA NTRS1977

The metallic microstructures and thermal histories of severely reheated chondrites

The metallographic structures of eight severely reheated chondrites - Farmington, Ramsdorf, Orvinio, Wickenburg, Lubbock, Rose City, Arapahoe, and Tadjera - were studied using optical, SEM and electron microprobe techniques. The following metallographic criteria were used to estimate the post-shock residual temperature of the chondrites: melted metal-troilite appearance, presence of martensite, phosphorus enrichment of metal and averaging of central metal grain compositions. The presence of phosphides and secondary kamacite are due to slow post-shock cooling rates. Ni rim gradients indicate both extensive remelting of metal grains and relatively fast cooling.

Smith, B. A.↗
NASA NTRS1980

Preparation of monotectic alloys having a controlled microstructure by directional solidification under dopant-induced interface breakdown

Monotectic alloys having aligned spherical particles of rods of the minor component dispersed in a matrix of the major component are prepared by forming a melt containing predetermined amounts of the major and minor components of a chosen monotectic system, providing in the melt a dopant capable of breaking down the liquid solid interface for the chosen alloy, and directionally solidfying the melt at a selected temperature gradient and a selected rate of movement of the liquid-solid interface (growth rate). Shaping of the minor component into spheres or rods and the spacing between them are controlled by the amount of dopant and the temperature gradient and growth rate values. Specific alloy systems include Al Bi, Al Pb and Zn Bi, using a transition element such as iron.

Parr, R. A.↗
NASA NTRS1980

Microstructural characterization of the HRSI thermal protection system for space shuttle

Components of the space shuttle high temperature reusable surface insulation (HRSI) system were microscopically characterized, both separately and as a system, to obtain information needed for stress analysis models of the thermal protection system. A tension specimen of the HRSI system was loaded in steps and was microscopically observed at each load condition to demonstrate the tension failure mode associated with strain isolation pad (SIP) behavior. A local failure occurred which should be associated with transfer of load through transverse fibers in the SIP. Stress concentrations attributed to the SIP behavior necessitated strengthening of the HRSI by densification of the RSI at the bondline. An HRSI tile was microscopically characterized after the densification process. The densified surface layer blended into the RSI which caused a gradual change in density. The gradation in density does not appear to represent a sharp discontinuity in elastic modulus between the densified layer and the parent material.

Ransone, P. O.↗
NASA NTRS1980

Microstructure of the interplanetary magnetic field near 4 and 5 AU

Interplanetary magnetic field fluctuations near 4 and 5 AU are investigated on the basis of Pioneer 10 and 11 vector magnetic field measurements in order to identify extant wave modes and propagation directions as functions of frequency in the range 0.00004 to 0.009 Hz. Analysis of the approximately 500 spectral matrices as functions of frequency obtained from each spacecraft indicates the distributions of maximum variance directions to be peaked along the normal to the plane of the minimum variance direction and the mean magnetic field, as would be expected for a planar, small-amplitude Alfven wave with a minimum variance direction close to the wave vector. It is thus inferred that single small-amplitude Alfven waves are occasionally present in the temporal and frequency bands analyzed, however waves with wave vectors not well approximated by the minimum variance direction, Alfven wave ensembles, finite-amplitude waves and nonplanar fluctuations may also be present. Observations are also noted to suggest the predominance of the Alfven mode over the fast and slow modes, however do not support theoretical models of outward propagating plane Alfven waves of solar origin.

Parker, G. D.↗
NASA NTRS1981

Microstructure of Al2O3 scales formed on NiCrAl alloys

The structure of transient scales formed on pure and Y or Zr-doped Ni-15Cr-13Al alloys oxidized for 0.1 hr at 1100 C was studied by the use of transmission electron microscopy. Crystallographically oriented scales were found on all three alloys, but especially for the Zr-doped NiCrAl. The oriented scales consisted of alpha-(Al,Cr)2O3, Ni(Al,Cr)2O4 and gamma-Al2O3. They were often found in intimate contact with each other such that the close-packed planes and directions of one oxide phase were aligned with those of another. The prominent structural features of the oriented scales were approximately equal to micrometer subgrains; voids, antiphase domain boundaries and aligned precipitates were also prevalent. Randomly oriented alpha-Al2O3 was also found and was the only oxide ever observed at the immediate oxide metal interface. These approximately 0.15 micrometer grains were populated by intragranular voids which decreased in size and number towards the oxide metal interface. A sequence of oxidation was proposed in which the composition of the growing scale changed from oriented oxides rich in Ni and Cr to oriented oxides rich in Al. At the same time the structure changed from cubic spinels to hexagonal corundums with apparent precipitates of one phase in the matrix of the other. Eventually randomly oriented pure alpha-Al2O3 formed as the stable oxide with an abrupt transition: there was no gradual loss of orientation, no gradual compositional change or no gradual decrease in precipitate density.

Smialek, J. L.↗
NASA NTRS1980

Microstructure of the combustion zone: Thin-binder AP-polymer sandwiches

Experimental results are summarized for systematic quench-burning tests on ammonium perchlorate-HC binder sandwiches with binder thicknesses in the range 10 - 150 microns. Tests included three binders (polysulfide, polybutadiene-acrylonitrile, and hydroxy terminated polybutadiene), and pressures from 1.4 to 14 MPa. In addition, deflagration limits were determined in terms of binder thickness and pressure. Results are discussed in terms of a qualitative theory of sandwich burning consolidated from various sources. Some aspects of the observed results are explained only speculatively.

Price, E. W.↗
NASA NTRS1980

Microstructure and mechanical properties of bulk and plasma-sprayed y2O3-partially stabilized zirconia

Bulk 8.0 weight percent yttria partially stabilied zirconia (PSZ) was studied by light microscopy, transmission electron microscopy, X-ray analysis, microhardness testing, and fracture toughness testing. The as received PSZ contained spheroidal and grain boundary precipitates up to 4 micrometers in size. Spheroids up to 1.26 micrometers were metastable tetragonal; large spheroids were monoclinic. Grinding the PSZ into powder did not cause a significant amount of tetragonal to transform to monoclinic. This indicates that transformation toughness is not a significant mechanism in PSZ. Aging the PSZ at 1500 C caused the fine tetragonal precipitates to grow from 0.06 to 0.12 micrometers, in 250 minutes. A peak hardness of 1400 kg/sq mm was attained after 50 minutes. Solution annealing and quenching the as received PSZ eliminated the large precipitates, but fine tetragonal precipitates reformed on quenching. Aging at 1500 C caused the fine 0.02 micrometers tetragonal precipitates to grow into plates about 0.10 by 0.50 micrometers. A peak hardness of 1517 kg/sq mm was obtained after 250 minutes. On further aging, monoclinic percipitates formed along grain boundaries. The fracture toughness of the aged and unaged solution annealed and quenched PSZ was found to be between 2 and 3 MN /square root of m cubed. This range of fracture toughness is consistent with PSZ's that do not undergo transformation toughening.

Valentine, P. G.↗
NASA NTRS1981

Microstructure and mechanical properties of bulk yttria-partially-stabilized zirconia

A commercially available bulk 4.5 mole percent yttria-(Y2O3) partially stabilized zirconia (PSZ) was studied by light microscopy, X-ray analysis, microhardness measurement, and fracture toughness testing. The growth of the precipitates and the phase transformations were studied as a function of aging in air at 1500 C. Aging curves were constructed for both the as received and the solution annealed and quenched materials; the curves showed hardness peaks at 1397 and 1517 Kg/sq mm respectively. The rectangular plate shaped tetragonal precipitates were found to have a 110 habit plane. A total of twelve different types of tetragonal precipitates were found. Grinding of the Y2O3 PSZ into powder did not cause a significant amount of metastable tetragonal precipitates to transform into the monoclinc phase, thus indicating that transformation toughening is not a significant mechanism for the material.

Valentine, P. G.↗
NASA NTRS1981

Microstructure and mechanical properties of bulk yttria-partially-stabilized zirconia

A commercially available bulk 4.5 mole percent yttria-Y2O3)-partially-stabilized zirconia (PSZ) was studied by light microscopy, X-ray analysis, microhardness measurement, and fracture toughness testing. The growth of the precipitates and the phase transformations were studied as a function of aging in air at 1500 C. Aging cuves were constructed for both the as-received and the solution-annealed-and-quenched materials; the curves showed hardness peaks at 1397 and 1517 kg/sq mm, respectively. A total of twelve different types of tetragonal precipitates were found. The rectangular plate-shaped tetragonal precipitates were found to have a (110) habit plane. Grinding of the Y2O3 PSZ into powder did not cause a significant amount of metastable tetragonal precipitates to transform into the monoclinic phase, thus indicating that transformation toughening is not a significant mechanism for the material. The fracture toughness of the aged and of the unaged solution-annealed-and-quenched PSZ was found to be between 2 and 3 MN/cu m/2.

Valentine, P. G.↗