The objectives of the Solar Probe mission and the current status of the Solar Probe thermal shield subsystem development are described. In particular, the discussion includes a brief description of the mission concepts, spacecraft configuration and shield concept, material selection criteria, and the required material testing to provide a database to support the development of the shield system.
Mechanical property characterization was performed on AS4/3501-6 graphite/epoxy and SC350G syntactic foam for the SRB Composite Nose Cap Shuttle Upgrades Project. Lamina level properties for the graphite/epoxy were determined at room temperature, 240 F, 350 F, 480 F, 600 F, and 350 F after a cycle to 600 F. Graphite/epoxy samples were moisture conditioned prior to testing. The syntactic foam material was tested at room temperature, 350 F, and 480 F. A high-temperature test facility was developed at MSFC. Testing was performed with quartz lamp heaters and high resistance heater strips. The thermal history profile of the nose cap was simulated in order to test materials at various times during launch. A correlation study was performed with Southern Research Institute to confirm the test methodology and validity of test results. A-basis allowables were generated from the results of testing on three lots of material.
The objectives are to demonstrate how the microstructure of materials may be revealed by abrasive polishing and chemical etching, and to illustrate how microstructural information is used to monitor manufacturing processes, provide in-depth inspection, and perform failure analysis. Microstructural analysis is the procedure used to reveal the internal microstructural details of a material or part by sectioning and polishing the cut surface so that it may be examined under a suitable microscope. A printed wiring board was selected as the test material because it contains both metals and nonmetals that have distinctive microstructures, and because this technique is used throughout the electronic industry as a key quality control tool. The three principle component materials in printed circuit boards are glass/epoxy laminates faced with copper foil; copper, deposited by both electroless and electrolytic plating; and tin/lead solder. Sample preparation, mounting, grinding, polishing, and examination and analysis are discussed.
Potential nondestructive test (NDE) methods were evaluated for detecting debonds and weak bonds in the thermal protection system (TPS) for the space shuttle solid rocket boosters. The primary thermal protection material is a sprayable, thick epoxy coating that is filled with lightweight and thermal insulating materials. Test panels were fabricated with a wide variety of hidden realistic defects, including contact debonds and weak bonds. Nondestructive test results were obtained. Candidate NDE methods evaluated for booster production applications include laser interferometry (e.g., electronic shearography), infrared thermography, radiography (e.g., computed tomography), acousto-ultrasonics, mechanical/acoustic impedance, ultrasonics, acoustic emission, and the tap test. Capabilities, advantages, disadvantages, and relative performances in defect detection of each test method for TPS bonding applications are reported. Electronic shearography NDE was technically the superior method for detecting debonds.
Foreign object damage (FOD) behavior of two commercial gas-turbine grade silicon nitrides, AS800 and SN282, was determined at ambient temperature through strength testing of flexure test specimens impacted by steel-ball projectiles with a diameter of 1.59 mm in a velocity range from 220 to 440 m/s. AS800 silicon nitride exhibited a greater FOD resistance than SN282, primarily due to its greater value of fracture toughness (K(sub IC)). Additionally, the FOD response of an equiaxed, fine-grained silicon nitride (NC132) was also investigated to provide further insight. The NC132 silicon nitride exhibited the lowest fracture toughness of the three materials tested, providing further evidence that K(sub IC) is a key material parameter affecting FOD resistance. The observed damage generated by projectile impact was typically in the forms of well- or ill-developed ring or cone cracks with little presence of radial cracks.
Increased human spaceflight operations utilize oxygen concentrations that are frequently varied with use of concentrations up to 100 percent oxygen. Even after exiting a higher percentage oxygen environment, high oxygen concentrations can still be maintained due to material saturation and oxygen entrapment between barrier materials. This paper examines the material flammability concerns that arise from changing oxygen environments during spaceflight operations. We examine the time required for common spacecraft and spacesuit materials exposed to oxygen to return to reduced ignitability and flammability once removed from the increased concentration. Various common spacecraft materials were considered: spacecraft cabin environment foams, Extra Vehicular Mobility Unit materials and foams, Advanced Crew Escape Suit materials, and other materials of interest such as Cotton, Nomex^ HT90-40, and Tiburon Surgical Drape. This paper presents calculated diffusion coefficients derived from experimentally obtained oxygen transmission rates for the tested materials and the analytically derived times necessary for reduced flammability to be achieved based on NASA flammability criteria. Oxygen material saturation and entrapment scenarios are examined. Experimental verification data on oxygen diffusion in saturation scenarios are also presented and discussed. We examine how to use obtained data to address flammability concerns during operational planning to reduce the likelihood of fires while improving efficiency for procedures.
This presentation discusses the combined irradiation testing methods, strategies, and high-level results of the Advanced Materials and Manufacturing Technologies program. Included are neutron irradiation, ion irradiation, and post-irradiation examination.
Ultrasonic radio frequency tone-bursts are launched into a sample of material tested. The amplitude of the tone-bursts and the slope of the resulting static displacement pulses are measured. These measurements are used to calculate the nonlinearities of the materials.
The National Aeronautics and Space Administration (NASA) Exploration Systems Mission Directorate initiated an Advanced Composite Technology Project through the Exploration Technology Development Program in order to support the polymer composite needs for future heavy lift launch architectures. As an example, the large composite dry structural applications on Ares V inspired the evaluation of autoclave and out-of-autoclave (OOA) composite materials. A NASA and industry team selected the most appropriate materials based on component requirements for a heavy lift launch vehicle. Autoclaved and OOA composites were fabricated and results will highlight differences in processing conditions, laminate quality, as well as initial room temperature thermal and mechanical performance. Results from this study compare solid laminates that were both fiber-placed and hand-laid. Due to the large size of heavy-lift launch vehicle composite structures, there is significant potential that the uncured composite material or prepreg will experience significant out-life during component fabrication. Therefore, prepreg out-life was a critical factor examined in this comparison. In order to rigorously test material suppliers recommended out-life, the NASA/Industry team extended the out-time of the uncured composite prepreg to values that were approximately 50% beyond the manufacturers out-time limits. Early results indicate that the OOA prepreg composite materials suffered in both composite quality and mechanical property performance from their extended out-time. However, the OOA materials performed similarly to the autoclaved composites when processed within a few days of exposure to ambient "shop" floor handling. Follow on studies evaluating autoclave and OOA aluminum honeycomb core sandwich composites are planned.
New materials in recent decades have enabled advances in thermal insulation systems for storage and transfer of cryogens. To preserve the cold and achieve efficient cryogenic systems, a combination of materials, testing, and engineering is required. The total heat leak into any cryogenic assembly is comprised of three main parts: 1) heat leak through the insulation, 2) heat leak through the support structures, and 3) heat leak attributed to piping penetrations and feedthroughs (and their negative effects on the insulation). This "cold triangle" approach provides a basis for evaluating performance benefits of new materials and analyzing the cost effectiveness in overall system design. Provided are thermophysical data for aerogels, aerogel composites, novel multilayered composites, and glass bubbles for standard test conditions of 293 K and 78 K under conditions from high vacuum to ambient pressure. Examples of cryogenic storage tanks show the relative importance of both insulation and structural materials for achieving designs of highest energy efficiency.
Simulants are geologically complex materials that are developed to represent the physical and/or compositional characteristics of a planetary surface (e.g., a naturally occurring soil or regolith). There are dozens of commercially available simulants that have been developed over the years; each simulant exhibits unique physical, chemical, and mineralogical characteristics. Simulants are derived from either natural or synthetic sources (i.e., “feedstocks”) of glass, minerals, and rocks. These feedstock components are processed by crushing, pulverizing, melting, etc., and then combined in the appropriate proportions to represent a particular site, surface, or region (e.g., Lunar Highlands Regolith). The process of creating simulants therefore requires the mechanical breakdown and reincorporation of feedstock components which may contain crystalline silica minerals such as quartz, cristobalite, and tridymite. Certain crystalline silica particles of the respirable fraction (<10 μm in diameter) are of great concern; chronic and acute exposure to these respirable crystalline silica (RCS) can lead to permanent damage and scarring of lung tissue, incurable lung diseases (i.e., silicosis), lung cancer, COPD (chronic obstructive pulmonary disease), and kidney disease. Planetary simulants are used extensively as test materials in the in scientific and engineering communities (e.g., testing of dust mitigation technologies, in-situ resource utilization, rover mobility, hardware, soft goods etc.). As such, this assessment was developed to serve as a guide for simulant users, local Safety and Occupational Health professionals, and Industrial Hygienists to evaluate the risk of silicosis across a wide variety of Lunar and Martian simulants. The goal of these works is to ensure that those working with simulant can do so safely and with an informed understanding of potential health risks.
Simulants are geologically complex materials that are developed to represent the physical and/or compositional characteristics of a planetary surface (e.g., a naturally occurring soil or regolith). There are dozens of commercially available simulants that have been developed over the years; each simulant exhibits unique physical, chemical, and mineralogical characteristics. Simulants are derived from either natural or synthetic sources (i.e., “feedstocks”) of glass, minerals, and rocks. These feedstock components are processed by crushing, pulverizing, melting, etc., and then combined in the appropriate proportions to represent a particular site, surface, or region (e.g., Lunar Highlands Regolith). The process of creating simulants therefore requires the mechanical breakdown and reincorporation of feedstock components which may contain crystalline silica minerals such as quartz, cristobalite, and tridymite. Certain crystalline silica particles of the respirable fraction (<10 μm in diameter) are of great concern; chronic and acute exposure to these respirable crystalline silica (RCS) can lead to permanent damage and scarring of lung tissue, incurable lung diseases (i.e., silicosis), lung cancer, COPD (chronic obstructive pulmonary disease), and kidney disease. Planetary simulants are used extensively as test materials in the in scientific and engineering communities (e.g., testing of dust mitigation technologies, in-situ resource utilization, rover mobility, hardware, soft goods etc.). As such, this assessment was developed to serve as a guide for simulant users, local Safety and Occupational Health professionals, and Industrial Hygienists to evaluate the risk of silicosis across a wide variety of Lunar and Martian simulants. The goal of these works is to ensure that those working with simulant can do so safely and with an informed understanding of potential health risks.
Short-term tensile and low-cycle fatigue data are reported for five advance copper-base alloys: Sputtered Zr-Cu as received, sputtered Zr-Cu heat-treated, Glidcop AL-10, and NASA alloys 1-1A and 1-1B. Tensile tests were performed in argon at 538 C using an axial strain rate of 0.002/sec. Yield strength and ultimate tensile strength data are reported along with reduction in area values. Axial strain controlled low-cycle fatigue tests were performed in argon at 538C using an axial strain rate of 0.002/sec to define the fatigue life over the range from 100 to 3000 cycles for the five materials studied. It was found that the fatigue characteristics of the NASA 1-1A and NASA 1-1B compositions are identical and represent fatique life values which are much greater than those for the other materials tested. The effect of temperature on NASA 1-1B alloy at a strain rate of 0.002/sec was evaluated along with the effect of strain rates of 0.0004 and 0.01/sec at 538 C. Hold-time data are reported for the NASA 1-1B alloy at 538 C using 5 minute hold periods in tension only and compression only at two different strain range values. Hold periods in tension were much more detrimental than hold periods in compression.
Tapered (0 deg) laminates of S2/CE9000 and S2/SP250 glass/epoxies, and IM6/1827I graphite/epoxy were tested in cyclic tension. The specimens usually showed some initial stable delaminations in the tapered region, but these did not affect the stiffness of the specimens, and loading was continued until the specimens either delaminated unstably, or reached 10(exp 6) to 2 x 10(exp 7) million cycles with no unstable delamination. The final unstable delamination originated at the junction of the thin and tapered regions. A finite-element model was developed for the tapered laminate with and without the initial stable delaminations observed in the tests. The analysis showed that for both cases the most likely place for an opening (Mode 1) delamination to originate is at the junction of the taper and thin regions. For each material type, the models were used to calculate the strain energy release rate, G, associated with delaminations originating at that junction and growing either into the thin region or tapered region. For the materials tested, cyclic G(sub Imax) values from DCB tests were used with the maximum strain energy release rates calculated from the finite-element analysis to predict the onset of unstable delamination at the junction as a function of fatigue cycles. The predictions were compared to experimental values of maximum cyclic load as a function of cycles to unstable delamination from fatigue tests in tapered laminates. For the IM6/1827I and S2/SP250 laminates, the predictions agreed very well with the test data. Predicted values for the S2/CE9000 were conservative compared to the test data.
Tapered (0 deg) laminates of S2/CE9000 and S2/SP250 glass/epoxies, and IM6/1827I graphite/epoxy were tested in cyclic tension. The specimens usually showed some initial stable delaminations in the tapered region, but these did not affect the stiffness of the specimens, and loading was continued until the specimens either delaminated unstably, or reached 10(exp 6) to 2 x 10 (exp 7) million cycles with no unstable delamination. The final unstable delamination originated at the junction of the thin and tapered regions. A finite-element model was developed for the tapered laminate with and without the initial stable delaminations observed in the tests. The analysis showed that for both cases the most likely place for an opening (Mode I) delamination to originate is at the junction of the taper and thin regions. For each material type, the models were used to calculate the strain energy release rate, G, associated with delaminations originating at that junction and growing either into the thin region or tapered region. For the materials tested, cyclic G(sub Imax) values from DCB tests were used with the maximum strain energy release rates calculated from the finite-element analysis to predict the onset of unstable delamination at the junction as a function of fatigue cycles. The predictions were compared to experimental values of maximum cyclic load as a function of cycles to unstable delamination from fatigue tests in tapered laminates. For the IM6/1827I and S2/SP250 laminates, the predictions agreed very well with the test data. Predicted values for the S2/CE9000 were conservative compared to the test data.
The objectives are to introduce basic problem-solving techniques for product safety including problem identification, definition, solution criteria, test process and design, and data analysis. The students are given a recycled milk jug made of high density polyethylene (HDPE) by blow molding. The objectives are to design and perform proper material test(s) so they can evaluate the product safety if the milk jug is used in a certain way which is specified in the description of the procedure for this investigation.
Large scale, simulated fire tests of aircraft interior materials were carried out in salvaged airliner fuselage. Two "design" fire sources were selected: Jet A fuel ignited in fuselage midsection and trash bag fire. Comparison with six established laboratory fire tests show that some laboratory tests can rank materials according to heat and smoke production, but existing tests do not characterize toxic gas emissions accurately. Report includes test parameters and test details.
Relative wear of low and high temperature self lubricating polytetrafluoroethylene cage materials tested in ball bearings operating at high speeds at various temperatures