Influence of the as-built microstructure on the recrystallization of an additively manufactured Inconel939 Ni-based superalloy
This study investigates the influence of the as-built microstructure on the recrystallization (RX) behavior and mechanical properties of the Ni-based superalloy Inconel 939 produced by laser powder bed fusion (PBF-LB/M). Two distinct as-built microstructures were obtained by varying the hatch distance (h d ): a columnar, strongly textured condition (h d =50, termed h d 50) and an equiaxed, weakly textured condition (h d =70, termed h d 70)). Both were subjected to nine solution treatments combining three temperatures (1100, 1150, and 1200 °C) and three holding times (1, 4, and 8 h). Comprehensive microstructural characterization was conducted to assess grain morphology, texture, grain boundary character, dislocation density, and precipitate distribution. Recrystallization was found to be significantly slower than in cast counterparts, requiring higher temperatures and longer times for completion. The initial microstructure plays a decisive role: full RX was achieved only in hd70 specimens after treatment at 1200 °C for 8 h, whereas hd50 samples exhibited delayed and incomplete RX under identical conditions. This behavior is attributed to the finer grain size and higher fraction of high-angle grain boundaries in hd70, which promote recrystallization. Mechanical testing revealed that hd70 samples subjected to a 1200 °C/8 h treatment followed by standard double ageing show higher yield and tensile strengths across the investigated temperature range than both printed and cast Inconel939 processed under conventional conditions, albeit with slightly reduced ductility. The enhanced mechanical performance is attributed to the larger grain size, which limits grain boundary sliding. These results demonstrate the critical importance of controlling the as-built microstructure and tailoring post-processing strategies to optimize high-temperature performance of PBF-LB/M Inconel939.