DOE OSTI2018
By means of experimental and ab initio investigations, in this article we report on the cubic phase stability of Cu doped zirconia (ZrO 2 ) at room temperature, and further characterize its structural, optical and magnetic properties. Various compositions of Zr 1– x Cu x O 2 (0.01 ≤ x ≤ 0.25) nanocrystallites of average size ~16 nm were synthesized using co-precipitation technique. Thermal analysis and kinetics of crystallization revealed that the cubic phase at ambient temperature can be stabilized by using a critical calcination temperature of 500 °C for 8 h in air and a critical composition of $x_c$ = 0.10 ± 0.05. For $x < x_c$, some undigested monoclinic phase of ZrO 2 exists together with the cubic structure. However, for $x > x_c$, the monoclinic CuO emerges as a secondary phase with shrinkage of unit-cell volume with increasing the Cu content. At x = 0.05 and 500 °C calcination temperature, we observe a high degree of cubic crystallinity which breaks down into monoclinic phase with increasing calcination temperature beyond 550 °C. Electron magnetic resonance studies provide evidence for the substitution of Cu 2+ ( 2 D 5/9 ,3d 9 ) ions at Zr 4+ sites with g ∥ = 2.250, g ⊥ = 2.018 and average g a = (g ∥ + 2g ⊥ )/3 ~ 2.1. The temperature dependence of magnetic susceptibility measurements from 2 K to 300 K exhibits Curie–Weiss behaviour whose analysis using g a = 2.1 and spin S = 1/2 yields x = 0.028 and x = 0.068 for the nominal x = 0.05 and x = 0.20 samples, respectively. This magnetic analysis confirms the findings from x-ray diffraction that only a part of Cu is successfully doped into cubic phase of Cu-doped ZrO 2 . The optical bandgap decreases with increasing x, which is due to the emergence of Cu-d states at Fermi-level near the valence bands, thus making Cu-doped zirconia a hole doped (p-type) semiconductor.