Microstructural features of SiC('SCS') fibers demonstrating growth properties have been investigated using scanning and transmission electron microscopy. An etchant of fused KOH:KNO3 was developed which adequately brought out previously undetermined features.
A nonlinear plasma theory for self-modulation of pulsar radio pulses is discussed. A nonlinear Schroedinger equation is derived for strong electromagnetic waves propagating in an electron-positron plasma. The nonlinearities arising from wave-intensity-induced particle-mass variation may excite the modulational instability of circularly and linearly polarized pulsar radiation. The resulting wave envelopes can take the form of periodic wave trains or solitons. These nonlinear stationary waveforms may account for the formation of pulsar microstructures.
Hot pressed Si3N4 doped with 10 wt pct zyttrite as a sintering aid was studied. An equiaxed, fine grained microstructure was predominant, with no apparent porosity. Bend strengths were determined at room temperature and high temperatures (up to 1370 C). Oxidation was measured by weight gain at 1370 C in air. The resulting material exhibited very good room temperature strength (755 MPa). The work showed that room temperature strength can be improved significantly by using controlled Si3N4 powder with 10 wt pct zyttrite. High temperature strength (514 MPa) at 1370 C was nearly double that of hot-pressed Si3N4 (NC-132). The oxidation resistance at 1370 C was also higher than that of NC-132.
The microstructures of directionally grown monotectic alloys in metallic and organic systems fall into two categories those which can form aligned fibrous composite structures with even phase spacings and fiber sections, and those in which the phase distribution is coarser and less regular. This division appears to relate to the form of the phase diagram and has been rationalized by Cahn (1977, 1979) in terms of the relative surface energies between solid and two liquids to give steady state or nonsteady state profiles. The transition in growth behavior occurs when the ratio of the monotectic temperature to that of the upper consolute temperature is approximately 0.9. Differences in phase spacings between a range of monotectic and eutectic systems are discussed in terms of the expected growth interface shapes and the factors which will influence them.
The evolution of microalloyed steels from plain carbon steels is examined with emphasis on grain size control by use of Nb, Ti and V additions and by the application of controlled rolling. The structural changes during controlled rolling are described as well as the influence of alloying elements on these changes, and on the final microstructure. The achievement of high strength and toughness is discussed including the role of inclusions.
Columbium, for which the United States is 100 percent import reliant, is of strategic importance to the U.S. aerospace industry. A major amount of the Cb is used in Inconel 718. Should Cb sources be disrupted, it may be desired to use a grade of Cb melting stock having greater Sn content then the preferred vacuum rade. Additions of Sn to Inconel 718 were varied from none added to 1 wt %. The Sn additions below 800 ppm had no detrimental effects on 650 C stress rupture behavior; however, 1-wt % Sn severely degraded both life and ductility. Additions of Sn in excess of 200 ppm were slightly detrimental to the 425 C tensile yield strength and ductility. The Sn additions had no effect on the microstructure of Inconel 718 even after stress rupture testing for over 6000 hr at 650 C.
The history of research into the microstructure and properties of ceramic ware is discussed; methods of producing ceramics with particular characteristics are investigated. Bubbles, sintering, cracks, and electron microscopy are discussed.
Ni-Mo alloys of compositions ranging from pure Ni to Ni-40 at % Mo were rapidly solidified by Chill Block Melt Spinning in vacuum and were examined by optical metallography, X-ray diffraction and transmission electron microscopy. Rapid solidification resulted in an extension of molybdenum solubility in nickel from 28 to 37.5 at %. A number of different phases and microstructures were seen at different depths (solidification conditions) from the quenched surface of the melt spun ribbons.
It is demonstrated that layered synthetic microstructures (LSMs) can provide mirrors with enhanced normal incidence reflectance in the 300-A spectral region. Experimental results are presented for Pt-Si and Ir-Si structures fabricated by electron-beam deposition at pressures of about 10 to the -6th Torr, and it is shown that the enhancement is realized over a limited bandwidth of 75 A. One potential application of LSMs is their use as coatings on diffraction gratings to enhance normal incidence reflection efficiencies. Preliminary results for the Ir-Si combination on a diffraction grating show that LSMs enhance grating efficiencies in the EUV by a factor of about 3.
Microstructural characteristics of Al2O3 scales grown as protective coatings on NiCrAl alloys used in jet engines are described. The alloys were pure or doped with 0.3 percent Zr or Y and oxidized in 1 atm air at 1100 C for 0.1, 1 or 20.0 hr. The scales were then examined under a microscope. Transient epitaxial scales, formed during the 0.1 hr treatment and containing Ni, Cr and Al, consisted of a mosaic of subgrains and precipitates of different phases. The Y and Zr dopants had no effect on the nucleation site locations. The appearance of intergranular porosity at 0.1 hr was exacerbated after the 1 hr treatment. A bimodal void distribution appeared after 20 hr, when no porosity was evident. The detection of local areas of preferred orientation is taken as a spur to further studies of scale growth to gain control of the grain size or even to produce single crystal scales.
A transmission electron microscopy (TEM) examination of aluminum-lithium-copper alloys was conducted. The principal purpose is to characterize the nature, size, and distribution of stringer particles which result from the powder metallurgy (P/M) processing of these alloys. Microstructural features associated with the stringer particles are reported that help explain the stress corrosion susceptibility of the powder metallurgy-processed Al-Li-Cu alloys. In addition, matrix precipitaton events are documented for a variety of heat treatments and process variations. Hot rolling is observed to significantly alter the nature of matrix precipitation, and the observations are correlated with concomitant mechanical property variations.
A microstructural examination and chemical analysis are conducted for reaction-bonded Si3N4 specimens that were isostatically hot pressed at 1850, 1950, and 2050 C. The present observations indicate that the previously reported increase in the 1200 C bend strength of reaction-bonded Si3N4, after pressing at 2050 C exclusively, is due to the relative oxygen levels of the isostatically hot pressed specimens; calculations show that an SiO2 content of less than about 2.2 vol pct is needed to yield the 1200 C strength increase.
The Ni-base superalloy MAR-M246 (Hf) was directionally solidified during low gravity maneuvers aboard a NASA KC-135 aircraft. Gravity force variations during this process yielded a concomitant variation in microstructure and microsegregation. Secondary dendrite arm spacings are noted to be larger in the low-g portion; this, in turn, decreases the extent of interdendritic segregation. The amount of Hf in both the carbides and interdendritic eutectic increases as the gravity force diminishes. Fewer carbides are present in the low-g regions.
The use of microgravity for industrial research in the processing of cast iron was investigated. Solidification experiments were conducted using the KC-135 and F-104 aircraft, and an experiment plan was developed for follow-on experiments using the Shuttle. Three areas of interest are identified: (1) measurement of thermophysical properties in the melt; (2) understanding of the relative roles of homogeneous nucleation, grain multiplication, and innocultants in forming the microstructure; and (3) exploring the possibility of obtaining an aligned graphite structure in hypereutectic Fe, Ni, and Co.
The automotive Stirling engine now under development by DOE/NASA as an alternative to the internal combustion engine, imposes severe materials requirements for the hot portion of the engine. Materials selected must be low cost and contain a minimum of strategic elements so that availability is not a problem. Heater head tubes contain high pressure hydrogen on the inside and are exposed to hot combustion gases on the outside surface. The cylinders and regenerator housings must be readily castable into complex shapes having varying wall thicknesses and be amenable to brazing and welding operations. Also, high strength, oxidation resistance, resistance to hydrogen permeation, cyclic operation, and long-life are required. A research program conducted by NASA Lewis focused on alloy chemistry and microstructural control to achieve the desired properties over the life of the engine. Results of alloy selection, characterization, evaluation, and actual engine testing of selected materials are presented.
The effects of N2 pressure (0.1 to 50 MPa) during sintering on the thickness of the microstructurally heterogeneous layer (MHL) formed near the surface of the compact, transverse-rupture strength, were investigated for Si3N4-(10 to 20) mol % MgO-5.5 mol % Al2O3 ceramics. The sintering temperature and time were 1973 K and 3.6 ks, respectively. The N2 gas was introduced into the furnace at about 1273 K. When the compacts were sintered under a certain N2 pressure, for example, about 20 and 7 MPa for 10 and 15 mol% MgO, respectively, the evolutions of N and Si were suppressed. The thickness of the MHL became very small and at the same time the strength of the surface layer of the compact (which was normally less than that of the inside in the case of 0.1 MPa) became nearly the same value as that of the inside. At higher pressure, the strength of both surface layer and the inside decreased considerably. Some discussion was made on these results.
The influence of composition on the microstructure of single crystal nickel-base superalloys was investigated. Co was replaced by Ni, and Ta was replaced by either Ni or W, according to a matrix of compositions based on MAR-M247. Substitution of Ni for Co caused an increase in gamma-prime solvus temperature, an increase in gamma-gamma-prime lattice mismatch, and the precipitation of W-rich phases in the alloys with high refractory metal levels. Substitution of Ni for Ta caused large decreases in gamma-prime solvus temperature, gamma-prime volume fraction, and gamma-gamma-prime lattice mismatch, whereas substitution of W for Ta resulted in smaller decreases in these features. For the alloys with gamma-prime particles that remained coherent, substitution of Ni for Co caused an increase in gamma-prime coarsening rate. The two alloys with the largest magnitude of lattice mismatch possessed gamma-prime particles which lost coherency during unstressed aging and exhibited anomalously low coarsening rates. Creep exposure at 1000 C resulted in the formation of gamma-prime lamellae oriented perpendicular to the applied stress axis in all alloys.
An investigation of the fatigue crack propagation FCP behavior of two aluminum alloys is performed to simulate spectrum loading conditions found at critical locations in high performance fighter aircraft. Negative loads are shown to be eliminated for the tension-compression spectrum for low to intermediate maximum stress intensities, and load interactions are found to be more significant at higher stress intensities and with more plasticity at the crack tip. In the second part, the influence of microstructural features including grain size, inclusions, and dispersoids on constant amplitude and spectrum crack growth behavior in aluminum alloys is studied. At low stress intensities the I/M alloy demonstrated better FCP resistance than the P/M 7091 alloy for both constant amplitude and spectrum testing, and the inhomogeneous planar slip and large grain size of 7050 limit dislocation interactions, thereby improving FCP performance.