DOE OSTI2018

Microstructural Characterization of FeCrAl C26M Tubes

The present report summarizes the initial nanoindentation characterization of a FeCrAl alloy, C26M. Microstructural analysis using electron backscatter diffraction showed a highly textured system with the axial surface favoring orientations near the [110] and the longitudinal surface near the [111]. A large spread of grain sizes was observed from a few μm’s to 100 μm with an average grain size of ~70 μm. Nanoindentation with a Berkovich tip measured a similar hardness and modulus of ~4.4 GPa and ~240 GPa on the two surfaces, respectively. Mounting specimens in epoxy was found to be the cause of a lower stiffness and, consequently, a lower hardness and modulus value. Spherical nanoindentation was measured on the longitudinal surface of the tube to determine the nanoindentation modulus and nanoindentation yield strength. Using a 10 μm tip, the measured modulus was ~220 GPa and the yield strength was ~1.4 GPa. Indentation with a 100 μm tip resulted in a measured modulus value of ~220 GPa and yield strength of ~1.1 GPa. Some early characterization of the differences in spherical nanoindentation response of the axial and longitudinal surfaces showed a small difference between the two, but a more detailed analysis with a stiffer mounting configuration is needed to draw conclusions.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Exploring Electron/Proton Transfer and Conformational Changes in the Nitrogenase MoFe Protein and FeMo-cofactor Through Cryoreduction/EPR Measurements

Here, we combine cryoreduction/annealing/EPR measurements of nitrogenase MoFe protein with results of earlier investigations to provide a detailed view of the electron/proton transfer events and conformational changes that occur during early stages of [e - /H + ] accumulation by the MoFe protein. This includes reduction of (i) the non-catalytic state of the iron-molybdenum cofactor (FeMo-co) active site that is generated by chemical oxidation of the resting-state cofactor (S = 3/2)) within resting MoFe (E 0 ), and (ii) the catalytic state that has accumulated n =1 [e - /H + ] above the resting-state level, denoted E 1 (1H) (S ≥ 1) in the Lowe-Thorneley kinetic scheme. FeMo-co does not undergo a major change of conformation during reduction of oxidized FeMo-co. In contrast, FeMo-co undergoes substantial conformational changes during the reduction of E 0 to E 1 (1H), and of E 1 (1H) to E 2 (2H) (n = 2; S = 3/2). The experimental results further suggest that the E 1 (1H) → E 2 (2H) step involves coupled delivery of a proton and electron (PCET) to FeMo-co of E 1 (H) to generate a non-equilibrium S = ½ form E 2 (2H)*. This subsequently undergoes conformational relaxation and attendant change in FeMo-co spin state, to generate the equilibrium E 2 (2H) (S = 3/2) state. Unexpectedly, these experiments also reveal conformational coupling between FeMo-co and P-cluster, and between Fe protein binding and FeMo-co, which might play a role in gated ET from reduced Fe protein to FeMo-co.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2014

Improved gas sensing and dielectric properties of Fe doped hydroxyapatite thick films: Effect of molar concentrations

Highlights: • We report improved gas sensing and dielectric characteristics of Fe ion exchanged HAp films. • Fe doped HAp film shows maximum gas response at relatively lower temperature. • Response and gas uptake capacity of sensors is improved for appropriate amount of Fe ions in HAp matrix. • Fe-HAp films exhibit remarkable improvement in dielectric properties compared to pure HAp. • Fe doped HAp films show significant improvement in gas sensing as well as in dielectric properties. - Abstract: In the present work Fe doped hydroxyapatite (Fe-HAp) thick films has been successfully utilized to improve the gas sensing as well as its dielectric properties. Initially, HAp nano powder is synthesized by chemical precipitation process and later on Fe ions are doped in HAp by ion exchange process. Structural and morphological modifications are observed by means of X-ray diffraction and scanning electron microscopy analysis. The sensing parameters such as operating temperature, response/recovery time and gas uptake capacity are experimentally determined. The Fe-HAp (0.05 M) film shows improved CO and CO{sub 2} gas sensing capacity at lower operating temperature compared to pure HAp. Moreover, variation of dielectric constant and dielectric loss for pure and Fe-HAp thick films are studied as a function of frequency in the range of 10 Hz–1 MHz. The study reveals that Fe doped HAp thick films improve the sensing and dielectric characteristics as compared to pure HAp.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Effect of sputtering pressure on microstructure and bolometric properties of Nb:TiO{sub 2−x} films for infrared image sensor applications

This study aims to investigate the influence of the sputtering pressure (P{sub S}) on Nb:TiO{sub 2−x} films to enhance the bolometric properties. A decrease in the growth rate with the sputtering pressure was perceived in amorphous Nb:TiO{sub 2−x} films. The incorporation of oxygen with P{sub S} was confirmed in an X-ray photo electron spectroscopy analysis. The electrical resistivity was increased with an increase in P{sub S} due to a decrease in the number of oxygen vacancies. The linear I-V characteristics confirmed the ohmic contact behavior between the Nb:TiO{sub 2−x} layer and the electrode material. The present investigation finds that the sample with lower resistivity has good bolometric properties with low noise and high universal bolometric parameters. Finally, the Nb:TiO{sub 2−x} sample deposited at a sputtering pressure of 2 mTorr shows better bolometric properties than other materials for infrared image sensor applications.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2011

Dispersion Morphology of Poly(methyl acrylate)/Silica Nanocomposites

Nearly monodisperse poly(methyl acrylate) (PMA) and spherical SiO{sub 2} nanoparticles (NP, d = 14 {+-} 4 nm) were co-cast from 2-butanone, a mutually good solvent and a displacer of adsorbed PMA from silica. The effects of NP content and post-casting sample history on the dispersion morphology were found by small-angle X-ray scattering supplemented by transmission electron microscopy. Analysis of the X-ray results show that cast and thermally annealed samples exhibited a nearly random particle dispersion. That the same samples, prior to annealing, were not well-dispersed is indicative of thermodynamic miscibility during thermal annealing over the range of NP loadings studied. A simple mean-field thermodynamic model suggests that miscibility results primarily from favorable polymer segment/NP surface interactions. The model also indicates, and experiments confirm, that subsequent exposure of the composites to the likely displacer ethyl acetate results in entropic destabilization and demixing into NP-rich and NP-lean phases.

36 MATERIALS SCIENCE↗
DOE OSTI2012

High-Performance LiNi0.5Mn1.5O4 Spinel Controlled by Mn3+ Concentration and Site Disorder

The influences of Mn3+ ions on the properties of high voltage spinel LiNi0.5Mn1.5O4 is systematically investigated in this work. The content of Mn3+ ions in the spinel is tuned by further annealing of the sample or partially substitution of Ni2+ in the lattice structure. The former decreases the amount of Mn3+ while the latter increases Mn3+ concentration, which has been confirmed by both X-ray diffraction (XRD) and electron diffraction analysis. It has also been experimentally and theoretically proven that Mn3+ ions are directly related to the disordering between Ni2+ and Mn4+ on the octahedral sites in the spinel structure which facilitates the transportation of Li+ ions especially at elevated current densities. An extremely cycling stability as well as good rate capability have been observed in the Cr-substituted spinel confirming that an appropriate amount of Mn3+ ions is the key for a high performance high voltage spinel.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Big Data Analytics for Scanning Transmission Electron Microscopy Ptychography

Electron microscopy is undergoing a transition; from the model of producing only a few micrographs, through the current state where many images and spectra can be digitally recorded, to a new mode where very large volumes of data (movies, ptychographic and multi-dimensional series) can be rapidly obtained. In this paper, we discuss the application of so-called “big-data” methods to high dimensional microscopy data, using unsupervised multivariate statistical techniques, in order to explore salient image features in a specific example of BiFeO 3 domains. Remarkably, k-means clustering reveals domain differentiation despite the fact that the algorithm is purely statistical in nature and does not require any prior information regarding the material, any coexisting phases, or any differentiating structures. While this is a somewhat trivial case, this example signifies the extraction of useful physical and structural information without any prior bias regarding the sample or the instrumental modality. Further interpretation of these types of results may still require human intervention. Finally, however, the open nature of this algorithm and its wide availability, enable broad collaborations and exploratory work necessary to enable efficient data analysis in electron microscopy.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Disruption of crystalline structure of Sn3.5Ag induced by electric current

This study presented the disruption of the Sn and Ag{sub 3}Sn lattice structures of Sn3.5Ag solder induced by electric current at 5–7 × 10{sup 3} A/cm{sup 2} with a high resolution transmission electron microscope investigation and electron diffraction analysis. The electric current stressing induced a high degree of strain on the alloy, as estimated from the X-ray diffraction (XRD) peak shift of the current stressed specimen. The XRD peak intensity of the Sn matrix and the Ag{sub 3}Sn intermetallic compound diminished to nearly undetectable after 2 h of current stressing. The electric current stressing gave rise to a high dislocation density of up to 10{sup 17}/m{sup 2}. The grain morphology of the Sn matrix became invisible after prolonged current stressing as a result of the coalescence of dislocations.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2014

Laser assisted high entropy alloy coating on aluminum: Microstructural evolution

High entropy alloy (Al-Fe-Co-Cr-Ni) coatings were synthesized using laser surface engineering on aluminum substrate. Electron diffraction analysis confirmed the formation of solid solution of body centered cubic high entropy alloy phase along with phases with long range periodic structures within the coating. Evolution of such type of microstructure was a result of kinetics associated with laser process, which generates higher temperatures and rapid cooling resulting in retention of high entropy alloy phase followed by reheating and/or annealing in subsequent passes of the laser track giving rise to partial decomposition. The partial decomposition resulted in formation of precipitates having layered morphology with a mixture of high entropy alloy rich phases, compounds, and long range ordered phases.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2018

Characteristics of Calcium-Aluminate Slags and Pig Iron Produced from Smelting-Reduction of Low-Grade Bauxites

Low-grade bauxite ores are not favorable in the conventional Bayer process for alumina production, as they are producing more bauxite residue (red mud) and accompanying lower alumina yield than high-grade ores. In the current study, the thermodynamics and characterization of calcium-aluminate slags and pig iron produced from smelting reduction of high iron- and silica-containing bauxites are studied. Coke and limestone are used to reduce the iron oxide and adjust the basicity of slag during smelting. There is evidence that complete iron separation from bauxite is feasible through smelting-reduction process, and up to 99.9 pct of iron can be eliminated. Moreover, it is shown that the partial separation of silicon, titanium, and other elements from the Al{sub 2}O{sub 3}-containing slag occurs. The phase compositions and the distribution of elements between the metal and slag phases provide information about the high-temperature behavior of the bauxite components during smelting reduction. Employing electron microscopy analysis, it is indicated that the morphologies of CaO·Al{sub 2}O{sub 3}, 12CaO·7Al{sub 2}O{sub 3}, 2CaO·Al{sub 2}O{sub 3}·SiO{sub 2}, and CaO·Al{sub 2}O{sub 3}·SiO{sub 2} phases in the slag, as well as the complex oxides of Ca-Al-Si-Ti in the slag behave differently as the mass ratio of Al{sub 2}O{sub 3}/(Fe{sub 2}O{sub 3 }+ SiO{sub 2}) in the bauxite changes. It is also shown that the phases of slag produced from smelting-reduction below 5 K s{sup −1} of cooling rate are proper for further leaching process.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Origin of giant dielectric constant and conductivity behavior in Zn{sub 1−x}Mg{sub x}O (0 ≤ x ≤ 0.1) ceramics

Highlights: • Mg doped zinc oxide ceramics were fabricated by co-precipitation/solid state reaction. • MZO ceramics shown a Debye type and colossal dielectric response. • Physical absorption of atmospheric water vapor contributes these high permittivity. • The fabricated ceramic shows Maxwell–Wagner type of relaxation. - Abstract: Zn{sub 1−x}Mg{sub x}O ( ≤ x ≤ 0.1) ceramics were fabricated by conventional solid-state reaction of co-precipitated zinc oxide and magnesium hydroxide nanoparticles. Structural and morphological properties of the fabricated ceramics were studied using X-ray diffraction and scanning electron microscopic analysis. The dielectric measurements of the ceramics were carried out as a function of frequency and temperature respectively. Interestingly, Mg doped ZnO (MZO) samples exhibited colossal dielectric response (∼1 × 10{sup 4} at 1 kHz) with Debye like relaxation. The detailed dielectric studies and thermal analyses showed that the unusual dielectric response of the samples were originated from the defected grain and grain boundary (GB) conductivity relaxations due to the absorbed atmospheric water vapor (moisture). Impedance spectroscopy was employed to determine the defected grain and GB resistances, capacitances and which supported Maxwell–Wagner type relaxation phenomena.

36 MATERIALS SCIENCE↗
DOE OSTI2014

Defect structure of ultrafine MgB{sub 2} nanoparticles

Defect structure of MgB{sub 2} bulk and ultrafine particles, synthesized by solid state reaction route, have been investigated mainly by the aid of X-band electron paramagnetic resonance spectrometer. Two different amorphous Boron (B) precursors were used for the synthesis of MgB{sub 2}, namely, boron 95 (purity 95%–97%, <1.5 μm) and nanoboron (purity >98.5%, <250 nm), which revealed bulk and nanosized MgB{sub 2}, respectively. Scanning and transmission electron microscopy analysis demonstrate uniform and ultrafine morphology for nanosized MgB{sub 2} in comparison with bulk MgB{sub 2}. Powder X-ray diffraction data show that the concentration of the by-product MgO is significantly reduced when nanoboron is employed as precursor. It is observed that a significant average particle size reduction for MgB{sub 2} can be achieved only by using B particles of micron or nano size. The origin and the role of defect centers were also investigated and the results proved that at nanoscale MgB{sub 2} material contains Mg vacancies. Such vacancies influence the connectivity and the conductivity properties which are crucial for the superconductivity applications.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2018

Effects of Fe concentration on helium bubble formation in NiFe x single-phase concentrated solid solution alloys

The formation of helium bubbles and the consequential property degradation are critical challenges for materials used in advanced nuclear energy systems. The mechanism of helium bubble formation in a series of NiFe x (x = 0, 20, 35, or 50 at.%) single-phase concentrated solid solution alloys (SP-CSAs) are studied in this work. Transmission electron microscopy analysis shows that with increasing Fe concentration, the average bubble size decreases while the bubble number density increases, indicating the growth of large helium bubbles in NiFe x SP-CSAs is suppressed by increasing the alloy chemical complexity through increased Fe concentration. Mechanisms for the slower bubble growth rate in NiFe x binary SP-CSAs compared Ni are identified. These mechanisms include promotion of Frenkel pair recombination, denser and more homogeneously distributed nucleation sites, and increased helium atom densities inside the bubbles. Here, the results demonstrate that optimizing the chemical complexity in SP-CSAs can be an effective approach to design materials with superior resistance to helium bubble nucleation and growth.

36 MATERIALS SCIENCE↗
DOE OSTI2015

Preparation of the egg membrane bandage contained the antibacterial Ag nanoparticles

Silver nanoparticles were synthesized using a rapid, single step, and completely green biosynthetic method employing aqueous aloe leaf extracts as both the reducing and capping agent. Transmission electron microscopy analysis revealed the average size of silver nanoparticles approximately 18.05 nm. Fourier transform infrared spectroscopy observation showed the estimation of two kinds of binding sites between aqueous aloe leaf and aqueous aloe leaf with silver nanoparticles. In addition, the critical roles of the concentration of silver nitrate, temperature, and reaction time in the formation of silver nanoparticles had been illustrated. Furthermore, silver nanoparticles were deposited on egg membrane bandage, forming a new egg membrane bandage that contained silver nanoparticles that exhibiting excellent antibacterial effects against Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus, which was 2.5 times stronger than the commercially available bandage. - Graphical Abstract: Display Omitted.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2017

Effect of adjusting composition on the crystallization and luminescence properties in NaYF{sub 4}:Er{sup 3+} embedded glass ceramics

Highlights: • Intense 2.7 μm emission was achieved in transparent glass ceramics containing NaYF{sub 4}:Er{sup 3+} nanocrystals. • The crystallization and luminescence properties of the nanocrystals embedded glass ceramics are tuned by adjusting the Na{sub 2}O/NaF ratio. • Modifying the properties of glass ceramics through adjusting the glass composition is an effective route. - Abstract: Intense 2.7 μm emission was achieved in transparent glass ceramics containing NaYF{sub 4}:Er{sup 3+} nanocrystals. The effect of adjusting Na{sub 2}O/NaF ratio in glass composition on the crystallizing and luminescence behavior in the glass ceramics was investigated. The controllable crystallization property of NaYF{sub 4} nanocrystals was remained after modifying the glass composition and the crystallization temperature was largely reduced for the samples with high Na{sub 2}O content. The X-ray diffraction and transmission electron microscopy analysis evidenced the shrink of lattice parameter with increasing Na{sub 2}O content. High transparency was kept for these glass ceramic samples, and intense upconversion, near- and mid-infrared emissions were obtained in Er{sup 3+}-doped glass ceramics with an increase of red/green ratio and prominent Stark splits in the sample with high Na{sub 2}O content, indicating the change of crystal field around Er{sup 3+} in the host matrix. Our results indicate that the crystallization and luminescence properties of glass ceramics could be modified through adjusting the glass composition, and it is an effective route to develop glass ceramics with favorable properties.

36 MATERIALS SCIENCE↗
DOE OSTI2014

Yttria-stabilized zirconia buffered silicon to optimize in-plane electrical conductivity of [Ca{sub 2}CoO{sub 3}]{sub 0.62}[CoO{sub 2}] thin films

The monolithic integration of thermoelectric generators and magnetoresistive functionality on the basis of misfit cobaltate [Ca{sub 2}CoO{sub 3}]{sub 0.62}[CoO{sub 2}] thin films into silicon technology is a prerequisite for their application in miniaturized electric circuits. Here, we report on [Ca{sub 2}CoO{sub 3}]{sub 0.62}[CoO{sub 2}] thin films grown by pulsed laser deposition on (001)-silicon with a thin epitaxial yttria-stabilized zirconia (YSZ) buffer layer. X-ray diffraction and cross-sectional high resolution transmission electron microscopy analysis reveal that high quality c-axis oriented heteroepitaxial [Ca{sub 2}CoO{sub 3}]{sub 0.62}[CoO{sub 2}] films with a 12-fold in-plane rotational symmetry can be grown, which exhibit remarkable lower electrical resistivity compared to those with random in-plane orientation. This result is explained by energetically preferred epitaxial growth directions of the pseudo hexagonal [CoO{sub 2}] sublayer in monoclinic [Ca{sub 2}CoO{sub 3}]{sub 0.62}[CoO{sub 2}] onto the cubic (001)-YSZ surface leading to a highly symmetric in-plane mutual orientation of the charge transporting CoO{sub 2} sublayer domains.

36 MATERIALS SCIENCE↗
DOE OSTI2013

THERMAL STRUCTURE OF CORONAL LOOPS AS SEEN WITH NORIKURA CORONAGRAPH

The thermal structure of a coronal loop, both along and across the loop, is vital in determining the exact plasma heating mechanism. High-resolution spectroscopic observations of the off-limb corona were made using the 25 cm Norikura coronagraph, located at Norikura, Japan. Observations on a number of days were made simultaneously in four forbidden iron emission lines, namely, the [Fe XI] 7892 A line, the [Fe XIII] 10747 A and 10798 A lines, and the [Fe XIV] 5303 A line and on some days made only in the [Fe XI] 7892 A and [Fe X] 6374 A lines. Using temperature sensitive emission line ratios [Fe XIV] 5303 A/[Fe XIII] 10747 A and [Fe XI] 7892 A/[Fe X] 6374 A, we compute the electron temperatures along 18 different loop structures observed on different days. We find a significant negative temperature gradient in all of the structures observed in Fe XIV and Fe XIII and a positive temperature gradient in the structures observed in Fe XI and Fe X. Combining these results with the previous investigations by Singh and his collaborators, we infer that the loop tops, in general, appear hotter when observed in colder lines and colder when observed in relatively hotter lines as compared to their coronal foot points. We suggest that this contrasting trend observed in the temperature variation along the loop structures can be explained by a gradual interaction of different temperature plasma. The exact mechanism responsible for this interaction must be investigated further and has the potential to constrain loop heating models.

79 ASTRONOMY AND ASTROPHYSICS↗
DOE OSTI2016

Catastrophic degradation of the interface of epitaxial silicon carbide on silicon at high temperatures

Epitaxial cubic silicon carbide on silicon is of high potential technological relevance for the integration of a wide range of applications and materials with silicon technologies, such as micro electro mechanical systems, wide-bandgap electronics, and graphene. The hetero-epitaxial system engenders mechanical stresses at least up to a GPa, pressures making it extremely challenging to maintain the integrity of the silicon carbide/silicon interface. In this work, we investigate the stability of said interface and we find that high temperature annealing leads to a loss of integrity. High–resolution transmission electron microscopy analysis shows a morphologically degraded SiC/Si interface, while mechanical stress measurements indicate considerable relaxation of the interfacial stress. From an electrical point of view, the diode behaviour of the initial p-Si/n-SiC junction is catastrophically lost due to considerable inter-diffusion of atoms and charges across the interface upon annealing. Temperature dependent transport measurements confirm a severe electrical shorting of the epitaxial silicon carbide to the underlying substrate, indicating vast predominance of the silicon carriers in lateral transport above 25 K. This finding has crucial consequences on the integration of epitaxial silicon carbide on silicon and its potential applications.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗