Overview of the PM-HIP work performed on stainless steel 316H as part of the microreactor program. High temperature mechanical testing was performed, with concerns identified with the creep-fatigue performance. Variations in feedstock and processing parameters did not conclusively identify the primary factor in the reduced creep-fatigue performance.
Preliminary results are presented on performing Resonance Ultrasound Spectroscopy (RUS) measurements on stainless steel 316 H fabricated using Laser Powder Bed Fusion (LPBF) additive manufacturing methods. The elastic constants determined using RUS measurements are compared to tensile tests and RUS measurements on wrought stainless steel 316 L. Good agreement is found between the RUS measurements and the mechanical testing results.
The Advanced Materials and Manufacturing Technology (AMMT) program develops cross-cutting technologies in support of a broad range of nuclear reactor technologies and maintains U.S. leadership in materials and manufacturing technologies for nuclear energy applications. The overarching vision of AMMT is to accelerate the development, qualification, demonstration, and deployment of advanced materials and manufacturing technologies to enable reliable and economical nuclear energy. Solid-state advanced manufacturing techniques can overcome some of the challenges in liquid-based additive manufacturing (AM) processes and should therefore be considered in material design and manufacturing as well. The work presented in this report forms part of a study on solid-state AM techniques of 316 stainless steels (SS) and oxide dispersion strengthened (ODS) steel components and supports the vision and goals of the AMMT program relevant to accelerate the development and deployment of advanced manufacturing processes. Achieving this can provide a safety improvement through larger safety margins, economic benefit for higher efficiency during operation, and a cost reduction through more effective manufacturing processes and less waste. This study provides preliminary information on development of the fused-filament fabrication (FFF) process using different powder types to demonstrate the sensitivity, and therefore the characterization of these sample components. The full solid-state manufacturing feasibility study will be completed and reported in a final feasibility evaluation during 2025. The study investigation used two 14YWT ODS powder batches, which provided information and the effect of different powder morphologies on manufacturability. The two 316SS powders demonstrated the effect of powder size on the manufacturability using FFF. Two product forms, namely a honeycomb structure and flat samples, were manufactured to demonstrate the flexibility of product form.
This study provides the first- of- a- kind results of direct tube formation through shear assisted processing and extrusion (ShAPE) for oxide dispersion strengthened (ODS) steel material; previously only bar was successfully made. The Advanced Materials and Manufacturing Technology (AMMT) program develops cross-cutting technologies in support of a broad range of nuclear reactor technologies and maintains U.S. leadership in materials and manufacturing technologies for nuclear energy applications. The overarching vision of AMMT is to accelerate the development, qualification, demonstration, and deployment of advanced materials and manufacturing technologies to enable reliable and economical nuclear energy. Solid-state advanced manufacturing techniques can overcome some of the challenges in liquid-based additive manufacturing processes and should therefore be considered in material design and manufacturing as well. The work presented in this report forms part of a study on solid-state additive manufacturing techniques of 316 stainless steels and ODS steel components and supports the vision and goals of the AMMT program relevant to accelerate the development and deployment of advanced manufacturing processes. Achieving this can provide a safety improvement through larger safety margins, economic benefit for higher efficiency during operation, and a cost reduction through more effective manufacturing processes and less waste.
The University of California, Davis is involved in a project to deploy and enhance an artificial intelligence (AI) system for predicting and preventing plasma disruptions on the DIII D tokamak, under the funding from Department of Energy DE-SC0023500 (title: AI/Deep Learning FRNN Software for Prediction & Real-Time Control of DIII-D Plasma Control System (PCS)). The overarching goal is to demonstrate that real-time, AI-guided intervention can proactively modify the plasma state to avoid or mitigate disruptions—a critical challenge for the future of fusion energy.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Powder metallurgy hot isostatic pressing (PM-HIP) Microreactor Project presentation for the 2023 Advanced Reactor Technology (ART) program review.
Explore the source record for details and available documents.
To harness the potential of laser powder bed fusion (LPBF) 316H stainless steel (SS) for use in advanced nuclear reactors, extensive research efforts are needed to develop optimal laser processing parameters and appropriate heat treatments, taking into account various manufacturing platforms and locations. Furthermore, it is crucial to assess the material properties in environments relevant to reactor operating conditions. In collaboration with Oak Ridge National Laboratory (ORNL) and Los Alamos National Laboratory (LANL), Argonne National Laboratory (ANL) is dedicated to gaining insights into how the manufacturing process and post-build treatments impact the performance of LPBF 316H SS. This report provides an overview of ANL's research findings for FY23, focusing on LPBF 316H SS produced using a Renishaw AM400 laser system. Specifically, our research has concentrated on three key areas: 1) Optimum laser processing parameters: Leveraging the high-throughput printing technology, we systematically varied the laser power, exposure time and point distance within the same build. By measuring the as-printed porosity, we identified an optimum printing parameter window that produced materials with near-complete density; 2) Post-built treatment development: Materials printed with the optimum laser parameters underwent treatments including stress relief, solution annealing, and hot isostatic pressing. Subsequently, we fabricated tension, creep, and fatigue specimens from materials subjected to these different conditions. Over the next year, a series of scoping tests will be conducted to facilitate the selection of the most suitable post-build treatment condition; 3) Thermal aging effects on microstructure and properties: thermal aging at 550°C, 650°C and 750°C was conducted on LPBF 316H SS specimens up to 2500 h. Microstructural characterization was performed with electron microscopy, and the evolution of the dislocation cell structures and secondary phases was studied. Microhardness tests and tension tests were conducted to quantify changes in mechanical properties. The results revealed that the aged LPBF 316H SS exhibited a high density of Cr-rich and Mo-rich fine precipitates within grains due to the presence of a high density of dislocations and the globally distributed dislocation cell structures, which served as heterogeneous nucleation sites for secondary phases. Along grain boundaries, a Mo-Cr-rich phase, observed in 750°C-aged conditions, displayed significant thermal coarsening. Throughout the aging process, various mechanisms, including stress relaxation, dislocation cell structure recovery, solution hardening, and precipitation hardening, competed to influence materials strength. These results contribute towards establishing the technical basis for qualifying LPBF 316H SS for advanced nuclear reactor applications.
Comparison of SEM images obtained for samples 316H-1, 5, 7, and 10 revealed that samples 1 and 5 were subjected to more corrosion than the other two samples. Pores of an average of 1µm size were also observed scattered near the edge of each sample. Corrosion layer thickness was measured from edge of the corroded surface to the pore region. It was found that 316H-1 and 316H-5 had more corrosion damage with 82.40µm and 100µm respectively. Sample 316H-5 posed a challenge in measuring the corrosion layer thickness due to it breaking off from the parent sample during polishing. Samples 316H-7 and 316H-10 are less corroded with 26.57µm and 39.94µm thickness respectively.
We report the corrosion behavior and tensile properties of oxide dispersion strengthened (ODS) FeCr, FeCrAl, FeCrAlMo steels and 316H stainless steel were evaluated after 1000 h at 700 °C in static sodium with and without an oxygen getter (Zr foil). Without Zr foil to getter the dissolved oxygen in the liquid sodium, combined oxidation (formation of Cr, Fe-rich or Al-rich oxides) and dissolution of the studied materials was observed. For the ODS FeCr, Cr- and Fe-rich oxide formation and dissolution induced Cr depletion in the underlying alloy and led to the formation of laves phases that were observed to be detrimental to the room temperature tensile properties. For ODS FeCrAlMo and FeCrAl Al-rich oxide formation and dissolution resulted in Al depletion in the underlying alloys but did not impact tensile properties at room temperature. For 316H temperature induced sensitization combined with oxidation decreased room temperature tensile properties. With Zr foil added as oxygen getter, roughened surfaces and Al depletion profiles suggested the dissolution of ODS FeCr and FeCrAl into the liquid sodium while limited dissolution was observed for ODS FeCrAlMo and 316H. For the 316H and ODS FeCrAlMo steels, precipitates were formed at the grain boundaries after exposure. Tensile properties of ODS FeCr, FeCrAl and FeCrAlMo were not affected by the 1000 h corrosion exposure with Zr foil added to the sodium but for 316H temperature-induced grain boundary sensitization negatively affected the tensile properties.
To address the considerable interest in LiF-BeF 2 (FLiBe) compatibility for fission and fusion reactor applications, static and flowing compatibility experiments were conducted to assess the compatibility with type 316H stainless steel. In static testing at 550° and 650 °C, small mass changes were measured and posttest characterization of the FLiBe showed increased levels of Fe, Cr, Ni and Mn in the salt. Adding Be in the static salt test reduced the dissolution of Fe and Ni. Further, an initial assessment of mass transfer in flowing FLiBe without a Be addition was conducted using a monometallic 316H thermal convection loop (TCL) operated for 1000 h with a peak temperature of 650 °C. Similar to prior results in flowing FLiNaK salt, the 316H specimens exhibited small mass losses in the hot leg. Posttest characterization of the 316H specimens suggested Cr surface depletion in the hot and cold legs and possibly Fe deposition in the cold leg. To further understand this behavior, Cr and Fe dissolution was measured in static FLiBe at 550–650 °C.
Assessing the compatibility of 316H stainless steel with molten fluoride salts has been identified as a key research topic for molten salt reactor development. Current developers are interested in 316H stainless steel due to its ready availability and ASME code qualification. Previous studies of 316H stainless steel compatibility in molten fluoride salts have shown general agreement that Cr is selectively removed from the alloy during the exposures in molten salts. However, the extent of Cr dissolution depends on the initial purity of the salt and Fe also readily dissolves in the salt. In order to model dissolution, it is necessary to understand how time and temperature affect the dissolution rates of the alloying elements which may lead to saturation of these elements in the salt. To study the dissolution of 316H, Cr and Fe specimens were exposed in FLiNaK and LiFBeF2 (FLiBe) salt at three different temperatures (550°-750°C) and three different durations (100-2000 h) in isothermal capsule experiments.
This study investigates the irradiation performance of laser powder bed fusion (LPBF) 316L and 316H stainless steels (SS), and their wrought counterparts. While LPBF 316L has been more studied, LPBF 316H is relatively new, with little prior data on its irradiation behavior. The research involved fabricating, preparing, irradiating, and characterizing six materials: LPBF 316L (two variants), LPBF 316H (two variants), and wrought 316L and 316H. LPBF materials were subjected to various heat treatments, including solution annealing and stress relief, and were irradiated using in-situ and ex-situ ion techniques at temperatures of 300°C and 600°C, with doses ranging from 0.2 dpa to 25 dpa. Under ex-situ irradiation with 4 MeV Ni 2+ ions at 600°C, the dislocation cell structures in LPBF316L-1 and LPBF316H-1 gradually evolved into a uniform dislocation network. At a low irradiation dose (0.2 dpa), the cell structures were still partially visible. At 2 dpa, a uniform dislocation network formed, though remnants of the original cell structure were still discernible as contrast domains. At 5 dpa and 10 dpa, even the contrast domains vanished. For irradiation at 300°C, the cell structure was still clearly visible at 0.2 dpa for LPBF316L-1. For LPBF316H-1, the dislocation cell structure was less apparent at the same dose but was still recognizable. With further increase in dose at 300°C, the dislocation cell walls were completely replaced by irradiation-induced defects and no longer visible. Void formation was observed for irradiation at 600°C. At 2 dpa, no evident voids were observed in either LPBF316L-1 or LPBF316H-1.
This report focuses on summarizing mechanical behavior of 316H stainless steel (SS) printed using laser powder bed fusion (LPBF). 316H SS is one of the six alloys that has been qualified for use in nuclear reactors. The Advanced Materials and Manufacturing Technologies (AMMT) program has identified the use of the additive manufacturing (AM) process of LPBF as one of the manufacturing modalities to fabricate components for nuclear applications. Unlike wrought material, AM material displays significant heterogeneity in properties, resulting from changes in process parameters, machine-to-machine variability, and minor changes in feedstock chemistry from one batch to another. Although significant work has been done on 316L SS in the literature and has been summarized in several review papers, very limited data exist on 316H SS. Therefore, this report aims to provide a concise summary of the properties of 316H SS printed using different machines and at different locations as a part of the AMMT program.