Torsion Test of a Monocoque Box

A monocoque box beam consisting of a 24S-T aluminum-alloy sheet reinforced by four bulkheads and by longitudinal stringers and corner posts was subjected to bending loads as follows: pure bending about the lift axis, cantilever bending about the lift axis, and pure bending about both lift and drag axis. Longitudinal strains were measured for loads up to a load at which permanent set became measurable. The loads were sufficient to produce buckling of the sheet between stringers on the compression side of the box. The only noticeable effect of this buckling was a small increase in extreme-fiber strain on the compression side. The measured strains and measured deflections differed less than 10 percent from those computed from the simple beam theory after taking account of the effective width of the buckled sheet. The effect of the bulkheads on the distribution of stringer strain was negligible.

Mcpherson, Albert E↗

The Effect of Hole Quality on the Fatigue Life of 2024-T3 Aluminum Alloy Sheet

This paper presents the results of a study whose main objective was to determine which type of fabrication process would least affect the fatigue life of an open-hole structural detail. Since the open-hole detail is often the fundamental building block for determining the stress concentration of built-up structural parts, it is important to understand any factor that can affect the fatigue life of an open hole. A test program of constant-amplitude fatigue tests was conducted on five different sets of test specimens each made using a different hole fabrication process. Three of the sets used different mechanical drilling procedures while a fourth and fifth set were mechanically drilled and then chemically polished. Two sets of specimens were also tested under spectrum loading to aid in understanding the effects of residual compressive stresses on fatigue life. Three conclusions were made from this study. One, the residual compressive stresses caused by the hole-drilling process increased the fatigue life by two to three times over specimens that were chemically polished after the holes were drilled. Second, the chemical polishing process does not appear to adversely affect the fatigue life. Third, the chemical polishing process will produce a stress-state adjacent to the hole that has insignificant machining residual stresses.

Everett, Richard A., Jr.↗

Plasticity and Damage Modeling of Stress Asymmetry and Dynamic Behavior of AFS Additive Manufactured Aluminum Alloy 2219

The Solid State Additive Manufacturing (AM) process referred as MELD that fabricated the samples in this study, provides a new path for repairing, coating, joining and additive manufacturing metals and metal matrix composites. This research will be the first application of a physics-based microstructure dependent internal state variable (ISV) plasticity and damage material model to capture the mechanical response of an AM Aluminum Alloy (AA) 2219 via the MELD process. In this research, a microstructure-based internal state variable (ISV) plasticity-damage model was used to capture the mechanical behavior of AFS 2219 aluminum alloy. Aeroprobe Corporation, creator and patent holder for the MELD process, fabricated the material by pushing a solid filler rod of AA2219-T861 material through a hollow rotating tool onto an AA2219 T851 plate substrate. As feedstock, solid or powder precursor metals are pushed through a nonconsumable rotating cylindrical tool. Herein, added layers are deposited and metallurgically bonded to substrate material or previously deposited layers by the heat generated from the rotating tool through plastic deformation of the filler material. Once a layer has been added, the tool height increases, and starts the deposition of the next layer. This process results in beneficial properties such as grain refinement, homogenization and reduced porosity (fully dense). This process will experience temperatures similar to those in the weld nugget zone (WNZ) in friction stir welding (FSW), ranging from 0.6-0.9 Tm, with Tm being the melting point of the material. MELD is highly scalable with AA deposition rates reaching over 1000 cm3/hr, which allows for MELD being used for repairs, coatings, and building components. A motivating factor driving the research for physics-based history dependent material modeling of MELD components is the ability to accurately capture the stress-state and strain rate dependence in the material caused by variations in material microstructure from the MELD processing of new or repaired components. The ISV model incorporates microstructural content and is consistent with continuum level kinematics, kinetics, and thermodynamics. These features allow the ISV model to capture large deformations at the structural scale using the kinematic and isotropic hardening, while microscale damage is obtained from the microstructural features. The benefits of the ISV model arise from the inclusion of structure-property relationships identified from microstructural characterization and experimentation. The Bauschinger effect (BE) is an important concept, vital in the accurate prediction of cyclic stress-strain response of ductile materials such as metals. The ISV model has been successfully used to capture the behavior and damage, and the BE of different aluminum alloys and steels. The ISV model uses kinematic and isotropic hardening to help capture deformations of the material at the macro scale. To understand this hardening relationship, calculating the kinematic and isotropic hardening relationship in the material is warranted for a high-fidelity model. Electron Backscattered Diffraction (EBSD) was used to characterize the as-fabricated microstructure, where a fully-dense equiaxed grain morphology with average grain size of 2.5 μm was observed. Microhardness mapping of the as-built structures, monotonic tension and compression experiments at both quasi-static (0.001/s) strain rates, tension-followed-by-compression and compression-followed-by-tension experiments were performed to obtain the set of plasticity and damage constants necessary to capture strain rate and stress state behavior of this additive material. To calibrate the plasticity-damage model, a single set of constants were determined to capture the different stress states the MELD AA2219. One set of the constants was determined from experimental true stress-strain curves for the tension and compression data. Additionally, microstructural information and data from the open literature were used as the other model constants. This research is a first of its kind for AFS AA2219, includes correlating the ISV model to the monotonic experimental results that capture the isotropic and kinematic plasticity mechanical response.

Rivera, O. G.↗

Oxidation Behavior of Binary Niobium Alloys

This investigation concludes a study to determine the effects of up to 25 atomic percent of 55 alloying additions on the oxidation characteristics of niobium. The alloys were evaluated by oxidizing in an air atmosphere for 4 hours at 1000 C and 2 hours at 1200 C. Titanium and chromium improved oxidation resistance at both evaluation conditions. Vanadium and aluminum improved oxidation resistance at 1000 C, even though the V scale tended to liquefy and the Al specimens became brittle and the scale powdery. Copper, cobalt, iron, and iridium improved oxidation resistance at 1200 C. Other investigations report tungsten and molybdenum are protective up to about 1000 C, and tantalum at 1100 C. The most important factor influencing the rate of oxidation was the ion size of the alloy additions. Ions slightly smaller than the Nb(5+) ion are soluble in the oxide lattice and tend to lower the compressive stresses in the bulk scale that lead to cracking. The solubility of the alloying addition also depends on the valence to some extent. All of the elements mentioned that improve the oxidation resistance of Nb fit this size criterion with the possible exception of Al, whose extremely small size in large concentrations would probably lead to the formation of a powdery scale. Maintenance of a crack-free bulk scale for as long as possible may contribute to the formation of a dark subscale that ultimately is rate- controlling in the oxidation process. The platinum-group metals, especially Ir, appear to protect by entrapment of the finely dispersed alloying element by the incoming Nb2O5 metal-oxide interface. This inert metallic Ir when alloyed in a sufficient amount with Yb appears to give a ductile phase dispersed in the brittle oxide. This scale would then flow more easily to relieve the large compressive stresses to delay cracking. Complex oxide formation (which both Ti and Zr tend to initiate) and valence effects, which probably change the vacancy concentration in the scale, are masked by the overriding tendency for a porous scale.

Barrett, Charles A.↗

Characterization of Cracking and Crack Growth Properties of the C5A Aircraft Tie-Box Forging

Detailed destructive examinations were conducted to characterize the integrity and material properties of two aluminum alloy (7075-T6) horizontal stabilizer tie box forgings removed.from US. Air Force C5A and C5B transport aircraft. The C5B tie box forging was,found to contain no evidence of cracking. Thirteen cracks were found in the CSA,forging. All but one of the cracks observed in the C5A component were located along the top cap region (one crack was located in the bottom cap region). The cracks in the C5A component initiated at fastener holes and propagated along a highly tunneled intergranular crack path. The tunneled crack growth configuration is a likelv result of surface compressive stress produced during peening of the .forging suijace. The tie box forging ,fatigue crack growth, fracture and stress corrosion cracking (SCC) properties were characterized. Reported herein are the results of laboratory air ,fatigue crack growth tests and 95% relative humidity SCC tests conducted using specimens machined from the C5A ,forging. SCC test results revealed that the C5A ,forging material was susceptible to intergranular environmental assisted cracking: the C5A forging material exhibited a SCC crack-tip stress-intensity factor threshold of less than 6 MPadn. Fracture toughness tests revealed that the C5A forging material exhibited a fracture toughness that was 25% less than the C5B forging. The C5A forging exhibited rapid laboratory air fatigue crack growth rates having a threshold crack-tip stress-intensity factor range of less than 0.8 MPa sup m. Detailed fractographic examinations revealed that the ,fatigue crack intergranular growth crack path was similar to the cracking observed in the C5A tie box forging. Because both fatigue crack propagation and SCC exhibit similar intergranular crack path behavior, the damage mechanism resulting in multi-site cracking of tie box forgings cannot be determined unless local cyclic stresses can be quantified.

Piascik, Robert S.↗

Surface Enhancement Improves Crack Resistance

The low plasticity burnishing (LPB) process produces a deep layer of surface compression in a quick and affordable manner to produce metal surfaces free of scratches, nicks, and gouges. The process, designed for easy inclusion in the manufacturing environment, can be performed with conventional Computer Numerical Control machine tools. This allows parts to be processed during manufacturing, rather than as a post process in a separate facility. A smooth, free-rolling spherical ball suspended in a fluid allows for single-point contact. The ball comes into mechanical contact only with the surface to be burnished, and can be moved in any direction. LPB can be applied to all types of carbon and alloy steel, stainless steel, cast iron, aluminum, titanium, and nickel- based super alloys. In addition to improving a surface's resistance to fatigue and damage, treatment stops the growth of shallow cracks. The LPB process is used on the leading edges of turbine blades to improve resistance to foreign object damage and crack growth. This means significant savings for aircraft owners, since maintenance requirements to inspect for fatigue damage, replace parts, and remove corrosion damage increase the cost of operation.

Source record↗

Split mandrel versus split sleeve coldworking: Dual methods for extending the fatigue life of metal structures

It is common practice to use split sleeve coldworking of fastener holes as a means of extending the fatigue life of metal structures. In search of lower manufacturing costs, the aerospace industry is examining the split mandrel (sleeveless) coldworking process as an alternative method of coldworking fastener holes in metal structures. The split mandrel process (SpM) significantly extends the fatigue life of metal structures through the introduction of a residual compressive stress in a manner that is very similar to the split sleeve system (SpSl). Since the split mandrel process is significantly less expensive than the split sleeve process and more adaptable to robotic automation, it will have a notable influence upon other new manufacture of metal structures which require coldworking a significant number of holes, provided the aerospace community recognizes that the resulting residual stress distributions and fatigue life improvement are the same for both processes. Considerable testing has validated the correctness of that conclusion. The findings presented in this paper represent the results of an extensive research and development program, comprising data collected from over 400 specimens fabricated from 2024-T3 and 7075-T651 aluminum alloys in varied configurations, which quantify the benefits (fatigue enhancement and cost savings) of automating a sleeveless coldworking system.

Rodman, Geoffrey A.↗

Flexible Ceramic-Metal Insulation Composite and Method of Making

A method for joining a woven flexible ceramic fabric and a thin metal sheet creating an integral metal surfaced flexible thermal protection article, which methods compress: placing multiple dots of high temperature metallic or fabric and the thin metal sheet in a random or organized pattern, with the proviso that the brazing material covers about 10% or less of the surface of one flat side of the metal sheet; heating the flexible ceramic fabric, brazing material and thin metal sheet for a predetermined period of time to integrally connect the same; and cooling the formed flexible article to ambient temperature. Preferably the flexible ceramic is selected from fibers comprising atoms of silicon, carbon, nitrogen, boron, oxygen or combinations thereof. The flexible thermal protection article produced is also part of the present invention. The thin metal sheet is comprised of titanium, aluminum, chromium, niobium or alloys or combinations thereof. The brazing material is selected from copper/silver or copper/gold or is a ceramic brazing or adhesive material.

Rasky, Daniel J.↗

An assessment of the small-crack effect for 2024-T3 aluminum alloy

Data on small-crack behavior were obtained for a single-edge-notched tensile specimen made of 2024-T3 Al alloy and used to evaluate the capability of a semiempirical crack-growth and closure model to predict the fatigue life of notched specimens. Fatigue tests were conducted under either constant-amplitude loading (with stress ratios of 0.5, 0, -1, and -2) or spectrum loading, using a replication technique to record growth. It was found that small cracks exhibited the 'small-crack' effect in that they grew faster than large cracks when subjected to the same stress intensity factor range. Experimental small-crack growth rates agreed well with the model predictions. For making predictions of fatigue life, an initial surface defect void size of 3 x 12 x 0.4 microns was used in all calculations; predicted fatigue lives agreed well with experimentally determined values obtained in all tests. The crack-closure model indicated that the 'small-crack' effect on fatigue life was greatest in tests involving significant compressive loads.

Newman, J. C., Jr.↗

Experimental Investigation at Mach Number 3.0 of the Effects of Thermal Stress and Buckling on the Flutter of Four-Bay Aluminum Alloy Panels with Length-Width Ratios of 10

Skin-stiffener aluminum alloy panels consisting of four bays, each bay having a length-width ratio of 10, were tested at a Mach number of 3.0 at dynamic pressures ranging from 1,500 psf to 5,000 psf and at stagnation temperatures from 300 F to 655 F. The panels were restrained by the supporting structure in such a manner that partial thermal expansion of the skins could occur in both the longitudinal and lateral directions. A boundary faired through the experimental flutter points consisted of a flat-panel portion, a buckled-panel portion, and a transition point at the intersection of the two boundaries. In the region where a panel must be flat when flutter occurs, an increase in panel skin temperature (or midplane compressive stress) makes the panel more susceptible to flutter. In the region where a panel must be buckled when flutter occurs, the flutter trend is reversed. This reversal in trend is attributed to the panel postbuckling behavior.

Dixon, Sidney C.↗

The influence of modifications of a fatigue loading history program on fatigue lifetime

Rectangular specimens of 7075 and 2014 aluminum alloys with two holes (stress concentration factor of 3.24) have been tested under axial fatigue loading on a six-rod test bed with modifications of the loading program, the surface particulars, and the frequency. The length of the precrack stage was investigated by use of a new crack detector. In most cases the two alloys behaved similarly, with similar life to crack start under the same loading. Some overloads lengthened the life. Truncation by omission of the lowest peak loads should be limited to about 20 percent of the ultimate load. Simplifying counting methods gave misleading results. Very thin surface layers of anodizing, protection by vinyl, dry nitrogen atmosphere, as well as stepwise reaming or grinding the surface of the holes, lengthened the life; thick anodized layers shortened the life. Compressing the hole surface by rolling had no influence. Frequencies at about 210 to 240 cpm produced shorter lives than those at 40 cpm. At 5.4 cpm the life was considerably longer. A model to better understand the precrack-stage fatigue mechanism is discussed.

Branger, J.↗

Strain Gauges Indicate Differential-CTE-Induced Failures

A method of detecting mechanical failure induced by variation in temperature at an adhesive bond between two materials that have different coefficients of thermal expansion (CTEs) involves monitoring of strain-gauge readings. This method can be regarded as an exploitation of the prior observation that the readings of strain gauges commonly used in tensile and compressive testing of material specimens include features indicative of incremental failures in the specimens. In this method, one or more strain gauges are bonded to either or both of the two materials near the bond between the materials. (The adhesive used to bond the strain gauges would not ordinarily be the same as the one used to bond the two materials). Then strain-gauge readings are recorded as the temperature of the materials is varied through a range of interest. Any significant discontinuity in the slope of the resulting strain-versus-temperature curve(s) is taken to be a qualitative indication of a failure of the bond between the two materials and/or a failure within one of the materials in the vicinity of the bond. The method has been demonstrated in experiments on specimens consisting of polyacrylonitrile-fiber/epoxy-matrix laminated composite plates bonded by epoxy to smaller plates made, variously, of aluminum, titanium, and a low-CTE nickel/iron alloy. In preparation for each experiment, strain gauges were bonded, by use of cryogenic-rated adhesives, to the composite plate near the corners of the metal plate (see Figure 1). In each experiment, strain-gauge and temperature readings were taken as the specimen was cooled from room temperature to 20 K. The specimens were then returned to room temperature and ultrasonically inspected for damage in the bond region. No failure events were detectable in the strain-gauge readings from the composite/ titanium and composite/low-thermalexpansion- alloy specimens, and ultrasonic inspection of these specimens revealed no damage. However, failure events were seen in the strain-gauge readings from the composite/aluminum specimens (see Figure 2), and ultrasonic inspection confirmed that there was damage in the bond regions of these specimens.

Harris, Brian↗