Plutonium migration and phase evolution in irradiated U-Pu-Zr metallic fuels: An integrated EPMA-SEM-TEM study
Constituent redistribution is a defining feature of irradiated U-Pu-Zr metallic fuels, yet its mechanisms and effects on fuel performance are not sufficiently resolved to guide model development. Although decades of irradiation testing have established broad trends, a true mechanistic understanding of constituent redistribution has not been achieved. Here, in this study, we use electron probe microanalysis (EPMA), scanning electron microscopy (SEM), and transmission electron microscopy-based (TEM) selective area electron diffraction (SAED) on a EBR-II irradiated U-19 wt.% Pu-6 wt.% Zr fuel pin cross-section to correlate the composition, porosity, and crystallographic phases formed after irradiation. Constituent redistribution is thought to consist of three distinct zones, in which uranium and zirconium migrate while plutonium remains relatively unchanged. Our EPMA results resolve eight distinct compositional regions, and more importantly, show that plutonium redistributes alongside zirconium, contrary to historical assumptions. The distribution of fission products was highly asymmetric with a few large lanthanide precipitates observed at isolated sites on the pin periphery instead of a uniform distribution of smaller precipitates around the periphery. Using thermodynamic data from TAF-ID and the measured EPMA compositions, matrix phase fractions were predicted across the fuel radius. Phase predictions based on composition did not match TEM/SAED results, which revealed a much higher fraction of α−U phase than would be expected if phases were retained from reactor temperatures. These findings highlight the need for expanded SAED phase identification to capture post-irradiation and storage effects, as well as rigorous uncertainty quantification in fuel performance and phase diagram modeling to better constrain predictions from compositional data.