NASA NTRS1971

Mach 1 oxidation of thoriated nickel chromium at 1204 C (2200 F)

TD NiCr was exposed to a Mach 1, 1-atmosphere gas stream at 1204 C for times up to 50 hours. Weight change, metal thickness loss, X-ray diffraction, metallographic, and electron microprobe analyses were made. Neither surface preparation nor thermal cycling had an appreciable effect on the results. Initially, Cr2O3 formed and volatilized, allowing a rapid metal loss rate of 40 microns per hour. After about 1 hour the Cr2O3 broke down, resulting in an NiO overgrowth. The metal loss rate then slowed to 2.5 microns per hour and remained constant to 50 hours.

Lowell, C. E.↗
NASA NTRS1975

Several braze filler metals for joining an oxide-dispersion-strengthened nickel-chromium-aluminum alloy

An evaluation was made of five braze filler metals for joining an aluminum-containing oxide dispersion-strengthened (ODS) alloy, TD-NiCrAl. All five braze filler metals evaluated are considered suitable for joining TD-NiCrAl in terms of wettability and flow. Also, the braze alloys appear to be tolerant of slight variations in brazing procedures since joints prepared by three sources using three of the braze filler metals exhibited similar brazing characteristics and essentially equivalent 1100 C stress-rupture properties in a brazed butt-joint configuration. Recommendations are provided for brazing the aluminum-containing ODS alloys.

Gyorgak, C. A.↗
NASA NTRS1960

Oxidation Behavior of Binary Niobium Alloys

This investigation concludes a study to determine the effects of up to 25 atomic percent of 55 alloying additions on the oxidation characteristics of niobium. The alloys were evaluated by oxidizing in an air atmosphere for 4 hours at 1000 C and 2 hours at 1200 C. Titanium and chromium improved oxidation resistance at both evaluation conditions. Vanadium and aluminum improved oxidation resistance at 1000 C, even though the V scale tended to liquefy and the Al specimens became brittle and the scale powdery. Copper, cobalt, iron, and iridium improved oxidation resistance at 1200 C. Other investigations report tungsten and molybdenum are protective up to about 1000 C, and tantalum at 1100 C. The most important factor influencing the rate of oxidation was the ion size of the alloy additions. Ions slightly smaller than the Nb(5+) ion are soluble in the oxide lattice and tend to lower the compressive stresses in the bulk scale that lead to cracking. The solubility of the alloying addition also depends on the valence to some extent. All of the elements mentioned that improve the oxidation resistance of Nb fit this size criterion with the possible exception of Al, whose extremely small size in large concentrations would probably lead to the formation of a powdery scale. Maintenance of a crack-free bulk scale for as long as possible may contribute to the formation of a dark subscale that ultimately is rate- controlling in the oxidation process. The platinum-group metals, especially Ir, appear to protect by entrapment of the finely dispersed alloying element by the incoming Nb2O5 metal-oxide interface. This inert metallic Ir when alloyed in a sufficient amount with Yb appears to give a ductile phase dispersed in the brittle oxide. This scale would then flow more easily to relieve the large compressive stresses to delay cracking. Complex oxide formation (which both Ti and Zr tend to initiate) and valence effects, which probably change the vacancy concentration in the scale, are masked by the overriding tendency for a porous scale.

Barrett, Charles A.↗
NASA NTRS1985

Effects of chromium and aluminum on mechanical and oxidation properties of iron-nickel-base superalloys based on CG-27

The effects of chromium and aluminum on the mechanical and oxidation properties of a series of gamma-prime-strengthened alloys based on CG-27 were studied. Gamma-prime dispersion and solid-solution strengthening were the principal modes of alloy strengthening. The oxidation attack parameter K sub a decreased with increasing Cr and Al contents for each alloy group based on Al content. As a group, alloys with 3 wt % Al had the lowest attack parameters. Therefore, 3 wt % is the optimum level of Al for parabolic oxidation behavior. Spalling, due to diffusion-induced grain growth, was controlled by the overall Cr and Al levels. The alloy with 4 wt % Cr and 3 wt % Al had stress-rupture properties superior to those of the base alloy, CG-27, and maintained parabolic oxidation behavior while the Cr content was reduced by two-thirds of its value in cast CG-27.

Schuon, S. R.↗
NASA NTRS1974

High-velocity-oxidation performance of metal-chromium-aluminum (MCrAl), cermet, and modified aluminide coatings on IN-100 and type VIA alloys at 1093 C

Cermet, MCrAl, and modified aluminide types of coatings applied to IN-100 and NASA-TRW-VIA alloy specimens were cyclically oxidation tested in a high velocity (Mach 1) gas flame at 1093 C. Several coating compositions of each type were evaluated for oxidation resistance. The modified aluminide coating, Pt-Al, applied to alloy 6A proved to be the best, providing oxidation protection to approximately 750 hours based on weight change measurements. The second best, a CoCrAlY coating applied to 6A, provided protection to 450 hours. The third best was a cermet + aluminide coating on 6A with a protection time to 385 hours.

Deadmore, D. L.↗
NASA NTRS1973

Friction, wear, and transfer of carbon and graphite to copper, chromium, and aluminum metal surfaces in vacuum

Sliding friction experiments were conducted with amorphous and fully graphitized carbons sliding on copper and on films of chromium and aluminum on copper. Auger emission spectroscopy analysis was used to monitor carbon transfer to the metal surfaces. Friction and wear were also measured. Metal surfaces were examined both in the clean state and with normal oxides present. Results indicate that different metals have an important effect on friction, wear, and transfer characteristics. With amorphous carbon, the least chemically active metal gave the highest wear and amount of carbon transfer. Both forms of carbon gave lower friction and wear and lower transfer rates when in contact with clean, as opposed to oxide-covered, chromium surfaces. With copper, the reverse was true; cleaning was detrimental.

Buckley, D. H.↗
NASA NTRS2004

Thermal Effects on a Low Cr Modification of PS304 Solid Lubricant Coating

PS304 is a high temperature composite solid lubricant coating composed of Ni-Cr, Cr2O3, BaF2-CaF2 and Ag. The effect of reducing chromium content on the formation of voids in the Ni-Cr particles after heat treatment in PS304 coating was investigated. Coatings were prepared with Ni-20Cr or Ni-10Cr powder and in various combinations with the other constituents of PS304 (i.e., chromia, silver and eutectic BaF2-CaF2 powders) and deposited on metal substrates by plasma spray. Specimens were exposed to 650 C for 24 hr or 1090 C for 15 hr and then examined for changes in thickness, coating microstructure and adhesion strength. Specimens with Ni-10Cr generally had less thickness increase than specimens with Ni-20Cr, but there was great variance in the data. Reduction of chromium concentration in Ni-Cr powder tended to reduce the appearance of voids in the Ni-Cr phase after heat exposure. The presence of BaF2-CaF2 resulted in a significant increase in coating adhesion strength after heat treatment, while coatings without BaF2-CaF2 had no significant change. Chemical composition analysis suggested that the void formation was due to oxidation of chromium in the Ni-Cr constituent.

Stanford, Malcolm K.↗
NASA NTRS1975

Solid state welding processes for an oxide dispersion strengthened nickel-chromium-aluminum alloy

Solid-state welding processes were evaluated for joining TD-NiCrAl (Ni-16Cr-4Al-2ThO2) alloy sheet. Both hot-press and resistance spot welding techniques were successfully applied in terms of achieving grain growth across the bond line. Less success was achieved with a resistance seam welding process. In stress-rupture shear and tensile shear tests of lap joints at 1100 C, most failures occurred in the parent material, which indicates that the weld quality was good and that the welds were not a plane of weakness. The overall weld quality was not as good as previously attained with TD-NiCr, probably because the presence of alumina at the faying surfaces and the developmental TD-NiCrAl sheet, which was not of the quality of the TD-NiCr sheet in terms of surface flatness and dimensional control.

Moore, T. J.↗
NASA NTRS1976

Resistance of nickel-chromium-aluminum alloys to cyclic oxidation at 1100 C and 1200 C

Nickel-rich alloys in the Ni-Cr-Al system were evaluated for cyclic oxidation resistance in still air at 1,100 and 1,200 C. A first approximation oxidation attack parameter Ka was derived from specific weight change data involving both a scaling growth constant and a spalling constant. An estimating equation was derived with Ka as a function of the Cr and Al content by multiple linear regression and translated into countour ternary diagrams showing regions of minimum attack. An additional factor inferred from the regression analysis was that alloys melted in zirconia crucibles had significantly greater oxidation resistance than comparable alloys melted otherwise.

Barrett, C. A.↗
NASA NTRS1973

Oxidation resistant, thoria-dispersed nickel-chromium-aluminum alloy

Modified thoria-dispersed nickel-chromium alloy has been developed that exhibits greatly improved resistance to high-temperature oxidation. Additions of aluminum have been made to change nature of protective oxide scale entirely and to essentially inhibit oxidation at temperatures up to 1260 C.

Baranow, S.↗
NASA NTRS1971

Development of oxidation resistance in thoriated nickel-chromium base alloys

A pack process was developed which permits the introduction of nearly six weight percent aluminum into solid solution in the near-surface region of TDNiCr (Ni-20Cr-2ThO2. At this aluminum concentration an adherent alumina scale is produced on the alloy surface upon exposure to an environment of 1330 n/sq m (10 torr) or 101,000 n/sq m (760 torr) air at temperatures of 1093 C (2000 F) and 1204 C (2200 F). Room temperature mechanical properties of the aluminized alloys compare favorably with those of TDNiCr as received. While diffusivities for aluminum are a factor of three higher than those for chromium in TDNiCr or Ni-20Cr, the diffusion rates are similar for either of these elements in the thoriated or unthoriated alloy for a given temperature and grain size.

Seltzer, M. S.↗
NASA NTRS1991

Oxidation-chlorination of binary Ni-Cr alloys in flowing Ar-O2-Cl2 gas mixtures at 1200 K

Nickel-chromium alloys are resistant to oxidation because of the selective oxidation of chromium to form a protective Cr2O3 scale. In chlorine-containing environments, volatile corrosion products can also be formed. The mixed oxidation-chlorination of Ni-4.5Cr, Ni-13.8Cr, and Ni-26.5Cr (by weight) alloys in Ar-O2-Cl2 gas mixtures is investigated using thermogravimetric analysis and atmospheric-pressure-sampling mass spectrometry, followed by examination of the corrosion products using scanning electron microscopy and X-ray diffraction analysis. The overall kinetics of the corrosion are affected by the relative amounts of oxides and chlorides formed and the composition of the oxide corrosion products.

Mcnallan, M. J.↗