Results for “dry storage canisters” — Page 4

DOE OSTI2022

SNF Interim Storage Canister Corrosion and Surface Environment Investigations (FY22 Status Update)

High-level purpose of this work: This report summarizes work carried out by Sandia National Laboratories (SNL) in the fiscal year 2022 (FY22) to evaluate the potential occurrence of stress corrosion cracking (SCC) on spent nuclear fuel (SNF) dry storage canisters. The U.S. currently lacks a repository for permanent disposal of SNF; thus, dry storage systems will be in use for much longer time periods than originally intended. Gap analyses by the US Department of Energy (DOE), the Nuclear Regulatory Commission (NRC), the Nuclear Waste Technical Review Board (NWTRB), and the Electric Power Research Institute (EPRI) have all determined that an improved understanding of the occurrence and risk of canister SCC is critical to demonstrating the safety of long-term dry storage. Should canister penetration by SCC occur, the containment boundary represented by the canister would be breached. A loss of the inert environment (helium) within the canister could occur and intrusion of air and moisture could react with and damage the fuel within the canister. For this reason, the DOE is funding an effort to evaluate the potential occurrence and consequences of dry storage canister SCC and to develop prevention, mitigation, and repair technologies for this degradation mechanism.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Preliminary Modeling of Deposition on Spent Nuclear Fuel Canisters in Dry Storage.

Abstract not provided.

Jensen, Philip↗

DOE OSTI2023

FY23 Status Report: SNF Interim Storage Canister Corrosion and Surface Environment Investigations

Work evaluating spent nuclear fuel (SNF) dry storage canister surface environments and canister corrosion progressed significantly in FY23, with the goal of developing a scientific understanding of the processes controlling initiation and growth of stress corrosion cracking (SCC) cracks in stainless steel canisters in relevant storage environments. The results of the work performed at Sandia National Laboratories (SNL) will guide future work and will contribute to the development of better tools for predicting potential canister penetration by SCC.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Continued Investigations of Respirable Release Fractions for Stress Corrosion Crack-Like Geometries

The formation of a stress corrosion crack (SCC) in the canister wall of a dry cask storage system (DCSS) has been identified as a potential issue for the long-term storage of spent nuclear fuel. The presence of an SCC in a storage system could represent a through-wall flow path from the canister interior to the environment. Modern, vertical DCSSs are of particular interest due to the commercial practice of using relatively high backfill pressures (up to approximately 800 kPa) in the canister to enhance internal natural convection. This pressure differential offers a comparatively high driving potential for blowdown of any particulates that might be present in the canister. In this study, the rates of gas flow and aerosol transmission of a spent fuel surrogate through an engineered microchannel with dimensions representative of an SCC were evaluated experimentally using coupled mass flow and aerosol analyzers. The microchannel was formed by mating two gage blocks with a linearly tapering slot orifice nominally 13 μm (0.005 in.) tall on the upstream side and 25 μm (0.0010 in.) tall on the downstream side. The orifice is 12.7 mm (0.500 in.) wide by 8.89 mm (0.350 in.) long (flow length). Surrogate aerosols of cerium oxide, CeO 2 , were seeded and mixed with either helium or air inside a pressurized tank. The aerosol characteristics were measured immediately upstream and downstream of the simulated SCC at elevated and ambient pressures, respectively. These data sets are intended to demonstrate a new capability to characterize SCCs under well-controlled boundary conditions. Modeling efforts were also initiated that evaluate the depletion of aerosols in a commercial dry storage canister. These preliminary modeling and ongoing testing efforts are focused on understanding the evolution in both size and quantity of a hypothetical release of aerosolized spent fuel particles from failed fuel to the canister interior and ultimately through an SCC.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Large Plate Experiment of Chloride-induced Stress Corrosion Cracking in Spent Nuclear Fuel Storage Canisters

This report is the comprehensive description of the completed experiment to evaluate the corrosion behavior of a large section of welded plate material harvested from the Sandia National Laboratories’ (SNL) full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The plate was subjected to conditions aggressive to chloride-induced stress corrosion cracking for a total time of 2 years. The details of the establishment of this experiment, and the corrosion results are reported. This work is intended to inform aging management programs for SNF canisters under conditions of extended dry storage.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2023

Predeployment progress of the Canister Deposition Field Demonstration

This report updates the high-level test plan for evaluating surface deposition on three commercial 32PTH2 spent nuclear fuel (SNF) canisters inside NUTECH Horizontal Modular Storage (NUHOMS) Advanced Horizontal Storage Modules (AHSMs) from Orano (formerly Transnuclear Inc.) and provides a summary of the surface sampling activities that have been conducted to date. The details contained in this report represent the best designs and approaches explored for testing as of this publication. Given the rapidly developing nature of this test program, some of these plans may change to accommodate new objectives or requirements. One goal of this testing is to collect defensible and detailed dust deposition measurements from the surface of dry storage canisters in a marine coastal environment to guide chloride-induced stress corrosion cracking (CISCC) research. Another goal is to provide data for the validation of computational fluid dynamics (CFD) based deposition modeling. To facilitate surface sampling, the otherwise highly prototypic dry storage systems will not contain SNF but rather will be electrically heated to mimic the decay heat and thermal hydraulic environment. Test and heater design is supported by detailed CFD modeling. Instrumentation throughout the canister, storage module, and environment will provide extensive information about the thermal-hydraulic behavior of horizontal dry cask storage systems. Manual sampling over a comprehensive portion of the canister surface at regular time intervals will offer detailed quantification and composition of the deposited particulates from a realistic storage environment. Discussions of a potential host site for the Canister Deposition Field Demonstration (CDFD) are ongoing. Until a host site is chosen, testing of key CDFD hardware components including the heater assemblies, power skid, and remote data acquisition system will continue. Functional testing of the finalized heater assemblies and test apparatus started this fiscal year. These initial heater tests have shown the assemblies are performing within design specifications. Staged surface sampling of a mockup of a canister outside the AHSM on a transfer skid was also performed. Refinements to the sampling procedures and techniques were captured from observation of these activities and lessons-learned debriefs. These updated sampling procedures and techniques are planned to be tested again in the field using the mockup in order to assure personnel are using the most accurate and repeatable methods possible prior to deployment for actual CDFD testing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Large Plate Experiment of Chloride-induced Stress Corrosion Cracking in Spent Nuclear Fuel Storage Canisters

This report provides a description of the testing (in progress at the Savannah River National Laboratory) to evaluate the corrosion behavior of a large section of welded plate material harvested from the Sandia National Laboratories’ full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The details of the establishment of this plate test, the interim corrosion results (from visual examination), and the general plan for examination of the plate in CY21 to evaluate crack growth behavior (if any) are provided. This work is intended to inform aging management programs for SNF canisters under conditions of extended dry storage. A “large plate” (approximately 51 x 46 cm with thickness 16 mm and weight about 30 kg) and containing a circumferential weldment from the mockup is the test specimen. The knowledge of the salt, temperature, humidity conditions for chloride-induced stress corrosion cracking (CISCC) including the threshold stress intensity factor, K iscc , were used to setup the large plate test in which a set of part-through-wall and through-wall electrical discharge machined (EDM) defects were positioned in the weld residual stress field of the welded plate material from the mockup canister. A marine salt solution was applied to this plate specimen with an air-brush spray, then dried, and then exposed to a sustained 71-73% RH condition at an ambient room temperature of 22 °C. The salt loading and environmental condition is expected to be aggressive to cause CISCC

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Development of a numerical model for simulating stress corrosion cracking in spent nuclear fuel canisters

Abstract Prediction and detection of the chloride-induced stress corrosion cracking (CISCC) in Type 304 stainless steel spent nuclear fuel canisters are vital for the lifetime extension of dry storage canisters. This paper conducts a critical review that focuses on the numerical modeling and simulation on the research progress of the CISCC. The numerical models emphasizing the residual stress, susceptible microstructure, and corrosive environment are summarized individually. Meanwhile, the simulation studies on the role of hydrogen-assisted cracking are reviewed. Finally, a multi-physical numerical model, which combines the different fields is proposed based on our recent investigation.

Materials Science↗

DOE OSTI2021

Ground Motion Inputs for the Seismic Shake Table Test

Currently, spent nuclear fuel (SNF) is stored in on-site independent spent-fuel storage installations (ISFSIs) at seventythree (73) nuclear power plants (NPPs) in the US. Because a site for geologic repository for permanent disposal of SNF has not been constructed, the SNF will remain in dry storage significantly longer than planned. During this time, the ISFSIs, and potentially consolidated storage facilities, will experience earthquakes of different magnitudes. The dry storage systems are designed and licensed to withstand large seismic loads. When dry storage systems experience seismic loads, there are little data on the response of SNF assemblies contained within them. The Spent Fuel Waste Disposition (SFWD) program is planning to conduct a full-scale seismic shake table test to close the gap related to the seismic loads on the fuel assemblies in dry storage systems. This test will allow for quantifying the strains and accelerations on surrogate fuel assembly hardware and cladding during earthquakes of different magnitudes and frequency content. The main component of the test unit will be the full-scale NUHOMS 32 PTH2 dry storage canister. The canister will be loaded with three surrogate fuel assemblies and twenty-nine dummy assemblies. Two dry storage configurations will be tested – horizontal and vertical above-ground concrete overpacks. These configurations cover 91% of the current dry storage configurations. The major input into the shake table test are the seismic excitations or the earthquake ground motions – acceleration time histories in two horizontal and one vertical direction that will be applied to the shake table surface during the tests. The shake table surface represents the top of the concrete pad on which a dry storage system is placed. The goal of the ground motion task is to develop the ground motions that would be representative of the range of seismotectonic and other conditions that any site in the Western US (WUS) or Central Eastern US (CEUS) might entail. This task is challenging because of the large number of the ISFSI sites, variety of seismotectonic and site conditions, and effects that soil amplification, soil-structure interaction, and pad flexibility may have on the ground motions.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Status Update for the Canister Deposition Field Demonstration

This report updates the high-level test plan for evaluating surface deposition on three commercial 32PTH2 spent nuclear fuel (SNF) canisters inside NUTECH Horizontal Modular Storage (NUHOMS) Advanced Horizontal Storage Modules (AHSM) from Orano (formerly Transnuclear Inc.) and provides a description of the surface characterization activities that have been conducted to date. The details contained in this report represent the best designs and approaches explored for testing as of this publication. Given the rapidly developing nature of this test program, some of these plans may change to accommodate new objectives or requirements. The goal of the testing is to collect highly defensible and detailed surface deposition measurements from the surface of dry storage canisters in a marine coastal environment to guide chloride-induced stress corrosion crack (CISCC) research. To facilitate surface sampling, the otherwise highly prototypic dry storage systems will not contain SNF but rather will be electrically heated to mimic the thermal-hydraulic-environment. Instrumentation throughout the canister, storage module, and environment will provide an extensive amount of information for the use of model validation. Manual sampling over a comprehensive portion of the canister surface at regular time intervals will offer a high-fidelity quantification of the conditions experienced in a harsh yet realistic environment.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2022

Status Update for the Canister Deposition Field Demonstration

This report updates the high-level test plan for evaluating surface deposition on three commercial 32PTH2 spent nuclear fuel (SNF) canisters inside NUTECH Horizontal Modular Storage (NUHOMS) Advanced Horizontal Storage Modules (AHSMs) from Orano (formerly Transnuclear Inc.) and provides a description of the surface characterization activities that have been conducted to date. The details contained in this report represent the best designs and approaches explored for testing as of this publication. Given the rapidly developing nature of this test program, some of these plans may change to accommodate new objectives or requirements. The goal of the testing is to collect highly defensible and detailed dust deposition measurements from the surface of dry storage canisters in a marine coastal environment to guide chloride-induced stress corrosion crack (CISCC) research. To facilitate surface sampling, the otherwise highly prototypic dry storage systems will not contain SNF but rather will be electrically heated to mimic the decay heat and thermal hydraulic environment. Test and heater design is supported by detailed computational fluid dynamics modeling. Instrumentation throughout the canister, storage module, and environment will provide extensive information about thermal-hydraulic behavior. Manual sampling over a comprehensive portion of the canister surface at regular time intervals will offer a high-fidelity quantification of the conditions experienced in a harsh yet realistic environment. Functional testing of the finalized heater assemblies and test apparatus is set to begin in December 2022. The proposed delivery of the canisters to the host test site is June/July 2023, which is well ahead of when the AHSM installations would be completed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

THERMAL STRESS ANALYSIS OF A SPENT NUCLEAR FUEL CANISTER

The potential for chloride induced stress corrosion cracking (CISCC) in spent nuclear fuel dry storage canisters is a current topic of research by the US Department of Energy Spent Fuel and Waste Science and Technology program. One of the important prerequisites for CISCC is a tensile residual stress state. This study utilizes computational models to provide an initial analysis of thermal stresses in a generic spent nuclear fuel canister. A STAR-CCM+ thermal fluid model provides a temperature profile analysis of the canister based on four different ambient temperature conditions. An ANSYS APDL finite element model incorporates the temperature profiles to analyze the thermal stresses in the canister. The calculated thermal stress magnitudes are in the range of 10 MPa to 80 MPa, which could be significant for crack propagation through the canister wall. The maximum thermal stress is not a concern for the structural failure of the canister, but it is high enough that it is a significant contribution to the total stress state of the canister wall, which also includes residual stress from fabrication, internal pressure from helium cover gas, and potential transient mechanical loads, such as earthquakes. This paper describes the initial finite element thermal stress analysis that was completed in 2020, reports the initial findings, and identifies areas where model refinement is still needed to complete this work in the future.

Jensen, Ben J.↗

DOE OSTI2024

Pretest Modeling A Spent Nuclear Fuel Seismic Shake Test

The U.S. Department of Energy Spent Fuel and Waste Science and Technology (SFWST) program is planning to conduct a series of full-scale shake table tests to simulate hypothetical earthquake conditions and record the response of surrogate spent nuclear fuel (SNF) assemblies in a dry canister storage system mockup. The shake table motions will represent a range of hypothetical earthquake conditions at hypothetical locations in the continental U.S. to generally define the range of mechanical loads that SNF can be expected to experience during extended dry storage periods. This paper describes the pretest predictions made with LS-DYNA models of the mockup storage systems. The test will use two dry storage system configurations, a mockup vertical concrete cask (VCC) and a mockup horizontal storage module (HSM). The test will use a production-quality canister and basket. Within the canister will be four instrumented fuel assemblies with fuel rods containing surrogate mass and 28 instrumented dummy assemblies that are intended to match the mass and outer dimension of a fuel assembly. The finite element models include models of the VCC and HSM on the shake table to calculate the system level dynamic responses and separate single fuel assembly models to calculate stress and strain in fuel assembly components. Both types of models include nonlinear behavior like rod-to-rod contact and the ability for VCC’s to rock and slide. This paper presents the expected response of the VCC, HSM, and fuel assemblies to the shake table testing that is planned to start in April of 2024. The earthquake conditions represent seismic hazards in the 2,000-to-20,000-year return period range. The test data is expected to confirm the expectation that fuel rod cladding will remain intact, fuel assembly structural components like guide tubes will remain intact, and no significant VCC sliding or tipping will occur in the range of conditions to be tested with the shake table.

Klymyshyn, Nicholas A.↗

DOE OSTI2022

Summary of Chloride-induced Stress Corrosion Cracking Experiments with a Spent Fuel Storage Canister Large Plate

This report provides a comprehensive summary of the crack growth rate testing and the experiments to evaluate the corrosion behavior of welded plate material taken from the Sandia National Laboratories’ full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The information includes that previously reported, and new work on detailed surface characterization of the corrosion attack from the large plate experiment. The work and the results inform aging management programs for the SNF canisters.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2023

FY23 Update: Aerosol Sampling for the Canister Deposition Field Demonstration

This report describes the results of preliminary testing of aerosol monitoring equipment that will be used to continuously monitor the aerosol source term for the multi-year Canister Deposition Field Demonstration (CDFD). These data are required inputs for the development and validation of models for the deposition of dust and potentially corrosive salts on the surface of spent nuclear fuel (SNF) dry storage canisters. Surface salt loads correlate with the extent of corrosion damage on a metal surface, and potentially to the likelihood and timing of initiation of stress corrosion cracks. Aerosols will be monitored at the CDFD site using three instruments. A Dekati ® ELPI+ cascade impactor will be used for real-time monitoring of aerosol particle sizes. It will also collect dust in 14 size bins on impactor targets that can be chemically analyzed to determine the soluble salts present as a function of particle size. However, this instrument can only measure dried aerosols, with a diameter of <10 µm. The second instrument is a Topas laser particle size spectrometer, which provides real-time monitoring of aerosol particle sizes up to ~40 µm in size. It monitors both the ambient (potentially deliquesced) aerosol particle size distributions required for the dust deposition models and the distributions of the equivalent dried particles, allowing correlation with the Dekati ® data. However, it does not discriminate between inert dust particles and salt aerosols, and it does not retain samples of the different particle sizes for later analysis. The third instrument that will monitor aerosols at the CDFD site is a Clean Air Status and Trends Network (CASTNET) tower, which uses a multiple canister system to collect weekly samples for analysis to total suspended aerosol particle compositions and atmospheric gas concentrations. This status report describes work in FY23 to develop the capabilities for using these tools. In two training exercises, the cascade impactor and laser particle sizer were deployed in two different testing environments, one indoor and one outdoor. For the cascade impactor, the tests provided opportunities for the operators to familiarize themselves with impactor substrate preparation, and post-test sample removal and analysis. For the laser particle sizer, the tests were used to evaluate different instrument parameters, to determine the most appropriate settings for capturing transient events. Data and samples were collected for weeks to months for each test, and the results are presented here. In addition to the preliminary testing, contracts were developed with WSP Analytical Labs for sample preparation and analysis of the cascade impactor samples. The impactor tower from outdoor test was delivered to WSP and used to train the staff there in disassembly, sample extraction, sample analysis, and tower reassembly with new target substrates. These are tasks that WSP will be performing routinely for the CDFD project. The CASTNET system cannot be purchased or tested until an actual site has been selected for the CDFD test. Work for this FY has been restricted to preparation of contracts for purchasing the CASTNET tower, and for sample analysis, once the tower is in operation.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

SNF Canister Coatings for Corrosion Prevention and Mitigation (FY21 Status Report)

This report summarizes the current actives in FY21 related to the effort by Sandia National Laboratories to identify and test coating materials for the prevention, mitigation, and repair of spent nuclear fuel dry storage canisters against potential chloride-induced stress corrosion cracking. This work follows up on the details provided in Sandia National Laboratories FY20 report on the same topic, which provided a detailed description of the specific coating properties desired for application and implementation on spent nuclear fuel canisters, as well as provided detail into several different coatings and their applicability to coat spent nuclear fuel canisters. In FY21, Sandia National Laboratories has engaged with private industry to create a Memorandum of Understanding and established a collaborative R&D program building off the analytical and laboratory capabilities at Sandia National Laboratories and the material design and synthesis capabilities of private industry. The resulting Memorandum of Understanding included four companies to date (Oxford Performance Materials, White Horse R&D, Luna Innovations, and Flora Coating) proposing six different coating technologies (polyetherketoneketone, modified polyimide/polyurea, modified phenolic resin, silane-based polyurethane hybrid with and without a Znrich primer, and a quasi-ceramic sol-gel polyurethane hybrid) to be tested, evaluated, and optimized for their potential use for this application. This report provides a detailed description of each of the coating systems proposed by the participating industry partners. It also provides a description of the planned experimental actives to be performed by Sandia National Laboratories including physical tests, electrochemical tests, and characterization methods. These analyses will be used to identify specific ways to further improve coating technologies toward their application and implementation on spent nuclear fuel canisters. In FY21, Sandia National Laboratories began baseline testing of the base metal material in according with activities of the Memorandum of Understanding. In FY22, Sandia National Laboratories will receive coated coupons from each of the participating industry partners and begin characterization, physical, and electrochemical testing following the test plan described herein.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2023

MODELING A SPENT NUCLEAR FUEL CASK SEISMIC TEST

The US Department of Energy Spent Fuel and Waste Science and Technology (SFWST) program is planning to conduct a series of full-scale shake table tests to simulate hypothetical earthquake conditions and record the response of surrogate spent nuclear fuel (SNF) assemblies in a canister dry storage system mockup. The shake table motions will represent a range of hypothetical earthquake conditions at hypothetical locations in the continental US to generally define the range of mechanical loads that SNF can be expected to experience during extended dry storage periods. The earthquake conditions will represent seismic hazards in the 2,000-to-20,000-year return period range. The test will use instrumented pressurized water reactor fuel assemblies with surrogate mass inside the fuel rods instead of radioactive fuel pellets. Dummy assemblies with similar mass and dimensions to actual fuel assemblies will occupy the rest of the fuel assembly locations in a SNF canister that holds 32 fuel assemblies. The canister will be located inside a mockup vertical concrete cask. Instrumentation will record the motion of the major components of the complex dynamic system, and strain gauges will be used to record the cladding strain at select locations. Preparations for the test require modeling predictions to identify the range of response of the system and to help select specific earthquake cases to be simulated on the shake table from a large set of potential cases. This paper describes the pretest nonlinear finite element modeling efforts that have been completed to date, including cask system level modeling and fuel assembly modeling in LS-DYNA. The cask system level models are critical for anticipating sliding or tipping of an unanchored cask during the test. The fuel assembly model is needed to estimate the range of cladding strain response and fuel assembly structural response to be expected during the test and cladding strain measurements will be key metrics for model validation and the development of modeling best practices after the test is concluded.

Klymyshyn, Nicholas A.↗

DOE OSTI2023

A Vacuum Drying Study of Simulated Failed Nuclear Fuel (FY23)

This report documents work performed under the Office of Spent Fuel and Waste Disposition’s (SFWD’s) Spent Fuel and Waste Science and Technology program for the US Department of Energy (DOE) Office of Nuclear Energy (NE). This work was performed to fulfill Level 4 milestone M4SF-23OR010203013. Over the 70 years of light-water reactor (LWR) operation, fuel rod failures have occurred during reactor operation. Based on the Unified Database that SFWD maintains, there are ~5,400 LWR fuel rods that developed leaks during reactor operation of the >19 million rods operated. The Unified Database indicates that ~4,200 of these rods remain in the spent fuel pool, and ~1,200 are in dry storage canisters. It is expected that all failed rods are “waterlogged” in the spent fuel pool, meaning the inside of the rods contain some volume of water. There are two related objectives of this work. The first is to develop a simple and inexpensive experiment to better understand removal of water from inside failed spent nuclear fuel (SNF) rods, and the second is to develop a model to predict drying of simulated failed fuel in the simple experiment. Once a model captures the phenomenon in the simple experiment, it can be extended to predict drying under more prototypical conditions.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗