DOE OSTI2024

Suppressing Atmospheric Degradation of Sulfide-Based Solid Electrolytes via Ultrathin Metal Oxide Layers

Sulfide-based solid-state electrolytes (SSEs) are promising materials with superior Li-ion conductivity; however, their poor atmospheric stability limits commercial manufacturing at scale. Here, we investigate the impact of ultrathin metal oxide layers deposited via atomic layer deposition (ALD) on the stability of Li 6 PS 5 Cl (LPSCl). Al 2 O 3 layers grown directly on LPSCl particles significantly stabilize the surface chemistry and Li-ion transport properties relative to uncoated material upon exposure to both an ambient atmosphere (22% relative humidity, RH) and humidified O 2 (100% RH). Detailed investigations indicate that coatings impede the surface and bulk degradation kinetics of exposed materials, even for coatings as thin as ∼1 Å. Furthermore, this suggests that stabilization is due to more than just a physical barrier. Shifts in valence band edge positions of coated LPSCl indicate that ALD coatings alter the surface electronic structure and resulting oxidation tendency of underlying LPSCl, suggesting new avenues to improving the environmental stability of sulfide SSEs.

Atmospheric chemistry↗
DOE OSTI2025

Locally Confined Polysulfide-Reactive Electrolytes for Shuttle-Free Sodium–Sulfur Batteries

Sodium-sulfur batteries promise high-energy-density and sustainable electrochemical energy storage but suffer from uncontrolled polysulfides dissolution and high sodium reactivity. These challenges fundamentally originate from poor electrolyte-electrode compatibility. Current electrolyte research inadequately addresses the trade-off between minimal polysulfides solvation and stabilizing sodium interfaces. Here, we present a locally-confined polysulfide-reactive electrolyte strategy that mediates the polysulfide dissolution dynamics and sodium stability by leveraging an electrophilic solvating species with a localized high-concentration electrolyte. This design enables shuttle-free cell operation by synergistically restricting the global solvating power of the electrolyte through intermolecular interactions and locally scavenging sparingly dissolved polysulfides via electrolyte electrophilicity. The precisely confined surface reaction facilitates a protective cathode-electrolyte interface, realizing a quasi-solid-state sulfur conversion in our liquid ether-based electrolyte, which crucially avoids crossover-induced catastrophic sodium-metal degradation. The proposed electrolyte demonstrates long-term cycling of high-mass-loading sulfur cathodes (> 3 mg S cm −2 with commercial carbon host and 70 wt% sulfur content), which afford 710 mA h g −1 over 400 cycles in coin cells and steady pouch cell operation over 180 cycles. Furthermore, this work establishes a scalable electrolyte design protocol that regulates the reaction chemistry of highly reactive electrodes, offering a pathway toward sustainable renewable energy storage.

25 ENERGY STORAGE↗
NASA NTRS1990

Antireduction Insulator For Solid-Electrolyte Cell

Depletion of oxygen from electrolyte prevented. Proposed to add layer of electrical insulation between solid electrolyte and portion of porous negative electrode under negative metal contact in solid-electrolyte cell. Helps maintain efficiency of cell by preventing "shadow" effect degrading portion of electrolyte under negative contact and sometimes near seals.

Shlichta, Paul J.↗
DOE OSTI2020

First-principles Modeling and Design of Solid-State Interfaces for the Protection and Use of Lithium Metal Anodes

Li-ion batteries are one of the most advanced energy storage technologies in use today. Li-ion batteries are used in a multitude of applications ranging from consumer electronics, medical devices, sensors and grid storage. However, improving the capacity and energy density delivered by current Li-ion technology requires advanced materials research into novel chemical systems. In this project we have focused particularly in the use of solid-state electrolytes with lithium metal electrodes. Research into all solid-state batteries (ASSB) with Li metal electrodes has significantly expanded in recent years, however most studies reported experimental findings, which left substantial room for theoretical and modeling work as a tool to understand and determine design principles allowing reliable and safe use of ASSBs with Li metal. Among the remaining obstacles preventing reliable use of ASSBs with a Li metal electrode, the stability of the interface between the solid electrolyte and Li metal, and the propagation/dendrite formation of Li metal and resulting mechanical degradation of the electrolyte are key phenomenon that are yet to be fully understood. In the current project we have addressed these two coupled phenomena using first principles calculations and mesoscale continuum modeling. We have obtained chemical and electrochemical stability windows for several solid electrolyte materials. Additionally, from mathematical and numerical modeling of Li protrusion and dendrite initiation during plating and stripping we have determined design criteria in terms of chemical, electrochemical, and mechanical properties and operating conditions for which stable deposition can occur. We also considered the effects of mixed electronic-ionic conduction in solid electrolytes, which has more recently been suggested as another important mechanism involved in ASSB failure. Throughout our work we have successfully addressed important questions necessary for the use of ASSB’s. We have determined guiding principles for materials properties and operating conditions necessary to operate ASSB’s. And have proposed novel solid electrolyte materials with predicted chemical stability an ionic conductivity. Although this represents significant progress in our understanding, open questions remain in order to fully develop reliable and safely operate ASSBs with Li metal. Future work, building on this project will require further experimental, theoretical and simulation efforts to address remaining questions.

25 ENERGY STORAGE↗
DOE OSTI2022

Characterization and Accelerated Life Testing of a New Solid Oxide Electrolysis Cell

The project aims to develop mechanistic degradation models that realistically predict long-term Solid Oxide Electrolysis Cell (SOEC) durability, using input data from accelerated electrochemical life testing combined with quantitative microstructural and microchemical evaluation. A promising SOEC type will be further developed. The understanding achieved by combining experimental results and theory will be used to guide improvements in long-term SOEC durability, and validate that this technology can reach DOE H 2 production cost and durability targets. Planned outcomes include: (1) new experimental accelerated testing data on SOEC degradation at the oxygen electrode, fuel electrode, and electrolyte; (2) predictive theory of degradation developed based on the accelerated test data; (3) new electrode materials and processing methods that minimize degradation rate; (4) determination of the impact of SOEC electrolyte thickness and electrode composition/microstructure on performance and degradation; (5) determination of the operating conditions where degradation is minimized; and (6) validation of degradation models for extrapolating accelerated test data to predict long-term durability.

08 HYDROGEN↗
NASA NTRS2012

Accelerated Aging Experiments for Capacitor Health Monitoring and Prognostics

This paper discusses experimental setups for health monitoring and prognostics of electrolytic capacitors under nominal operation and accelerated aging conditions. Electrolytic capacitors have higher failure rates than other components in electronic systems like power drives, power converters etc. Our current work focuses on developing first-principles-based degradation models for electrolytic capacitors under varying electrical and thermal stress conditions. Prognostics and health management for electronic systems aims to predict the onset of faults, study causes for system degradation, and accurately compute remaining useful life. Accelerated life test methods are often used in prognostics research as a way to model multiple causes and assess the effects of the degradation process through time. It also allows for the identification and study of different failure mechanisms and their relationships under different operating conditions. Experiments are designed for aging of the capacitors such that the degradation pattern induced by the aging can be monitored and analyzed. Experimental setups and data collection methods are presented to demonstrate this approach.

Prognostics of Electronics↗
DOE OSTI2021

The Impact of Different Substituents in Fluorinated Cyclic Carbonates in the Performance of High Voltage Lithium-Ion Battery Electrolyte

Ethylene carbonate (EC) has been used as the Solid-Electrolyte Interphase (SEI) former in the conventional electrolyte for decades. However, its low anodic stability leads to severe capacity decay during cycling under high voltage operation. Therefore, finding a viable electrolyte with high anodic stability and the ability to form robust SEI for high voltage lithium-ion batteries is of primary importance. In this study, a series of electrolytes containing various fluorinated cyclic carbonates as the SEI former have been designed, synthesized and evaluated. Linear sweep voltammetry study suggested that fluorinated cyclic carbonates generally possess higher anodic stability than EC. Based on the cycling performance of LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NMC532)/ graphite full cells, the electrolyte with DFEC/FEMC (1.0 M LiPF 6 ) inhibited the oxidation side reaction on the cathode and forms a vigorous SEI on the anode. The high voltage NMC532/Graphite cell utilizing the novel electrolyte exhibits excellent cycling durability under both room and elevated temperature. The superior performance of the DFEC based electrolyte was further unveiled by SEM, EDAX and XRD. Both the anode and cathode of the full cell employing DFEC based electrolyte retained their intrinsic structures after cycling while the electrodes cycled in conventional electrolyte showed severe degradation.

25 ENERGY STORAGE↗
DOE OSTI2022

Controlling dendrite propagation in solid-state batteries with engineered stress

Metal-dendrite penetration is a mode of electrolyte failure that threatens the viability of metal-anode-based solid-state batteries. Whether dendrites are driven by mechanical failure or electrochemical degradation of solid electrolytes remains an open question. If internal mechanical forces drive failure, superimposing a compressive load that counters internal stress may mitigate dendrite penetration. Here, we investigate this hypothesis by dynamically applying mechanical loads to growing dendrites in Li 6.6 La 3 Zr 1.6 Ta 0.4 O 12 solid electrolytes. Operando microscopy reveals marked deflection in the dendrite growth trajectory at the onset of compressive loading. For sufficient loading, this deflection averts cell failure. Using fracture mechanics, we quantify the impact of stack pressure and in-plane stresses on dendrite trajectory, chart the residual stresses required to prevent short-circuit failure, and propose design approaches to achieve such stresses. For the materials studied here, we show that dendrite propagation is dictated by electrolyte fracture, with electronic leakage playing a negligible role.

25 ENERGY STORAGE↗
DOE OSTI2025

The Solid Electrolyte Interphase Dispersion Can Predict Cycle and Calendar Lifetimes in Silicon Anodes for Lithium-Ion Batteries

The solid electrolyte interphase (SEI) plays a critical role in lithium-ion battery (LIB) anodes. It is responsible for passivating the reactive surface of lithiated anodes against degradation of the electrolyte which enables long cycle and calendar lifetimes for LIBs. This role is especially important in high energy density anodes like silicon, that undergo massive volumetric changes during electrochemical cycling. The mechanism by which the SEI performs this role, however, is not clear which makes designing an SEI to passivate silicon anodes impossible. Through decades of research, dozens of chemical species have been identified within the SEI ranging from inorganic solids to polymeric coatings all of which simultaneously exist in a 'mosaic' composition at the anode surface. This mosaic creates a highly dispersive environment in which electrostatic screening of the anode surface from the electrolyte is not always complete. Here, we present an electrochemical technique to directly test the dispersion at the anode surface. We use this technique to screen more than 20 different electrolytes against silicon anodes and find correlations between both the cycle life and calendar life. The insights from this study offer a new framework to think about the SEI and a rapid screening method to test novel electrode/electrolyte combinations.

battery↗
DOE OSTI2021

Stabilizing electrode–electrolyte interfaces to realize high-voltage Li||LiCoO 2 batteries by a sulfonamide-based electrolyte

High-voltage lithium-metal batteries (LMBs) with LiCoO 2 (LCO) as the cathode have high volumetric and gravimetric energy densities. However, it remains a challenge for stable cycling of LCO >4.5 V Li . Here we demonstrate that a rationally designed sulfonamide-based electrolyte can greatly improve the cycling stability at high voltages up to 4.7 V Li by stabilizing the electrode–electrolyte interfaces (EEIs) on both the Li-metal anode (LMA) and high-voltage LCO cathode. With the sulfonamide-based electrolyte, commercial LCO cathodes retain 89% and 85% of their capacities after 200 and 100 cycles under high charging voltages of 4.55 V Li and 4.6 V Li , respectively, significantly outperforming traditional carbonate-based electrolytes. The surface degradation, impedance growth, and detrimental side reactions in terms of gas evolution and Co dissolution are well suppressed. Our work demonstrates a promising strategy for designing new electrolytes to realize high-energy Li||LCO batteries.

25 ENERGY STORAGE↗
DOE OSTI2025

High-voltage water-scarce hydrogel electrolytes enable mechanically safe stretchable Li-ion batteries

Soft Li-ion batteries, based on conventional organic electrolytes, face performance degradation challenges due to moisture penetration and safety concerns due to possible leakage of toxic fluorine compounds and flammable solvents under mechanical damage. We design a water-scarce hydrogel electrolyte with fluorine-free lithium salt to achieve wide electrochemical stability window (up to 3.11 volts) in ambient air without hermetic packaging while balancing high stretchability (1348%), ion conductivity (41 millisiemens per centimeter), and self-healing capabilities for mechanically and chemically safe stretchable Li-ion batteries. Molecular synergy between hydrophilicity and lithiophilicity of zwitterionic polymer backbone is revealed by molecular dynamics simulations. The battery exhibits capacity retention under harsh mechanical stresses—enduring stretching, twisting, folding, and multiple through-punctures by a needle—while self-healing from repeated through cuts by a razor blade. Stable ambient operation for 1 month over 500 charge-discharge cycles (average coulomb efficiency, 95%) is achieved. A prototype self-healing electronic system with embedded soft batteries demonstrates practical application as a durable embodied energy source.

Science & Technology - Other Topics↗
DOE OSTI2025

Understanding the Cathode Electrochemistry of Humidified Solid‐State Lithium‐Oxygen Batteries

Lithium-oxygen batteries (LOBs) possess a high theoretical energy density, making them potential candidates for next-generation energy storage. However, challenges such as reactive oxygen species-induced component degradation hinder their practical use. Inorganic solid-state electrolytes offer an alternative to degradation-prone aprotic electrolytes, while also protecting lithium anodes from potential atmospheric reactants. Here, this study explores the cathode electrochemistry of solid-state LOBs using humidified oxygen, which forms an aqueous catholyte during initial cycling, thereby improving cathode-electrolyte contact. To quantitatively analyze the cathode electrochemistry, a ‘Humidity-Incorporated’ Differential Electrochemical Gas Monitoring System (HiDEMS) is developed to control humidity and monitor gas consumption and evolution in real time. When studying a Li-O 2 cell that employs a NASICON-type Li 1.3 Al 0.3 Ti 1.7 (PO 4 ) 3 (LATP) solid electrolyte and a porous carbon cathode, a shift in discharge products from Li 2 O 2 to LiOH is observed over repeated cycles. While Li 2 O 2 evolves O 2 during charging, LiOH oxidation leads to minimal O 2 release and increased CO 2 production, originating from oxidation of carbon electrodes. Further, dissolution of Al and P from LATP is observed, likely driven by the formation of the alkaline catholyte. The findings highlight the need for carbon-free cathode materials and more stable solid-state conductors to minimize side reactions and improve rechargeability in humidified solid-state Li-O 2 batteries.

LATP degradation↗
DOE OSTI2020

Structural Degradation of High Voltage Lithium Nickel Manganese Cobalt Oxide (NMC) Cathodes in Solid-State Batteries and Implications for Next Generation Energy Storage

In this study, we report the stability of the layered high voltage cathode NMC622 with respect to a standard liquid electrolyte and in an all solid-state configuration. NMC622 cathodes with a (104) orientation were found to suffer from degradation at high voltage (4.5 V vs Li/Li + ) due to electrolyte-promoted degradation of the layered structure in a carbonate electrolyte. The lithium phosphorus oxynitride (LiPON) electrolyte was able to suppress the extent of this decomposition in solid-state cells but not totally prevent it from occurring. In the solid-state cells the capacity decreased from 203 to 93 mAh/g in the first cycle and from 93 to 79 mAh/g over the subsequent 99 cycles, whereas, after 20 cycles, the liquid cell charge capacity was dominated by the irreversible electrolyte degradation. Furthermore, the interfacial resistances of the solid-state cells were stable with cycling, suggesting minimal degradation of the NMC622/LiPON interface and incumbent losses due to structural evolution associated with cathode orientation. This data indicates that accessing stable high voltage capacity in NMCs will not be enabled by simply stabilizing the cathode–electrolyte interface. Optimizing cathode crystallographic orientation may be the key to accessing this high voltage regime.

25 ENERGY STORAGE↗
NASA NTRS1992

Protecting Li/TiS2 Cells Against Overcharge

New electrolyte additive, N,N,N',N'- tetramethyl-1,4-phenylenediamine (TMPD), helps protect lithium/titanium disulfide rechargeable cells against overcharge. TMPD is redox couple: during overcharge, it undergoes electrochemical reactions at both electrodes and takes up excess input charge. Without TMPD, overcharge results in oxidative degradation of nonaqueous electrolyte, leading to loss of rechargeability and safety problems. Li/TiS2 cells currently being considered for spacecraft and military applications.

Narayanan, S. R.↗
DOE OSTI2021

Evaluating temperature dependent degradation mechanisms of silicon-graphite electrodes and the effect of fluoroethylene carbonate electrolyte additive

Understanding and overcoming the relatively high rate of degradation observed with silicon (Si)-based anodes in lithium (Li)-ion batteries (LiBs) is crucial for developing cells with increased energy density. The capacity fade of Si-graphite (Gr) electrodes in electrolytes with and without 10 wt% fluoroethylene carbonate (FEC) is explored during cycling at temperatures of 25, 45, and 70 °C, focusing on the complex degradation modes arising from loss of active material, loss of Li inventory, and cell resistance growth. We first show the common half-cell testing cannot be used at elevated temperatures as the performance of Li metal overshadows the behavior of Si-Gr electrode. Symmetric cell configuration successfully eliminates the effect of foreign materials, and reveals that while the presence of FEC provides better passivation of Si, it also results in greater parasitic reactions at 70 °C and faster capacity fade. The electrolyte without FEC, on the other hand, shows higher capacity retention at 70 °C. Finally, we propose a multi-step test protocol which can successfully deconvolute the information on loss of Li inventory and of active material. By combining half-cell and symmetric cell test methods, we demonstrate that loss of active material is reduced at higher temperatures and the dominant mechanisms of capacity loss for Si-Gr electrodes at elevated temperatures is loss of Li inventory.

25 ENERGY STORAGE↗