NASA NTRS2012

Thermography Inspection for Early Detection of Composite Damage in Structures During Fatigue Loading

Advanced composite structures are commonly tested under controlled loading. Understanding the initiation and progression of composite damage under load is critical for validating design concepts and structural analysis tools. Thermal nondestructive evaluation (NDE) is used to detect and characterize damage in composite structures during fatigue loading. A difference image processing algorithm is demonstrated to enhance damage detection and characterization by removing thermal variations not associated with defects. In addition, a one-dimensional multilayered thermal model is used to characterize damage. Lastly, the thermography results are compared to other inspections such as non-immersion ultrasonic inspections and computed tomography X-ray.

Zalameda, Joseph N.↗
NASA NTRS2005

Space Shuttle Partial Stack Rollout Test Analytical Correlation In Support Of Fatigue Load Development

A rollout test with only the Solid Rocket Boosters was conducted in November 2003 to gather structural dynamic response data of the transportation environment from the Vehicle Assembly Building to the Launch Pad. The data was acquired to develop and validate analytical methods used to predict rollout Orbiter fatigue load spectra. Earlier predictions computed by a base drive approach with only 5 input drive degrees-of-freedom raised questions that commissioned the partial stack test. Not only was there a concern because of the input degree-of-freedom omission due to measurement limitations, but there was also a concern with the implementation of the "large mass" itself. Three methods were evaluated with the partial stack test data. The analytical correlations to measured strain derived SRB base loads and acceleration5 showed the earlier 5 degree-of-freedom base drive approach to yield the most conservative results for all quantities monitored except the SRB base moment about the axis in which the input drive was missing. This non-conservative shortcoming led to a recommendation to use either the 6 degree-of-freedom base drive or the 12 degree-of-freedom Craig-Bampton boundary drive methods whose results did not substantially differ.

DelBasso, Steve↗
NASA NTRS2018

A Benchmark Example for Delamination Propagation Predictions Based on the Single Leg Bending Specimen Under Quasi-Static and Fatigue Loading

Benchmark examples based on Single Leg Bending (SLB) specimens with equal and unequal bending arm thicknesses were used to assess the performance of delamination prediction capabilities in finite element codes. First, the development of the quasi-static benchmark cases using the Virtual Crack Closure Technique (VCCT) is discussed in detail. Second, based on the quasi-static benchmark results, additional benchmark cases to assess delamination propagation under fatigue loading are created. Third, the application is demonstrated for the commercial finite element code Abaqus Standard 2018. The benchmark cases are compared to results obtained from VCCT-based, automated quasi-static propagation analysis. A comparison with results from automated fatigue propagation analysis was not performed at this point since the current version of Abaqus does not include this capability under variable mixed-mode conditions. In general, good agreement between the results obtained from the quasi-static propagation analysis and the benchmark results were achieved. Overall, the benchmarking procedure proved valuable for analysis verification.

Krueger, Ronald↗
NASA NTRSDate not supplied

A Benchmark Example for Delamination Propagation Predictions Based on the Single Leg Bending Specimen under Quasi-static and Fatigue Loading

Benchmark examples based on Single Leg Bending (SLB) specimens with equal and unequal bending arm thicknesses were used to assess the performance of delamination prediction capabilities in finite element codes. First, the development of the quasi-static benchmark cases using the Virtual Crack Closure Technique (VCCT) is discussed in detail. Second, based on the quasi-static benchmark results, additional benchmark cases to assess delamination propagation under fatigue loading are created. Third, the application is demonstrated for the commercial finite element code Abaqus Standard 2018. The benchmark cases are compared to results obtained from VCCT-based, automated quasi-static propagation analysis. A comparison with results from automated fatigue propagation analysis was not performed at this point since the current version of Abaqus does not include this capability under variable mixed-mode conditions. In general, good agreement between the results obtained from the quasi-static propagation analysis and the benchmark results were achieved. Overall, the benchmarking procedure proved valuable for analysis verification.

Ronald Krueger↗
DOE OSTI2015

Extreme and fatigue loads on wind turbines during thunderstorm downbursts: The influence of alternative turbulence models

Downburst winds are inherently transient and non-stationary by nature. Field records have confirmed the often very rapid variation in time of both mean wind speed and wind direction during a downburst. Turbulence characteristics in a downburst are also different from those in the neutral boundary layer. Studies have indicated that turbulence power spectra during a downburst can deviate significantly from more traditional spectra used for the neutral boundary layer. Estimated power spectra from downburst records indicate additional turbulence energy in the mid-frequency range and often they do not follow the −5/3 slope in the inertial subrange. In this study, three turbulence models that can be combined with a non-turbulent downburst wind field model are presented. The influence of these three models on extreme and fatigue loads for a 5-MW wind turbine is investigated first. Then, a parametric study on the longitudinal turbulence length scale, turbulence intensity, and turbulence vertical component in downburst turbulence modeling is carried out. The influence of these various turbulence-related parameters on loads on the 5-MW wind turbine is discussed.

Nguyen, Hieu Huy↗
NASA NTRS1977

Biaxial fatigue loading of notched composites

Thin-walled, 2.54-cm diameter tubular specimens of graphite/epoxy were fatigue cycled in combinations of axial, torsional, and internal pressure loading. Two different four-ply layup configurations were tested: (0-90)s and (+ or- 45)s; each tube contained a 0.48-cm diameter circular hole penetrating one wall midway along the tube length. S-N curves were developed to characterize fatigue behavior under pure axial, torsional, or internal pressure loading, as well as combined loading fatigue. A theory was developed based on a plane stress model which enabled the S-N curve for combined stress states to be predicted from the S-N data for the uniaxial loading modes. Correlation of the theory with the experimental data proved to be remarkably good.

Francis, P. H.↗
NASA NTRS1954

Axial-Load Fatigue Properties of 24S-T and 75S-T Aluminum Alloy as Determined in Several Laboratories

In the initial phase of a NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 aluminum-alloy sheet have been made at the Battelle Memorial Institute and at the Langley Aeronautical Laboratory of the National Advisory Committee for Aeronautics. The test specimens were polished and unnotched. The manufacturer of the material, the Aluminum Company of America, has made axial-load tests on 24S-T4 and 75S-T6 rod material. The test techniques used at the three laboratories are described in detail; the test results are presented and are compared with each other and with results obtained on unpolished sheet by the National Bureau of Standards. (author)

Grover, H J↗
NASA NTRS1977

Biaxial fatigue loading of notched composites

Thin walled, 2.54-cm (1-in.) diameter tubular specimens of T300/934 graphite/epoxy were fabricated and fatigue cycled in combinations of axial, torsional, and internal pressure loading. Two different four-ply layup configurations were tested: (0/90)S and (+ or - 45)S; all tubes contained a 0.48-cm (3/16-in.) diameter circular hole penetrating one wall midway along the tube length. S-N curves were developed to characterize fatigue behavior under pure axial, torsional, or internal pressure loading, as well as combined loading fatigue. A theory was developed based on the Hill plane stress model which enabled the S-N curve for combined stress states to be predicted from the S-N data for the uniaxial loading modes. Correlation of the theory with the experimental data proved to be remarkably good.

Francis, P. H.↗
NASA NTRS1971

Effects of loading sequence for notched specimens under high-low two-step fatigue loading

The effects of loading sequence on crack-initiation period were investigated for notched aluminum-alloy specimens under high-low two-step loading with special emphasis on local cyclic stresses and strains at the notch root. Local stress and strain were determined by a procedure based on an equation proposed by Neuber which relates elastoplastic stress and strain at a notch. Local stress and strain were also measured experimentally to verify the Neuber equation. The effects of initial high load on the crack-initiation periods were demonstrated with notched specimens and were simulated in unnotched specimens fatigue tested with local stress sequences. An analysis of the results indicated that sequence effects were not caused solely by local residual stresses, as is usually assumed; the existence of a damaging effect, resulting from the high local strain cycles, was demonstrated. The sequence effects observed with notched specimens were interpreted as the combined result of residual stresses and high local strain cycles.

Crews, J. H., Jr.↗
NASA NTRS1989

Characterization of failure processes in tungsten copper composites under fatigue loading conditions

A fractographic and metallographic investigation was performed on specimens of a tungsten fiber reinforced copper matrix composite (9 vol percent), which had experienced fatigue failures at elevated temperatures. Major failure modes and possible failure mechanisms, with an emphasis placed on characterizing fatigue damage accumulation, were determined. Metallography of specimens fatigued under isothermal cyclic loading suggested that fatigue damage initiates in the matrix. Cracks nucleated within the copper matrix at grain boundaries, and they propagated through cavity coalescence. The growing cracks subsequently interacted with the reinforcing tungsten fibers, producing a localized ductile fiber failure. Examinations of interrupted tests before final failure confirmed the suggested fatigue damage processes.

Kim, Yong-Suk↗
NASA NTRS2004

Space Shuttle Crawler Transporter Vibration Analysis in Support of Rollout Fatigue Load Spectra Verification Program

The Crawler Transporter (CT), designed and built for the Apollo Program in the 1960's and surpassing its initial operational life, has become an integral part of the Space Shuttle Program (SSP). The CT transports the Space Shuttle Vehicle (SSV) stack, atop the Mobile Launch Platform (MLP), from the Vehicle Assembly Building (VAB) to the launch pad. This support structure provides hydraulic jacking, leveling and load equalization for the 12 million pound stack on its 3.5-5.0 mile rollout to the launch pad. Major elements of the SSV, consisting of the orbiter, solid rocket boosters (SRB) and external tank (ET) have required fatigue analyses as part of the mission life certification. Compared to rollout vibration, the SSV sees relatively high vibration loads during launch, ascent, descent and landing phases of the mission. Although preliminary measured SRB vibration levels during rollout were of low amplitude and frequency, the duration of the rollout phase is typically high, from 5-6 hours. As part of an expanded mission life assessment, additional certification effort was initiated to define fatigue load spectra for rollout. This study addresses the CT vibration analyses in support of the rollout fatigue study. Structural models developed for modal and vibration analyses were used to identify unique CT, CT/MLP and CT/MLP/SRB vibration characteristics for comparison to instrumented rollout tests. Whereas the main structural and vibration characteristics of the SSV are well defined, minimum analytical and vibration test data on the Crawler Transporter were available. Unique vibration characteristics of the CT are attributable to the drive mechanism, hydraulic jacking system, structural framing and the CT-to-MLP support pad restraints. Initial tests performed on the CT/MLP/SRB configuration showed reasonable correlation with predicted mode shapes and frequencies.

Margasahayam, Ravi N.↗
DOE OSTI2015

The Rehbinder effect in iron during giga-cycle fatigue loading

The influence of the adsorptive strength reduction effect (the Rehbinder effect) on the fatigue life of pure iron under the giga-cycle loading regime was investigated. Specimens were loaded by an ultrasonic testing machine with a frequency of 20 kHz in air and in contact with eutectic alloy of gallium with tin and indium. A significant (by several orders of magnitude) worsening of the life-time of iron in contact with a molten metal as compared with tests in air was established. The liquid metal penetrates into the material to a depth of 200 μm to the center of a fatigue crack. The mechanism of the fatigue crack initiation in the giga-cycle regime of loading in contact with a surfactant is differing: the crack is formed on the surface of the specimen rather than within it as is the case for air. Based on the electron and optical microscopy data for the fracture surface, it can be concluded that exactly the change in the crack initiation mechanism reduces the fatigue life of iron in contact with a liquid metal because the initiated crack propagates regardless of the surfactant.

36 MATERIALS SCIENCE↗
NASA NTRS1987

Random loading fatigue crack growth: Crack closure considerations

The prediction of fatigue crack growth is an important element of effective fracture control for metallic structures and mechanical components, especially in the aerospace industry. The prediction techniques available and applied today are mostly based on fatigue crack growth measurements determined in constant amplitude testing. However, while many service loadings are constant amplitude, many more loadings are random amplitude. An investigation to determine which statistics of random loadings are relevant to fatigue crack closure was conducted. The fundamentals of random processes and crack closure are briefly reviewed, then the relevance of certain random process parameters to the crack closure calculation are discussed qualitatively. A course for further research is outlined.

Ortiz, Keith↗
NASA NTRS1995

High Temperature Slow Crack Growth of Si3N4 Specimens Subjected to Uniaxial and Biaxial Dynamic Fatigue Loading Conditions

The slow crack growth of a hot-pressed silicon nitride was determined at 1300 C in air using dynamic fatigue testing under both uniaxial and biaxial stress states. Good agreement in fatigue parameter exists between the data obtained from uniaxial and biaxial loading conditions. A reasonable prediction of dynamic fatigue from one stress state to another was made using the recently developed CARES/LIFE computer code.

Choi, Sung R.↗
NASA NTRS2016

Large Area Nondestructive Evaluation of a Fatigue Loaded Composite Structure

Large area nondestructive evaluation (NDE) inspections are required for fatigue testing of composite structures to track damage initiation and growth. Of particular interest is the progression of damage leading to ultimate failure to validate damage progression models. In this work, passive thermography and acoustic emission NDE were used to track damage growth up to failure of a composite three-stringer panel. Fourteen acoustic emission sensors were placed on the composite panel. The signals from the array were acquired simultaneously and allowed for acoustic emission location. In addition, real time thermal data of the composite structure were acquired during loading. Details are presented on the mapping of the acoustic emission locations directly onto the thermal imagery to confirm areas of damage growth leading to ultimate failure. This required synchronizing the acoustic emission and thermal data with the applied loading. In addition, processing of the thermal imagery which included contrast enhancement, removal of optical barrel distortion and correction of angular rotation before mapping the acoustic event locations are discussed.

Joseph N Zalameda↗
NASA NTRS2014

Crack Growth Behavior in the Threshold Region for High Cycle Fatigue Loading

The research results described in this paper presents a new understanding of the behavior of fatigue crack growth in the threshold region. It is believed by some crack growth experts that the ASTM load shedding test method does not produce true or valid threshold properties. The concern involves the observed fanning of threshold region da/dN data plots for some materials in which the low R-ratio data fans out or away from the high R-ratio data. This data fanning or elevation of threshold values is obviously caused by an increase in crack closure in the low R-ratio tested specimens. This increase in crack closure is assumed by some investigators to be caused by a plastic wake on the crack surfaces that was created during the load shedding test phase. This study shows that the increase in crack closure is the result of an extensive occurrence of crack bifurcation behavior in some materials, particularly in aluminum alloys, when the crack tip cyclic yield zone size becomes less than the grain size of the alloy. This behavior is related to the high stacking fault energy (SFE) property of aluminum alloys which results in easier slip characteristics. Therefore, the particular fanning behavior in aluminum alloys is a function of intrinsic dislocation property of the materials and that the fanned data represents valid material properties. However, for corrosion sensitive steel alloys used in this study the fanning was caused by a build-up of iron oxide at the crack tip from fretting corrosion.

Forman, Royce G.↗
NASA NTRS2014

Crack Growth Behavior in the Threshold Region for High Cycle Fatigue Loading

This paper describes the results of a research program conducted to improve the understanding of fatigue crack growth rate behavior in the threshold growth rate region and to answer a question on the validity of threshold region test data. The validity question relates to the view held by some experimentalists that using the ASTM load shedding test method does not produce valid threshold test results and material properties. The question involves the fanning behavior observed in threshold region of da/dN plots for some materials in which the low R-ratio data fans out from the high R-ratio data. This fanning behavior or elevation of threshold values in the low R-ratio tests is generally assumed to be caused by an increase in crack closure in the low R-ratio tests. Also, the increase in crack closure is assumed by some experimentalists to result from using the ASTM load shedding test procedure. The belief is that this procedure induces load history effects which cause remote closure from plasticity and/or roughness changes in the surface morphology. However, experimental studies performed by the authors have shown that the increase in crack closure is a result of extensive crack tip bifurcations that can occur in some materials, particularly in aluminum alloys, when the crack tip cyclic yield zone size becomes less than the grain size of the alloy. This behavior is related to the high stacking fault energy (SFE) property of aluminum alloys which results in easier slip characteristics. Therefore, the fanning behavior which occurs in aluminum alloys is a function of intrinsic dislocation property of the alloy, and therefore, the fanned data does represent the true threshold properties of the material. However, for the corrosion sensitive steel alloys tested in laboratory air, the occurrence of fanning results from fretting corrosion at the crack tips, and these results should not be considered to be representative of valid threshold properties because the fanning is eliminated when testing is performed in dry air.

Forman, R. G.↗