Results for “hydrogen embrittlement”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 73 records · Page 4

Hydrogen embrittlement of Zircaloy-4 fabricated by ultrasonic additive manufacturing

Ultrasonic additive manufacturing (UAM) was successfully applied to the zirconium material system to create a planar geometry. Following fabrication, SS-J3 type tensile specimens of the UAM and wrought Zircaloy-4 with a nominal gage section of 5×1.2×0.75 mm were machined for hydriding studies and mechanical testing. The SS-J3 type tensile specimens were gas-charged with hydrogen using a custom system that precisely controls hydrogen gas flow rate, hydrogen partial pressure, and temperature. To avoid altering the UAM material, the maximum process temperature was limited to 550°C. Using different initial hydrogen gas pressures and flow rates, various hydrogen contents (70–1755 wppm) were achieved for Zircaloy-4 specimens. Tensile testing shows that, regardless of hydrogen content, all UAM specimens measured yield strengths in the range of 557±16 MPa and ultimate tensile strengths of 660±4MPa. However, total elongation clearly decreased as a function of increasing hydrogen content. Further, at the lowest hydrogen content, the total plastic elongation measured 21.5%, and this value decreased to less than 2% when the hydrogen content was increased to 1000 wppm. Cross-sectional optical microscopy images revealed that the hydride distributions are randomly oriented. For the low hydrogen content specimen, these randomly distributed hydrides are isolated from each other. A sandwiched structure, consisting of high-density and low-density layers, was also observed for the specimens with hydrogen content between 200 and 400 wppm. As the hydrogen content increases, the hydrides diffuse into the low-density hydride layers to form a network across the whole specimen. Although the tensile properties of UAM and wrought Zircaloy-4 exhibit the same behavior with increasing hydrogen content, the distinctions in grain orientations led to differences in the hydride orientations at low and intermediate hydrogen concentrations.

36 MATERIALS SCIENCE↗

On onsagers principle, dislocation motion and hydrogen embrittlement

Onsager's reciprocal relationships from the linear theory of irreversible thermodynamics are applied to hydrogen - dislocation interactions. Existing experimental evidence shows that dislocation motion causes localized hydrogen accumulation; thus, from the Onsager principle, localized hydrogen accumulations will affect dislocation motion and therefore the properties of metals and alloys exposed to hydrogen environments.

Louthan, M. R., Jr.↗

A study of the mechanisms of hydrogen embrittlement in molybdenum

The mechanical properties of polycrystalline molybdenum samples in both the 'as annealed' and hydrogenized conditions were studied. The results indicate that hydrogen does not alter the yield stress of samples significantly although it reduces both the ultimate tensile strength and the ductility considerably. Fractographic study of samples shows a tendency to intercrystalline cracking of the hydrogenised molybdenum at low temperatures. In the light of the results, a mechanism involving grain boundary weakening is suggested.

Taheri, M.↗

Stainless steel 301 and Inconel 718 hydrogen embrittlement

Conditions and results of tensile tests of 26 Inconel 718 and four cryoformed stainless steel specimens are presented. Conclusions determine maximum safe hydrogen operating pressure for cryogenic pressure vessels and provide definitive information concerning flaw growth characteristics under the most severe temperature and pressure conditions

Allgeier, R. K.↗

Characterization of hydrogen embrittlement in nickel base superalloy single crystals

In order to study the role of CMSX2 single crystal microstructure on the combined stress-hydrogen environment effects, hydrogen was introduced by cathodic charging. Concentration measurements were carried out to investigate the dependence of hydrogen solubility and trapping on microstructure. Mechanical properties were measured at room temperature on smooth tensile specimens as a function of heat treatment, crystal orientation and H charging conditions. SEM and TEM allow to study H induced cracks initiation and propagation. A large amount of hydrogen can be dissolved and trapped in CMSX2 single crystals when exposed to a high hydrogen fugacity environment. The strong H trapping evidenced in voids explains the predominant role of these defects as crack initiation sites. The strong detrimental effect of hydrogen on the material tenacity is discussed.

Chene, J.↗

The effects of hydrogen embrittlement of titanium

Titanium alloys, by virtue of their attractive strength to density ratio, fatigue, fracture toughness and corrosion resistance are now commonly used in various aerospace and marine applications. The cost, once very expensive, has been reduced, making titanium even more of a competitive material today. Titanium and titanium alloys have a great affinity to several elements. Hydrogen, even in small amounts, can cause embrittlement, which in turn causes a reduction in strength and ductility. The reduction of strength and ductility is the subject of this investigation.

Taylor, Delbert J.↗

Stress corrosion and hydrogen embrittlement

Service experience applications, experimental data generation, and the development of satisfactory quantitative theories relevant to the suppression and control of stress corrosion cracking in titanium are discussed. The impact of stress corrosion cracking (SCC) on the use of titanium alloys is considered, with emphasis on utilization in the aerospace field. Recent data on hot salt SCC, crack growth in hydrogen gas, and crack growth in liquid environments containing halide ions are reviewed. The status of the understanding of crack growth processes in these environments is also examined.

Blackburn, M. J.↗

Fatigue failure of hydrogen embrittled high strength steels

Results of an experimental investigation are presented concerning the fracture behavior of cathodically charged, quenched and tempered martensitic steels under cyclic load conditions. Introduction of H2 by cathodic charging reduced fatigue life by as much as 60%. It is proposed that subsurface transverse fatigue cracks nucleate simultaneously at multiple sites, such as at microcracks, voids, or inclusions. Fatigue crack growth then occurs on planes perpendicular to the major applied stress axis in the presence of the critical combination of applied external stress and hydrogen.

Kim, Y. G.↗

Neutron radiographic testing for hydrogen embrittlement

Neutron radiography (N-ray) inspection is similar to X-ray inspection in that both depend on variations in attenuation to achieve object contrast. However, effectiveness of methods differs significantly when certain combinations of elements are examined. Mass attenuation coefficient for N-rays is function of both scattering and capture possibilities for each element; thus, density of thickness of material is less important in determining its transparency to neutrons.

Dunstan, J.↗