DOE OSTI2023

Intermetallics Based on Sodium Chalcogenides Promote Stable Electrodeposition–Electrodissolution of Sodium Metal Anodes

Sodiophilic micro-composite films of sodium-chalcogenide intermetallics (Na 2 Te and Na 2 S) and Cu particles are fabricated onto commercial copper foam current collectors (Na 2 Te@CF and Na 2 S@CF). For the first time a controllable capacity thermal infusion process is demonstrated. Enhanced wetting by the metal electrodeposition leads to state-of-the-art electrochemical performance. For example, Na 2 Te@CF-based half-cells demonstrate stable cycling at 6 mA cm -2 and 6 mAh cm -2 , corresponding to 54 µm of Na electrodeposited/electrodissolved by geometric area. Sodium metal batteries with Na 3 V 2 (PO 4 ) 3 cathodes are stable at 30C (7 mA cm -2 ) and for 10 000 cycles at 5C and 10C. Cross-sectional cryogenic focused ion beam (cryo-FIB) microscopy details deposited and remnant dissolved microstructures. Sodium metal electrodeposition onto Na 2 Te@CF is dense, smooth, and free of dendrites or pores. On unmodified copper foam, sodium grows in a filament-like manner, not requiring cycling to achieve this geometry. Substrate–metal interaction critically affects the metal–electrolyte interface, namely the thickness and morphology of the solid electrolyte interphase. Density functional theory and mesoscale simulations provide insight into support-adatom energetics, nucleation response, and early-stage morphological evolution. On Na 2 Te sodium atomic dispersion is thermodynamically more stable than isolated clusters, leading to conformal adatom coverage of the surface.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Tin asymmetric membranes for high capacity sodium ion battery anodes

Sodium-ion batteries have attracted tremendous research attention as promising candidates for next generation energy storage systems due to low-cost and high abundancy. Furthermore, comparing to current Li-ion battery technology, limitations on the anode side seriously hinder the cell performance since sodium does not easily intercalate into graphite materials. Here, tin nanoparticles embedded in various asymmetric membrane structures were developed to leverage the high capacity of tin (847 mA h g -1 based on Na 15 Sn 4 ) and accommodate the significant volume expansion for long cycle life. It was demonstrated 762 mA h g -1 reversible capacity at 50 mA g -1 and stable cycling performance over 100 cycles with 92.1% capacity retention at 100 mA g -1 can be achieved for the tin asymmetric membrane electrode synthesized using polysulfone and tin tert-butoxide precursor.

25 ENERGY STORAGE↗
DOE OSTI2019

Dendrite–Free Potassium Metal Anodes in a Carbonate Electrolyte

Potassium (K) metal anodes suffer from a challenging problem of dendrite growth. In this study, it is demonstrated that a tailored current collector will stabilize the metal plating–stripping behavior even with a conventional KPF 6 –carbonate electrolyte. A 3D copper current collector is functionalized with partially reduced graphene oxide to create a potassiophilic surface, the electrode being denoted as rGO@3D–Cu. Potassiophilic versus potassiophobic experiments demonstrate that molten K fully wets rGO@3D–Cu after 6 s, but does not wet unfunctionalized 3D–Cu. Electrochemically, a unique synergy is achieved that is driven by interfacial tension and geometry: the adherent rGO underlayer promotes 2D layer–by–layer (Frank–van der Merwe) metal film growth at early stages of plating, while the tortuous 3D–Cu electrode reduces the current density and geometrically frustrates dendrites. The rGO@3D–Cu symmetric cells and half–cells achieve state–of–the–art plating and stripping performance. Here, the symmetric rGO@3D–Cu cells exhibit stable cycling at 0.1–2 mA cm –2 , while baseline Cu prematurely fails when the current reaches 0.5 mA cm –2 . The half–cells cells of rGO@3D–Cu (no K reservoir) are stable at 0.5 mA cm –2 for 10 000 min (100 cycles), and at 1 mA cm –2 for 5000 min. The baseline 3D–Cu, planar rGO@Cu, and planar Cu foil fails after 5110, 3012, and 1410 min, respectively.

25 ENERGY STORAGE↗
DOE OSTI2020

Multi-scale stabilization of high-voltage LiCoO 2 enabled by nanoscale solid electrolyte coating

LiCoO 2 (LCO) possess a high theoretical specific capacity of 274 mAh g -1 , and currently LCO charged to 4.48 V with a capacity of ~190–195 mAh g -1 is penetrating the commercial markets. Scalable strategies to further enhance the performance of LCO are highly attractive. Here, we develop a scalable ball-milling and sintering method to tackle this long-standing challenge by modifying LCO surface with only 1.5–3.5% ceramic solid electrolyte nanoparticles, specifically Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 (LAGP) as an example. Consequently, the atomic-to-meso multiscale structural stabilities have been significantly improved, even with a high cut-off voltage of 4.5 V vs. Li/Li + , leading to excellent electrochemical stabilities. The nano-LAGP modified Li|LCO cell exhibits high discharge capacity of 196 mAh g -1 at 0.1 C, capacity retention of 88% over 400 cycles, and remarkably enhanced rate capability (163 mAh g -1 at 6 C). These results show significant improvement compared to the Li|LCO cells. The as-prepared graphite|LAGP-LCO full cells also show steady cycling with 80.4% capacity retention after 200 cycles with a voltage cut-off of 4.45 V. This work provides a simple and scalable approach to achieve stable cycling of LCO at high voltage with high energy density.

25 ENERGY STORAGE↗
DOE OSTI2024

Healable and conductive sulfur iodide for solid-state Li–S batteries

Solid-state Li-S batteries (SSLSBs) are made of low-cost and abundant materials free of supply chain concerns. Owing to their high theoretical energy densities, they are highly desirable for electric vehicles. However, the development of SSLSBs has been historically plagued by the insulating nature of sulfur and the poor interfacial contacts induced by its large volume change during cycling, impeding charge transfer among different solid components. We report an S 9.3 I molecular crystal with I 2 inserted in the crystalline sulfur structure, which shows a semiconductor-level electrical conductivity (approximately 5.9 × 10 -7 S cm -1 ) at 25 °C; an 11-order-of-magnitude increase over sulfur itself. Iodine introduces new states into the band gap of sulfur and promotes the formation of reactive polysulfides during electrochemical cycling. Further, the material features a low melting point of around 65 °C, which enables repairing of damaged interfaces due to cycling by periodical remelting of the cathode material. As a result, an Li-S 9.3 I battery demonstrates 400 stable cycles with a specific capacity retention of 87%. The design of this conductive, low-melting-point sulfur iodide material represents a substantial advancement in the chemistry of sulfur materials, and opens the door to the practical realization of SSLSBs.

25 ENERGY STORAGE↗
DOE OSTI2020

Fluorinated co-solvent promises Li-S batteries under lean-electrolyte conditions

Practical lithium-sulfur batteries stipulate the use of a lean-electrolyte and a high Coulombic efficiency of the lithium metal anode. In this work, we employ 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether as a co-solvent in the electrolyte of Li-S batteries to meet the demands. The co-solvent fosters the formation of a LiF-rich solid electrolyte interphase on lithium metal anode, as revealed by Ab initio molecular dynamics and Femtosecond Stimulated Raman spectroscopy. The co-solvent results in an average Coulombic efficiency of 99.4% for lithium plating/stripping cycles. Full cells with a capacity ratio of 2 between lithium anode and the S@PAN cathode (3 gs cm –2 ) exhibited a stable cycle life over 100 cycles at an electrolyte/sulfur ratio of 2 µL mg –1 , validating the high Coulombic efficiency of the lithium anode and demonstrating the compatibility of the electrolyte with both electrodes. To enhance the energy density, we prepared a hybrid cathode composed of 45 wt.% VS 2 mixed with ZnS-coated Li 2 S@graphene as the cathode. Based on the mass of both electrodes and the electrolyte, the full cell delivers an energy density of 483 Wh kg –1 , which demonstrates viable Li-S batteries with the lean-electrolyte.

25 ENERGY STORAGE↗
DOE OSTI2026

Interfacial and Kinetic Origins of Voltage Loss in Neutral Zinc‐Air Batteries

Rechargeable zinc-air batteries are promising candidates for grid-scale energy storage; however, their practical deployment is limited by oxygen electrocatalysis inefficiencies and interfacial instabilities, particularly outside conventional alkaline electrolytes. Here, in this work, zinc-air batteries operating under neutral electrolyte conditions using ZnCl 2 soaked KC-PAA-PAM gel polymer electrolytes and electrochemically synthesized Ni/Fe layered double hydroxide electrocatalysts is investigated. Ni/Fe-LDH is intentionally employed as an OER-biased benchmark catalyst to diagnose electrolyte and interface driven limitations rather than as a bifunctional ORR/OER solution. Full cells exhibit highly stable cycling over hundreds of hours, yet operate at substantially suppressed charge and discharge voltages relative to the thermodynamic value. Electrochemical impedance analysis shows that ohmic losses contribute only minimally to this voltage suppression. Post-mortem X-ray photoelectron spectroscopy reveals metallic zinc accumulation on the air cathode and chloride-containing species on the anode, indicating parasitic interfacial processes. Synchrotron-based soft X-ray absorption spectroscopy confirms stable Ni 2+ and Fe 3+ oxidation states during cycling, consistent with OER-biased catalytic behavior, while neutral-electrolyte oxygen evolution measurements demonstrate strong electrolyte-induced suppression of oxygen kinetics. Together, these results show that electrolyte chemistry and cathode-side parasitic processes, rather than catalyst identity alone, dominate voltage losses in neutral zinc-air batteries, providing mechanistic insight into the fundamental challenges associated with neutral electrolyte operation.

Long duration energy storage↗
DOE OSTI2024

Interfacial solvation-structure regulation for stable Li metal anode by a desolvation coating technique

Rechargeable lithium (Li) metal batteries face challenges in achieving stable cycling due to the instability of the solid electrolyte interphase (SEI). The Li-ion solvation structure and its desolvation process are crucial for the formation of a stable SEI on Li metal anodes and improving Li plating/stripping kinetics. This research introduces an interfacial desolvation coating technique to actively modulate the Li-ion solvation structure at the Li metal interface and regulate the participation of the electrolyte solvent in SEI formation. Through experimental investigations conducted using a carbonate electrolyte with limited compatibility to Li metal, the optimized desolvation coating layer, composed of 12-crown-4 ether-modified silica materials, selectively displaces strongly coordinating solvents while simultaneously enriching weakly coordinating fluorinated solvents at the Li metal/electrolyte interface. This selective desolvation and enrichment effect reduce solvent participation to SEI and thus facilitate the formation of a LiF-dominant SEI with greatly reduced organic species on the Li metal surface, as conclusively verified through various characterization techniques including XPS, quantitative NMR, operando NMR, cryo-TEM, EELS, and EDS. The interfacial desolvation coating technique enables excellent rate cycling stability (i.e., 1C) of the Li metal anode and prolonged cycling life of the Li||LiCoO 2 pouch cell in the conventional carbonate electrolyte (E/C 2.6 g/Ah), with 80% capacity retention after 333 cycles.

42 ENGINEERING↗
DOE OSTI2023

Interplay of molten salt and dopants in tuning the performance of single-crystalline LiNiO 2

Single-crystalline layered oxide cathodes have seen great research interest in recent years. Adoption of single-crystal morphology improves mechanical robustness and eliminates intergranular boundaries, improving the chemical stability of the cathode. Furthermore, single-crystal cathodes also suffer from worsened lithium-diffusion kinetics stemming from the significantly increased diffusion path lengths. Sluggish lithiation kinetics induce concentration gradients within the cathode particle during cell operation, resulting in the accumulation of lattice strain, which deteriorates cell performance. Foreign dopants have been shown to greatly improve ion diffusion in many high-Ni layered oxide cathode systems. In particular, we identify Ti and Te as promising dopants to ameliorate the slow diffusion kinetics. We find that doping 1 mol.% Te into single crystal LiNiO 2 greatly improves Li + diffusivity, as determined through galvanostatic intermittent titration technique. Further incorporating 2 mol.% Al and pairing with lithium-metal anode in a localized high concentration electrolyte (LHCE) delivers 206 mA h g -1 at C/3 rate and retains 94% capacity after 100 cycles in Li metal half cells. By addressing kinetically mediated degradation with Te doping, and surface-based degradation with Al and LHCE, the cathode experiences very little polarization and overpotential growth, enabling stable cycling with high accessible capacity.

25 ENERGY STORAGE↗
DOE OSTI2023

Interfacial pressure improves calendar aging of lithium metal anodes

Lithium (Li) metal is a promising anode because its theoretical specific capacity is approximately ten times larger than graphite. However, Li anodes suffer from long-term capacity fade due to Li stranding (becoming electronically disconnected) and electrolyte decomposition. Applied interfacial pressure has been shown to improve Li anode cycling, likely due to reincorporating stranded or “dead” Li into the anode. Calendar aging can also lead to Li capacity loss due to electrolyte decomposition/Li corrosion and the formation of stranded Li. Some research suggests that calendar aging during cycling results in reversible capacity losses due to Li stranding and reconnection. We here investigate the effect of applied interfacial pressure on Li anode calendar aging during cycling with incorporated rest steps in a localized high-concentration electrolyte (LHCE) to understand if pressure can mitigate stranded Li formation during rest by manipulating the Li morphology. Pouch cells exhibit more stable cycling and denser Li deposits between 10 kPa and 1,000 kPa of applied pressure compared to no applied pressure. Despite drops in CE during periodic rest cycles, the average cumulative lost capacity and average coulombic efficiency (CE) of cells over 50 cycles show that cells aged with incorporated rest steps perform similarly to cells cycled without added rests. This similar average CE suggests that dead Li is largely responsible for drops in CE during rest rather than irreversible Li corrosion and that the dead Li can be reconnected in subsequent cycling. The addition of a lithiophilic ZnO coating to the Cu working electrode increases the adhesion and coverage of Li deposits at low pressures and improves CE during the first cycle.

25 ENERGY STORAGE↗
DOE OSTI2025

Shape‐Stabilization of Phase Change Materials with Carbon‐Conscious Poly(hydroxy)Urethane Foams

Thermal energy regulation is a significant challenge, contributing to over 30% of annual greenhouse gas emission (GHG) emissions. Phase change materials (PCMs) offer a promising solution by storing thermal energy, which can enable the reuse of waste heat for heating and cooling; however, developing materials for shape-stabilized PCMs remains crucial. This work investigates a self-foaming poly(hydroxy)urethane (PHU), derived from a non-isocyanate polyurethane (NIPU), as a porous support for shape-stabilizing paraffinic and salt hydrate PCMs. PHU-encapsulated paraffinic PCMs exhibited excellent thermal stability over repeated cycles. Thermal stability with salt hydrate PCMs, specifically calcium chloride hexahydrate (CaCl 2 •6H 2 O), is achieved by the incorporation of 5 wt.% barium carbonate (BaCO 3 ) into the PHU foam. This enabled stable cycling for over 48 cycles with desirable thermal properties, i.e., a melting point ≈30 °C, high enthalpy (ca. 138 J g −1 per cycle), and a consistent freezing point ≈20 °C, making it suitable for applications in buildings and electric vehicle battery insulation. Also, incorporating graphite (1.5–10 wt.%) into the foam enhanced the thermal conductivity of shape-stabilized CaCl 2 •6H 2 O during heating and cooling cycles. Overall, the approach detailed here offers a carbon-conscious and chemically tunable material for thermal energy storage.

25 ENERGY STORAGE↗
DOE OSTI2022

Investigation of the Electrode-Electrolyte Interphase in Ester-Based Electrolytes in NCM523/Graphite Cells

The use of methyl acetate (MA) and methyl propionate (MP) as co-solvents in carbonate/LiPF 6 electrolytes have been investigated in LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523)/graphite cells to improve electrochemical performance at low temperature (−20 °C). Consistent with previous investigations, improved low temperature performance was observed with all electrolyte formulations containing esters. Detailed ex situ surface analysis of the surface films generated with the ester-based electrolytes containing electrolyte additives reveal significant changes to the SEI on graphite upon cycling at moderately elevated temperature (45 °C). In the presence of vinylene carbonate (VC) lithium plating is observed upon cycling at low temperature (−20 °C) which leads to a thicker solid electrolyte interface (SEI) upon cycling at 45 °C. Incorporation of fluoroethylene carbonate (FEC) as an electrolyte additive results in the generation of a thin SEI and alters the structure of the surface film on the NCM523 cathode resulting in stable cycling over a wide temperature range.

Rodrigo, Nuwanthi D. (ORCID:0000000343129536)↗
DOE OSTI2026

Prelithiated SiO x /Graphite-NMC811 Cells: Capacity Loss, Impedance Rise and Hidden Degradation Pathways Revealed Using Three-Electrode Diagnostics

Electrodes containing SiO x /graphite (Gr) materials are attractive as anodes for high-energy lithium-ion batteries. However, their mechanical deformation, electrochemical response, and impedance evolution during long-term cycling are strongly coupled, complicating accurate diagnosis of performance fade mechanisms. In this work, the behavior of electrochemically prelithiated SiO x /Gr anodes paired with NMC811 cathodes is systematically investigated using techniques that include in-situ dilatometry, three-electrode electrochemistry, and multiscale post-cycling microscopy. The SiO x /Gr electrode exhibits a maximum expansion of 49% upon lithiation to 10 mV vs Li + /Li, with 84% of the expansion and 91% of the capacity being reversible. In full cells, relatively stable cycling with only 12% capacity fade over 500 cycles is observed. Three-electrode experiments reveal cell-level impedance growth, which is dominated by the NMC811 cathode: the SiO x /Gr anode exhibits minimal net impedance rise and an initial impedance decrease at low potentials. Despite this apparent electrochemical stability, cross-sectional SEM, PFIB tomography, and cryo-STEM reveal irreversible anode thickening caused by the accumulation of an inorganic-rich solid electrolyte interphase (SEI) permeating the anode bulk. Electrode potential-shift analysis further demonstrates that Li + ions released from lithium reservoirs in the prelithiated anode mask true lithium inventory loss during aging. These results demonstrate that low-expansion SiO x /Gr anodes can simultaneously exhibit favorable cycling and impedance metrics while undergoing substantial, hidden degradation, underscoring the importance of electrode-resolved diagnostics for evaluating prelithiated silicon-based anodes.

25 ENERGY STORAGE↗
DOE OSTI2022

Amorphization of Pseudocapacitive T−Nb 2 O 5 Accelerates Lithium Diffusivity as Revealed Using Tunable Isomorphic Architectures

Abstract Intercalation pseudocapacitance can combine capacitor‐like power densities with battery‐like energy densities. Such surface‐limited behavior requires rapid diffusion where amorphization can increase solid‐state diffusivity. Here intercalation pseudocapacitive materials with tailored extents of amorphization in T‐Nb 2 O 5 are first reported. Amorphization was characterized with WAXS, XPS, XAFS, and EPR which suggested a peroxide‐rich (O 2 2− ) surface that was consistent with DFT predictions. A series of tunable isomorphic architectures enabled comparisons while independently varying transport parameters. Through process of elimination, solid‐state lithium diffusion was identified as the dominant diffusive‐constraint dictating the maximum voltage sweep rate for surface‐limited kinetics ( v SLT ), termed the Surface‐Limited Threshold (SLT). The v SLT increased with amorphization however stable cycling required crystalline T‐Nb 2 O 5 . A current‐response model using series‐impedances well‐matched these observations. This perspective revealed that amorphization of T‐Nb 2 O 5 enhanced solid‐state diffusion by 12.2 % and increased surface‐limitations by 17.0 % (stable samples). This approach enabled retaining 95 % lithiation capacity at ∼800 mV s −1 (1,600 C‐rate equivalent).

25 ENERGY STORAGE↗
DOE OSTI2024

Dynamical Janus Interface Design for Reversible and Fast-Charging Zinc–Iodine Battery under Extreme Operating Conditions

Aqueous zinc (Zn) iodine (I 2 ) batteries have emerged as viable alternatives to conventional metal-ion batteries. However, undesirable Zn deposition and irreversible iodine conversion during cycling have impeded their progress. Here, to overcome these concerns, we report a dynamical interface design by cation chemistry that improves the reversibility of Zn deposition and four-electron iodine conversion. Due to this design, we demonstrate an excellent Zn-plating/-stripping behavior in Zn||Cu asymmetric cells over 1000 cycles with an average Coulombic efficiency (CE) of 99.95%. Moreover, the Zn||I 2 full cells achieve a high-rate capability (217.1 mA h g –1 at 40 A g –1 ; C rate of 189.5C) at room temperature and enable stable cycling with a CE of more than 99% at -50 °C at a current density of 0.05 A g –1 . In situ spectroscopic investigations and simulations reveal that introducing tetraethylammonium cations as ion sieves can dynamically modulate the electrode–electrolyte interface environment, forming the unique water-deficient and chloride ion (Cl – )-rich interface. Such Janus interface accounts for the suppression of side reactions, the prevention of ICl decomposition, and the enrichment of reactants, enhancing the reversibility of Zn-stripping/-plating and four-electron iodine chemistry. This fundamental understanding of the intrinsic interplay between the electrode–electrolyte interface and cations offers a rational standpoint for tuning the reversibility of iodine conversion.

25 ENERGY STORAGE↗
DOE OSTI2022

Electrochemical Stability and Reversibility of Aqueous Polysulfide Electrodes Cycled Beyond the Solubility Limit

Batteries which use dissolved redox-active species, such as redox flow batteries (RFBs), are often considered to be constrained in their operation and energy density by the solubility limit of the redox species. Here, we show that soluble redox active electrolytes can be reversibly cycled deeply into the precipitation regime, permitting higher effective concentrations, energy densities, and lower costs. Using aqueous sodium polysulfide negative electrolytes cycled in the nominal Na 2 S 2 to Na 2 S 4 capacity range as an example, we show that the effective solubility can be increased from 5 M in the fully-dissolved state to as much as 10 M using the precipitation strategy. Stable cycling was observed at 8 M concentration over more than 1600h at room temperature. We also analyze the range of polysulfide electrochemical stability, and characterize the precipitate composition. This enhanced effective concentration approach may be generalized to other redox chemistries that utilize solubilized reactants, and may be especially useful for long-duration storage applications where slow charge-discharge rates allow equilibration of precipitated species with the redox-active solution.

25 ENERGY STORAGE↗
DOE OSTI2025

Molecular engineering of ethereal electrolyte for ultrastable Si-based high voltage full cells

The successful application of Si-based high-energy Li-ion batteries (LIBs) depends on our ability to tailor electrolyte properties to achieve long-term stability and reliable performance. In this work, we demonstrate our rationale for the molecular design of ethereal solvents to address low anodic stability issues and produce a highly electrochemically stable electrolyte for Si‖LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811) high-energy full cells. Unlike the trimethylsilyl group, the trifluoromethyl (–CF 3 ) group exerts a very strong electron-withdrawing effect on the glycol ether backbone, reducing the highest occupied molecular orbital (HOMO) energy level of the fluorinated glycol ether (FGE) and significantly enhancing its oxidation potential. The FGE-based electrolyte enables stable cycling of Si‖NMC811 full cells, delivering high specific capacity (900 mA h g −1 ) and coulombic efficiency (>99.78%) over extended (500) cycles. The improved electrochemical performance originates from the terminal fluorination of the diglyme backbone, which strengthens anion coordination in the solvation structure, leading to the preferential reduction of the FSI anion and the formation of robust solid electrolyte interphases (SEIs) on the Si surface. Through molecular engineering of ethereal solvents, we have discovered a promising candidate for a next-generation stable electrolyte, paving the way for the design of practical and commercially viable Si batteries.

Silicon anode↗
DOE OSTI2024

Rechargeable Manganese Dioxide||Hard Carbon Lithium Batteries in an Ether Electrolyte

Earth-abundant, cost-effective electrode materials are essential for sustainable rechargeable batteries and global decarbonization. Manganese dioxide (MnO 2 ) and hard carbon both exhibit high structural and chemical tunability, making them excellent electrode candidates for batteries. Herein, we elucidate the impact of electrolytes on the cycling performance of commercial electrolytic manganese dioxide in Li chemistry. We leverage synchrotron X-ray analysis to discern the chemical state and local structural characteristics of Mn during cycling, as well as to quantify the Mn deposition on the counter electrode. By using an ether-based electrolyte instead of conventional carbonate electrolytes, we circumvent the formation of a surface Mn(II)-layer and Mn dissolution from Li x MnO 2 . Consequently, we achieved an impressive ~100% capacity retention for MnO 2 after 300 cycles at C/3. To create a lithium metal-lean full cell, we introduce hard carbon as the anode which is compatible with ether-based electrolytes. Commercial hard carbon delivers a specific capacity of ~230 mAh g -1 at 0.1 A g -1 without plateau, indicating a surface-adsorption mechanism. The resulting manganese dioxide||hard carbon full cell exhibits stable cycling and high Coulombic efficiency. Our research provides a promising solution to develop cost-effective, scalable, and safe energy storage solutions using widely available manganese oxide and hard carbon materials.

25 ENERGY STORAGE↗