DOE OSTI2019

Microstructure, Texture, and Mechanical Properties of AM60 Magnesium Alloy Processed by Extrusion and Multidirectional Forging

In the present paper, multidirectional forging (MDF), as a severe plastic deformation process, was carried out on an extruded AM60 magnesium alloy. The microstructure, texture, and mechanical properties of the MDFed samples were examined. Microstructural findings indicated that the grain size of the alloy decreased from 10.2 to 3.7 µm after six MDF passes, carried out at a constant temperature of 220 °C. Textural studies revealed that after six MDF passes, the fiber texture of the extruded material was transformed to another texture, in which the basal planes tend to rotate toward 45{sup o} to the transverse direction. Shear punch testing (SPT) was employed to assess the shear yield stress (SYS) and ultimate shear strength (USS) at room temperature. Both SYS and USS were enhanced after two MDF passes, but decreased in the next pressing stages, despite developing finer grains at higher levels of imposed strain. The observed drop in strength is ascribed to texture softening that counterbalances the grain refinement strengthening effects. The variation in average microhardness values after different passes of MDF showed the trend that was in concurrence with the rise and fall of the SPT results. Finally, the changes in mechanical properties were discussed, based on the microstructural and textural findings.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Microstructure Evolution and Mechanical Properties of the AZ91 Magnesium Alloy with Sr and Ti Additions in the As-Cast and As-Aged Conditions

Effect of different amounts of Sr and Ti additions with T6 heat treatment on microstructure and mechanical properties of the AZ91 alloy was investigated. The microstructure of the AZ91 alloy is consisted of the α-Mg phase surrounded by the semicontinuous network of β-Mg{sub 17}Al{sub 12} intermetallics. The average grain size and volume fraction of β phase decreased up to 1 wt.% Sr and 0.1 wt.% Ti additions. Exceeding Ti additions led to increase in both grain size and volume fraction. It was found that the grain refinement mechanism of AZ91 alloys with Sr additions was grain restriction factor. Also, 0.1 wt.% Ti addition could refine the grain structure of the AZ91 alloy by the formation of Al{sub 3}Ti particles that act as nucleation sites for the α-Mg phase. Furthermore, adding 1 wt.% Sr and 0.1 wt.% Ti enhanced the hardness values for both cast and aged AZ91 alloy. Moreover, ultimate tensile strength and tensile elongation values reached their maximum amounts with the 0.5 wt.% Sr and 0.1 wt.% Ti additions and more Sr and Ti additions deteriorated the mechanical properties of cast and aged AZ91 alloys. The fracture surface characterizations had good relations with the tensile properties. The fracture modes were cleavage and quasi-cleavage in the cast and aged AZ91 alloys. Furthermore, the optimum levels of Sr and Ti additions altered the fracture modes to more quasi-cleavage fractures.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure, texture and mechanical properties of AA 1060 aluminum alloy processed by cryogenic accumulative roll bonding

Highlights: • The Al sheets were accumulative roll bonded to five cycles at cryogenic temperature. • The microstructure, texture and mechanical properties of ARB sheets were investigated. • The texture evolution at surface layer was quantified by mathematical formulae. • The strength of the β fiber at center layer was affected by the initial texture and the strain. - Abstract: AA 1060 aluminum alloy sheet was processed to five accumulative roll bonding (ARB) cycles at cryogenic temperature. The microstructure, texture and mechanical properties of the ARB processed sheets were investigated. The results show that the surface layer of the ARB processed sheets exhibits a significant r-cube shear texture. Initial cube orientation at the surface layer was gradually rotated to the r-cube orientation during the ARB process, leading to the increase in the strength of the r-cube shear texture with ARB cycles. The texture evolution at the surface layer was quantified in terms of a simple relation between the texture volume fractions and accumulated true strain. The strength of the β fiber rolling texture and the distribution of orientation intensities along the β fiber at the center layer were strongly affected by the initial texture. As the ARB cycles increased, the initial texture was changed from the cube texture to the r-cube texture, leading to a continuous increase in the strength of the β fiber rolling texture dominated by the C orientation. The yield and ultimate tensile strength of the ARB processed sheets increased markedly after the first ARB cycle and then increased slowly with increasing ARB cycles, while the elongation decreased accordingly.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructural evolution and mechanical properties of maraging steel produced by wire + arc additive manufacture process

Highlights: • Wire + arc additive manufacture (WAAM) was applied to produce maraging steel structures. • Microstructure evolution of WAAM alloy was characterized and correlated with the layer-by-layer building manner. • Mechanical properties of WAAM alloy were tested and correlated with the aging response of WAAM microstructure. • Retained austenite content was measured and correlated with the tensile strength loss. - Abstract: Wire + arc additive manufacture is developed for producing large-scale metallic components. In this paper, maraging steel parts were produced, and the microstructure and mechanical properties were investigated. The microhardness and tensile strength of the as deposited alloy reduced from the bottom to the top due to the transient thermal cycling, which resulted in partial aging and non-uniform formation of intermetallic compounds along the building direction. Solutionizing, followed by 3 h aging, significantly reduced the microstructural heterogeneity and increased the mechanical properties by 24.7% through the formation of large amounts of finely distributed precipitates. The as deposited alloy possessed superior strength to the wrought alloy in solutionized condition but inferior to the later in aged condition, which was attributed to the less pronounced aging response of the low-angle columnar grains characterized microstructure and the presence of retained and reverted austenite.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Microstructural Characteristics and Mechanical Properties of Friction-Stir-Welded CuSn6 Tin Bronze

Tin bronze is widely applied in various industries for its excellent wear and corrosion resistance. Friction stir welding is a solid-state welding process, which generates less heat and avoids the melting-related defects. CuSn6 tin bronze plates of 4 mm in thickness were friction-stir-welded at welding speeds ranging from 50 to 150 mm/min under a constant rotation speed. The microstructural and mechanical properties of joints were investigated. The microstructure of the stir zone consists of refined equiaxed grains. The grain size decreased from top to bottom of the welds. The mean grain size is increased with increasing welding speed. The largest strength and elongation of welded joints were both obtained at the welding speed of 100 mm/min. During tensile test, all of the joints were fractured at the heat affected zone of retreating side with typical plastic fracture feature, since the grains were coarsened by welding heat.

36 MATERIALS SCIENCE↗
NASA NTRS2008

The Effects of Heat Treatment and Microstructure Variations on Disk Superalloy Properties at High Temperature

The effects of heat treatment and resulting microstructure variations on high temperature mechanical properties were assessed for a powder metallurgy disk superalloy LSHR. Blanks were consistently supersolvus solution heat treated and quenched at two cooling rates, than aged at varying temperatures and times. Tensile, creep, and dwell fatigue crack growth tests were then performed at 704 C. Gamma' precipitate microstructures were quantified. Relationships between heat treatment-microstructure, heat treatment-mechanical properties, and microstructure-mechanical properties were assessed.

Gabb, Timothy P.↗
DOE OSTI2018

Microstructure Evolution and Mechanical Properties of High-Speed Friction Stir Welded Aluminum Alloy Thin Plate Joints

Sound friction stir welded (FSW) joints of 6061-T6 aluminum alloy sheets with an 0.8 mm thickness were obtained at conventional speed (2000 rpm, 300 mm/min) and high speed (11,000 rpm, 1500 mm/min). The recrystallization mechanism, precipitate evolution, mechanical properties and fracture behavior were investigated in detail. Microstructure analyses revealed that the grain structure evolution in the nugget zone (NZ) was dominated by continuous dynamic recrystallization. In the process of FSW, high speed facilitates the formation of finer equiaxed recrystallized grains, higher density of dislocations and substructures, and a larger number of precipitates in the NZ compared to the conventional speed, which further significantly improves the hardness and tensile strength of the joints. The maximum tensile strength was obtained with 292.6 MPa, 83.2% for the 6061-T6 aluminum alloy and 122.6% for the conventional-speed FSW joints. This work provides an effective method for preparing FSW aluminum alloy thin plate joints with excellent mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Microstructure and Mechanical Behavior of Friction Stir-Welded Sc-Modified Al-Zn-Mg Alloys Made Using Different Base Metal Tempers

The microstructure and property of friction stir weld joints of a Sc-modified Al-Zn-Mg alloy developed using base metal in hot-rolled (HR) and T6 temper were studied and compared in this work. The results showed that the microstructure and property exhibited significant difference between the two friction stir weld joints. The weld efficiency of the FSW joint developed using base metal in HR condition is over 90%, while that of the FSW joint developed using base metal in T6 condition is only 70%. The hardness of the weld nugget of HR joint is obviously higher than that of the weld nugget of T6 joint, due to the different changes in the original precipitates during the friction stir welding process. The strengthening mechanism in different zones of the two FSW joints was discussed to examine the microstructure–properties relationship, and the main difference of the strengthening mechanism between the two FSW joints was revealed.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Phase composition of polycrystalline HfNx (0.45 ≤ x ≤ 1.60) and effects of low-energy ion irradiation on microstructure, texture, and physical properties

We have investigated the phase composition of HfNx as a function of x and the effects of low-energy ion irradiation on the microstructure and physical properties of polycrystalline layers grown on SiO2 at 350 °C by ultrahigh vacuum reactive dc magnetron sputtering of Hf in mixed N2/Ar discharges. X-ray diffraction and Rutherford backscattering spectrometry results show that the phases obtained in polycrystalline HfNx layers with increasing x are hcp-structure α-Hf:N (x ≲ 0.6); multiphase mixtures consisting of α-Hf, NaCl-structure δ-HfN, rhombohedral ɛ-Hf3N2, and/or ζ-Hf4N3 (0.6 ≲ x ≲ 0.9); δ-HfN single phase (0.9 ≲ x ≲ 1.3); and mixtures of δ-HfN and higher nitrides (x ≳ 1.3). HfNx layers with 0.9 ≲ x ≲ 1.2 grown under mild ion irradiation (incident ion energy Ei ≃ 7 eV and ion-to-Hf flux ratios Ji/JHf = 1−3) are underdense with mixed orientation, low in-plane stress, and rough surface morphology due to limited adatom mobilities resulting in kinetic roughening and atomic shadowing during film growth. However, the use of intense ion irradiation (Ei = 25 eV and Ji/JHf = 4−20) results in HfNx layers, which are fully dense with strongly 111-oriented texture, compressive in-plane stress, and smooth surfaces due to ion irradiation enhanced adatom surface mobilities. In addition, the latter films have lower resistivity and higher hardness. For stoichiometric δ-HfN layers, ρ decreases from 69.7 to 35.2 μΩ cm and H increases from 22.1 to 27.4 GPa, with increasing ion-irradiation intensity. However, for HfNx layers with 1.2 ≲ x ≲ 1.6, the correspondingly higher steady state atomic N surface coverages during deposition alter growth kinetics in favor of 001 texture with a fully dense structure and compressive in-plane stress.

Materials Science↗
DOE OSTI2019

The Effect of Casting Speed on Microstructure, Microsegregation, and Mechanical Properties of High-Strength Mg-Nd-Zn-Zr Alloy

High-quality Mg-Nd-Zn-Zr magnesium alloy billets were successfully prepared by direct chill casting. The effect of casting speed on microstructure, microsegregation, and mechanical properties of the Mg-Nd-Zn-Zr alloy was systematically investigated. The results show that the as-cast microstructure is composed of equiaxed α-Mg and Mg{sub 12}Nd. Optimum values of mechanical properties were obtained corresponding to the casting speed of 90 mm/min. An age hardening at 200 °C took a remarkable effect on the mechanical properties of billets. The maximum ultimate tensile strength ~ 323.4 MPa was obtained in the billet undergoing T6 heat treatment. The shapes of concentration curves of various alloying elements (e.g., Nd and Zn) in Mg-Nd-Zn-Zr, as predicted by the Gulliver–Scheil model, resemble reasonably with the shapes measured by electron probe microanalysis.

36 MATERIALS SCIENCE↗
NASA NTRS2009

Microhardness Testing of Aluminum Alloy Welds

A weld is made when two pieces of metal are united or fused together using heat or pressure, and sometimes both. There are several different types of welds, each having their own unique properties and microstructure. Strength is a property normally used in deciding which kind of weld is suitable for a certain metal or joint. Depending on the weld process used and the heat required for that process, the weld and the heat-affected zone undergo microstructural changes resulting in stronger or weaker areas. The heat-affected zone (HAZ) is the region that has experienced enough heat to cause solid-state microstructural changes, but not enough to melt the material. This area is located between the parent material and the weld, with the grain structure growing as it progresses respectively. The optimal weld would have a short HAZ and a small fluctuation in strength from parent metal to weld. To determine the strength of the weld and decide whether it is suitable for the specific joint certain properties are looked at, among these are ultimate tensile strength, 0.2% offset yield strength and hardness. Ultimate tensile strength gives the maximum load the metal can stand while the offset yield strength gives the amount of stress the metal can take before it is 0.2% longer than it was originally. Both of these are good tests, but they both require breaking or deforming the sample in some way. Hardness testing, however, provides an objective evaluation of weld strengths, and also the difference or variation in strength across the weld and HAZ which is difficult to do with tensile testing. Hardness is the resistance to permanent or plastic deformation and can be taken at any desired point on the specimen. With hardness testing, it is possible to test from parent metal to weld and see the difference in strength as you progress from parent material to weld. Hardness around grain boundaries and flaws in the material will show how these affect the strength of the metal while still retaining the sample. This makes hardness testing a good test for identifying grain size and microstructure.

Bohanon, Catherine↗
DOE OSTI2018

Superconducting Performance, Structure, Microstructure, and Trapped Field of Top-Seeded Melt-Processed Bulk Y{sub 3}Ba{sub 5}Cu{sub 8}O{sub x}

The sintering temperature for the production of Y{sub 3}Ba{sub 5}Cu{sub 8}O{sub 18} (Y-358) preform powders synthesized in sol-gel spontaneous combustion technique was optimized. A large single-grain bulk Y-358 crystal was fabricated employing a top-seeded melt-growth technique utilizing the optimally sintered preform powders (i.e., at 900 {sup ∘}C for 12 h). Structural, microstructural, elemental, and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscopy, and SQUID, respectively. The structural characterization indicated that the sample is highly textured in (00l) direction. The Y-358 phase fractions were estimated in both preform powders and bulk sample using Rietveld refinement. The onset of superconducting transition is observed at 92.5 K, and the curve is very sharp indicative of the high quality of the produced bulk sample. The field dependence of critical current density (J{sub c}) was determined at 77 K, and the self-field J{sub c} was found to be ∼26 kA/cm{sup 2}. A magnetic field of 0.27 T was trapped by the sample at 77 K.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2019

A New Alumina-Forming Ni-Co-Cr Base Alloy for Service in Gas Turbine Engine Combustors and Other High-Temperature Applications

HAYNES{sup ®} 233™ alloy based on the Ni-Co-Cr-Mo-Al system has been developed for service at high temperatures. The origins of 233 alloy can be traced to a couple of Haynes alloys: 230 alloy and 214 alloy. The former is a premier high-temperature alloy with superb creep strength and is widely accepted in the gas turbine industry. It is also chromia forming. The alumina-forming 214 alloy with its 4.5% Al content possesses outstanding oxidation resistance at high temperatures, but its creep strength above ~ 1800 °F (982 °C) is very poor. The new 233 alloy attempts to bridge this performance. This paper will present preliminary test results for 233 alloy from the products of the first production heats, including the tensile and creep properties of the alloy, microstructure, oxidation properties, as well as fabricability. These results will be compared and discussed with those of popular gas turbine alloys such as 230, 214, 617, and X alloys. The preliminary test results indicate that HAYNES 233 alloy has a unique combination of excellent oxidation resistance and creep-rupture strength while at the same time being readily fabricable. These properties make the alloy an attractive candidate for a wide variety of gas turbine and other high-temperature applications.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Structural, Thermal, and Mechanical Characterization of a Thermally Conductive Polymer Composite for Heat Exchanger Applications

Polymer composites are being considered for numerous thermal applications because of their inherent benefits, such as light weight, corrosion resistance, and reduced cost. In this work, the microstructural, thermal, and mechanical properties of a 3D printed polymer composite with high thermal conductivity are examined using multiple characterization techniques. Infrared spectroscopy and X-ray diffraction reveal that the composite contains a polyphenylene sulfide matrix with graphitic fillers, which is responsible for the high thermal conductivity. Furthermore, differential scanning calorimetry determines that the glass transition and melting point of the composite are 87.6 °C and 285.6 °C, respectively. Thermogravimetric analysis reveals that the composite is thermally stable up to ~400 °C. Creep tests are performed at different isotherms to evaluate the long-term performance of the composite. The creep result indicates that the composite can maintain mechanical integrity when used below its glass transition temperature. Nanoindentation tests reveal that modulus and hardness of the composite is not significantly influenced by heating or creep conditions. These findings indicate that the composite is potentially suitable for heat exchanger applications.

36 MATERIALS SCIENCE↗
NASA NTRS2009

Pin Tool Geometry Effects in Friction Stir Welding

In friction stir welding (FSW) there is significant evidence that material can take one of two different flow paths when being displaced from its original position in front of the pin tool to its final position in the wake of the weld. The geometry of the pin tool, along with the process parameters, plays an important role in dictating the path that the material takes. Each flow path will impart a different thermomechanical history on the material, consequently altering the material microstructure and subsequent weld properties. The intention of this research is to isolate the effect that different pin tool attributes have on the flow paths imparted on the FSWed material. Based on published weld tool geometries, a variety of weld tools were fabricated and used to join AA2219. Results from the tensile properties and microstructural characterization will be presented.

Querin, J. A.↗
DOE OSTI2026

Coupling Microstructural Evolution Simulations to Material Property Degradation Predictions for Plasma-Facing Materials

Reliable material performance is required for plasma-facing material (PFM) candidates. Previous research has shown that plasma and neutron radiation exposure induces microstructural changes in PFMs; changes in thermal and electrical conductivities and in material hardening and embrittlement were also observed after neutron irradiation. These material property changes will negatively impact the performance of the PFMs in a fusion reactor. Despite the well-known connection between material microstructure, properties, and performance, there is a need for validated modeling capabilities connecting PFM property degradation with microstructural evolution under fusion-relevant conditions. We are developing a simulation capability to couple plasma-induced microstructural evolution to material property degradation. Our approach relies on deliberate mapping between individual simulation models and experimental characterization for validation. The open-source Multiphysics Object-Oriented Simulation Environment (MOOSE) software was used for this simulation capability development. A MOOSE phase-field model was coupled with the cluster dynamics code, Xolotl, to predict microstructural evolution. Microstructure characterization techniques, including scanning electron microscopy (SEM), transmission electron microscopy (TEM), and laser scanning confocal microscopy (LSCM) are used to validate these microstructural evolution simulations. Calculation of thermal and electrical conductivities with first principles simulations was performed for bulk material and for grain boundaries; these results are used within MOOSE models to calculate effective thermal and electrical conductivities as a function of grain characteristics. Thermoreflectance and four-probe techniques were employed to measure the thermal and electrical conductivities, respectively. A MOOSE crystal plasticity model was adapted to predict microstructure-sensitive deformation behavior, and X-ray diffraction (XRD) was used to collect bulk dislocation density data for validation. After individual simulation validation, these models are coupled to predict material property changes resulting from plasma exposure. We focused here on an experimental design to emphasize the separate effects of moderate thermal loads and plasma exposure using tungsten. Annealing of tungsten was performed under a protective environment for temperatures ranging from 500 C to 1500 C. The plasma exposure was completed in the Tritium Plasma Experiment at Idaho National Laboratory under a deuterium flux of 1e22 D/m^2-s. This incremental approach is employed to build confidence in the modeling capability: separate-effects tests ensure that the models capture key mechanisms from single environmental conditions before predicting PFM property degradation under combined loads. We will show our early results from coupling these simulation models to predict PFM property changes from microstructural evolution. Comparisons of the simulation results with preliminary validation data will be discussed.

36 - MATERIALS SCIENCE↗
DOE OSTI2018

Characteristics of kinetic sprayed Ta in terms of the deposition behavior, microstructural evolution and mechanical properties: Effect of strain-rate-dependent response of Ta at high temperature

Highlights: • The effect of high-temperature rate-dependent response of BCC Ta on the deposition state of kinetic sprayed Ta particles with synergistic effect of powder oxidation • Abnormal increase of dislocation density above certain powder preheating temperature under the lower condition (N{sub 2} carrier gas), whereas considerable occurrence of grain refinement under the higher condition (He carrier gas). • Most significant dislocation density with the smallest volume-averaged domain size under the condition of 600 {sup o}C powder pre-heating with N{sub 2} carrier gas due to characteristic response of Ta. - Abstract: Numerous efforts have been focused on the fundamental research regarding kinetic spraying processes, but previous studies were biased to only few kinds of metallic materials. In particular, for Ta with body-centered cubic crystal structure, systematic studies are currently lacking in the literature. In this study, the characteristic deposition behaviors, microstructures, and mechanical properties of kinetic sprayed Ta under various impact conditions were systematically investigated. Generally, unusual features were usually related to strain-rate-dependent response (i.e. Peierls-Nabarro short range barriers) of Ta at high-temperature. This made thermal softening effect to be saturated above a certain degree of temperature, contributing to inferior deposition efficiency for the pre-heating at 600 °C than those of 400 and 500 °C by creating synergy with powder oxidation. In terms of microstructural evolutions, the dislocation density was abnormally increased at a certain powder preheating temperature (i.e., 600 °C), owing to the strain-rate-dependent response of Ta at high-temperature. On the other hand, grain refinement generated by rotational dynamic recrystallization was mainly observed under the higher kinetic energy condition (He carrier gas) at RT. Especially, the dislocation density and volume-average domain size evaluated via high-resolution X-ray diffraction peak profile analysis were corresponding to the results of the microstructural observations. Additionally, the nanomechanical properties (i.e., nanohardness and elastic modulus) evaluated via nanoindentation tests were in good agreement with the results from transmission electron microscopy investigations.

36 MATERIALS SCIENCE↗
NASA NTRS1987

Ultrasonic nondestructive evaluation, microstructure, and fracture toughness interrelations

Ultrasonic techniques for mechanical property characterizations are reviewed and conceptual models are advanced for explaining and interpreting the empirically based results. At present, the technology is generally empirically based and is emerging from the research laboratory. Advancement of the technology will require establishment of theoretical foundations for the experimentally observed interrelations among ultrasonic measurements, mechanical properties, and microstructure. Conceptual models are applied to ultrasonic assessment of fracture toughness to illustrate an approach for predicting correlations found among ultrasonic measurements, microstructure, and mechanical properties.

Vary, Alex↗