NASA NTRS2007

Post-Flight Analysis of Selected Fluorocarbon and Other Thin Film Polymer Specimens Flown on MISSE-5

Twenty thin film specimens were flown on M1SSE-5 as a cooperative effort between several organizations. This presentation will report results of initial inspections and post-flight measurements of the optical properties and recession of these materials due to the approx.13 month exposure period on the exterior of the International Space Station. These specimens were located on the "anti-solar" side of the MISSE-5 container and received a low number of Equivalent Sun Hours of solar UV exposure. Profilometry and/or ATF measurements will be conducted to determine thickness changes and atomic oxygen-induced recession rates Six of the specimens were covered with thin Kapton films, 0.1 and 0.3 mil in thickness. The 0.1 mil Kapton was almost completely eroded, suggesting that the atomic oxygen fluence is <8 x 10(exp 19) atoms/sq cm, similar to levels experienced during Space Shuttle materials experiments in the 1980's and 1990's. A comparison of results from MISSE-5 and Space Shuttle experiments will be included for those materials common to both the short and long-term exposures.

DeGroh, Kim↗
NASA NTRS2008

Effect of LEO Exposure on Aromatic Polymers Containing Phenylphosphine Oxide Groups

As part of the Materials on The International Space Station Experiment (MISSE), aromatic polymers containing phenylphosphine oxide groups were exposed to low Earth orbit for approx.4 years. All of the aromatic polymers containing phenylphosphine oxide groups survived the exposure despite the high fluence of atomic oxygen that completely eroded other polymer films such as Kapton(TradeMark) and Mylar(Trademark) of comparable or greater thickness. The samples were characterized for changes in physical properties, thermal/optical properties surface chemistry, and surface topography. The data from the polymer samples on MISSE were compared to samples from the same batch of material stored under ambient conditions on Earth. In addition, comparisons were made between the MISSE samples and those subjected to shorter term space flight exposures. The results of these analyses will be presented.

Lillehei, P. T.↗
NASA NTRS2008

Estimated Environmental Exposures for MISSE-3 and MISSE-4

Describes the estimated environmental exposure for MISSE-2 and MISSE-4. These test beds, attached to the outside of the International Space Station, were planned for 3 years of exposure. This was changed to 1 year after MISSE-1 and -2 were in space for 4 years. MISSE-3 and -4 operate in a low Earth orbit space environment, which exposes them to a variety of assaults including atomic oxygen, ultraviolet radiation, particulate radiation, thermal cycling, and meteoroid/space debris impact, as well as contamination associated with proximity to an active space station. Measurements and determinations of atomic oxygen fluences, solar UV exposure levels, molecular contamination levels, and particulate radiation are included.

Finckenor, Miria M.↗
NASA NTRS2011

NASA Tech Briefs, August 2011

Topics covered include: Miniature, Variable-Speed Control Moment Gyroscope; NBL Pistol Grip Tool for Underwater Training of Astronauts; HEXPANDO Expanding Head for Fastener-Retention Hexagonal Wrench; Diagonal-Axes Stage for Pointing an Optical Communications Transceiver; Improvements in Speed and Functionality of a 670-GHz Imaging Radar; IONAC-Lite; Large Ka-Band Slot Array for Digital Beam-Forming Applications; Development of a 150-GHz MMIC Module Prototype for Large-Scale CMB Radiation; Coupling Between Waveguide-Fed Slot Arrays; PCB-Based Break-Out Box; Multiple-Beam Detection of Fast Transient Radio Sources; Router Agent Technology for Policy-Based Network Management; Remote Asynchronous Message Service Gateway; Automatic Tie Pointer for In-Situ Pointing Correction; Jitter Correction; MSLICE Sequencing; EOS MLS Level 2 Data Processing Software Version 3; DspaceOgre 3D Graphics Visualization Tool; Metallization for Yb14MnSb11-Based Thermoelectric Materials; Solvent/Non-Solvent Sintering To Make Microsphere Scaffolds; Enhanced Fuel-Optimal Trajectory-Generation Algorithm for Planetary Pinpoint Landing; Self-Cleaning Coatings and Materials for Decontaminating Field-Deployable Land and Water-Based Optical Systems; Separation of Single-Walled Carbon Nanotubes with DEP-FFF; Li Anode Technology for Improved Performance; Post-Fragmentation Whole Genome Amplification-Based Method; Microwave Tissue Soldering for Immediate Wound Closure; Principles, Techniques, and Applications of Tissue Microfluidics; Robotic Scaffolds for Tissue Engineering and Organ Growth; Stress-Driven Selection of Novel Phenotypes; Method for Accurately Calibrating a Spectrometer Using Broadband Light; Catalytic Microtube Rocket Igniter; Stage Cylindrical Immersive Display; Vacuum Camera Cooler; Atomic Oxygen Fluence Monitor; Thermal Management Tools for Propulsion System Trade Studies and Analysis; Introduction to Physical Intelligence; Technique for Solving Electrically Small to Large Structures for Broadband Applications; Accelerated Adaptive MGS Phase Retrieval; Large Eddy Simulation Study for Fluid Disintegration and Mixing; Tropospheric Correction for InSAR Using Interpolated ECMWF Data and GPS Zenith Total Delay; Technique for Calculating Solution Derivatives With Respect to Geometry Parameters in a CFD Code; Acute Radiation Risk and BRYNTRN Organ Dose Projection Graphical User Interface; Probabilistic Path Planning of Montgolfier Balloons in Strong, Uncertain Wind Fields; Flight Simulation of ARES in the Mars Environment; Low-Outgassing Photogrammetry Targets for Use in Outer Space; Planning the FUSE Mission Using the SOVA Algorithm; Monitoring Spacecraft Telemetry Via Optical or RF Link; and Robust Thermal Control of Propulsion Lines for Space Missions.

Source record↗
NASA NTRS2012

Estimated Environmental Exposures for MISSE-7B

This paper details the 18-month environmental exposure for Materials International Space Station Experiment 7B (MISSE-7B) ram and wake sides. This includes atomic oxygen, ultraviolet radiation, particulate radiation, thermal cycling, meteoroid/space debris impacts, and observed contamination. Atomic oxygen fluence was determined by measured mass and thickness loss of polymers of known reactivity. Diodes sensitive to ultraviolet light actively measured solar radiation incident on the experiment. Comparisons to earlier MISSE flights are discussed.

Finckenor, Miria M.↗
NASA NTRS2016

System and Method for Determining Fluence of a Substance

A system and method for measuring a fluence of gas are disclosed. The system has a first light detector capable of outputting an electrical signal based on an amount of light received. A barrier is positionable adjacent the first light detector and is susceptible to a change in dimension from the fluence of the gas. The barrier permits a portion of light from being received by the first light detector. The change in the dimension of the barrier changes the electrical signal output from the first light detector. A second light detector is positionable to receive light representative of the first light detector without the barrier. The system and method have broad application to detect fluence of gas that may cause erosion chemical reaction causing erosive deterioration. One application is in low orbit Earth for detecting the fluence of atomic oxygen.

Banks, Bruce A.↗
NASA NTRSDate not supplied

Space-qualified Chalcogenide Materials through ISS MISSE Exposure —From Property to Application

In March 2021, twenty-four samples of various phase change materials (PCMs - Ge2Sb2Te5, Ge2Sb2Se4Te1, and Sb2Se3) along with metasurface optical components comprised of these PCMs, were delivered to the International Space Station (ISS) as part of the Materials International Space Station Experiment (MISSE-14) test campaign [1]. Although PCMs have previously been noted for their resilience to various forms of radiation [2], they had not been tested in a realistic space environment until this exposure campaign with joint NASA and MIT collaboration. During the six-month total open exposure time in low earth orbit (LEO), high-resolution cameras scanned and captured photographs of the samples to detect changes as a function of time along with on-orbit measured temperature, UV radiation, total atomic oxygen fluence, and total ionizing radiation doses. The samples were returned to NASA Langley Research Center in March 2022 for post-flight characterization. This duplicated the preflight characterization (i.e., material composition and crystallinity that limits switching speed, index contrast, loss, etc.) conducted before launch. The space sector has witnessed tremendous growth within the past decade—not only from government agencies but also entrants from the private sector. Future growth in the capabilities of Earth observation, deep space, and planetary surface missions using miniaturized spacecraft platforms can only be sustained by innovations in the design of remote sensors and other sub-systems. Active metasurface optics with enhanced tunability and reconfigurability continues to redefine the boundaries of optical science [3]. The introduction of PCM technology and associated optical devices will help to accelerate the adoption of new architectures for reduced size, weight, power, and cost (SWaP-C) platforms in space.Here we introduce results obtained from the MISSE-14 mission related to space qualification of PCM-based optic devices and constituent materials. We then discuss our recent work developing active integrated photonic devices and metasurface optics based on PCMs for space applications. This includes tunable and reconfigurable optical metasurface devices to support NASA space communication and LIDAR applications. PCMs are quickly becoming interesting photonics materials but questions related to mission suitability remain, particularly in regard to key properties like figures-of-merit (FOM, Δn/Δk), glass forming temperatures, and phase transition speeds. This talk will describe efforts to afford researchers the ability to have access to cost-effective data on exposure-induced changes to PCM fundamental physical and optical properties to assess their utility for space applications. The MISSE-14 sample exposure campaign allows a complete understanding of the limitations of the PCMs for various space-based electronic and optoelectronic applications.

Chalcogenide Phase change material↗
NASA NTRS1995

Exposure of LDEF materials to atomic oxygen: Results of EOIM 3

The third Effects of Oxygen Atom Interaction with Materials (EOIM 3) experiment flew on STS-46 from July 31 to August 8, 1992. The EOIM-3 sample tray was exposed to the low-earth orbit space environment for 58.55 hours at an altitude of 124 nautical miles resulting in a calculated total atomic oxygen (AO) fluence of 1.99 x 10(exp 20) atoms/sq cm. Five samples previously flown on the Long Duration Exposure Facility (LDEF) Experiment M0003 were included on the Aerospace EOIM 3 experimental tray: (1) Chemglaze A276 white thermal control paint from the LDEF trailing edge (TE); (2) S13GLO white thermal control paint from the LDEF TE; (3) S13GLO from the LDEF leading edge (LE) with a visible contamination layer from the LDEF mission; (4) Z306 black thermal control paint from the LDEF TE with a contamination layer from the LDEF mission; and (5) anodized aluminum from the LDEF TE with a contamination layer from the LDEF mission. The purpose of this experiment was twofold: (l) investigate the response of trailing edge LDEF materials to atomic oxygen exposure, thereby simulating LDEF leading edge phenomena; (2) investigate the response of contaminated LDEF samples to atomic oxygen in attempts to understand LDEF contamination-atomic oxygen interactions. This paper describes the response of these materials to atomic oxygen exposure, and compares the results of the EOIM 3 experiment to the LDEF mission and to ground-based atomic oxygen exposure studies.

Jaggers, C. H.↗
NASA NTRS1992

Interactions of atomic oxygen with material surfaces in low Earth orbit: Preliminary results from experiment A0114

The atomic oxygen experiment consisted of two trays (one-sixth of a Long Duration Exposure Facility (LDEF) tray each) of 64 one inch diameter solid samples. It was intended that the effects of atomic oxygen and solar ultraviolet irradiation on the surface properties of each material could be distinguished from each other and from the effects of aging. Sixteen of the samples were placed on a thermally isolated plate of highly polished aluminum, while the main plate was coated with the thermal control coating S13-GLO. Though the experiment was entirely passive, it was hoped that the effects of thermal activation might be observed, if present. The plates were expected to stabilize at temperatures differing by 20-30 C. The samples included thin films of metals Os, Ir, Pt, Ni, Mo, and Al coated onto silica optical flats, metal carbides (WC, SiC), solid carbons of various types, eight polymers, and some other coatings of various types. Analysis is essentially complete using stylus profilometry with high sensitivity Talystep and lower sensitivity Talysurf machines. Though the integrated fluence of O atoms on the LDEF was 30 times that of previous missions, etch depths of the polymers such as the polyimide Kapton show excellent agreement with extrapolations from previous flight data. However, some new effects were observed. We demonstrated on a previous experiment on STS-8 that profilometry of this kind can show steps of 50 A (for example those due to oxide film growth on metals) and this is now the preferred method for estimating etch depth (or mass loss) of erodible substances.

Gregory, John C.↗
NASA NTRS1992

Monte Carlo modeling of atomic oxygen attack of polymers with protective coatings on LDEF

Characterization of the behavior of atomic oxygen interaction with materials on the Long Duration Exposure Facility (LDEF) will assist in understanding the mechanisms involved, and will lead to improved reliability in predicting in-space durability of materials based on ground laboratory testing. A computational simulation of atomic oxygen interaction with protected polymers was developed using Monte Carlo techniques. Through the use of assumed mechanistic behavior of atomic oxygen and results of both ground laboratory and LDEF data, a predictive Monte Carlo model was developed which simulates the oxidation processes that occur on polymers with applied protective coatings that have defects. The use of high atomic oxygen fluence-directed ram LDEF results has enabled mechanistic implications to be made by adjusting Monte Carlo modeling assumptions to match observed results based on scanning electron microscopy. Modeling assumptions, implications, and predictions are presented, along with comparison of observed ground laboratory and LDEF results.

Banks, Bruce A.↗
NASA NTRS1993

LDEF fiber-composite materials characterization

Degradation of a number of fiber/polymer composites located on the leading and trailing surfaces of LDEF where the atomic oxygen (AO) fluences ranged from 10(exp 22) to 10(exp 4) atoms/cm(sup 2), respectively, was observed and compared. While matrices of the composites on the leading edge generally exhibited considerable degradation and erosion-induced fragmentation, this 'asking' process was confined to the near surface regions because these degraded structures acted as a 'protective blanket' for deeper-lying regions. This finding leads to the conclusion that simple surface coatings can significantly retard AO and other combinations of degrading phenomena in low-Earth orbit. Micrometeoroid and debris particle impacts were not a prominent feature on the fiber composites studied and apparently do not contribute in a significant way to their degradation or alteration in low-Earth orbit.

Miglionico, C. J.↗
NASA NTRS1993

The effects of long-duration space exposure on the mechanical properties of some carbon-reinforced resin matrix composites

Long Duration Exposure Facility (LDEF) Experiment A0175 involved the non-instrumented exposure of seven carbon-fiber reinforced resin-matrix advanced composite panels contained in two trays - A7 and A1. These two trays were located, respectively, on the leading and trailing faces of LDEF, obliquely oriented to the RAM (Row 9) and WAKE (Row 3) directions. The identity and location of the seven panels, which consisted of six flat laminates of the following material systems are shown: carbon/epoxy (T300/934), carbon/bismaleimide (T300/F178), and carbon/polyimide (C6000/LARC-160 and C6000/PMR-15), plus one bonded honeycomb sandwich panel (T300/934 face sheets and Nomex core) patterned after the Space Shuttle payload bay door construction. These material systems were selected to represent a range of then-available matrix resins which, by virtue of their differing polymer chemistry, could conceivably exhibit differing susceptibility to the low-earth orbit (LEO) environment. The principal exposure conditions of the LDEF environment at these tray locations are shown. Noteworthy to some of the observations discussed is the four-orders-of magnitude difference in the atomic oxygen (AO) fluence, which made a shallow incidence angle (approximately 22 deg) to Tray A7, while Tray A1 on the trailing face was essentially shielded from AO exposure. This evaluation focused on determining the individual and relative suitability of a variety of resin-matrix composite systems for long-term space structural applications. This was accomplished primarily by measuring and comparing a range of engineering mechanical properties on over 300 test coupons sectioned from the flight panels and from identical control panels, and tested at ambient and elevated temperatures. This testing was supported by limited physical characterization, involving visual examination of flight panel surface features, measurements of weight loss and warpage, and examination for changes in internal integrity (micro cracking, delamination) by ultrasonic c-scan and polished cross-sections.

Vyhnal, Richard F.↗
NASA NTRS1993

Atomic oxygen erosion considerations for spacecraft materials selection

The Long Duration Exposure Facility (LDEF) satellite carried 57 experiments that were designed to define the low-Earth orbit (LEO) space environment and to evaluate the impact of this environment on potential engineering materials and material processes. Deployed by the Shuttle Challenger in April of 1984, LDEF made over 32,000 orbits before being retrieved nearly 6 years later by the Shuttle Columbia in January of 1990. The Solar Array Passive LDEF Experiment (SAMPLE) AO171 contained approximately 300 specimens, representing numerous material classes and material processes. AO171 was located on LDEF in position A8 at a yaw of 38.1 degrees from the ram direction and was subjected to an atomic oxygen (AO) fluence of 6.93 x 10(exp 21) atoms/sq cm. LDEF AO171 data, as well as short-term shuttle data, will be discussed in this paper as it applies to engineering design applications of composites, bulk and thin film polymers, glassy ceramics, thermal control paints, and metals subjected to AO erosion.

Whitaker, Ann F.↗
NASA NTRS1993

An overview of the Evaluation of Oxygen Interaction with Materials-third phase (EOIM-3) experiment: Space Shuttle Mission 46

The interaction of the atomic oxygen (AO) component of the low earth orbit (LEO) environment with spacecraft materials has been the subject of several flight experiments over the past 11 years. The effect of AO interactions with materials has been shown to be significant for long-lived spacecraft such as Space Station Freedom and has resulted in materials changes for externally exposed surfaces. The data obtained from previous flight experiments, augmented by limited ground-based evaluation, have been used to evaluate hardware performance and select materials. Questions pertaining to the accuracy of this data base remain, resulting from the use of long-term ambient density models to estimate the O-atom fluxes and fluences needed to calculate materials reactivity in short-term flight experiments. The EOIM-3 flight experiment was designed to produce benchmark AO reactivity data and was carried out during STS-46. Ambient density measurements were made with a quadrupole mass spectrometer which was calibrated for AO measurements in a unique ground-based test facility. The combination of these data with the predictions of ambient density models allows an assessment of the accuracy of measured reaction rates on a wide variety of materials, many of which had never been tested in LEO before. The mass spectrometer is also used to obtain a better definition of the local neutral and plasma environments resulting from interaction of the ambient atmosphere with various spacecraft surfaces. In addition, the EOIM-3 experiment was designed to produce information on the effects of temperature, mechanical stress, and solar exposure on the AO reactivity of a wide range of materials. An overview of the EOIM-3 methods and results are presented.

Leger, Lubert J.↗
NASA NTRS2007

Comparison of the Atomic Oxygen Erosion Depth and Cone Height of Various Materials at Hyperthermal Energy

Atomic oxygen readily reacts with most spacecraft polymer materials exposed to the low Earth orbital (LEO) environment. If the atomic oxygen arrival comes from a fixed angle of impact, the resulting erosion will foster the development of a change in surface morphology as material thickness decreases. Hydrocarbon and halopolymer materials, as well as graphite, are easily oxidized and textured by directed atomic oxygen in LEO at energies of approx.4.5 eV. What has been curious is that the ratio of cone height to erosion depth is quite different for different materials. The formation of cones under fixed direction atomic oxygen attack may contribute to a reduction in material tensile strength in excess of that which would occur if the cone height to erosion depth ratio was very low because of greater opportunities for crack initiation. In an effort to understand how material composition affects the ratio of cone height to erosion depth, an experimental investigation was conducted on 18 different materials exposed to a hyperthermal energy directed atomic oxygen source (approx.70 eV). The materials were first salt-sprayed to provide microscopic local areas that would be protected from atomic oxygen. This allowed erosion depth measurements to be made by scanning microscopy inspection. The polymers were then exposed to atomic oxygen produced by an end Hall ion source that was operated on pure oxygen. Samples were exposed to an atomic oxygen effective fluence of 1.0x10(exp 20) atoms/sq cm based on Kapton H polyimide erosion. The average erosion depth and average cone height were determined using field emission scanning electron microscopy (FESEM). The experimental ratio of average cone height to erosion depth is compared to polymer composition and other properties.

Waters, Deborah L.↗
NASA NTRS2013

The Komplast Experiment: Space Environmental Effects after 12 Years in LEO (and Counting)

The Komplast materials experiment was designed by the Khrunichev State Research and Production Space Center, together with other Russian scientific institutes, and has been carried out by Mission Control Moscow since 18. Komplast panels fitted with material samples and sensors were located on the International Space Station (ISS) Functional Cargo Block (FGB) module exterior surface. Within the framework of this experiment, the purpose was to study the effect of the low earth orbit (LEO) environment on exposed samples of various materials. The panels were sent into orbit with the FGB when it launched on November 20, 1998. Panels #2 and #10 were retrieved during Russian extravehicular activity in February 2011 and sealed within cases to temporarily protect the samples from exposure to air until they could be studied on the ground. Panel #2 contained an experiment to detect micrometeoroid and orbital debris (MMOD) impacts, radiation and UV sensors, several pieces of electrical cable, and samples made from elastomeric and fluoroplastic materials. Panel #10 contained a temperature sensor, and both carbon composite and adhesive-bonded samples. A figure shows the location of panels #2 and #10 on the FGB module aft endcone. The panels were subsequently returned to Earth by Space Shuttle Discovery on the STS-133/ULF-5 mission after 12 years of LEO exposure and opened in an argon chamber at the Institute of Nuclear Physics at Moscow State University in July 2011. Based on the results of analyzing the readings from sensors located on Komplast panels and in studying material samples from the panels, the comprehensive effect of spaceflight factors on the FGB (at the locations of Panels #2 and #10) was evaluated. Total solar exposure was determined to be 960 +/- 200 kJ/square cm or 21,000 equivalent solar hours. Because of location of these two panels and the ISS flight attitude, atomic oxygen (AO) fluence was relatively low for such a long duration exposure, approximately 1.5x10 (exp 21) O atoms/sq. cm. Most of the AO fluence occurred during the early phase of ISS assembly. Temperatures ranged from a maximum of 107 C to a minimum of -80 C. The MMOD environment was determined, as is shown. Interestingly, the distribution of craters and low-velocity impact particles observed in the 5-50 micron size range was approx 2-3 orders of magnitude higher than that predicted by the ORDEM2000 model of natural and artificial origin microparticles in the ISS orbit. Contamination observations were also made, through the evaluation of optical properties on thermal control coatings and by the examination of visible deposits located near several samples on the panels, primarily from elastomeric samples. These elastomer samples were extensively investigated for their physical property changes and sealing capability. In addition, 16 samples of adhesive-bonded joints using three types of epoxy adhesive were evaluated studying fracture toughness, failure surface, and adhesive volume properties. Both rubber and adhesive-bonded specimens also underwent additional (post-flight) ground-based exposures to simulate a total 30 years in LEO prior to their evaluation. Overall, results indicate that space environmental effects will not adversely impact the service life of the FGB through 2028. Our investigation is complete and a summary of the results obtained from this uniquely long-duration exposure experiment will be presented.

Shaevich, S. K.↗
NASA NTRS2018

Degradation of Intercalated Graphite Epoxy Composites Exposed to Low Earth Orbit

Four different graphite fiber/epoxy composites were exposed to the wake-side low Earth orbit (LEO) environment on the Optical Reflector Materials Experiment III (ORMatE-III) platform mounted on the exterior of the ISS for two years in order to determine their long term durability in the space environment. Three of the composite samples used bromine intercalated P100 fibers and one used pristine P100 fibers. One of the P100-Br samples was coated with a protective SiO2 layer, and half of another was coated with SiO2. Results were compared with the EOIM-III experiment which exposed the same materials in LEO in the ram direction for 42 h on the Space Shuttle. Although the atomic oxygen (AO) fluence of the ORMatE-III samples was one-third of the EOIM-III exposure, the resulting effects were qualitatively the same. Both found that SiO2 coated intercalated graphite composites showed no AO erosion, verifying that conventional protection strategies are applicable to bromine intercalated composites. Both found that bromine intercalation does not alter the AO erosion rates of graphite fiber/epoxy composites. Both found no bromine was detected to have migrated into the surrounding epoxy, even for highly eroded fibers and epoxy, allaying fears that bromination could compromise the properties of the epoxy. And both found no corrosive bromine was detected to have been released by the fibers allaying fears that outgassing could degrade sensitive electronics. The uncoated EOIM-III samples suffered slightly greater erosion resulting in a slightly higher solar absorptance. The general conclusion is that ram AO exposure had very similar effects on graphite fiber epoxy composites in both the EOIM-III and ORMatE-III experiments, and in neither case did bromine intercalation of the fibers substantially influence that degradation.

Intercalated graphite↗
NASA NTRS1995

Low earth orbit durability of protected silicone for refractive photovoltaic concentrator arrays

Photovoltaic power systems with novel refractive silicone solar concentrators are being developed for use in low Earth orbit (LEO). Because of the vulnerability of silicones to atomic oxygen and ultraviolet radiation, these lenses are coated with a multilayer metal oxide protective coating. The objective of this work was to evaluate the effects of atomic oxygen and thermal exposures on multilayer coated silicone. Samples were exposed to high-fluence ground-laboratory and low-fluence in-space atomic oxygen. Ground testing resulted in decreases in both total and specular transmittance, while in-space exposure resulted in only small decreases in specular transmittance. A contamination film, attributed to exposed silicone at coating crack sites, was found to cause transmittance decreases during ground testing. Propagation of coating cracks was found to be the result of sample heating during exposure. The potential for silicone exposure, with the resulting degradation of optical properties from silicone contamination, indicates that this multilayer coated silicone is not durable for LEO space applications where thermal exposures will cause coating crack development and propagation.

McCollum, Timothy A.↗