Characterization of Additively Manufacture GRCop-42 and GRCop-84

GRCop-42 (Cu-4 at.% Cr-2 at.% Nb) is a copper-based alloy optimized for high temperature, high thermal conductivity applications such as regenerative cooled rocket engine liners. For this application, it is important to minimize contamination such as trace elements and ceramic inclusions. NASA initiated a series of ten builds by eight companies to assess the repeatability of GRCop-42 between vendors and machines. Utilizing inductively coupled plasma – atomic emission spectroscopy (ICP-AES) and energy dispersive spectroscopy (EDS) techniques allowed for identification of contaminants and quantification of their chemistry. In addition, additive manufacturing (AM) creates a unique microstructure that is often highly textured in the build (Z) direction. Electron backscattered diffraction (EBSD) was used to begin quantifying the degree of crystallographic texture in the copper matrix grains. It was also used to identify the crystallographic form of Cr2Nb, the main strengthening phase, present in the samples. Results showed the presence of ceramic inclusions, highly textured grains, and both the low and high temperature phases of Cr2Nb being present.

copper↗

Holographic microscopy studies of emulsions

A holographic microscopy system that records and observes the dynamic properties of separation of dispersed immiscible fluids is described. The holographic construction system and reconstruction system that were used to obtain particle size and distribution information from the holograms are discussed. The holographic microscopy system is used to observed the phase separating processes in immiscible fluids that were isothermally cooled into the two phase region. Nucleation, growth rates, coalescence, and particle motion are successfully demonstrated with this system. Thus a holographic particle sizing system with a resolution of 2 micrometers and a field of view of 100 cu cm was developed that provides the capability of testing the theories of separating immiscible fluids for particle number densities in the range of 10 to 10 to the 7th power particles.

Witherow, W. K.↗

Pt: Ti Diffusion Barrier, Interconnect, and Simultaneous Ohmic Contacts to n- and p-type 4H-SiC

We report the initial results of using co-sputtered Pt:Ti 80:20 at. % composition ratio metallization as a diffusion barrier against gold (Au) and oxygen (O), as an interconnect layer, as well as forming simultaneous ohmic contacts to n-and p-type 4H-SiC. Having a single conductor with such combined multi-functional attributes would appreciably reduce the fabrication costs, processing time and complexity that are inherent in the production of SiC based devices. Auger Electron Spectroscopy, Focused Ion Beam-assisted Field Emission Scanning Electron Microscopy and Energy Dispersive Spectroscopy analyses revealed no Au and O migration to the SiC contact surface and minimal diffusion through the Pt:Ti barrier layer after 15 minutes of exposure at 800 °C in atmosphere, thus offering potential long term stability of the ohmic contacts. Specific contact resistance values of 7 x 10(exp -5) and 7.4 x 10(exp -4) Ω-sq.cm were obtained on the n (N(sub d)=7 x 10(exp 18) per cu.cm and p (N(sub a)=2 x 10(exp 20) per cu. cm) -type 4H-SiC, respectively. The resistivity of 75 μΩ-cm was obtained for the Pt:Ti layer that was sandwiched between two SiO2 layers and annealed in pure O ambient up to 900 °C, which offers promise as a high temperature interconnect metallization.

Simultaneous Ohmic Contact↗

The influence of buoyant forces and volume fraction of particles on the particle pushing/entrapment transition during directional solidification of Al/SiC and Al/graphite composites

Directional solidification experiments in a Bridgman-type furnace were used to study particle behavior at the liquid/solid interface in aluminum metal matrix composites. Graphite or silicon-carbide particles were first dispersed in aluminum-base alloys via a mechanically stirred vortex. Then, 100-mm-diameter and 120-mm-long samples were cast in steel dies and used for directional solidification. The processing variables controlled were the direction and velocity of solidification and the temperature gradient at the interface. The material variables monitored were the interface energy, the liquid/particle density difference, the particle/liquid thermal conductivity ratio, and the volume fraction of particles. These properties were changed by selecting combinations of particles (graphite or silicon carbide) and alloys (Al-Cu, Al-Mg, Al-Ni). A model which consideres process thermodynamics, process kinetics (including the role of buoyant forces), and thermophysical properties was developed. Based on solidification direction and velocity, and on materials properties, four types of behavior were predicted. Sessile drop experiments were also used to determine some of the interface energies required in calculation with the proposed model. Experimental results compared favorably with model predictions.

Stefanescu, Doru M.↗

The Influence of Coastal Fronts on the Movement and Dispersion of Oil Slicks

The author has identified the following significant results. LANDSAT, aircraft, and boats were used successfully to study estuarine and coastal fronts or boundaries. Fronts are a major hydrographic feature in Delaware Bay and in other estuaries. Horizontal salinity gradients of 4% in one meter and convergence velocities of the order of 0.1 m/sec were observed. Visibility improved from one meter to two meters as certain boundaries were crossed. Fronts near the mouth of the bay are associated with the tidal exchange with shelf water. The formation of fronts in the interior of the bay appears to be associated with velocity shears induced by differences in bottom topography with horizontal density difference in the deep water portion of the estuary. Surface slicks and foam collected at frontal convergence zones near boundaries were found to contain concentrations of Cr, Cu, Fe, Hg, Pb, and Zn higher by two to four orders of magnitude than concentrations in mean ocean water.

Klemas, V.↗

Reaction layer formation at the graphite/copper-chromium alloy interface

Sessile drop tests were used to obtain information about copper chromium alloys that suitably wet graphite. Characterization of graphite/copper-chromium alloy interfaces subjected to elevated temperatures were conducted using scanning electron micrography, energy dispersive spectroscopy, auger electron spectroscopy, and x ray diffraction analyses. These analyses indicate that during sessile drop tests conducted at 1130 C for one hour, copper alloys containing greater than 0.98 percent chromium form continuous reaction layers of approximately 10 micron thickness. The reaction layers adhere to the graphite surface. The copper wets the reaction layer to form a contact angle of 60 degrees or less. X ray diffraction results indicate that the reaction layer is chromium carbide. The kinetics of reaction layer formation were modelled in terms of bulk diffusion mechanisms. Reaction layer thickness is controlled initially by the diffusion of Cr out of Cu alloy and later by the diffusion of C through chromium carbide.

Devincent, Sandra M.↗

Observational evidence for a hot gaseous Galactic corona

Galactic absorption features observed in high-dispersion far-UV spectra of two Large Magellanic Cloud (LMC) stars obtained with the IUE satellite are discussed. The stars observed were HD 38268 (OB + WN5) and HD 38282 (WN6), which lie at a distance of about 55 kpc and in the galactic direction corresponding to a latitude of about -32 deg and a longitude of about 280 deg. The line of sight to these stars passes through the disk and halo of the Milky Way and the halo and disk of the LMC. Evidence is presented for the existence of a hot (somewhat below 1 million K), low-density (about 0.001 H atom per cu cm) Galactic corona.

Savage, B. D.↗

Reaction layer formation at the graphite/copper-chromium alloy interface

Sessile drop tests were used to obtain information about copper chromium alloys that suitably wet graphite. Characterization of graphite/copper-chromium alloy interfaces subjected to elevated temperatures were conducted using scanning electron micrography, energy dispersive spectroscopy, Auger electron spectroscopy, and X-ray diffraction analyses. These analyses indicate that during sessile drop tests conducted at 1130 C for one hour, copper alloys containing greater than 0.98 percent chromium form continuous reaction layers of approximately 10 micron thickness. The reaction layers adhere to the graphite surface. The copper wets the reaction layer to form a contact angle of 60 degrees or less. X-ray diffraction results indicate that the reaction layer is chromium carbide. The kinetics of reaction layer formation were modelled in terms of bulk diffusion mechanisms. Reaction layer thickness is controlled initially by the diffusion of Cr out of Cu alloy and later by the diffusion of C through chromium carbide.

Devincent, Sandra M.↗

Sequentially evaporated thin Y-Ba-Co-O superconducting films on microwave substrates

The development of high T sub c superconducting thin films on various microwave substrates is of major interest in space electronic systems. Thin films of YBa2Cu3O(7-Delta) were formed on SrTiO3, MgO, ZrO2 coated Al2O3, and LaAlO3 substrates by multi-layer sequential evaporation and subsequent annealing in oxygen. The technique allows controlled deposition of Cu, BaF2 and Y layers, as well as the ZrO buffer layers, to achieve reproducibility for microwave circuit fabrication. The three layer structure of Cu/BaF2/Y is repeated a minimum of four times. The films were annealed in an ambient of oxygen bubbled through water at temperatures between 850 C and 900 C followed by slow cooling (-2 C/minute) to 450 C, a low temperature anneal, and slow cooling to room temperature. Annealing times ranged from 15 minutes to 5 hrs. at high temperature and 0 to 6 hr. at 450 C. Silver contacts for four probe electrical measurements were formed by evaporation followed with an anneal at 500 C. The films were characterized by resistance-temperature measurements, energy dispersive X-ray spectroscopy, X-ray diffraction, and scanning electron microscopy. Critical transition temperatures ranged from 30 K to 87 K as a function of the substrate, composition of the film, thicknesses of the layers, and annealing conditions. Microwave ring resonator circuits were also patterned on these MgO and LaAlO3 substrates.

Valco, G. J.↗

The luminosity distribution and total space density of pulsars

The detailed distribution of dispersion measures and spectral fluxes for a sample of 50 pulsars in part of the galactic plane near longitude 50 deg is analyzed, and the intrinsic luminosity distribution of the pulsars is obtained along with some constraints on their spatial distribution. Expressions for the observed distributions of spectral fluxes, distances, and directions are given in terms of the spatial and luminosity distributions of the sources as well as the sensitivity of the detector. A previous analysis of the same sample is reviewed, and the intrinsic luminosity distribution is determined from the distribution of observed distances as well as from the observed distribution of spectral fluxes. The results indicate that the scale height of pulsars cannot be significantly less than 400 pc, the total space density of active pulsars is about 30 per cu kpc, and the birthrate required to maintain this population is about one in the Galaxy every 980 (450-2600) years.

Roberts, D. H.↗

Applicability of Micro X-Ray Fluorescence Spectroscopy to Astromaterials Curation and Research

Introduction: The Astromaterials Acquisition and Curation Office at NASA’s Johnson Space Center (JSC) curates NASA’s astromaterial sample collections which includes: Apollo samples, Luna samples, Ant-arctic meteorites, cosmic dust particles, microparticle impacts into space-flown materials, Genesis solar wind atoms, Stardust comet Wild-2 particles, Stardust inter-stellar particles, Hayabusa asteroid Itokawa particles, Hayabusa 2 asteroid Ryugu particles, and future OSIRIS-Rex asteroid Bennu particles (landing in Sep-tember, 2023) [1–3]. To enhance JSC’s advanced cu-ration capabilities, we have recently installed a high-performance micro-X-ray fluorescence (µXRF) spec-trometer to assist in sample characterization through rapid, non-destructive, in-situ elemental analyses that do not require the sample preparation protocols (i.e., polishing and carbon-coating) commonly needed for electron beam analyses. With this new instrument, we are capable of detecting all elements down to carbon in a variable-pressure or He-purged chamber for anal-ysis of a wide range of sample types. Here we describe the instrumental set-up, capabilities, and applicability of µXRF analysis to astromaterials curation and re-search. Instrumentation and Methodology: The X-ray fluorescence and computed tomography lab (X-FaCT) lab at JSC is now equipped with a Bruker M4 Tornado Plus µXRF (Fig. 1). This system is an energy-dispersive x-ray spectrometer equipped with two 60 mm2 silicon drift detectors (SDD) that are able to be used simulta-neously for output count rates ~500,000 cps. New light element windows allow detecting and analyzing the entire elemental range from carbon to americium. Two x-ray tubes (micro-focus Rh with polycapillary lenses and W with collimators of 0.5, 1.0, 2.0, and 4.5 mm) with max excitation parameters of 50 kV, 30 W and 50 kV, 40 W, respectively, allow for more flexibility of the analysis of high energy lines. The motorized X-Y-Z stage has a mapping range of 190 x 160 mm and can support samples up to 7 kg (~15.5 lbs) and a height of 120 mm [4]. Analytical modes include elemental analysis (down to ~20 µm spot size) via point, line, or area of bulk materials (rock surfaces, thin sections, thick sections, etc.) as well as coating analysis (determination of thickness and composition) of samples. This system has a variable vacuum chamber (1 mbar to 1 atm) that is also equipped with a He-purge system which accommodates vacuum sensitive samples while still allowing detection of light elements at atmospheric pressure. Utility and Applicability of µXRF in Astro-materials research and exploration science (ARES): Elemental analysis using µXRF is commonly em-ployed for both terrestrial and planetary geological science disciplines [5]. It is especially useful for analy-sis of astromaterials given the limited sample prepara-tion required, which is not feasible for certain materi-als. Here we show select applications of µXRF anal-yses of astromaterials that can, have, and will be done at JSC’s X-FaCT lab. Point analysis: In-situ spot analyses (~20 µm spot size) on a cut slab of Martian meteorite NWA 10922 allowed for the discovery, qualitative elemental analy-sis and determination of different feldspar minerals [6]. These point analyses served as an effective prelim-inary step for subsequent quantitative analyses. Ana-lytical standards can be employed for more accurate quantification of µXRF spot analyses. Area analysis: This analytical mode measures all detectable elements (from C to Am) at each pixel (>5 µm pixel size) in a user-defined area. The results are shown as elemental maps which can be extracted as 16-bit TIFF’s for further data processing. In Fig. 2. we show elemental distribution maps of the high-Ti basalt 73001,531 that have been processed using ImageJ software. From these maps you can accurately and quickly (this map took ~50 mins.) identify mineral components, such as pyroxene, plagioclase, oxides, and phosphates, compositional zoning, and mineral textures. Detection of high-Z phases: µXRF techniques are es-pecially effective at analyzing trace minerals with high-atomic-number (high-Z) elements because the high-energy characteristic X-rays used (relative to SEM EDS) allow for mapping of K lines in elements up to La (typically SEM maps use L X-ray lines for elements >Zn, and these can often have interferences). Thus, µXRF is especially suited for identifying minerals like zircon, baddeleyite, REE-rich phosphates, Fe-rich met-als, oxides, sulfides, and phosphides [4]. In Fig. 3 we show elemental distribution maps for 73001,530 where we are able to correlate the original video image with, Zr, Si, Y and Hf elemental maps together identi-fying the location of a zircon. In this location you would expect lower Si compared to surrounding mate-rial, as well as higher Zr, Y, and Hf content compared to surrounding material, all of which is confirmed by our XRF ele-mental distribution maps (Figure 2.) Conclusions: The new M4 Tornado Plus µXRF within the Astromaterials Acquisition and Curation office at NASA JSC allows for rapid and non-destructive elemental analysis of astromaterials with limited or no sample preparation. µXRF analyses pro-vide crucial compositional knowledge for the prelimi-nary examination and curation of astromaterials. This instrument enhances the advanced curation capabili-ties in the X-FaCT laboratory at JSC by allowing pro-ductive, cohesive, and non-destructive multi-modal x-ray analyses on astromaterial samples, which is neces-sary for the comprehensive curation and study of our current and future astromaterial collections. Addition-ally, µXRF can provide complimentary information to researchers for studies on astromaterials. References: [1] Allen, C. et al., (2011). Chemie De Erde Geochemistry, 71, 1-20. [2] McCubbin, F. M. et al., (2016) 47th LPSC, abstract #2668 [3] Zeigler, R. A. et al., (2017) 48th LPSC, abstract #2772 [4] Bruker User Manual [5] Young et al., (2016) Appl. Geochemistry, 72, 77-87 [6] Mor-ris, R. V. et al., (2023) 54th LPSC.

E W O'Neal↗

Laser Brazing of High Temperature Braze Alloy

The Space Shuttle Main Engine (SSME) consists of 1080 conical tubes, which are furnace brazed themselves, manifolds, and surrounding structural jacket making almost four miles of braze joints. Subsequent furnace braze cycles are performed due to localized braze voids between the coolant tubes. SSME nozzle experiences extremely high heat flux (180 mW/sq m) during hot fire. Braze voids between coolant tubes may result in hot combustion gas escape causing jacket bulges. The nozzle can be disqualified for flight or result in mission failure if the braze voids exceed the limits. Localized braze processes were considered to eliminate braze voids, however, damage to the parent materials often prohibited use of such process. Being the only manned flight reusable rocket engine, it has stringent requirement on the braze process. Poor braze quality or damage to the parent materials limits the nozzle service life. The objective of this study was to develop a laser brazing process to provide quality, localized braze joints without adverse affect on the parent materials. Gold (Au-Cu-Ni-Pd-Mn) based high temperature braze alloys were used in both powder and wire form. Thin section iron base superalloy A286 tube was used as substrate materials. Different Laser Systems including CO2 (10.6 micrometers, 1kW), ND:YAG (1.06 micrometers, 4kW). and direct diode laser (808nm. 150W) were investigated for brazing process. The laser process variables including wavelength. laser power, travel speed and angle of inclination were optimized according to bead geometry and braze alloy wetting at minimum heat input level, The properties of laser brazing were compared to that of furnace brazing. Microhardness profiles were used for braze joint property comparison between laser and furnace brazing. The cooling rate of laser brazing was compared to furnace brazing based on secondary dendritic arm spacing, Both optical and Scanning Electron Microscope (SEM) were used to evaluate the microstructures of the braze materials and tube substrate. Metallography of the laser braze joint was compared to the furnace braze. SEM Energy Disperse X-Ray Spectra (EDX) and back scattered imaging were used to analyze braze alloy segregation. Although all of the laser systems, CO2, ND:YAG, and direct diode laser produced good braze joint, the direct diode laser was selected for its system simplicity, compactness and portability. Excellent laser and braze alloy coupling is observed with powder alloy compared to braze alloy wire. Good wetting is found with different gold based braze alloys. The laser brazing process can be optimized so that the adverse affect on the parent materials can be eliminated. Metallography of the laser braze joint has shown that quality braze joint was produced with laser brazing process. Penetration of the laser braze to the substrate is at neglectable level. Zero penetration is observed. Microstructure examinations shown that no observable changes of the microstructure (grain structure and precipitation) in the HAZ area between laser braze and furnace braze. Wide gaps can be laser brazed with single pass for up to 0.024 inches. Finer dendritic structure is observed in laser brazing compared with equiaxial and coarser grain of the furnace brazing microstructure. Greater segregation is also found in the furnace braze. Higher hardness of the laser braze joint comparing to furnace braze is observed due to the fast cooling rate and Finer microstructure in the laser brazing. Laser braze joint properties meet or exceed the furnace joint properties. Direct diode laser for thin section tube brazing with high temperature braze alloys have been successfully demonstrated. The laser's high energy density and precise control has shown significant advantages in reducing process heat input to the substrates and provide high quality braze joints comparing to other localized braze process such as torch, TIG, and MPTA processes. Significant cost savings can be realized particularly with localized braze comparing to a full furnace braze cycle.

Gao, Y. P.↗

Bubble Generation in a Flowing Liquid Medium and Resulting Two-Phase Flow in Microgravity

The present investigation reports a study of bubble generation under reduced gravity conditions, using both a co-flow and a cross-flow configuration. This study may be used in the conceptual design of a space-based thermal management system. Ensuing two-phase flow void fraction can be accurately monitored using a single nozzle gas injection system within a continuous liquid flow conduit, as utilized in the present investigation. Accurate monitoring of void fraction leads to precise control of heat and mass transfer coefficients related to a thermal management system; hence providing an efficient and highly effective means of removing heat aboard spacecraft or space stations. Our experiments are performed in parabolic flight aboard the modified DC-9 Reduced Gravity Research Aircraft at NASA Lewis Research Center, using an air-water system. For the purpose of bubble dispersion in a flowing liquid, we use both a co-flow and a cross-flow configuration. In the co-flow geometry, air is introduced through a nozzle in the same direction with the liquid flow. On the other hand, in the cross-flow configuration, air is injected perpendicular to the direction of water flow, via a nozzle protruding inside the two-phase flow conduit. Three different flow conduit (pipe) diameters are used, namely, 1.27 cm, 1.9 cm and 2.54 cm. Two different ratios of nozzle to pipe diameter (D(sub N))sup * are considered, namely (D(sub N))sup * = 0.1 and 0.2, while superficial liquid velocities are varied from 8 to 70 cm/s depending on flow conduit diameter. It is experimentally observed that by holding all other flow conditions and geometry constant, generated bubbles decrease in size with increase in superficial liquid velocity. Detached bubble diameter is shown to increase with air injection nozzle diameter. Likewise, generated bubbles grow in size with increasing pipe diameter. Along the same lines, it is shown that bubble frequency of formation increases and hence the time to detachment of a forming bubble decreases, as the superficial liquid velocity is in-creased. Furthermore, it is shown that the void fraction of the resulting two-phase flow increases with volumetric gas flow rate Q(sub d), pipe diameter and gas injection nozzle diameter, while they decrease with surrounding liquid flow. The important role played by flowing liquid in detaching bubbles in a reduced gravity environment is thus emphasized. We observe that the void fraction can be accurately controlled by using single nozzle gas injection, rather than by employing multiple port injection, since the later system gives rise to unpredictable coalescence of adjacent bubbles. It is of interest to note that empirical bubble size and corresponding void fraction are somewhat smaller for the co-flow geometry than the cross-flow configuration at similar flow conditions with similar pipe and nozzle diameters. In order to supplement the empirical data, a theoretical model is employed to study single bubble generation in the dynamic (Q(sub d) = 1 - 1000 cu cm/s) and bubbly flow regime within the framework of the co-flow configuration. This theoretical model is based on an overall force balance acting on the bubble during the two stages of generation, namely the expansion and the detachment stage. Two sets of forces, one aiding and the other inhibiting bubble detachment are identified. Under conditions of reduced gravity, gas momentum flux enhances, while the surface tension force at the air injection nozzle tip inhibits bubble detachment. In parallel, liquid drag and inertia can act as both attaching and detaching forces, depending on the relative velocity of the bubble with respect to the surrounding liquid. Predictions of the theoretical model compare well with our experimental results. However, at higher superficial liquid velocities, as the bubble loses its spherical form, empirical bubble size no longer matches the theoretical predictions. In summary, we have developed a combined experimental and theoretical work, which describes the complex process of bubble generation and resulting two-phase flow in a microgravity environment. Results of the present study can be used in a wide range of space-based applications, such as thermal energy and power generation, propulsion, cryogenic storage and long duration life support systems, necessary for programs such as NASA's Human Exploration for the Development of Space (HEDS).