DOE OSTI2025

Validation of a Custom Ball-on-Ring Apparatus and Consideration of Common Issues for Use in Further Testing (SULI Deliverables)

Ceramic materials are well-known for their high hardness and strength but are limited in their application due to low toughness and sudden failure. As a potential solution, inspiration can be taken from dental enamel nanostructure, where undulating rods cause cracks to branch or deflect, increasing the energy needed to cause total fracture of a ceramic part. Following the dental enamel structure, a novel ceramic which uses 3D printed Yttria stabilized Zirconia rods in an alumina matrix was developed. To test this bio-inspired ceramic material, a proper testing apparatus needed to be created and tested to verify its accuracy. For this project, a bespoke ball on ring testing apparatus was created and tested using both conventionally sintered alumina disks and purchased alumina disks to validate its accuracy. By comparing the Weibull distribution of rupture strengths measured by the tests to literature values, it was shown that the testing frame had a wide distribution of strength which did not align with literature values on the lower end. Through fractography, it was found that some samples fractured from the contact stress induced by the ball indenter, which could not be used to calculate rupture strength. This fracture was often linked to low stress to failure, which was initiated by a flaw on the surface near the indenter which acted as a stress concentrator. Removal of these samples from the data set increased the accuracy of the reported rupture strength values for the ceramic. Considering the equations for the magnitude of contact and flexural strength, along with observations of initiating flaws, several measures can be taken for testing the bio-inspired composite. These measures include proper polishing of both sides of the sample, reducing sample thickness, and potentially using a softer indenter material.

36 - MATERIALS SCIENCE↗
DOE OSTI2024

Development of Ti 3 SiC 2 MAX phase tubular structures for solar receiver applications

Solar receiver tubes are key components of concentrating solar-thermal power (CSP) systems that harvest solar energy. For better efficiency, the Gen3 CSP receivers, which collect heat into a heat transfer fluid, require a temperature exceeding 700 °C during operation and need to perform under extreme conditions of high temperature and high thermal stress. Operators are seeking CSP designs using new high-temperature structural materials with high thermal conductivity and high creep resistance to achieve a design life of 30 years and thus help recover the plant capital cost sooner. MAX phase materials, which consist of an early transition metal element, an A-group element, and carbon or nitrogen, are expected to exhibit high creep resistance as well as high fracture toughness. Here, in this paper, we describe fabricating both (1) dense Ti 3 SiC 2 MAX phase disks and (2) short-length tubes using field-assisted sintering technology (FAST). First, the disk samples that we fabricated are fully dense and contain ≈90 % Ti 3 SiC 2 MAX phase materials and ≈10 % TiC phase materials. We determined a flexure strength of 519 ± 32 MPa by conducting a four-point bending test at room temperature with rectangular bar samples of ≈100 % density. The thermal conductivity of the Ti 3 SiC 2 MAX phase samples, measured by light flashing analysis, decreases linearly from a value of 41 W . m -1 . K -1 at room temperature to a value of 36 W . m -1 . K -1 at 650 °C. A solar reflectance measurement of the Ti 3 SiC 2 MAX phase revealed that, temperature increases from 400 to 1400 °C, thermal emittance increases from 0.39 to 0.49, while selectivity decreases from 1.8 to 1.4, respectively. Whereas the surface oxidized MAX phase samples after 100 h exposure to air at 1000 °C exhibit that of SiC. Next, we discuss fabrication of the crack-free Ti 3 SiC 2 MAX phase tubular structures accomplished by using FAST processing in graphite bedding. A Ti 3 SiC 2 MAX phase content of > 95 % with traceable ≈3% remaining TiC phase and ≈15 % porosity were demonstrated after high-temperature annealing. An average fracture strength of ≈250 MPa was determined with Ti 3 SiC 2 MAX phase tubes of ≈85 % density by diametral compression testing at room temperature. Our work demonstrated that using FAST processing to produce Ti 3 SiC 2 MAX phase tubular structures for CSP receiver applications is a viable approach.

14 SOLAR ENERGY↗
DOE OSTI2023

A Sustainable and Environmentally Friendly Concrete for Structural Applications

The purpose of this study is to utilize waste products—precipitated calcium carbonate (PCC) and upcycled recycled concrete aggregate (upcycled RCA or UCA)—in civil works projects. To do so, tests must be performed to determine the engineering properties of the materials in which PCC and UCA are sequestered. PCC is a fine to coarse grain waste product generated during the production of sugar from sugar beets. UCA is produced from demolished and returned concrete by the extraction of primarily calcium and alkalinity. The study also includes the use of both PCC and UCA in the same concrete mix design. The test results on PCC alone show that the optimum content to achieve a minimum 28 MPa (4000 psi) compressive strength is 25% and 30%. The corresponding compressive strength of mixes in which conventional aggregate was replaced by UCA is about 48 MPa (7000 psi) to 55 MPa (8000 psi) at the same water: cement ratio (0.44) by weight. The compressive strength of concrete with 25% to 30% cement replaced by PCC and varying aggregates replaced with UCA ranges from 19.3 to 40 MPa (2800 to 5800 psi). Other tests on PCC and UCA include tensile strength of 2 to 3 MPa (293 to 423 psi) and flexural strength of 1.3 to 1.9 MPa (183 to 279 psi). Analytical techniques such as X-ray diffraction (XRD), energy-dispersive X-ray spectrometry (EDX), and scanning electron microscopy (SEM) were used to identify the constituent elements and chemical compounds present in PCC, including calcium carbonate and silica. Based on the test results, the composition of PCC by weight indicates 45.9% calcium, 39.4% oxygen, and 9.2% carbon. Based on the results of this study, we can expect to reduce carbon emissions in the production of cement and aggregates, as well as utilize waste products in the civil engineering field.

42 ENGINEERING↗
DOE OSTI2024

Vascular Carbon/Carbon composites for concentrated solar power

Due to their exceptional mechanical and thermal properties under high temperature conditions, for the first time, a novel vascular (embedded channels) Carbon/Carbon (C/C) composite was developed for use as a modular concentrated solar power (CSP) gas receiver. The fabrication process involves the combination of the vaporization of sacrificial component (VaSC) technique with conventional methods to produce C/C composites with well preserved channels. Different heat treatments were evaluated together with X-ray diffraction (XRD) analysis to determine optimal fabrication conditions that maintains the material and channel’s integrity. Mechanical testing confirms that structural integrity is maintained, with statistical analyses indicating no compromise in flexural strength or modulus. Furthermore, this research introduces an innovative pathway for efficient CSP gas receivers, which can bridge the gap towards improved energy generation efficiency in next-gen CSP plants through higher operating temperatures with the use of C/C composites.

14 SOLAR ENERGY↗
DOE OSTI2022

Project 7.3 Characterization of Kevlar®-reinforced Composites for Predictive Simulation

The IACMI 7.3 project between DuPont and Purdue University required the mechanical testing of a 2x2 twill Kevlar® weave with Hexion EPIKOTE resin. The tension, shear, flexure, and compressive behavior of this material system was characterized, and the results can be seen in Table 1. These material properties can now be further evaluated for use in performance simulations of automotive components to represent the properties of composites based on woven materials containing Kevlar. This report will provide details regarding the effort required to arrive at these material properties.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Design and Analysis of an Advanced Three-Point Bend Test Approach for Miniature Irradiated Disk Specimens

Candidate tungsten armor materials in a magnetic confinement fusion device must be able to withstand thermal variation that leads to internal stresses caused by the impinging heat load. In addition, the thermomechanical properties of these materials are degraded by irradiation-induced defect accumulation. Fission reactor–based irradiation data are used to predict the fusion neutron damage and property change. This study examines the motivation and design of a custom-designed three-point bend test for neutron-irradiated disk specimens that are 3 mm in diameter to be able to define the flexural strength of advanced tungsten materials, alloys, and composites—and to the extent that embrittlement occurs after neutron irradiation. The theory provided shows a calculation for the flexural deflection and shear deflection due to the small-geometry constraints. A finite element deformation analysis is performed to evaluate the mechanical stress field of disk bend specimens. The stress values above 80% of the maximum stress are concentrated in 2.4 mm of the 3.0-mm length of the centerline across the tungsten disk diameter. A bend test fixture has been designed and fabricated to enable testing of these specimens with precisely engineered tolerance and minimal machine compliance. This fixture will be able to be placed inside a universal testing frame at elevated temperatures for the mechanical property evaluation of future neutron-irradiated disk specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Fabrication of Six Degrees-of-Freedom Hexflex Positioner With Integrated Strain Sensing Using Nonlithographically Based Microfabrication

In this study, a process flow is described for the low cost, flexible fabrication of metal micro-electromechanical systems (MEMS) with high performance integrated sensing. The process is capable of producing new designs in ≈1 week at an average unit cost of <$1 k/device even at batch sizes of ≈1–10, with expected sensing performance limits of about 135 dB over a 10 kHz sensor bandwidth. This is a ≈20× reduction in cost, ≈25× reduction in time, and potentially >30× increase in sensing dynamic range over comparable state-of-the-art compliant nanopositioners. The nonlithographically based microfabrication (NLBM) process is uniquely suited to create high performance nanopositioning architectures which are customizable to the positioning requirements of a range of nanoscale applications. These can significantly reduce the cost of nanomanufacturing research and development, as well as accelerate the development of new processes and the testing of fabrication process chains without excess capital investment. A six degrees-of-freedom (6DOF) flexural nanopositioner with integrated sensing for all 6DOF was fabricated using the newly developed process chain. The fabrication process was measured to have ≈30 μ m alignment. Sensor arm, flexure, and trace widths of 150 μ m, 150 μ m, and 800 μ m, respectively, were demonstrated. Process capabilities suggest lower bounds of 25 μ m, 50 μ m, and 100 μ m, respectively. Dynamic range sensing of 52 dB was demonstrated for the nanopositioner over a 10 kHz sensor bandwidth. Improvements are proposed to approach sensor performance of about 135 dB over a 10 kHz sensor bandwidth.

42 ENGINEERING↗
DOE OSTI2024

Material property characterization of 3D printed polypropylene wood plastic composites

Abstract Wood flour (WF) at 10 wt.% and 20 wt.% loadings was used as a reinforcing filler to enhance the applicability of polypropylene (PP) for 3D printing. After performing printability tests of PP wood plastic composites (WPCs), the mechanical properties of both injection‐molded and 3D‐printed PP WPC specimens were explored. Test specimens were prepared from 3D printed hexagons for analyzing the mechanical properties. Adding WF to neat PP increased the storage modulus and the glass transition temperature while decreasing the degree of crystallinity and the coefficient of thermal expansion, while enhancing the printability of neat PP. The tensile strength, tensile modulus of elasticity, flexural strength, and flexural modulus of elasticity of injection‐molded neat PP improved by up to 21%, 59%, 30%, and 56%, respectively, with 20 wt.% WF. However, the impact strength of injection‐molded neat PP decreased by 85%, with 20 wt.% WF. After 3D printing, the tensile strength and tensile modulus of elasticity of printed neat PP increased by up to 84% and 60%, respectively, with 20 wt.% WF. The flexural strength and flexural modulus of elasticity of neat printed PP remained unchanged compared to those of PP filled with 20 wt.% WF, while the impact strength decreased by 87%. Highlights WF was used as a reinforcement in polypropylene designed for 3D printing A pilot‐scale, pellet‐fed 3D printer was used to print hollow hexagons, and then test specimens were fabricated from these hexagons for mechanical properties The tensile and flexural properties of 3D printed neat polypropylene improved, while the impact strength decreased after adding 20 wt.% WF to the neat PP.

Hwang, Sungjun↗
DOE OSTI2025

Bioinspired Dry‐Steam Superinsulation Straw Foam

Abstract Cellulosic materials offer sustainable advantages for building energy conservation. However, their development has been hindered by reduced thermal performance, often caused by structural collapse during the transition from solution to solid. Inspired by natural goose down, a bio‐based, lightweight insulation foam derived from agricultural waste straw is presented. Through in situ synthesis, bio‐silica fibers with branched structures capable of supporting hollow silica microspheres are fabricated. After steam‐mediated processing, the resulting foam exhibit low density (95 mg cm − 3 ), high porosity (95.5%), low thermal conductivity (0.03 ± 0.003 W mK −1 ), and a cyclic compressive strength of 90 kPa at 50% strain. Owing to the synergistic microstructure formed by branched bio‐fibers and hollow silica spheres, the bio‐silica foam exhibit outstanding thermal insulation performance relative to other bio‐based foams prepared by ambient drying. A passivated insulation panel is further developed by incorporating this material as the core component, achieving a thermal conductivity of 0.0275 W mk −1 and flexural strength of 6.85 MPa. The panel demonstrated durability with stable thermal performance throughout a 60‐day outdoor test. Moreover, the bio‐silica foam shows a carbon footprint of 7.50 kgCO₂ kg −1 at 70.2 wt.% silica, highlighting its promise as a sustainable insulation solution for green buildings.

Chemistry↗
DOE OSTI2022

Photoinitiator Selection and Concentration in Photopolymer Formulations towards Large-Format Additive Manufacturing

Photopolymers are an attractive option for large-format additive manufacturing (LFAM), because they can be formulated from structural thermosets and cure rapidly in ambient conditions under low-energy ultraviolet light-emitting diode (UV LED) lamps. Photopolymer cure is strongly influenced by the depth penetration of UV light, which can be limited in the 2–4 mm layer thicknesses typical of LFAM. Photoinitiator (PI) systems that exhibit photobleaching have proven useful in thick-section cure applications, because they generate a photoinitiation wavefront, but this effect is time-dependent. This study investigates the light transmission and through-thickness cure behavior in (meth)acrylate photopolymer formulations with the photobleaching initiator bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide (BAPO). Utilizing an optical model developed by Kenning et al., lower concentrations (0.1 wt% to 0.5 wt%) of BAPO were predicted to yield rapid onset of photoinitiation. In situ cure measurements under continuous UV LED irradiation of 380 mW/cm2 showed that a 0.1 wt% concentration of BAPO achieved peak polymerization rate within 2.5 s at a 3-mm depth. With only 1 s of irradiation at 1.7 W/cm2 intensity, the 0.1 wt% BAPO formulation also achieved the highest level of cure of the formulas tested. For an irradiation dose of 5.5 J/cm2 at a duration of 3.7 s, cured polymer specimens achieved a flexural strength of 108 MPa and a flexural modulus of 3.1 GPa. This study demonstrates the utility of optical modeling as a potential screening tool for new photopolymer formulations, primarily in identifying an upper limit to PI concentration for the desired cure depth. The results also show that photobleaching provides only a limited benefit for LFAM applications with short (1.0 s to 3.7 s) UV irradiation times and indicate that excess PI concentration can inhibit light transmission even under extended irradiation times up to 60 s.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Novel ductile wellbore cementitious composite for geologic CO 2 storage

CO 2 leakage through damaged wellbore cement sheaths is a major risk of geologic CO 2 storage (GCS), as conventional wellbore cement is brittle and can be damaged due to acid attack and downhole stresses during CO 2 injection. Here we examine a novel fiber-reinforced engineered cementitious composite (ECC) proposed as a substitute to conventional wellbore cement due to its superior ductility and intrinsic crack width control. ECC and conventional wellbore cement coupons were exposed to water in equilibrium with CO 2 at 50 °C and 10 MPa. The samples were retrieved after several days and their mechanical performance was evaluated using a four-point bending test, microhardness, and compressive strength analyses. Optical microscopy and mercury intrusion porosimetry were used to characterize the progression of the carbonation front and pore structures of the specimens. Control experiments were conducted under the same temperature and pressure conditions but with a N 2 headspace to isolate the impact of CO 2 . It was found that carbonation increased the ultimate flexural strength of ECC but decreased its ductility. However, the ductility of carbonated ECC remained higher than that of conventional wellbore cements that exhibited brittle failure under all test conditions. Additionally, ECC exhibited minimal material loss and continued resistance to deformation in comparison to conventional wellbore cements. This suggests that while the exposure of ECC to CO 2 will alter its mechanical properties, altered ECC will continue to exhibit mechanical performance superior to conventional wellbore cement, and therefore shows promise as a highly durable wellbore cementing material for GCS applications.

58 GEOSCIENCES↗
DOE OSTI2022

Infusible thermoplastic resin based sandwich structures for wind blade applications and the influence of scrim on facesheet to core interface debonding

Infusible thermoplastic Elium® family of resins from Arkema have garnered much attention in recent years as a possible replacement for thermoset resins in laminate and sandwich composite manufacturing for wind blade applications due to its ease of recyclability and the ability to utilize existing manufacturing processes without imposing complicated variations. However, physical and mechanical properties of the proposed Elium® based thermoplastic composites must be comparable to existing epoxy (thermoset) based composites using manufacturing processes relevant for large wind turbine blades. A 13-meter-long demonstration blade was manufactured for that purpose and sandwich samples were obtained from that project for a detailed study. This paper details three-point flexural properties of unidirectional E-glass fiber reinforced acrylic and epoxy based sandwich panels with identical balsa wood core materials. In addition, to evaluate the relative merit considering debond failure mode, the interfacial critical strain energy release rate, predominantly in mode-1, was compared via single cantilever beam testing. In sandwich composites constructed with balsa wood core material, resin uptake by the balsa core is traditionally impeded via the insertion of a scrim material at the facesheet to core interface. Results revealed that inclusion of scrim mesh layer at the facesheet to core interface reduced flexural properties and strain energy release rates in panels infused with acrylic resin but did not significantly reduce these properties in epoxy infused facesheets.

Engineering↗
DOE OSTI2020

Mechanical and Thermophysical Properties of 3D-Printed SiC-FY20

In the Transformational Challenge Reactor (TCR), the fuel blocks consist of an additively-manufactured silicon carbide (SiC) matrix and uranium nitride tristructural isotropic (UN TRISO) fuel particles, which are stacked to form fuel columns. The SiC matrix is manufactured using binderjet 3D printing followed by loading the TRISO fuel particles and the chemical vapor infiltration (CVI) process. Because the fuel matrix is a primary component of the TCR core and its response to mechanical and thermal loads during operation is one of the most influential factors on the integrity of TCR core, testing and evaluation have focused on producing mechanical and thermophysical properties data for the binderjet/CVI SiC. Mechanical and thermophysical properties were measured from various types of specimens printed for two or three orientations, which included equibiaxial flexural failure strength, elastic constants, thermal diffusivity and conductivity, density, and the coefficient of thermal expansion. Flexural failure strength datasets showed similar Weibull distributions regardless of sample variants including different orientations. The mean failure strengths of the 3D-printed SiC variants were in the range of 286–306 MPa, which are 22–27% lower than that of the CVD SiC. Thermophysical test results showed that specific heat and thermal expansion are not sensitive to the build directions of SiC samples, while thermal diffusivity is highly dependent on the build direction and can be correlated to the anisotropic character of the 3D-printed SiC. This report also includes discussions on the uniaxial tensile properties of the as-printed SiC before CVI and on ongoing efforts for irradiation effects studies.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2021

Mechanical and Thermophysical Properties of 3D-Printed SiC before and after Neutron Irradiation – FY21

This report presents the mechanical and thermophysical properties of 3D-printed SiC before and after neutron irradiation that have been evaluated to assess the fuel matrix material for the Transformational Challenge Reactor (TCR). The TCR fuel form consists of an additively-manufactured silicon carbide (SiC) matrix and uranium nitride tristructural isotropic (UN TRISO) fuel particles, which is manufactured through a newly developed processing route combining binderjet 3D printing, TRISO fuel particle loading, and chemical vapor infiltration (CVI). Because the fuel matrix is a primary component of the TCR core and its response to mechanical and thermal loads during operation is one of the most influential factors on the integrity of TCR core, testing and evaluation have focused on producing mechanical and thermophysical properties data for the binderjet/CVI SiC. Baseline mechanical and thermophysical properties were measured from the disk specimens printed for different and sizes orientations, which included equibiaxial flexural failure strength, elastic constants, thermal diffusivity and conductivity, density, and the coefficient of thermal expansion. Flexural failure strength datasets showed similar Weibull distributions regardless of sample variants including different orientations. The mean failure strengths of the 3D-printed SiC variants were in the range of 280–310 MPa, which are slightly lower than that of the chemical vapor deposition (CVD) SiC. Thermophysical test results showed that specific heat and thermal expansion are not sensitive to the build direction of SiC samples, while thermal conductivity is highly dependent on the build direction and can be correlated to the anisotropic character of the 3D-printed SiC. Neutron irradiation tests were carried out on the 3D-printed 6-mm diameter SiC disk specimens. Irradiation was carried to 2.3 dpa over a temperature range of 360–880°C. No significant degradation in strength was observed in SiC after irradiations in various conditions and with different orientations. Anisotropy that had been observed in the thermal conductivity of 3D-printed SiC prior to irradiation vanished after irradiation as the irradiation defect thermal resistivity accumulated in the material. Electron microscopy of the microstructure after neutron irradiation showed distinct defect morphologies in the heterogenous material, but no evidence for irradiation-induced cracking or degradation in the microstructure was observed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

Why Firn Quakes

Snow dampens sounds, but anecdotal reports concisely describe audible propagating collapse events—firnquakes—in Antarctic and Arctic snowfields. We propose combining granular and continuum mechanics to form a testable theory for conditioning, triggering, and propagation of firnquakes consistent with scarce data. A central condition for collapse events is unconsolidated firn at depth. As firn grains compact, stresses are transmitted along force chains which carry the overburden and transition into a continuous medium by pressure sintering. This granular legacy creates solid-like supports of denser layers that keep the material below unconsolidated. Dynamic amplification triggers local brittle failure of the supports, which induces a cascade of collapse propagation. Using bulk density from ice cores as proxy for stiffness, we find the flexural wave speed by collapsing supports matches the recorded firnquake velocities on the order of 100 m/s. Our theory is to be tested in firn sheets and other compacting granular materials.

Voigtländer, A. [Lawrence Berkeley National Labora↗
DOE OSTI2022

Equibiaxial Flexure Strength of a Superfine-Grained Nuclear Graphite

The strength of advanced graphite is reported in accordance with ASTM D7846-16 using a two-parameter Weibull distribution for uniaxial strength testing. The rule of thumb for Weibull distributions is to use a minimum of 30 strength measurements to have a high level of confidence in the Weibull characteristic strength and the Weibull modulus. These large sample sets for statistical confidence are easily obtained for as-manufactured graphite, but determination of the Weibull two-factor parameters on graphite that has been exposed to neutron irradiation is nearly impossible due to irradiation testing restraints on specimen size and space limitations in test reactors for the accommodation of specimens. These restrictions have resulted in irradiation programs that use sub-sized specimens to measure uniaxial strength change, but the specimen geometries still hinder the number of replicate specimens for each irradiation condition. In contrast, this work used an advanced ceramic standard, ASTM C1499-05, as the foundation for equibiaxial strength testing of a superfine-grained nuclear graphite to investigate the irradiation-induced strength change and any changes to the two-parameter Weibull distribution. The goal was to investigate the effect of specimen size on the two-parameter Weibull distribution parameters in support of the small specimens and geometry desired for irradiation. A study of the effect of a reduced sample population was also undertaken to investigate the reliability of using the two-parameter Weibull distribution to study changes to the materials properties caused by neutron irradiation damage. The results of this work suggest that these equibiaxial specimens would be ideal for statistically significant studies of the effects of irradiation on the Weibull characteristic strength (but not the modulus) and for providing a method for surveillance specimen campaigns for future operating commercial reactors.

Campbell, Anne↗
DOE OSTI2022

Stability Evaluation for a Damped, Constrained-Motion Cutting Force Dynamometer

This paper describes the dynamic stability evaluation of a constrained-motion dynamometer (CMD) with passive damping. The CMD’s flexure-based design offers an alternative to traditional piezoelectric cutting force dynamometers, which can exhibit adverse effects of the complex structural dynamics on the measurement accuracy. In contrast, the CMD system’s structural dynamics are nominally single degree of freedom and are conveniently altered by material selection, flexure element geometry, and element arrangement. In this research, a passive damping approach is applied to increase the viscous damping ratio and, subsequently, the stability limit. Cutting tests were completed and the in situ CMD displacement and velocity signals were sampled at the spindle rotating frequency. The periodic sampling approach was used to determine if the milling response was synchronous with the spindle rotation (stable) or not (chatter) by constructing Poincaré maps for both experiment and prediction (time-domain simulation). It was found that the viscous damping coefficient was increased by 130% and the critical stability limit was increased from 4.3 mm (no damping) to 15.4 mm (with damping).

36 MATERIALS SCIENCE↗
DOE OSTI2020

Build orientation, surface roughness, and scan path influence on the microstructure, mechanical properties, and flexural fatigue behavior of Ti–6Al–4V fabricated by electron beam melting

In the present work, microstructure and fatigue behavior of Electron Beam Melted (EBM) Ti–6Al–4V have been systematically studied. Fatigue behavior was investigated using four-point bend tests of rectangular bars with internal features fabricated with different build orientations, scan paths, and surface conditions. Microstructural variations were evaluated by optical microscopy and Vickers micro-hardness indentations, both of which were found to be consistent throughout the build and within ranges reported in the literature. The fatigue performance of the EBM material was comparable to wrought Ti–6Al–4V when the loading direction was parallel to the build direction, but severely limited when loaded perpendicular to the build direction or if surface roughness defects were present. Scanning electron microscopy and interrupted fatigue tests were utilized to characterize fracture surfaces, failure mechanisms, crack initiation, and propagation behavior. Crack initiation sites in the vertically-oriented specimens were identified to be melt-related defects formed by insufficient melting.

36 MATERIALS SCIENCE↗