Intrinsic Kinetic Limitations in Substituted Lithium-Layered Transition-Metal Oxide Electrodes
Substituted Li-layered transition-metal oxide (LTMO) electrodes such as Li x Ni y Mn z Co 1-y-z O 2 (NMC) and Li x Ni y Co 1-y-z Al z O 2 (NCA) show reduced first cycle Coulombic efficiency (90-87% under standard cycling conditions) in comparison with the archetypal Li x CoO 2 (LCO; similar to 98% efficiency). Focusing on Li x Ni 0.8 Co 0.15 Al 0.0.5 O 2 as a model compound, we use operando synchrotron X-ray diffraction (XRD) and nuclear magnetic resonance (NMR) spectroscopy to demonstrate that the apparent first-cycle capacity loss is a kinetic effect linked to limited Li mobility at x > 0.88, with near full capacity recovered during a potentiostatic hold following the galvanostatic charge- discharge cycle. This kinetic capacity loss, unlike many capacity losses in LTMOs, is independent of the cutoff voltage during delithiation and it is a reversible process. The kinetic limitation manifests not only as the kinetic capacity loss during discharge but as a subtle bimodal compositional distribution early in charge and, also, a dramatic increase of the charge-discharge voltage hysteresis at x > 0.88. 7 Li NMR measurements indicate that the kinetic limitation reflects limited Li transport at x > 0.86. Electrochemical measurements on a wider range of LTMOs including Li x (Ni,Fe) y Co 1-y O 2 suggest that 5% substitution is sufficient to induce the kinetic limitation and that the effect is not limited to Ni substitution. In this paper, we outline how, in addition to a reduction in the number of Li vacancies and shrinkage of the Li-layer size, the intrinsic charge storage mechanism (two-phase vs solid-solution) and localization of charge give rise to additional kinetic barriers in NCA and nonmetallic LTMOs in general.