NASA NTRS2019

Dust Abrasion Damage on Martian Solar Arrays: Experimental Investigation and Opportunity Rover Performance Analysis

Here we investigate the effects of erosion and weathering that occur on III-V cover-glass interconnected cells (CICs) after exposure to Mars dust storm conditions. The durability of these materials in a Martian environment is not well characterized so we perform analogous experimentation. To replicate the dust impingement, test coupons were placed in an enclosure and sandblasted with Mars dust simulant. We show the J-V response dependency on both incident angle and exposure times. We find that the simulated Martian dust storm often results in damage to the anti-reflective coating and subsequent reduced short circuit current. Reduction in the open circuit voltage is observed, likely caused by structural damage to the crystal lattice after CIC fracture. We employ data-driven modeling to determine a performance degradation rate that is consistent with zero within uncertainty. We also quantify the soiling contribution and power degradation of the photovoltaic cells on Mars through analysis of 4.95 Martian years of report-out power conditions from the Opportunity rover. We find that atmospheric dust suspended due to a weather event does not result in instantaneous settled dust on the PV cells. We calculate via autocorrelation function that the dust settling rate is approximately 21 Sols from atmospheric dust suspension. The findings presented here deliver a realistic approximation for the insolation values and subsequent PV power expected over time on the Martian surface thus informing future dust abatement systems.

McMillon-Brown, Lyndsey↗
NASA NTRS2019

Dust Abrasion Damage on Martian Solar Arrays: Experimental Investigation and Opportunity Rover Performance Analysis

Here we investigate the effects of erosion and weathering that occur on III-V cover-glass interconnected cells (CICs) after exposure to Mars dust storm conditions. The durability of these materials in a Martian environment is not well characterized so we perform analogous experimentation. To replicate the dust impingement, test coupons were placed in an enclosure and sandblasted with Mars dust simulant. We show the J-V response dependency on both incident angle and exposure times. We find that the simulated Martian dust storm often results in damage to the anti-reflective coating and subsequent reduced short circuit current. Reduction in the open circuit voltage is observed, likely caused by structural damage to the crystal lattice after CIC fracture. We employ data-driven modeling to determine a performance degradation rate that is consistent with zero within uncertainty. We also quantify the soiling contribution and power degradation of the photovoltaic cells on Mars through analysis of 4.95 Martian years of report-out power conditions from the Opportunity rover. We find that atmospheric dust suspended due to a weather event does not result in instantaneous settled dust on the PV cells. We calculate via autocorrelation function that the dust settling rate is approximately 21 Sols from atmospheric dust suspension. The findings presented here deliver a realistic approximation for the insolation values and subsequent PV power expected over time on the Martian surface thus informing future dust abatement systems.

McMillon-Brown, Lyndsey↗
NASA NTRSDate not supplied

Martian Dust Abrasion Damage on Solar Arrays: HALT Experimental Investigation and Opportunity Rover Performance Analysis

We explored the utility of ground-based highly accelerated life testing (HALT) on epitaxial lift-off (ELO) triple-junction coverglass interconnected cells (CICs) after exposure to simulated Martian dust storms. Dust storm impingement was replicated by sandblasting CICs with Mars dust simulant replicating conditions similar to the weather conditions reported by the Viking landers. We observed that even in cases when there are no observable open circuit voltage (VOC) losses, the minority carrier lifetime is reduced. Short circuit current (JSC) losses can be recovered upon cleaning, suggesting JSC losses are not linked to permanent damage, like cell cracking. This suggests a permanent degradation could be determined by quantifying the difference between recoverable and non-recoverable power loss. We mined field data from the Mars Exploration Rover, Opportunity and extracted a degradation rate to compare to our experimental data. We found exceptional agreement between 4.9 Martian years of mined field data (9.4%) and the irreversible damage observed in our HALT experiment (9.7%). We demonstrate that the laboratory method for exposing CICs to Martian dust storm conditions well represents the physical reality of long duration CIC operation on Mars.

Lyndsey McMillon-Brown↗