NASA NTRS2009

Use of Atomic Oxygen for Increased Water Contact Angles of Various Polymers for Biomedical Applications

The purpose of this study was to determine the effect of atomic oxygen (AO) exposure on the hydrophilicity of nine different polymers for biomedical applications. Atomic oxygen treatment can alter the chemistry and morphology of polymer surfaces, which may increase the adhesion and spreading of cells on Petri dishes and enhance implant growth. Therefore, nine different polymers were exposed to atomic oxygen and water-contact angle, or hydrophilicity, was measured after exposure. To determine whether hydrophilicity remains static after initial atomic oxygen exposure, or changes with higher fluence exposures, the contact angles between the polymer and water droplet placed on the polymer s surface were measured versus AO fluence. The polymers were exposed to atomic oxygen in a 100-W, 13.56-MHz radio frequency (RF) plasma asher, and the treatment was found to significantly alter the hydrophilicity of non-fluorinated polymers. Pristine samples were compared with samples that had been exposed to AO at various fluence levels. Minimum and maximum fluences for the ashing trials were set based on the effective AO erosion of a Kapton witness coupon in the asher. The time intervals for ashing were determined by finding the logarithmic values of the minimum and maximum fluences. The difference of these two values was divided by the desired number of intervals (ideally 10). The initial desired fluence was then multiplied by this result (2.37), as was each subsequent desired fluence. The flux in the asher was determined to be approximately 3.0 x 10(exp 15) atoms/sq cm/sec, and each polymer was exposed to a maximum fluence of 5.16 x 10(exp 20) atoms/sq cm.

deGroh, Kim↗
NASA NTRS1992

The LDCE Particle Impact Experiment as flown on STS-46

Many materials and techniques have been developed by the authors to sample the flux of particles in Low Earth Orbit (LEO). Though regular in-site sampling of the flux in LEO the materials and techniques have produced data which compliment the data now being amassed by the Long Duration Exposure Facility (LDEF) research activities. Orbital debris models have not been able to describe the flux of particles with d sub p less than or = 0.05 cm, because of the lack of data. Even though LDEF will provide a much needed baseline flux measurement, the continuous monitoring of micron and sub-micron size particles must be carried out. A flight experiment was conducted on the Space Shuttle as part of the LDCE payload to develop an understanding of the Spatial Density (concentration) as a function of size (mass) for particle sizes 1 x 10(exp 6) cm and larger. In addition to the enumeration of particle impacts, it is the intent of the experiment that hypervelocity particles be captured and returned intact. Measurements will be performed post flight to determine the flux density, diameters, and subsequent effects on various optical, thermal control and structural materials. In addition to these principal measurements, the Particle Impact Experiment (PIE) also provides a structure and sample holders for the exposure of passive material samples to the space environment, e.g., thermal cycling, and atomic oxygen, etc. The experiment will measure the optical property changes of mirrors and will provide the fluence of the ambient atomic oxygen environment to other payload experimenters. In order to augment the amount of material returned in a form which can be analyzed, the survivability of the experiment as well as the captured particles will be assessed. Using Sandia National Laboratory's hydrodynamic computer code CTH, hypervelocity impacts on the materials which comprise the experiments have been investigated and the progress of these studies are reported.

Maag, Carl R.↗
NASA NTRS1991

LEO space environmental effects: TRW LDEF experimental trays

Comprised of two identical trays, the TRW Long Duration Exposure Facility (LDEF) experiment (A0054) provided a unique opportunity to study long term space environmental effects on a variety of materials exposed to two different space environments. The leading edge tray saw micrometeors and anthropogenic space debris, ultraviolet radiation, and energetic atomic oxygen. In contrast, the trailing edge tray was exposed to ultraviolet and micrometeors but saw relatively little, if any, space debris fluence and no energetic atomic oxygen. The striking difference in appearance of the two experimental trays is directly attributable to the nonuniformity of the space environment about the LDEF. It is estimated that the majority of the erosion to the Kapton polyimide dielectric material occurred during the last month on orbit due to the sharply nonlinear increase in atomic oxygen number density as orbital altitude decayed over the life of the mission.

Blakkolb, B. K.↗
NASA NTRS1986

Protecting spacecraft from atomic oxygen

Findings are reported from Space Shuttle flights STS-3, 4, 5, and 8 regarding the degradation of materials exposed to atomic oxygen in low earth orbit. Atomic oxygen, a strong oxidizing agent, is present in low concentrations at such altitudes, and a spacecraft can sweep up considerable volumes of it at orbital velocities of 5 miles/s, especially if mission lifetimes are measured in years or decades. Material loss has been found to be a function of the fluence (the number of oxygen atoms striking a unit area of surface over a given period); fluence is proportional to atmospheric density, orbital velocity, surface attitude relative to velocity vector, and duration of exposure. Atmospheric density depends first on altitude and second on the phase of the 11-year solar activity cycle. Metals, in the experiments, reacted less than nonmetals. Graphs and a table are included, permitting calculation of how far a surface of various organic materials will recede on a spacecraft in low earth orbit. The limited data base on atomic oxygen interactions with materials, using both Shuttle flight experiments and ground-based facilities must be augmented. Space Station design is imminent, and the understanding of such interactions is critical to the success of that design.

Leger, L. J.↗
NASA NTRS1985

A consideration of atomic oxygen interactions with space station

A computer model is developed in order to calculate fluence for a generalized spacecraft in orbital flight based on mass spectrometer and incoherent scatter (MSIS) measurements of ambient density. The calculations are used to identify criteria for the selection of materials for the construction of an LEO Space Station. The model is generalized such that the surfaces for study can be oriented in any direction with respect to: a body coordinate system fixed to the spacecraft (E surfaces); and a solar inertial coordinate system. A parametric study was performed in order to evaluate the effects of altitude, inclination, and solar activity on atomic oxygen fluence. Values are obtained for samples of Mylar, Kevlar, Kapton, Tedlar, Teflon and sulfone, as well as for some ethylene polymers. The range of values for material reactivities is from 360 microns for ram-facing surfaces to 200 microns for solar power surfaces during each cycle of solar activity. The possibility of improving reactivity by employing certain chemical coatings is also discussed.

Leger, L. J.↗
NASA NTRS2013

Overview of the MISSE 7 Polymers and Zenith Polymers Experiments After 1.5 Years of Space Exposure

As part of the Materials International Space Station Experiment 7 (MISSE 7), two experiments called the Polymers Experiment and the Zenith Polymers Experiment were flown on the exterior of the International Space Station (ISS) and exposed to the low Earth orbit (LEO) space environment for 1.5 years. The Polymers Experiment contained 47 samples, which were flown in a ram or wake flight orientation. The objectives of the Polymers Experiment were to determine the LEO atomic oxygen erosion yield (Ey, volume loss per incident oxygen atoms, given in cu cm/atom) of the polymers, and to determine if atomic oxygen erosion of high and low ash containing polymers is dependent on fluence. The Zenith Polymers Experiment was flown in a zenith flight orientation. The primary objective of the Zenith Polymers Experiment was to determine the effect of solar exposure on the erosion of fluoropolymers. Kapton H (DuPont, Wilmington, DE) was flown in each experiment for atomic oxygen fluence determination. This paper provides an introduction to both the MISSE 7 Polymers Experiment and the MISSE 7 Zenith Polymers Experiment, and provides initial erosion yield results.

Yi, Grace T.↗
NASA NTRS1995

Degradation of FEP thermal control materials returned from the Hubble Space Telescope

After an initial 3.6 years of space flight, the Hubble Space Telescope was serviced through a joint effort with the NASA and the European Space Agency. Multi-layer insulation (MLI) was retrieved from the electronics boxes of the two magnetic sensing systems (MSS), also called the magnetometers, and from the returned solar array (SA-I) drive arm assembly. The top layer of each MLI assembly is fluorinated ethylene propylene (FEP, a type of Teflon). Dramatic changes in material properties were observed when comparing areas of high solar fluence to areas of low solar fluence. Cross sectional analysis shows atomic oxygen (AO) erosion values up to 25.4 mu m (1 mil). Greater occurrences of through-thickness cracking and surface microcracking were observed in areas of high solar exposure. Atomic force microscopy (AFM) showed increases in surface microhardness measurements with increasing solar exposure. Decreases in FEP tensile strength and elongation were measured when compared to non-flight material. Erosion yield and tensile results are compared with FEP data from the Long Duration Exposure Facility. AO erosion yield data, solar fluence values, contamination, micrometeoroid or debris impact sites, and optical properties are presented.

Zuby, Thomas M.↗
NASA NTRS2017

Genetic Correlation with the DNA Repair Assay in Mice Exposed to High-LET

We hypothesize that DNA damage induced by high local energy deposition, occurring when cells are traversed by high-LET (Linear Energy Transfer) particles, can be experimentally modeled by exposing cells to high doses of low-LET. In this work, we validate such hypothesis by characterizing and correlating the time dependence of 53BP1 radiation-induced foci (RIF) for various doses and LET across 72 primary skin fibroblast from mice. This genetically diverse population allows us to understand how genetic may modulate the dose and LET relationship. The cohort was made on average from 3 males and 3 females belonging to 15 different strains of mice with various genetic backgrounds, including the collaborative cross (CC) genetic model (10 strains) and 5 reference mice strains. Cells were exposed to two fluences of three HZE (High Atomic Energy) particles (Si 350 megaelectronvolts per nucleon, Ar 350 megaelectronvolts per nucleon and Fe 600 megaelectronvolts per nucleon) and to 0.1, 1 and 4 grays from a 160 kilovolt X-ray. Individual radiation sensitivity was investigated by high throughput measurements of DNA repair kinetics for different doses of each radiation type. The 53BP1 RIF dose response to high-LET particles showed a linear dependency that matched the expected number of tracks per cell, clearly illustrating the fact that close-by DNA double strand breaks along tracks cluster within one single RIF. By comparing the slope of the high-LET dose curve to the expected number of tracks per cell we computed the number of remaining unrepaired tracks as a function of time post-irradiation. Results show that the percentage of unrepaired track over a 48 hours follow-up is higher as the LET increases across all strains. We also observe a strong correlation between the high dose repair kinetics following exposure to 160 kilovolts X-ray and the repair kinetics of high-LET tracks, with higher correlation with higher LET. At the in-vivo level for the 10-CC strains, we observe that drops in the number of T-cells and B-cells found in the blood of mice 24 hours after exposure to 0.1 gray of 320 kilovolts X-ray correlate well with slower DNA repair kinetics in skin cells exposed to X-ray. Overall, our results suggest that repair kinetics found in skin is a surrogate marker for in-vivo radiation sensitivity in other tissue, such as blood cells, and that such response is modulated by genetic variability.

cosmic radiation↗
NASA NTRS1989

Working group written presentation: Atomic oxygen

Earlier Shuttle flight experiments have shown NASA and SDIO spacecraft designed for operation in low-Earth orbit (LEO) must take into consideration the highly oxidative characteristics of the ambient flight environment. Materials most adversely affected by atomic oxygen interactions include organic films, advanced (carbon-based) composites, thermal control coatings, organic-based paints, optical coatings, and thermal control blankets commonly used in spacecraft applications. Earlier results of NASA flight experiments have shown prolonged exposure of sensitive spacecraft materials to the LEO environment will result in degraded systems performance or, more importantly, lead to requirements for excessive on-orbit maintenance, with both conditions contributing significantly to increased mission costs and reduced mission objectives. Flight data obtained from previous Space Shuttle missions and results of the Solar Max recovery mission are limited in terms of atomic oxygen exposure and accuracy of fluence estimates. The results of laboratory studies to investigate the long-term (15 to 30 yrs) effects of AO exposure on spacecraft surfaces are only recently available, and qualitative correlations of laboratory results with flight results have been obtained for only a limited number of materials. The working group recommended the most promising ground-based laboratories now under development be made operational as soon as possible to study the full-life effects of atomic oxygen exposure on spacecraft systems.

Leger, Lubert J.↗
NASA NTRS1996

Atomic Oxygen Durability of Second Surface Silver Microsheet Glass Concentrators

Second surface silver microsheet glass concentrators are being developed for potential use in future solar dynamic space power systems. Traditional concentrators are aluminum honeycomb sandwich composites with either aluminum or graphite epoxy face sheets, where a reflective aluminum layer is deposited onto an organic leveling layer on the face sheet. To protect the underlying layers, a SiO2 layer is applied on top of the aluminum reflective layer. These concentrators may be vulnerable to atomic oxygen degradation due to possible atomic oxygen attack of the organic layers at defect sites in the protective and reflective coatings. A second surface microsheet glass concentrator would be inherently more atomic oxygen durable than these first surface concentrators. In addition, a second surface microsheet glass concentrator design provides a smooth optical surface and allows for silver to be used as a reflective layer, which would improve the reflectivity of the concentrator and the performance of the system. A potential threat to the performance of second surface microsheet glass concentrators is atomic oxygen attack of the underlying silver at seams and edges or at micrometeoroid and debris (MMD) impacts sites. Second surface silver microsheet glass concentrator samples were fabricated and tested for atomic oxygen durability. The samples were iteratively exposed to an atomic oxygen environment in a plasma asher. Samples were evaluated for potential degradation at fabrication seams, simulated MMD impact sites, and edges. Optical microscopy was used to evaluate atomic oxygen degradation. Reflectance was obtained for an impacted sample prior to and after atomic oxygen exposure. After an initial atomic oxygen exposure to an effective fluence of approx. 1 x 10(exp 21) atoms/cm(exp 2), oxidation of the silver at defect sites and edges was observed. Exposure to an additional approx. 1 x 10(exp 21) atoms/cm(exp 2) caused no observed increase in oxidation. Oxidation at an impact site caused negligible changes in reflectance. In all cases oxidation was found to be confined to the vicinity of the seams, impact sites, edges or defect sites. Asher to in-space atomic oxygen correlation issues will be addressed.

deGroh, Kim K.↗
NASA NTRS2016

Atomic Oxygen Erosion Yield Dependence Upon Texture Development in Polymers

The atomic oxygen erosion yield (volume of a polymer that is lost due to oxidation per incident atom) of polymers is typically assumed to be reasonably constant with increasing fluence. However polymers containing ash or inorganic pigments, tend to have erosion yields that decrease with fluence due to an increasing presence of protective particles on the polymer surface. This paper investigates two additional possible causes for erosion yields of polymers that are dependent upon atomic oxygen. These are the development of surface texture which can cause the erosion yield to change with fluence due to changes in the aspect ratio of the surface texture that develops and polymer specific atomic oxygen interaction parameters. The surface texture development under directed hyperthermal attack produces higher aspect ratio surface texture than isotropic thermal energy atomic oxygen attack. The fluence dependence of erosion yields is documented for low Kapton H (DuPont, Wilmington, DE) effective fluences for a variety of polymers under directed hyperthermal and isotropic thermal energy attack.

oxygen atoms↗
NASA NTRS1988

Atomic oxygen effects on candidate coatings for long-term spacecraft in low earth orbit

Candidate atomic oxygen protective coatings for long-term low Earth orbit (LEO) spacecraft were evaluated using the Los Alamos National Laboratory O-atom exposure facility. The coatings studied include Teflon, Al2O3, SiO2, and SWS-V-10, a silicon material. Preliminary results indicate that sputtered PTFE Teflon (0.1 micrometers) has a fluence lifetime of 10 to the 19th power O-atoms/cm (2), and sputtered silicon dioxide (0.1 micrometers), aluminum oxide (0.1 micrometers), and SWS-V-10, a silicone, (4 micrometers) have fluence lifetimes of 10 to the 20th power to 10 to the 21st power O-atoms/cm (2). There are large variations in fluence lifetime data for these coatings.

Lan, E. H.↗
NASA NTRS2017

A Spaceflight Experiment to Determine the Effect of Chamfered Sample Holders on Atomic Oxygen Erosion

The exteriors of low Earth orbit (LEO) spacecraft are subjected to many environmental threats that can cause the surface materials to degrade. One of these threats is atomic oxygen (AO), which is formed by photo dissociation of molecular oxygen by energetic UV radiation. Atomic oxygen exposure can result in oxidative erosion of polymers leading to structural or thermal failure of spacecraft components. The amount of AO erosion expected during a mission can be calculated by knowing the AO erosion yield (Ey, volume loss per incident atom) of the material and the AO fluence expected for the mission. The Ey can be determined through dehydrated mass loss measurements of test samples if one knows the AO fluence, density, and exposure area. Such measurements have been made as part of flight experiments, including the Materials International Space Station Experiment 2 (MISSE 2) Polymers Experiment. The MISSE 2 Polymers Experiment sample holders had chamfered circular apertures that controlled the exposure area, but also allowed some additional AO to scatter from the chamfered edges onto the samples thus causing some samples to erode thru and peel at their perimeter due to this scattering effect. By modeling the scattered AO flux one can predict the actual total AO fluence, and hence more accurate sample Ey. Sample holders with different chamfered-perimeter to exposed-area ratios have been designed for future spaceflight experiments that allow a more accurate determination of the Ey for large area polymers, representative of their use on spacecraft surfaces.

Earth Orbital Environments↗
NASA NTRS1991

Atomic oxygen erosion of polymer matrix composites

Results are presented on atomic oxygen erosion of circular tubes and flat plates fabricated from different epoxy matrix composites containing, boron and Kevlar fiber reinforcements. The UTIAS experiment was located at station D-12, at 90 deg to the LDEF leading edge which was yawed about approximately 8 to 10 deg relative to the velocity vector. This resulted in enhanced atomic oxygen exposure at D-12, providing a total fluence of about 4 x 10(exp 20) atoms/sq cm. Thickness loss measurements were obtained for both flat plates and cylindrical tubes. The effect of reflected atomic oxygen on erosion yield and surface morphology on back surfaces (not directly exposed to AO) are graphically demonstrated. Erosion yields are also compared with other space flight data for similar materials, and ground-based tests in the UTIAS AO simulator. The effect of angle of incidence on surface morphology, erosion profiles and thickness losses are presented and the results correlated with simulator tests as well.

Tennyson, R. C.↗
NASA NTRS2014

Effects of Low Earth Orbit on Docking Seal Materials

Spacecraft docking seals are typically made of silicone elastomers. When such seals are exposed to low Earth orbit (LEO) conditions, they can suffer damage from ultraviolet (UV) radiation and atomic oxygen (AO, or monoatomic oxygen, the predominant oxygen species in LEO). An experiment flew on the International Space Station (ISS) to measure the effects of LEO on seal materials S0383-70 and ELA-SA-401 and various mating counterface materials which included anodized aluminum. Samples flown in different orientations received different amounts of UV and AO. The hypotheses were that most of the damage would be from UV, and 10 days or more of exposure in LEO would badly damage the seals. Eighteen seals were exposed for 543 days in ram (windward), zenith (away from Earth), or wake (leeward) orientations, and 15 control samples (not flown) provided undamaged baseline leakage. To determine post-flight leak rates, each of the 33 seals were placed in an O-ring groove of a leak test fixture and pressure tested over time. Resistance temperature detectors (RTDs), pressure transducers, and LabVIEW (National Instruments) programs were used to measure and analyze the temperature and pressure and calculate leakage. Average leakage of control samples was 2.6 x 10(exp -7) lbs/day. LEO exposure did not considerably damage ELA-SA-401. The S0383-70 flight samples leaked at least 10 times more than ELA-SA-401 in all cases except one, demonstrating that ELA-SA-401 may be a more suitable sealing material in LEO. AO caused greater damage than UV; samples in ram orientation (receiving an AO fluence of 4.3 x 10(exp 21) atoms/(sq cm) and in wake (2.9x 10(exp 20) atoms/(sq cm)) leaked more than those in zenith orientation (1.58 x 10(exp 20) atoms/(sq cm)), whereas variations in UV exposure did not seem to affect the samples. Exposure to LEO did less damage to the seals than hypothesized, and the data did not support the conjecture that UV causes more damage than AO.

Leakage↗
NASA NTRS2017

Optical Properties of Ar Ions Irradiated Nanocrystalline ZrC and ZrN Thin Films

Thin nanocrystalline ZrC and ZrN films (less than 400 nanometers), grown on (100) Si substrates at a substrate temperature of 500 degrees Centigrade by the pulsed laser deposition (PLD) technique, were irradiated by 800 kiloelectronvolts Ar ion irradiation with fluences from 1 times 10(sup 14) atoms per square centimeter up to 2 times 10(sup 15) atoms per square centimeter. Optical reflectance data, acquired from as-deposited and irradiated films, in the range of 500-50000 per centimeter (0.06–6 electronvolts), was used to assess the effect of irradiation on the optical and electronic properties. Both in ZrC and ZrN films we observed that irradiation affects the optical properties of the films mostly at low frequencies, which is dominated by the free carriers response. In both materials, we found a significant reduction in the free carriers scattering rate, i.e. possible increase in mobility, at higher irradiation flux. This is consistent with our previous findings that irradiation affects the crystallite size and the micro-strain, but it does not induce major structural changes.

ZrN↗
NASA NTRS2000

Cleaning at the Edge of Science: NASA's Genesis Mission

As part of NASA's continuing exploration of the origins of our solar system, the California Institute of Technology, Jet Propulsion Laboratory, Lockheed Martin Astronautics, Los Alamos National Laboratory, and the Johnson Space Center are working together to develop the Genesis mission to return solar matter for analysis in terrestrial laboratories. These samples will be used to define a baseline for the chemical and isotopic composition of the solar nebula. Deviations from the baseline resulted as the solar system evolved; thus, providing a tracer for materials incorporated into meteorites, comets and planetary bodies. These differences represent "fossil residues" that provide invaluable insight into how the solar nebula evolved to form the planets. We cannot collect a sample of the Sun as we would for a planet; fortunately, solar material comes to us in the form of the solar wind. Ultrapure materials will be exposed at the Earth-Sun L1, outside the Earth's magnetic influence, where solar wind nuclei will be captured for 2 years before returning to Earth in January 2001. The key challenge to obtaining a good sample of solar wind, uncontaminated by terrestrial atoms, is a clean collection surface in a clean sample canister and clean facilities with which to handle the samples for allocation and future reference. The Johnson Space Center QSQ is responsible for contamination control for the mission, for ensuring the cleanliness of collection surfaces and providing a clean environment for their subsequent handling. The level of cleanliness required is high; at the time of analysis (after sample return), the surface contamination by C, N, O must each be less than 10(exp 15) atoms per centimeter squared and for elements other than C, N, O, the number of atoms per centimeter squared of each surface contaminant shall not exceed the estimated solar wind fluence of the species (varies by element between U at approx. 10 (exp 4) atoms per centimeter squared to Fe, Si, Mg, and Ne at approx. 10(exp 12), atoms per centimeter squared). Typical spacecraft assembly is done in class 10,000 cleanrooms. The final cleaning and reintegration of the Genesis payload canister as well as all sample material handling will be done within a class 10 cleanroom using Dryden suits to protect the collector materials from any human debris. Each component is unique, no standard size, shape, material, or precleaning history. We are developing new final cleaning techniques utilizing ultra-pure water to minimize molecular residues on the hardware components.

Stansbery, Eileen K.↗
NASA NTRS1990

Atomic oxygen durability of solar concentrator materials for Space Station Freedom

The findings are reviewed of atomic oxygen exposure testing of candidate solar concentrator materials containing SiO2 and Al2O3 protective coatings for use on Space Station Freedom solar dynamic power modules. Both continuous and iterative atomic oxygen exposure tests were conducted. Iterative air plasma ashing resulted in larger specular reflectance decreases and solar absorptance increases than continuous ashing to the same fluence, and appears to provide a more severe environment than the continuous atomic oxygen exposure that would occur in the low Earth orbit environment. First generation concentrator fabrication techniques produced surface defects including scratches, macroscopic bumps, dendritic regions, porosity, haziness, and pin hole defects. Several of these defects appear to be preferential sites for atomic oxygen attack leading to erosive undercutting. Extensive undercutting and flaking of reflective and protective coatings were found to be promoted through an undercutting tearing propagation process. Atomic oxygen erosion processes and effects on optical performance is presented.

Degroh, Kim K.↗