DOE OSTI2020

Fracture toughness evaluation for thin-shell stainless steel weldment

Integrity of spent nuclear fuel (SNF) interim storage canisters are very important to the safety of the back-end nuclear fuel cycle. Stress corrosion cracking (SCC) potential of interim storage canister has been considered as a high priority. Because no post-weld heat treatment was required for forming these canisters, the high tensile residual stress existed within these canister welds. This can change the fracture resistance capacity significantly as well as increase SCC potential. Due to relative thin shell thickness of a canister weldment, the spiral notch torsion test (SNTT) method of small specimen approach was used to estimate the canister weldment fracture toughness. Most SNTT weldment samples fracture initiation sites are at heat-affected zone (HAZ) regions. The estimated fracture toughness $J_Q'$ for the baseline SS304 steel is at 283 kJ/m 2 . The estimated $J_Q'$ for the SS304/308 weld from HAZ and weld specimens are 126 kJ/m 2 and 148.9 kJ/m 2 , respectively.

36 MATERIALS SCIENCE↗
NASA NTRS2003

Strength, Fracture Toughness, and Slow Crack Growth of Zirconia/alumina Composites at Elevated Temperature

Various electrolyte materials for solid oxide fuel cells were fabricated by hot pressing 10 mol% yttria-stabilized zirconia (10-YSZ) reinforced with two different forms of alumina particulates and platelets each containing 0 to 30 mol% alumina. Flexure strength and fracture toughness of platelet composites were determined as a function of alumina content at 1000 C in air and compared with those of particulate composites determined previously. In general, elevated-temperature strength and fracture toughness of both composite systems increased with increasing alumina content. For a given alumina content, flexure strength of particulate composites was greater than that of platelet composites at higher alumina contents (greater than or equal to 20 mol%), whereas, fracture toughness was greater in platelet composites than in particulate composites, regardless of alumina content. The results of slow crack growth (SCG) testing, determined at 1000 C via dynamic fatigue testing for three different composites including 0 mol% (10-YSZ matrix), 30 mol % particulate and 30 mol% platelet composites, showed that susceptibility to SCG was greatest with SCG parameter n = 6 to 8 for both 0 and 30 mol% particulate composites and was least with n = 33 for the 30 mol% platelet composite.

Choi, Sung R.↗
DOE OSTI2021

Fracture Toughness Characterization of Generation II FeCrAl Alloys after ~18 dpa Irradiation

FeCrAl alloys are promising candidate materials for the accident tolerant fuel (ATF) cladding applications due to their excellent corrosion resistance to the elevated temperature steam environment. Currently, the handbook on FeCrAl material properties contains only limited data regarding the fracture toughness properties of any FeCrAl alloy. This includes alloys currently under investigation within the Advanced Fuels Campaign (AFC) at Oak Ridge National Laboratory (ORNL). In this project, a series of irradiation capsules have been irradiated in the High Flux Isotope Reactor (HFIR) at ORNL with two Generation II FeCrAl candidate alloys, i.e., C06M and C36M, to assess the fracture response of these alloys after neutron irradiation. These alloys represent the “book-end” compositions for C26M, the alloy currently being developed as the leading candidate for LWR cladding. A total of six irradiation capsules were irradiated in HFIR at target temperatures of 200°C, 330°C, and 500°C up to target damage doses of 8 displacements per atom (dpa) and 16 dpa. These damage doses represent the expected middle and end of life damage levels for typical LWR cladding while the irradiation temperature regimes will provide insight into the role of varying microstructural features on the fracture toughness properties of neutron irradiated FeCrAl alloys. To date, irradiation of all capsules has been completed in HFIR. This report summarizes the latest results of microhardness and fracture toughness PIE for the 16 dpa capsules (FCAB2, FCAB4, and FCAB6), for which the measured irradiation conditions were: 204°C/17.6dpa, 343°C/18.3dpa, and 507°C/18.6dpa. The main conclusions of this study can be summarized as follows: 1) After the 204°C/17.6dpa irradiation, both C06M and C36M exhibited significant irradiation hardening and embrittlement 2) After the 343°C/18.3dpa irradiation, both C06M and C36M exhibited small irradiation hardening without irradiation embrittlement 3) After the 507°C/18.6dpa irradiation, both C06M and C36M exhibited irradiation softening without irradiation embrittlement 4) Comparing the microhardness and Master Curve reference temperature T 0q before and after neutron irradiation, we did not observe a linear correlation between the two parameters for both C06M and C36M. This should be mainly due to a flat response of the Master Curve reference temperature T 0q to the irradiations at 166-204°C and 315-343°C ranges 5) C06M showed a lower T 0q , meaning better toughness, than C36M at the unirradiated condition and such trend was kept even after neutron irradiation except for the 166-204°C irradiation where both materials had similar T 0q . 6) In terms of hardening and embrittlement, the irradiation effect on both C06M and C36M appeared to saturate after an irradiation dose of 7 dpa.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Effect of Specimen Thickness on Fracture Toughness and Plane Stress to Plane Strain Transition in Medium-Density Polyethylene

This study investigates the effect of specimen thickness on fracture toughness and the transition from plane stress to plane strain conditions in Medium-Density Polyethylene (MDPE) using Single Edge Notched Bend (SENB) specimens. Three thickness groups (7.5 mm, 9.0 mm, and 12.1 mm) were tested following ASTM D5045 protocol. Conditional stress intensity factors (KQ) increased from 2.2 MPavm to 2.8 MPavm with increasing thickness, demonstrating significant size dependency. Confocal microscopy revealed a 34% reduction in maximum crack tip opening displacement (CTOD) from 0.478 mm to 0.314 mm as thickness increased, with plastic zone lateral extent decreasing by 32%. This quantitative evidence validates Irwin's theoretical prediction of plastic zone size transition from plane stress r_y˜ (1/2p) (K_I/s_y )^2 to plane strain conditions r_y˜ (1/6p) (K_I/s_y )^2.Scanning electron microscopy confirmed progressive suppression of shear lips and evolution from ductile tearing with extensive polymer chain drawing in thin specimens to localized crazing in thick specimens. Despite all specimens satisfying the ASTM D5045 criterion (B = 2.5(KQ/s_y )^2 ) ,residual shear lips persisted even in the thickest specimens, demonstrating that nominal size requirements alone are insufficient for achieving complete plane strain conditions in highly ductile polymers. The findings emphasize the necessity of integrated analytical and morphological assessment for valid fracture toughness characterization, with critical implications for life assessment and integrity prediction in thick-section polymer components such as natural gas distribution pipelines.

Medium-Density Polyethylene↗
NASA NTRS1985

Fracture toughness of hot-pressed beryllium

This paper presents the results of an investigation into the fracture toughness, sustained-load flaw growth, and fatigue-crack propagation resistance of S200E hot-pressed beryllium at room temperature. It also reviews the literature pertaining to the influence of various factors on the fracture toughness of hot-pressed beryllium determined using fatigue-cracked specimens.

Lemon, D. D.↗
NASA NTRS1992

Effect of fiber orientation on the fracture toughness of brittle matrix composites

The effective fracture toughness of brittle matrix materials can be increased through the addition of short, poorly bonded fibers which bridge the growing crack. The orientation distribution of the fibers is likely to be biased, and not in an ideal random or aligned state. A micromechanical model is formulated for the postcracking behavior using the force-displacement relation for an arbitrary fiber bridging a crack, the fiber orientation density function, and the fiber location density function. This model is then used to determine an effective traction law for the bridging fibers, as well as the steady state bridging toughness increment. In most cases, the results may be placed in the form of a product of the aligned fiber results times a modifying integrated orientation factor. The frictional shear stress on fiber pull-out is allowed to vary during pull-out, modeling the effects of matrix breakdown, fiber surface smoothing or wear debris accumulation. Results are presented for a variety of representative planar and three-dimensional fiber orientation states.

Jain, L. K.↗
NASA NTRS1976

Heavy section fracture toughness screening specimen

Size requirements for a pin loaded double edge notch + crack tension specimen proposed for fracture toughness screening heavy section alloys were studied. Ranking of eight selected alloys based on the specimen's net strength was compared with that based on the valid plane strain fracture toughness separately determined. Performance of the specimen was judged on the basis of that comparison. The specimen's net strength was influenced by three critical specimen dimensions: distance between the crack plane and the loading hole, specimen width, and specimen thickness. Interaction between the stress fields of the crack and the loading holes reduced the net strength, but this effect disappeared as the separation reached a dimension equal to the specimen width. The effects of specimen width and thickness are interrelated and affect the net strength through their influence on the development of the crack tip plastic zone.

Shannon, J. L., Jr.↗
NASA NTRS1989

Effects of aging condition on the fracture toughness of 2XXX and 7XXX series aluminum alloy composites

Results are presented on the effects of matrix aging condition (i.e., matrix temper) on the fracture toughness of 2XXX and 7XXX Al matrix alloys reinforced with SiC particulates, and the results are compared with the mechanical behavior. Fracture toughness testing was conducted on fatigue precracked bend specimens, and fracture surfaces were examined using SEM. Results revealed dramatic differences in the effect of matrix microstructure on the fracture properties of the two composite series. In the 7XXX material, the toughness values decreased from the underaged (UA) condition to the overaged (OA) condition by approximately 40 percent, while in the 2XXX series composite, the effect of matrix microstructure was marginal. In the 7XXX series composites, a transition in fracture mode from particle cracking (in UA) to matrix and linear-interface failure (in OA) was observed, while the 2XXX series composite failed predominantly by particle cracking.

Manoharan, M.↗
NASA NTRS1989

Aging effects on the fracture toughness of SiC whisker reinforced 2XXX aluminum alloys

The effect of aging (at 150 C) time on the fracture toughness behavior of a 2XXX alloy (Al-3.55Cu-1.29Mg-0.01Fe-trace Mn) reinforced with 5 vol pct F-8 SiC whiskers was investigated by measuring hardness and electrical conductivity followed by fracture toughness tests on center-cracked specimens. The ageing time-hardening response plots showed that, independent of whisker orientation, the initial rapid increase in hardness was followed by a more gradual increase, with a broad hardness peak between 32 and 128 hrs of aging. Coincident with the hardness changes, the electrical conductivity initially decreased, reached a minimum, and then increased at aging times beyond 32 hrs. Examination by SEM indicated that the initial increase in hardness and decrease in conductivity was due to the GPB zone formation, while the subsequent increase in electrical conductivity and decrease in hardness (overaging) was due to S nucleation and growth.

Ratnaparkhi, P. L.↗
NASA NTRS1980

Increased fracture toughness of graphite-epoxy composites through intermittent interlaminar bonding

The objective of this study was to increase the fracture toughness of multilayer continuous-filament graphite-epoxy composites. The method used is intermittent interlaminar bonding which can lead to a large increase in the fracture surface area. Intermittent bonding was achieved through introduction of thin perforated Mylar between the layers of the composite. For the optimum condition, fracture toughness was increased from about 100 kJ/sq m for untreated specimens to an average of about 500 kJ/sq m, while tensile strength dropped from 500 MPa to 400 MPa, and elastic modulus remained the same at about 75 GPa. An approximate analysis is presented to explain the improvement in toughness.

Jea, L.-C.↗
NASA NTRS1988

Fracture toughness computational simulation of general delaminations in fiber composites

A procedure is described to computationally simulate composite laminate fracture toughness in terms of strain energy release rate. It is also used to evaluate the degradation in laminate structural integrity in terms of displacements, loss in stiffness, loss in vibration frequencies and loss in buckling resistance. Specific laminates are selected for detail studies in order to demonstrate the generality of the procedure. These laminates had center delaminations, off-center delaminations, and pocket delaminations (center and off-center) at the free-edge and center delaminations at the interior. The laminates had two different thicknesses and were made from three different materials. The results obtained are presented in graphical form to illustrate the effects of delamination on the laminate structural integrity and on the laminate strain energy release rate (composite fracture toughness).

Wilt, T. E.↗
NASA NTRS1975

An investigation of fracture toughness, fatigue-crack growth, sustained-load flaw growth, and impact properties of three pressure vessel steels

The elastic fracture toughness of the three steels is shown to not decrease significantly with decreasing temperature from room temperature to about 244 K (-20 F.). The elastic fracture toughness of the three steels increased with increasing specimen width and thickness. The fatigue-crack-growth data for all three steels fall into relatively narrow scatter bands on plots of rate against stress-intensity range. An equation is shown to predict the upper bounds of the scatter bands reasonably well. Charpy impact energies decreased with decreasing temperature in the nominal temperature range from room temperature to 244 K (-20 F). The nil-ductility temperatures of the steels are discussed.

Hudson, C. M.↗
NASA NTRS1988

Fracture toughness computational simulation of general delaminations in fiber composites

A procedure is described to computationally simulate composite laminate fracture toughness in terms of strain energy release rate (SERR). It is also used to evaluate the degradation in laminate structural integrity in terms of displacements, loss in stiffness, loss in vibration frequencies and loss in buckling resistance. Specific laminates are selected for detail studies in order to demonstrate the generality of the procedure. These laminates had center delaminations, off-center delaminations, and pocket delaminations (center and off-center) at the free-edge and center delaminations at the interior. The laminates had two different thicknesses and were made from three different materials. The results obtained are presented in graphical form to illustrate the effects of delamination on the laminate structural integrity and on the laminate strain energy release rate (composite fracture toughness).

Murthy, P. L. N.↗
NASA NTRS1976

Effect of minor reactive metal additions on fracture toughness of iron: 12-percent nickel alloy at-196 deg and 25 deg C

The slow bend precracked Charpy fracture toughness and tensile behavior of arc-melted and hot-rolled Fe-12Ni alloys containing up to 4 atomic percent reactive metal additions were determined at -196 C and 25 C after water quenching from three annealing temperatures. The fracture toughness of Fe-12Ni at -196 C was improved by small amounts of Al, Ce, Hf, La, Nb, Ta, Ti, V, Y, and Zr, but not by Si. Cryogenic toughness was improved up to 7.5 times that of binary Fe-12Ni and varied with the reactive metal, its concentration, and the annealing temperature.

Witzke, W. R.↗
NASA NTRS1997

Composite Interlaminar Shear Fracture Toughness, G(sub 2c): Shear Measurement of Sheer Myth?

The concept of G2c as a measure of the interlaminar shear fracture toughness of a composite material is critically examined. In particular, it is argued that the apparent G2c as typically measured is inconsistent with the original definition of shear fracture. It is shown that interlaminar shear failure actually consists of tension failures in the resin rich layers between plies followed by the coalescence of ligaments created by these failures and not the sliding of two planes relative to one another that is assumed in fracture mechanics theory. Several strain energy release rate solutions are reviewed for delamination in composite laminates and structural components where failures have been experimentally documented. Failures typically occur at a location where the mode 1 component accounts for at least one half of the total G at failure. Hence, it is the mode I and mixed-mode interlaminar fracture toughness data that will be most useful in predicting delamination failure in composite components in service. Although apparent G2c measurements may prove useful for completeness of generating mixed-mode criteria, the accuracy of these measurements may have very little influence on the prediction of mixed-mode failures in most structural components.

OBrien, T. Kevin↗
NASA NTRS1968

Survey of fracture toughness test methods

Comprehensive survey presents current methods of fracture toughness testing that are based on linear elastic fracture mechanics. General principles of the basic two dimensional crack stress field model are discussed in relation to real three dimensional specimens. Methods of test instrumentation and procedure are described.

Brown, W. F., Jr.↗
NASA NTRS1989

Effect of particle size on fracture toughness of SiC/Al composite material

Discontinuous SiC/Al composites with SiC particles of different sizes were fabricated in order to study the role of particle size on the fracture process. The fracture process is confined to a very narrow band and takes place within the matrix in composites containing small SiC particle sizes. In the composite reinforced with SiC particles of 20 microns and above fracture of SiC begins to dominate. The matrix is influenced by the high density of dislocations generated at SiC/Al interfaces due to the difference in coefficient of thermal expansion between SiC and the Al matrix. Crack initiation fracture toughness does not depend on SiC particle size. Crack growth fracture toughness increases as the size of the SiC particle increase.

Flom, Y.↗