Thermally Insulating Transparent Barrier (THINNER) coatings on single pane windows
Conventional silica aerogel monoliths can provide remarkable thermal insulation but the presence of large pores (> 30 nm) tends to scatter visible light and render the material opaque or translucent instead of transparent. In addition, they are prone to cracking during synthesis and handling which makes them difficult to integrate in products and in particular in window solutions. This project developed two new solgel synthesis methods using silica precursors or preformed silica nanoparticles and ambient drying to produce mesoporous organo-silica monoliths. The monoliths were (i) thermally insulating, (ii) optically transparent, (iii) flexible, and (iv) hydrophobic. They feature porosity ranging from 50% to 90% with narrow pore size distribution with pore less than 20 nm resulting in excellent optical clarity (haze < 2%) and very low thermal conductivity (< 30 mW/mK). Interestingly, not only porosity but also pore size and mass fractal dimension were found to affect the thermal conductivity of the mesoporous silica. The superior transparency of the monoliths was shown to be attributed to dependent scattering among silica nanoparticles. Flexibility was achieved through trimethylchlorosilane surface modification. Furthermore, process scale-up and integration of the ambigel monoliths into window solutions using optically clear adhesives were also demonstrated in 6”x6” double-pane windows. The aerogel and the window solution were shown to be durable to accelerated aging under UV, moisture, and/or temperature gradient and thermal cycling. Overall, the window solution achieved the technical performance and the cost target of $10/sqft set for the SHIELD program. However, scaling to industry relevant scale (> 10’x10’) remains a challenge due to requirements on the drying process and fume hood size and to the propensity of large aerogel slab to crack during drying.