Assessment of buffer-IPyC thermomechanical debonding behavior using new experimental strength data in BISON
TRIstructural ISOtropic (TRISO) fuel is a nuclear fuel commonly used in High Temperature Gas-cooled Reactors (HTGRs). A single sub-millimeter-diameter TRISO fuel particle consists of a spherical fuel kernel surrounded by four coating layers: a low-density pyrocarbon buffer layer, an inner pyrolytic carbon (IPyC) layer, a silicon carbide (SiC) layer, and an outer pyrolytic carbon (OPyC) layer. The kernel is commonly made of UO2 or a mixture of uranium carbide and uranium oxide (UCO). During reactor operation, the TRISO coating layers are subjected to irradiation-induced dimensional changes and the associated thermomechanical behavior of each layer. One of the observed behaviors is gap formation between the buffer and IPyC layer due to the porous buffer’s irradiation-induced shrinkage exceeding that of the IPyC layer. Not all irradiated particles will experience buffer-IPyC gap formation. The debonding may be partial, or it may be nearly total. However, from post-irradiation examination of UCO TRISO fuels irradiated as part of the Advanced Gas Reactor (AGR) Fuel Development and Qualification Program, it was concluded that partial buffer-IPyC debonding was the most common type of buffer-IPyC interaction. To predict TRISO thermomechanical performance, multi-physics models have been built that are being continually updated and refined. The BISON code is a finite element-based nuclear fuel performance code that may be used for 1D, 2D, and 3D TRISO particle simulations. This code is used to calculate fuel temperature, kernel swelling, buffer densification, thermal and irradiation creep, fracture, and fission gas production and release. One of the recent additions to the BISON code is the ability to model the process of layer debonding. This paper will focus on the simulation results of the improved BISON debonding model that will utilize updated strengths measured from irradiated AGR TRISO fuel particles. The new experimental strength data from micromechanical tests of irradiated TRISO fuel samples were exercised in the BISON simulations and compared to baseline strength data to assess their applicability in the models. This also includes updated buffer-IPyC bond strengths to simulate layer delamination. Based on current experimental observations it is noted that the buffer-IPyC separation occurs not exactly at the junction of these two layers, but more on the side of the buffer layer. That observation is also implemented in the TRISO interface debonding model. This improved modeling approach using experimental strength data to characterize buffer-IPyC debonding and its potential subsequent cracking will be presented in the paper along with comparisons to available experimental observations.