The growth of small corrosion fatigue cracks in alloy 2024

The corrosion fatigue crack growth characteristics of small surface and corner cracks in aluminum alloy 2024 is established. The damaging effect of salt water on the early stages of small crack growth is characterized by crack initiation at constituent particle pits, intergranular microcracking for a less than 100 micrometers, and transgranular small crack growth for a micrometer. In aqueous 1 percent NaCl and at a constant anodic potential of -700 mV(sub SCE), small cracks exhibit a factor of three increase in fatigue crack growth rates compared to laboratory air. Small cracks exhibit accelerated corrosion fatigue crack growth rates at low levels of delta-K (less than 1 MPa square root of m) below long crack delta-K (sub th). When exposed to Paris regime levels of crack tip stress intensity, small corrosion fatigue cracks exhibit growth rates similar to that observed for long cracks. Results suggest that crack closure effects influence the corrosion fatigue crack growth rates of small cracks (a less than or equal to 100 micrometers). This is evidenced by similar small and long crack growth behavior at various levels of R. Contrary to the corrosion fatigue characteristics of small cracks in high strength steels, no pronounced chemical crack length effect is observed for Al by 2024 exposed to salt water.

Piascik, Robert S.↗

Advanced 3D characterisation of iodine induced stress corrosion cracks in zirconium alloys

Highlights: • Macroscopic crack direction is affected by metallurgical state. • High resolution XCT reveals complex crack morphology. • 3D-EBSD used to fully characterise attacked grain boundaries. • Evidence of iodine segregation ahead of a crack tip. - Abstract: In this study, a range of advanced techniques have been used to characterise iodine-induced stress corrosion cracks, and investigate their interaction with microstructure in zirconium alloys used as cladding material in nuclear power reactors. C-ring samples, machined from cladding tubes in a recrystallised and cold worked condition, were subjected to compressive stress while submerged in an iodine-ethanol solution to simulate stress corrosion cracks arising from pellet cladding interaction. The complex morphology of these stress corrosion cracks was imaged in 3D using X-ray computed tomography (XCT), and subsequent analysis using both 2D and 3D electron backscatter diffraction (EBSD) allowed for the interaction of these cracks with microstructure to be investigated. Intergranular cracking modes were observed to dominate in the recrystallised microstructure, resulting in cracking in the radial direction with variations on the order of the grain size. Crack propagation in the cold worked microstructure was observed to be correlated with the direction of the elongated grains, resulting in a more tangential crack path with less local variation and a microstructure potentially more susceptible to iodine-induced stress corrosion cracking. 3D-EBSD using serial sectioning allows for the determination of the full five-parameter grain boundary description, and opens up the possibility of a statistical analysis of susceptible boundaries to SCC. Nanoscale secondary ion mass spectrometry (NanoSIMS) was also used to map the chemical distribution in the crack tip region and provides possible evidence of iodine segregation ahead of the crack tip. The results provide new insight into crack propagation mechanisms in recrystallised and cold worked microstructures, and pave the way for a more mechanistic understanding of crack propagation through advanced characterisation of iodine-induced stress corrosion cracks in zirconium alloys.

36 MATERIALS SCIENCE↗

Development of a Thin Film Primary Surface Heat Exchanger for Advanced Power Cycles

This project objective is to develop a high-temperature design upgrade for an existing primary surface heat exchanger so that the redesigned hardware is capable of operation in CO 2 at temperatures up to 1,510°F (821°C) and pressure differentials up to 130 psi (9 bar). The heat exchanger is proposed for use as a recuperator in an advanced low-pressure oxy-fuel Brayton cycle that is predicted to achieve over 50% thermodynamic efficiency, although the heat exchanger could also be used in other high-temperature, low-differential pressure cycles. This report describes the progress to date, which includes continuing work performed to select and test new candidate materials for the recuperator redesign, final mechanical and thermal performance analysis results of various redesign concepts, and the preliminary design of a test loop for the redesigned recuperator including a budgetary estimate for detailed test loop design, procurement, and test operation. A materials search was performed in order to investigate high-temperature properties of many candidate materials, including high-temperature strength and nickel content. These properties were used to rank the candidate materials, resulting in a reduced list of nine materials for corrosion testing. Multiple test rigs were considered and analyzed for short-term corrosion testing and Thermal Gravimetric Analysis (TGA) was selected as the most cost-effective option for evaluating corrosion resistance of the candidate materials. In addition, tantalum, niobium, and chromium coatings were identified as potential options for increased corrosion resistance. The test results show that many materials exhibit relatively low weight gain rates, and that niobium and tantalum coatings may improve corrosion resistance for many materials, while chromium coatings appear to oxidize and debond quickly. Metallurgical analysis of alloys was also performed, showing evidence of intergranular attack in 282 that may cause long-term reliability problems in CO 2 service at these temperatures. However, long-term testing in a flowing environment is recommended in order to understand accurately the severity of the attack. Detailed economic modeling of the existing air cycle recuperator and CO 2 cycle recuperator options was also completed, including costs for material, fabrication, fuel, maintenance, and operation. The analysis results show that the increased capital cost for high-temperature materials may be offset by higher cycle efficiencies, decreasing the overall lifetime cost of the system. The economic analysis also examines costs associated with increased pressure drop and material changes for two redesign options. These results show that, even with slightly reduced performance and/or higher material costs, the lifetime cost per energy production may still be reduced by over 12%. The existing recuperator design information was provided by Solar Turbines, Inc. via several models, drawings, and design handoff meetings. Multiple fluid/thermal and structural models were created in order to analyze critical recuperator performance and mechanical strength in critical areas throughout the redesign process. These models were analyzed for a baseline condition (consistent with current Mercury 50 operation) for validation purposes. Results are presented for heat transfer coefficients and pressure drops, matching well with the existing operational data. Simulation of higher-temperature CO 2 conditions was also performed, showing a slight expected increase in both heat transfer and pressure drop. Mechanical analysis results for critical areas on the cross-flow and counter-flow sheets have also been obtained for air and CO 2 cases. These results show similar stresses in both cases but significantly reduced safety factors for the CO 2 case due to reduced yield and creep rupture strengths of alloy 625 at the higher temperatures. A concept brainstorm session and initial down-selection were completed in order to identify promising redesign options for further analysis. Detailed analysis of all promising redesign options was performed via finite element and computational fluid dynamic simulations in order to characterize mechanical and thermal-fluid performance of each option. These options included material change, various sheet thickness configurations, pitch and phasing of cross-flow and counter-flow sheets, and separator sheets. The analysis results have identified two viable redesign options that maintain existing safety margins optimally through a material change to Haynes 282 and (A) sheet thickness increases of 40% on the counter-flow sheet and 75% on the hot side cross-flow corrugation sheet or (B) addition of a separator sheet in the counter-flow section while maintaining the original counter-flow sheet thickness and increasing the cross-flow corrugation sheet thickness by 90% to account for the increase in cell height. While both options satisfy mechanical stress constraints, the separator sheet design has a higher part count, slightly reduced heat transfer, and slightly higher pressure drop than the first option and is not preferred. Finally, several test loop concepts have been developed for different full-scale and reduced-scale recuperator testing options. For each option, various loop components, such as heat exchangers, valves, heaters, and compressors, were evaluated in an effort to maximize utilization of existing resources. All concepts utilize an existing 3-MW CO 2 compressor, heater, and loop coolers, but the concepts vary by incorporating different amounts of new equipment for achieving various flow rates (all concepts operate at design pressure and temperature). The third concept achieves a 1 kg/s test without purchasing any costly equipment (coolers, heaters, blowers, etc.). Since the stacked cell design of the recuperator results in the same flow conditions at each core cell (even for a reduced-scale test). Thus, test loop Concept #3 was selected for the preliminary design. This loop design is detailed within the report, culminating in a budgetary estimate of $1,013,000.00 for the detailed design, construction, commissioning, and operation of a high-temperature recuperator test loop.

03 NATURAL GAS↗

Characterization of SCC Initiation Precursors in Cold-Worked Alloy 690

Due to its superior resistance to corrosion and stress corrosion cracking (SCC), high Cr, Ni-base Alloy 690 is now commonly used in pressurized water reactors (PWRs). Even though highly cold-worked (CW) Alloy 690 has been shown to be susceptible to SCC crack growth in PWR primary water environments, an open question remains whether SCC initiation was possible for these materials under constant load test conditions. Testing has been performed on a series of CW alloy 690 CRDM tubing specimens at constant load for up to 9,220 hours in 360°C simulated PWR primary water. A companion paper will discuss the overall testing approach and describe results on different alloy 690 heats and cold work levels. The focus of the current paper is to illustrate the use of focused ion beam (FIB), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for the high-resolution investigation of precursor damage and intergranular (IG) crack nucleation in these specimens. Three-dimensional (3D) FIB/SEM imaging has been conducted on a series of grain boundary (GB) damage precursors, such as IG small cavities, local corrosion and even shallow cracks observed at the specimen surface. Contrast variations and EDS mapping were used to distinguish oxides, carbides and cavities from the matrix material. Nanometer-sized cavities were observed associated with GB carbides in the highly CW specimens. Shallow IG cracks were present in the 30%CW specimens and exhibited oxidized crack flanks and a higher density of cavities ahead of the oxide front in all cases. The shape and distribution of carbides and cavities in the plane of the cracked GBs was analyzed in 3D to gain a mechanistic understanding of the processes that may be leading to crack initiation in highly CW alloy 690.

3D FIB/SEM↗

EFFECTS OF LASER SHOCK PEENING ON SCC BEHAVIOR OF ALLOY 600

In this study, the effects of laser shock peening (LSP) on stress corrosion cracking (SCC) behavior of Alloy 600 in tetrathionate solution were investigated. The degree of sensitization was quantified using double loop electrochemical potentiokinetic reactivation (DLEPR) tests. The sensitized Alloy 600 was demonstrated to be susceptible to intergranular SCC in tetrathionate solution. Following LSP, residual stresses and the amount of plastic strain introduced in Alloy 600 were characterized. The effects of LSP on SCC susceptibility of Alloy 600 in tetrathionate solution were evaluated by slow strain rate tests and constant load tests. Results indicate a significant increase in resistance to crack initiation and decreased susceptibility to SCC after LSP.

36 MATERIALS SCIENCE↗

Acid Solutions for Etching Corrosion-Resistant Metals

New study characterized solutions for etching austenitic stainless steels, nickel-base alloys, and titanium alloys (annealed). Solutions recommended for use remove at least 0.4 mil of metal from surface in less than an hour. Solutions do not cause intergranular attack on metals for which they are effective, when used under specified conditions.

Simmons, J. R.↗

Etchants for Some Corrosion-Resistant Metals

Solutions that etch some corrosion-resistant metals described in test report. Etchants selected remove at least 0.4 mil of surface material per hour from nickel alloys, austenitic stainless steel, and annealed titanium alloys, without intergranular attack.

Simmons, J.↗

Performance of Structural Alloys in Bio-oil Production, Upgrading, and Storage Systems

Selection of corrosion-resistant, cost-effective structural materials for the process and containment vessels required for the production, upgrading, and storage of biomass-derived oils has been the subject of study in our laboratory for many years. The wide variety of biomass resources and the many liquefaction techniques and processing conditions result in products with a broad range of properties and compositions. Here, this paper will address the materials issues in three distinct areas. In production, materials are exposed to temperatures that range from 350 to 550 °C depending upon the process. Generally, austenitic stainless steels have performed reasonably well, although thicker oxide scales and intergranular attack have sometimes been observed. For storage and transport of the bio-oil products, temperatures experienced by the containment materials are not expected to exceed 50 °C. Our studies have shown that most raw bio-oils contain significant concentrations of organic acids, and low-molecular-weight organic acids were quite corrosive to carbon and low alloy steels. For some applications, subsequent processing is required, which includes hydrotreating or co-processing with a petroleum-derived liquid. These processes utilize a catalyst that requires periodic retreatment with a sulfidizing gas, and the exposure to this gas at elevated temperatures can cause appreciable corrosion to the more common austenitic stainless steels. The materials considered most cost-effective and sufficiently corrosion-resistant for each of these environments were identified.

36 MATERIALS SCIENCE↗

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

Low alloy SA508 bainitic steel is often welded to 300 series austenitic stainless steel in nuclear power plants. These dissimilar metal weldments use 309L butter applied to the low alloy steel and 308L groove filler material to join the 309L to austenite. High alloy steels (such as the 308L and 309L material used here) have been identified as having greater susceptibility to irradiation-assisted stress corrosion cracking (IASCC). Evidence is presented here of cracking under tensile loads in 309L weldment butter in LWR hydrothermal conditions that correlates irradiation induced changes at δ ferrite–γ austenite phase boundaries and γ–γ grain boundaries; specifically intergranular Cr 23 C 6 precipitates. Cracking is not observed in irradiated 308L groove filler under the same conditions. Both the 309L butter and 308L filler material have a duplex or mixed δ–γ phase microstructure due to solidification during the welding procedure. We have performed constant extension rate autoclave immersion tests in BWR normal water chemistry hot water (288 °C, 10 MPa, 2000 wt. ppb dissolved oxygen, <100 nS/cm conductivity, neutral pH) of proton irradiated (2 MeV, approximately 3 displacements per atom at a depth of 10 μm) tensile specimens. Proton irradiation to the dpa levels used here induced Cr 23 C 6 carbide precipitation at γ–γ grain boundaries and δ–γ phase boundaries in the 309L butter but not the 308L filler. Cracking was observed in the proton-irradiated volume of 309L at these interfaces in the vicinity of the Cr 23 C 6 precipitates. We hypothesis the SA508 is the source of carbon in the 309L butter. Cr depletion at γ–γ grain boundaries was also observed and may also be a root cause of cracking. Furthermore, the 309L butter is under significant tensile residual stress in the weldment that adds to applied tensile loads and this too may be a contributing factor.

309L weld butter↗

Quantitative linkage between the stress at dislocation channel – Grain boundary interaction sites and irradiation assisted stress corrosion crack initiation

Localized deformation has emerged as a key factor in the crack initiation process for irradiated steels, as cracks are observed to nucleate preferentially at these sites. Using high resolution electron backscatter diffraction (HREBSD), the local stress tensor surrounding the dislocation channel-grain boundary interaction sites was quantified and coupled with fully determined grain boundary plane orientation information to determine, for the first time, the relationship between grain boundary normal stress and intergranular crack initiation in irradiated austenitic stainless steel. A Fe-13Cr-15Ni alloy was strained in simulated boiling water reactor, normal water chemistry after quantifying the residual stress tensor at discontinuous dislocation channel – grain boundary interaction sites where grain boundaries were determined to be well oriented with respect to the loading axis. Local stresses at the grain boundary were observed to reach magnitudes greater than 1.5 GPa at a distance of 200 nm from the intersection between the dislocation channel and the grain boundary. A pseudo-threshold stress of 0.9 GPa was measured, below which no cracking was observed. As the stress acting normal to the grain boundary increased above this value, the susceptibility to cracking increased with the cracking fraction reaching 100% at the high end of the stress range. This study shows for the first time that not only does intersection between discontinuous dislocation channels and grain boundaries result in peak local stresses, while the magnitude of the local tensile stress drives the crack initiation process.

36 MATERIALS SCIENCE↗

Reaction Control System Thruster Cracking Consultation: NASA Engineering and Safety Center (NESC) Materials Super Problem Resolution Team (SPRT) Findings

The shuttle orbiter s reaction control system (RCS) primary thruster serial number 120 was found to contain cracks in the counter bores and relief radius after a chamber repair and rejuvenation was performed in April 2004. Relief radius cracking had been observed in the 1970s and 1980s in seven thrusters prior to flight; however, counter bore cracking had never been seen previously in RCS thrusters. Members of the Materials Super Problem Resolution Team (SPRT) of the NASA Engineering and Safety Center (NESC) conducted a detailed review of the relevant literature and of the documentation from the previous RCS thruster failure analyses. It was concluded that the previous failure analyses lacked sufficient documentation to support the conclusions that stress corrosion cracking or hot-salt cracking was the root cause of the thruster cracking and lacked reliable inspection controls to prevent cracked thrusters from entering the fleet. The NESC team identified and performed new materials characterization and mechanical tests. It was determined that the thruster intergranular cracking was due to hydrogen embrittlement and that the cracking was produced during manufacturing as a result of processing the thrusters with fluoride-containing acids. Testing and characterization demonstrated that appreciable environmental crack propagation does not occur after manufacturing.

MacKay, Rebecca A.↗

Role of Material Condition in Precursor Corrosion Damage and Stress Corrosion Crack Initiation Behavior of Alloy 600 in PWR Primary Water

Stress corrosion crack (SCC) initiation testing has been performed on a 15% cold-worked UNS N06600 (Alloy 600) heat in the mill-annealed (MA), solution annealed (SA), and thermally treated (TT) conditions to assess the role of grain boundary (GB) carbides on stress-assisted intergranular attack (IGA) and short crack nucleation and growth. The SCC initiation tests were conducted at constant load equivalent to materials yield stress in 360oC simulated PWR primary water with dissolved hydrogen at the Ni/NiO stability line. Results revealed the highest SCC initiation susceptibility in the Alloy 600 MA material followed by the TT and SA materials, suggesting the GB carbide distribution did not have a controlling effect on SCC initiation resistance. Quantitative assessments were conducted on IGA and short cracks to help understand this phenomenon and the role of GB carbides on precursor damage development that lead to differences in macroscopic SCC initiation behavior are discussed.

Zhai, Ziqing↗

The relative stress-corrosion-cracking susceptibility of candidate aluminum-lithium alloys for aerospace structural applications

The microstructure and tensile properties of two powder metallurgy processed aluminum-lithium alloys were determined. Strength properties of 480 MPa yield and 550 MPa ultimate tensile strength with 5% strain to fracture were attained. Very little reduction in area was observed and fracture characteristics were brittle. The magnesium bearing alloy exhibited the highest strength and ductility, but fracture was intergranular. Recrystallization and grain growth, as well as coarse grain boundary precipitation, occurred in Alloy 2. The fracture morphology of the two alloys differed. Alloy 1 fractured along a plane of maximum shear stress, while Alloy 2 fractured along a plane of maximum tensile stress. It is found that a fixed orientation relationship exists between the shear fracture plane and the rolling direction which suggests that the PM alloys are strongly textured.

Pizzo, P. P.↗

Characterization of stress corrosion cracks in Ni-based weld alloys 52, 52M and 152 grown in high-temperature water

Ni-based weld alloys 52, 52M and 152 are extensively used in repair and mitigation of primary water stress corrosion cracking (SCC) in nuclear power plants. In the present study, a series of microstructure and microchemistry at the SCC tips of these alloys were examined with scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), scanning transmission electron microscopy (STEM) and energy filtered transmission electron microscopy (EFTEM). The specimens have similar chemical compositions and testing conditions. Intergranular (IG) and transgranular (TG) SCC was observed in all of them. The cracks were filled with nickel-oxides and partial precipitations of chrome carbides (CrCs), niobium carbides (NbCs), titanium nitrides (TiNs) and silicon carbides (SiCs), while iron (Fe) was largely dissolved into the solution. However, the crack densities, lengths and distributions were different for all three specimens. - Highlights: • Microstructure and microchemistry at the SCC tips of Ni-based weld alloys 52, 52M and 152 were examined. • The crack densities, lengths and distributions were found to be different for different alloys. • IGSCC and TGSCC were observed on alloy 52, only TGSCC was observed on alloy 52M and 152. • The cracks were filled by Ni-oxides and precipitated CrCs, NbCs, TiNs and SiCs.

36 MATERIALS SCIENCE↗

A potentiodynamic study of aluminum-lithium alloys in an aqueous sodium chloride environment

The characteristics of the potentiodynamic curves for Al-Li alloys in 3.5 percent NaCl aqueous solution are explained and the electrochemical parameters of the potentiodynamic technique are correlated to observed pitting and intergranular cracking behavior. It is shown that the oxygen content of the sodium chloride electrolyte plays an important role in the electrochemical behavior of Al-Li alloys. The potentiodynamic behavior of the alloys is found to be insensitive to variation in compositional content and heat treatment, both of which affect the stress-corrosion behavior. Stringer oxide particle attack and random pitting are observed. It is shown that alternate-immersion exposure prior to potentiodynamic polarization may offer a means of assessing susceptibility to stress-corrosion cracking.

Tsao, C.-H. T.↗

Focused Ion Beam Tomography of Alloy 617 Corroded in Molten Chloride Salt

Materials qualification of reactor structural materials is a critical step in rapid implementation of advanced nuclear reactor technologies, particularly to assess the corrosion performance in these designs. Accelerated qualification of reactor structural materials requires incorporating powerful computational toolsets, such as phase field modelling in the Multiphysics Object-Oriented Simulation Environment (MOOSE) framework, to predict the evolution of structural materials due to corrosion. Accordingly, computational toolsets will require experimental data generated at appropriate length scales to validate accuracy. Focused ion beam (FIB) provides a high degree of control over manipulation of materials for analytical purposes, including capturing data on the evolution in the microstructure and elemental composition of materials at the mesoscale, an appropriate length scale for phase field modelling of intergranular diffusion phenomena using the MOOSE framework. For instance, the FEI Helios G4 UX dual beam plasma FIB microscope at the Irradiated Materials Characterization Laboratory (IMCL) is capable of backscatter diffraction (EBSD) and energy-dispersive x-ray spectroscopy (EDS) documenting the evolution in the microstructure and elemental composition, respectively. The Helios can perform EDS and EBSD three-dimensionally (3D) using tomography, which is then combined using different software packages to visualize 3D volumes correlating elemental composition to microstructural data. The purpose of this investigation was to develop a streamlined characterization and data processing workflow for 3D tomography studies on the FEI Helios G4 plasma FIB. The investigation is segmented into three parts: 1) Optimizing the data collection workflow, 2) identifying appropriate data processing and visualization software (i.e. DREAM.3D, MIPAR, and VGStudioMax), and 3) establishing an infrastructure for public release. The optimization of the data collection workflow is in collaboration with members of the U220 department to setup formal training on the tomography operation of the G4, through ThermoFisher Scientific, and exploring DREAM.3D, MIPAR, and VGStudioMax data processing/visualization software packages. VGStudioMax currently demonstrates the most promise for future use. Optimization of the data collection and processing workflow is still ongoing. A collaboration with INL High Performance Computing (HPC) established an open-source license for expediting the public release of FIB tomography datasets through HPC. FIB tomography data generated by the G4 will provide comprehensive data for validating 3D phase field mesoscale modelling tools within the MOOSE framework for accelerated qualification of reactor structural materials.

Copeland-Johnson, Trishelle↗

Grain boundary damage evolution and SCC initiation of cold-worked alloy 690 in simulated PWR primary water

Long-term grain boundary (GB) damage evolution and stress corrosion crack initiation in alloy 690 are being investigated by constant load tensile testing in high-temperature, simulated PWR primary water. Six commercial alloy 690 heats are being tested in various cold work conditions loaded at their yield stress. This paper reviews the basic test approach and detailed characterizations performed on selected specimens after an exposure time of ~1 year. Intergranular crack nucleation was observed under constant stress in certain highly cold-worked (CW) alloy 690 heats and was found to be associated with the formation of GB cavities. Somewhat surprisingly, the heats most susceptible to cavity formation and crack nucleation were thermally treated materials with most uniform coverage of small GB carbides. Microstructure, % cold work and applied stress comparisons are made among the alloy 690 heats to better understand the factors influencing GB cavity formation and crack initiation.

Alloy 690↗

Mechanisms of Mitigating Chloride-Induced Stress Corrosion Cracking of Austenitic Steels by Laser Shock Peening

This study investigates the effect of laser shock peening (LSP) on the chloride-induced stress corrosion cracking (SCC) of 304 austenitic steels. LSP can induce a high compressive residual stress to a depth of 700 µm and plastic deformation structures of dislocations, deformation twins, and stacking faults. Constant-load SCC tests in MgCl2 solution suggested that LSP can retard the crack initiation and slow the crack growth. LSP-treated subsurface layers experience ductile fracture while the central regions exhibit intergranular SCC. The LSP-induced deformation structures may impede dislocation slips, while the LSP-induced compressive residual stress can lessen the stress intensity factor of crack tips and decrease the local stress for film rupture.

Materials Science↗