SEARCH · Search NASA

Results for “Neutron Irradiation”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 127 records · Page 7

All sources NASA NTRS DOE OSTI

DOE OSTI2020

Fullerene-like defects in high-temperature neutron-irradiated nuclear graphite

Irradiation-induced defect evolution in graphite is particularly important for its application in graphite-moderated nuclear reactors. The evolution of defects directly influences macroscopically observed property changes in irradiated nuclear graphite which, in turn, can govern the lifetime of graphite components. This article reports novel defect structures and the irradiation response of microstructural features occurring in high-temperature irradiated nuclear graphite IG-110. High resolution transmission electron microscopy (HRTEM) was used to characterize specimens neutron-irradiated at a high temperature (≥ 800°C) at doses of 1.73 and 3.56 atomic displacements per atom (dpa). Concentric shelled and fullerene-like defects were found to result in swelling along the c-axis and contraction along the a/b-axis of crystallites. Furthermore, such defects are shown to occur within, and partially fill, Mrozowski cracks prior to turnaround dose. In addition, in situ TEM under similar irradiation conditions was used to capture the real-time dynamic evolution of defects, providing unambiguous analysis of the evolution of the graphite structures during irradiation. Here, the results suggest the mainstream theory for radiation damage in nuclear graphite (which assumes additional basal plane formation as the sole reason) to be an incorrect interpretation of defect evolution contributing to irradiation-induced property changes at higher temperatures.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2025

Back to functional hydrides: Effects of neutron-irradiated microstructure on hydrogen retention in yttrium hydride

Functional hydrides are promising candidates for advanced nuclear reactors, particularly in portable or transportable applications, due to their high hydrogen-retention capabilities, enabling efficient neutron moderation, and compact reactor design. However, hydrogen mobility in hydrides at elevated irradiation temperatures poses significant technological challenges, necessitating a comprehensive understanding of their irradiation behavior. Furthermore, this study investigated the microstructural and chemical stability of neutron-irradiated yttrium hydrides to assess their hydrogen-retention capacity. A targeted literature review was also conducted to contextualize neutron-irradiation effects on functional hydrides with regards to structural stability and hydrogen retention. Experimental characterizations revealed that, at high temperatures, irradiated hydrides retained their phase stability, which was likely enhanced by irradiation-induced microstructure evolution. Notably, an amorphous yttrium and oxygen -rich surface layer was present at the free surface of the hydride. Its thickness decreased while a continuous crystalline Y-O-rich layer was formed with increasing neutron damage. Additionally, the number density of dislocation loops and cavities generally increased as a function of neutron dose. First-principles calculations of hydrogen behavior within yttrium vacancy clusters in yttrium hydrides demonstrated vacancy-size-dependent hydrogen stability and configuration, highlighting the role of vacancy geometry in regulating hydrogen retention. Thus, the presence of irradiation-induced dislocation loops and cavities were hypothesized to improve hydrogen retention. Collectively, these findings advance the understanding of hydride behavior under neutron irradiation as well as their technological readiness for portable or transportable nuclear reactors.

Defect clusters↗

DOE OSTI2020

The correlation between microstructure and nanoindentation property of neutron-irradiated austenitic alloy D9

The microstructure and nanomechanical properties of three samples of the modified stainless steel (referred as the alloy D9) were systematically characterized after neutron irradiation in the Advanced Test Reactor. The samples were irradiated to 5.0, 8.2, and 9.2 displacements per atom at 448, 430, and 683°C, respectively. The evolutions of dislocation loops, cavities, and radiation-induced precipitates were quantitatively studied to reveal their dose and temperature dependencies. Nanohardness and nanoindentation creep tests were conducted at room temperature on the irradiated samples. Unexpected radiation hardening was observed in the highest-temperature-irradiated sample due to the formation of an unknown type of Ni- and Si-rich precipitates whose contributions to the radiation and mechanical performances of the alloy were discussed. We provide the radiation-microstructure-property correlations of alloy D9 with new insights, which can benefit the development and optimization of advanced austenitic alloys for future nuclear applications.

36 MATERIALS SCIENCE↗

DOE OSTI2025

In-service corrosion and grain boundary oxidation in neutron-irradiated 316 stainless steel baffle-former bolts

Reactor core internal components such as baffle-former bolts (BFBs) are subjected to significant mechanical stress, corrosive environment, and neutron irradiation from the reactor core during the plant operation. Over the long operation period, these conditions lead to potential degradation and of the bolts. In this work, characterization was performed on the oxidized surface of stainless steel BFBs harvested from a commercial pressurized water reactor (PWR) after 40 years of operation. The analysis shows that a complex multilayered surface oxide with six identified layers formed that is different from 2-layer structure commonly observed in model experiments. The oxide varies by composition – predominantly Fe, Cr, and Ni, grain size, and phase, and has features resembling both unirradiated and radiation/ corrosion experiments likely due to the low radiation flux compared to ion-irradiation or the test reactor radiation. In addition, grain boundary oxidative attack featured a pathway for Fe and other elements to move from the metal matrix to the outermost oxide. In conclusion, the results help assess PWR lifetime extension, put into context previous experimental studies, and provide input for designing experiments combining radiation and corrosion effects.

Baffle-former bolt↗

DOE OSTI2022

Helium interaction with solutes and impurities in neutron-irradiated nanostructured ferritic alloys: A first principles study

Density functional theory calculations are performed to explore the binding between He and alloying solutes, impurities, and transmutation products expected in neutron irradiated nanostructured ferritic alloys (NFAs), here 14YWT is taken as an example. Elements that exhibit significant binding (attraction) with an interstitial He are Y (binding energy = 0.46 eV), Mg (0.32), O (0.33), Ti (0.16), and C (0.15). Those that provide significant binding to a substitutional He are O (1.44), Y (1.24), N (0.73), H (0.56), Mg (0.52), Ti (0.34), Si (0.34), C (0.33), Al (0.32), Ni (0.26), Ta (0.23), and Mn (0.16). The presence of these elements in Fe matrix could reduce the transport of He towards oxide particles, dislocations, and internal boundaries, and could promote He bubble nucleation in the matrix. For convenience, we compile existing binding energy data of He with He n and He n V (He-vacancy) clusters. Dissociation pathway analysis reveals that, in general, the most likely dissociation of a He n V cluster is by a sequential emission of individual He atoms. Furthermore, larger bubbles are more prone to dissociation than smaller ones. In addition, we estimate the binding energy (segregation energy) of He in bulk Y 2 Ti 2 O 7 (YTO) single crystal, YTO/Fe interface, and YTO particle embedded in Fe, with respect to interstitial He in Fe, from existing formation energies of He in these structures. We also compile available data of He binding with Fe self-interstitial atom (SIA), SIA clusters, and edge and screw dislocations. Note that given the absence of DFT data, the binding with SIA clusters and dislocations are gathered from simulations with empirical potentials. Finally, the data presented in this paper is important to inform multiscale simulations of He bubble accumulation.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Evidence of lithium mobility under neutron irradiation

Understanding the evolution of intermetallic materials in high-radiation environments is of great importance for fusion science and national security. Tritium ( 3 H) and lithium ( 6 Li, 7 Li) transport within neutron irradiated claddings coated with aluminide (FeAl3) has been investigated using state-of-the-art multimodal imaging. Specifically, scanning electron microscopy – focused ion beam (SEM-FIB) was used to prepare irradiated coating lift-out samples for follow-on microanalysis. Here, scanning transmission electron microscopy (STEM) was used to acquire atomic-scale information on the carbonaceous structure and elemental mapping. Atomic force microscopy (AFM) was used to determine lift-out dimensions nondestructively. Time-of-flight secondary ion mass spectrometry (ToF-SIMS) spectral and depth profiling show unexpected lithium isotopic distributions in the irradiated cladding, raising an important evidence of possible light isotope mobility within the cladding under elevated temperature and irradiation. ToF-SIMS three-dimensional chemical mappings of mid- and bottom-cladding coatings show light isotopic (e.g., 3 H, 6 Li, 7 Li) distributions in the irradiated coating and give new insights into the fundamental mechanism related to transport mechanisms within the cladding. Multimodal imaging is power to link microstructure, chemistry, and nanoscale defects that impact reliability of these materials. Furthermore, chemical mapping offers observations of the microstructural evolution due to irradiation and provides insights into unexpected material transport under extreme conditions.

36 MATERIALS SCIENCE↗

DOE OSTI2023

3-D reconstruction and microstructural characterization of neutron-irradiated U-10Zr fuel using FIB-SEM serial sectioning

Herein, focused ion beam-scanning electron microscopy serial sectioning was applied to characterize the three-dimensional (3-D) porosity and phase regions of a neutron-irradiated U-10 wt% Zr fuel. The specimen was removed from an intermediate radial region of a fuel pin irradiated to 5.7 at.% burn-up. Backscattered electron imaging and energy-dispersive spectroscopy were performed on each serial section, allowing for the characterization of microstructural morphology and composition. Porosity size followed a lognormal distribution, ranging from 1.46 × 10 –4 to 25.58 µm 3 with a total porosity volume fraction of 13.02%. Distinctive microstructural regions were identified by composition and porosity: (1) a Zr-rich region with an average composition of 28.4 wt% Zr and a local porosity fraction of 6.88%, and (2) a U-rich region with an average composition of 97.0 wt% U and a local porosity fraction of 14.11%; subdivided into U-rich—high porosity (16.68%) and U-rich—low porosity (8.04%) regions. The detailed 3-D compositional and porosity regions can improve nuclear fuel performance codes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2025

Temperature-dependent mechanism on hardening mitigation in thermomechanically processed 800H alloys under neutron irradiation

Irradiation induced hardening is commonly observed in structural materials, and is often associated with the degraded ductility. This study explores the role of thermomechanical processing (TMP) in mitigating irradiation-induced hardening in Incoloy 800H. The radiation response of solution-annealed and TMP-treated samples was systematically investigated to elucidate the underlying mechanisms of hardening reduction. Neutron irradiation was performed on solution-annealed and TMP-treated samples at 359, 431, and 580 °C, revealing consistently lower hardening in TMP samples. Microstructural characterization compared dislocation loops, cavities, clusters, and precipitates to assess their contributions to hardening. The strengthening contributions from individual microstructural features were estimated, and the microstructure-derived yield strength is consistent with the hardness-converted yield strength. The microstructure–properties correlation revealed the temperature-dependent primary hardening mechanism: dislocation loops dominated at lower temperature, whereas Ni3(Al,Ti) γ′ precipitates were predominant at higher temperature. TMP reduced radiation-induced hardening through two mechanisms: (1) increased sink strength from dislocations and Ti(C,N) precipitates limited dislocation loop formation at lower temperatures, and (2) reduced Ti solute within the matrix in TMP samples suppressed γ′ precipitate formation at higher temperatures. These findings identify the mechanisms governing radiation-induced hardening across different temperatures, which lays the foundation for TMP optimization for the development of advanced radiation-tolerant materials.

Zhong, Weicheng [ORNL] (ORCID:0000000231589271)↗

DOE OSTI2019

Experimental evidence for ‘buckle, ruck and tuck’ in neutron irradiated graphite

The current mainstream theory for radiation-induced dimensional change of nuclear graphite is based on the notion that interstitially displaced carbon atoms will coalesce into dislocation loops (i.e., additional basal planes). This standard atomic-displacement model has been challenged by theories based on first principles calculations. Furthermore, the so-called ‘ruck and tuck’ of basal planes has been proposed as an alternative mechanism to explain the observed c-axis expansion under irradiation; however, no such defects have been observed experimentally so far. In this study, the first experimental evidence for the presence of a ‘ruck and tuck’ defect in high-temperature neutron-irradiated nuclear graphite is introduced.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Fast neutron irradiation capability in existing thermal test reactors

In today’s nuclear industry, momentum towards the design, licensing, and construction of advanced nuclear demonstration plants, including fast reactors, is at a remarkably high level. However, there are currently no dedicated fast spectrum irradiation test facilities in the United States to support the development of fast spectrum technologies. As a result, a unique situation is developing where most of these plants will likely be designed by leveraging historic nuclear material technologies, but where the further optimization and advancement is impeded by the lack of fast neutron irradiation test facilities. While these circumstances present a challenge, there are some near-term opportunities that, if seized, can still help develop advanced fast reactor materials to a meaningful level of readiness to support future commercial fast reactors. Here, in this paper, we assess the feasibility of using thermal neutron filtering materials in existing experiment positions in the Advanced Test Reactor (ATR) at Idaho National Laboratory and the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory to simulate fast reactor test environments for nonfuel test specimens. Items investigated include the incident neutron flux (both fast and thermal), the total neutron fluence and cumulative atom displacements, helium production rate due to thermal neutron capture in nickel, and the potential impact that the thermal neutron filter material has on the cycle length of a given reactor. It is concluded that while HFIR provides the highest fast flux of all the options investigated, it is limited in the amount of thermal neutron filtering material that can be introduced into an experiment position without significantly affecting the operation of the reactor. Irradiation in Outboard-A positions in the ATR was found to be the most realistic near-term experiment avenue due to having ample space for several capsules in a moderately fast flux.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Qualitative and quantitative analysis of neutron irradiation effects in SiC/SiC composites using X-ray computed tomography

Silicon carbide fiber-reinforced silicon carbide matrix (SiC/SiC) composites are candidate materials for cladding of light water reactor (LWR) fuels. Loss of fission product gas retention due to the formation of microcrack networks is considered a potential failure mechanism for SiC/SiC-cladded fuels. In this work, a variety of SiC/SiC composite tubes were irradiated with and without an LWR-relevant radial heat flux in the High Flux Isotope Reactor, followed by detailed characterization with X-ray computed tomography (XCT). This first set of XCT data for neutron-irradiated samples confirmed that the internal stresses arising from a combination of temperature gradients and irradiation-induced swelling act as the primary driver for cracking. Consequently, while the observed cracking patterns varied depending on the tube architectures, the sharp edges of relatively large pores were found to be the common stress concentrator. These findings are useful to help improve the design and manufacturing of SiC/SiC fuel claddings for reduced failure probability.

42 ENGINEERING↗

DOE OSTI2022

Microstructure analysis of laser beam weldments performed on neutron-irradiated 304L steel containing 3 and 8 appm helium

We report that AISI 304 L austenitic stainless steel is one of the major structural materials used in light water reactors (LWRs). In the future, 304 L components may require repair, and several welding techniques have been proposed as candidates. In this study, laser beam welding using the low-energy contribution approach was performed in ~2016 on neutron-irradiated AISI 304 L steel with nominal values of 3 and 8 appm helium (He). The goal was to investigate the impact of helium on the irradiated material weldability and evaluate helium-associated damage. The weld and heat-affected zone (HAZ) microstructure was studied using scanning electron microscopy, electron backscatter diffraction, and transmission electron microscopy (TEM). Analysis of the weldment cross-sections did not reveal severe cracking. Still, evidence of incipient helium-associated damage was observed in the HAZ, manifesting as degraded grain boundaries (GBs) “decorated” by pore chains and mostly small (i.e., ≤ 25-30 µm) scattered cracks. The largest observed crack was ~50 µm in length. Helium-associated damage was localized within ~200-300 µm of the weld pool boundary, and the fraction of the compromised GBs, as a rule, was below ~9-11% of the total GB network. TEM analysis showed significant annealing of the radiation-induced defects at distances up to ~300 µm from the weld pool boundary. Inside the HAZ, the cavities (likely, helium bubbles) tended to form at GBs and inclusions, such as manganese sulfide precipitates in the grain interior. Crystallography analysis of the HAZ damage showed that random high-angle boundaries were most susceptible to helium-associated damage. In contrast, low-angle random boundaries and twin boundaries appeared to be strongly resistant to degradation from the combined effects of helium and welding.

36 MATERIALS SCIENCE↗

DOE OSTI2026

In situ TEM annealing of neutron-irradiated Ti reveals a two-stage mechanism for elevated temperature radiation damage recovery

Understanding how irradiation-induced defects evolve at elevated temperatures is of critical importance to predicting materials' behavior under steady-state and accident scenarios. However, such mechanistic insight into microstructural evolution is limited by the nature of ex situ annealing and subsequent imaging. Here we show direct observation and quantification of defect recovery in neutron-irradiated Ti using in situ transmission electron microscopy (TEM) annealing experiments. In agreement with our prior work, and at temperatures below the irradiation temperature (T irr = 300 °C), dislocation loops are observed to glide. At elevated temperatures (>500 °C), dislocation lines become mobile and promote significant recovery of the microstructure. These mechanisms challenge the established electron irradiation-based model for radiation damage recovery, which originally suggests dissolution of static defect clusters, and demonstrates the importance of in situ characterization in understanding defect evolution in irradiated materials.

Hirst, Charles A. [Univ. of Michigan, Ann Arbor, M↗

DOE OSTI2021

Depth-resolved cathodoluminescence and surface photovoltage spectroscopies of gallium vacancies in β-Ga 2 O 3 with neutron irradiation and forming gas anneals

The gallium vacancy is one of the dominant native point defects in β-Ga 2 O 3 , one that, together with its complexes, can have a major effect on free carrier densities and transport in this wide bandgap semiconductor. We used a combination of depth-resolved cathodoluminescence spectroscopy and surface photovoltage spectroscopy to identify the optical and energy-level properties of these defects as well as how their defect densities and spatial distributions vary with neutron irradiation and temperature-dependent-forming gas anneals. These studies reveal optical signatures that align closely with theoretical energy-level predictions. Likewise, our optical techniques reveal variations in these defect densities that are consistent with hydrogen passivation of gallium vacancies as a function of temperature and depth from the free Ga 2 O 3 surface. These techniques can help guide the understanding and control of dominant native point defects in Ga 2 O 3 .

42 ENGINEERING↗

DOE OSTI2021

Mechanical Properties of Additively Manufactured 316L Stainless Steel Before and After Neutron Irradiation (FY21)

This report presents the materials property data of additively manufactured (AM) 316L stainless steel (SS) accumulated for the assessment of core materials in the Transformational Challenge Reactor (TCR) program. The TCR manufacturing approach includes using the laser powder bed fusion (LPBF) method for metallic (316L and Inconel 718) components. To assess the mechanical performance of printed components in reactor-relevant conditions and build a property database for the AM materials, mechanical tests and evaluations were performed before and after neutron irradiation. Miniature tensile specimens were irradiated in the High Flux Isotope Reactor to 0.2, 2, 8, and 10 dpa at target temperatures of 300 and 600°C. Postirradiation evaluation for the 0.2 and 2 dpa specimens was performed during FY20 and FY21, and the results are presented and discussed in this document.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2024

TEM Characterization of Neutron Irradiated HfAl3-Al Composite Specimens

Particles comprised of a thermal neutron absorbing material (HfAl3) are dispersed in a metal matrix material with high thermal conductivity (aluminum) to conduct the heat generated by neutron capture away from the fuel and materials. This metal matrix composite is very promising for use as a conduction-cooled neutron absorber and has the potential to be useful as a shroud or heat sink for testing advanced fast reactor fuels and materials in an existing thermal reactor. To design and optimize the absorber block system for advanced reactor designs, fundamental understanding of the irradiation effect on material properties is necessary. This dataset contains TEM characterization results of neutron irradiated HfAl3-Al composite specimens. It is focused on the irradiation induced defects (dislocation lines and loops) characterization using the on-zone axis bright field STEM technique. This data was collected using a FEI Tecnai G2 F30 S/TEM at the Microscopy and Characterization Suite (MaCS), Center for Advanced Energy Studies (CAES).

Guillen, Donna↗

DOE OSTI2024

TEM Characterization of Neutron Irradiated HfAl3-Al Composite Specimens

Guillen, Donna↗

DOE OSTI2021

Understanding fission gas bubble distribution, lanthanide transportation, and thermal conductivity degradation in neutron-irradiated α-U using machine learning

U—10Zr based metallic nuclear fuel is the leading candidate for next-generation sodium-cooled fast reactors in the United States. US research reactors have used and tested this fuel type since the 1960s and accumulated considerable experience and knowledge about the fuel performance. Most of the knowledge, however, remains empirical. The lack of mechanistic understanding of fuel performance puts a large burden on proof through experimental verification for the qualification of U—10Zr fuel for commercial use. Further, this paper proposes an image data-driven machine learning approach, coupled with domain knowledge provided by advanced post irradiation examination, to provide unprecedented quantified insights into the morphology, size, density and the connectivity of fission gas bubbles and their effects on the fission product transportation and thermal conductivity. Specifically, we developed a method to automatically detect, extract statistics, and classify ~19,000 fission gas bubbles into different categories, and quantitatively link the data to lanthanide transportation through connected bubbles and degradation of thermal conductivity along the radial temperature gradient in a neutron irradiated U—10Zr annular fuel. Results indicate the approach can be modified to study other irradiation effects, such as secondary phase redistribution and gaseous fuel swelling in other irradiated nuclear fuels.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗