Search NASA⌕ Search

SEARCH · Search NASA

Results for “fuel cladding tube”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 127 records · Page 7
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

A study on texture stability and the biaxial creep behavior of as-hydrided CWSR Zircaloy-4 cladding at the effective stresses from 55 MPa to 65 MPa and temperatures from 300°C to 400°C

The creep rupture of high burnup used nuclear fuel (> 45 GWD/MTU) cladding is regarded as one of the failure mechanisms during long-term dry storage. A high amount of zirconium hydride in the cladding matrix would degrade the mechanical properties of the cladding especially leading to delayed hydride cracking. To better understand the influence of zirconium hydride on the biaxial thermal creep performance and the crystalline texture stability of Zircaloy-4 cladding, the pressurized tube technique is applied to test the durability of the as-hydrided material. Tests were performed on as-received Zircaloy-4 tubular specimens as well as-hydrided ones with targeted 300 wt parts per million (wppm) or 750 wppm hydrogen. The biaxial creep experiments were conducted at temperatures from 300 degrees C to 400 degrees C and at equivalent stresses at mid-wall from 55 MPa to 65 MPa. The hydridation process prior to creep tests induces the formation of FCC delta-hydride platelets along the circumferential direction of the tube. This alignment and phase structure of hydride show no significant change after biaxial creep tests. The creep strain-rate negatively depends on the hydrogen content. The synchrotron wide-angle X-ray diffraction (WAXD) technique and electron backscatter diffraction (EBSD) analysis were applied for the study of the crystallographic orientation relationship. zirconium-to-hydride grain orientation follows Shoji-Nishiyama crystallographic relationship. This relationship is stable before and after creep deformation. These results of creep performance and texture stability of Zircaloy-4 claddings can help support the design basis of interim and long-term dry storage facilities.

creep↗
DOE OSTI2021

Burst characteristics of advanced accident-tolerant FeCrAl cladding under temperature transient testing

Here assessment of burst characteristics of accident-tolerant fuel (ATF) claddings is essential to evaluate the safety margins of nuclear reactors, and better understanding can enable accelerated licensing for reactor concepts that include the new materials. Therefore, this study investigated the burst behavior of an ATF candidate of C26M, which is an iron–chromium–aluminum alloy (FeCrAl) under transient testing like the simulated loss-of-coolant accident (LOCA) conditions, except the water-quenching phase, in light-water reactors (LWRs). The effect of LOCA specimen length was assessed in terms of post-burst tube parameters. No critical length effect was determined on the burst pressure, burst location, and burst size measurements. Burst temperature showed larger variation likely due to its measurement approach used in this study. The post-test diametral strain was identified as the critical parameter to reduce the specimen length as compared to tube burst length or width. Postmortem optical metrology and digital image correlation were employed to determine the local strain-state during the simulated LOCA, which showed the loading path was close to equibiaxial conditions in regions away from the burst location, rather than internally pressurized conditions (or “plane-strain” tension). Pst-test microstructural characterizations of the FeCrAl revealed that ductile damage was present at the edge of the outer radial surface while the rest of the material was ruptured via cleavage at LOCA burst temperatures. Furthermore, internal grain boundary cracks were observed at locations away from the tube burst region. This behavior was considered to occur during the cooling down period of the simulated LOCA test. Overall, this study aimed to provide essential data for fuel performance code development by considering micromechanics of the deformation and failure.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Large-scale parametric modeling of spent nuclear fuel dynamics in the 30 cm package drop scenario

Packages used to transport spent nuclear fuel (SNF) are required by the U.S. Code of Federal Regulations 10 CFR 71.71 to demonstrate satisfactory performance during a drop scenario. While the CFR is meant to ensure safe package function, it does not evaluate survival of the SNF within. The U.S. Department of Energy Spent Fuel and Waste Science and Technology program is working on closing the knowledge gap related to the response of SNF to external mechanical loads, including the hypothetical 30 cm package drop scenario in the CFR. In support of this effort, LS-DYNA finite element simulations were developed by Pacific Northwest National Laboratory (PNNL) to model generic drop scenarios at both the package and fuel assembly level. The models were validated against one-third scale package and full scale fuel assembly drop test data and were exercised to predict fuel cladding strains in a narrow range of model configurations. This work describes a large-scale parametric study conducted by PNNL using the previously developed and validated PWR finite element model, with the addition of a new generic BWR assembly model. The motivation for the parametric study was to characterize the broad range of SNF responses in the 30 cm package drop scenario. This was accomplished by varying the drop orientation, fuel assembly type (17x17 PWR and 10x10 BWR), burnup, cladding temperature, spacer grid buckling load, package mass, impact limiter stiffness, and mechanical gap conditions within the basket. A MATLAB framework was developed to automate LS-DYNA model generation and execution on PNNL institutional computing resources. In total, over 2000 simulations were performed. For each simulation, the SNF response was quantified in terms of permanent grid deformation, fuel rod contact pressure, and strains within the fuel rods, guide tubes, and water rods. The results provide valuable insight into the range of responses that could be reasonably expected from SNF in the hypothetical drop scenario, as well as the sensitivity to each input parameter. The results of this parametric study are a key component of the testing and modeling strategy the Spent Fuel and Waste Science and Technology program is using to close the external loads knowledge gap.

Kadooka, Kevin↗
DOE OSTI2025

Irradiation Vehicles for Evaluating SiC/SiC Cladding Bowing Under Neutron Flux Gradients

Silicon carbide fiber–reinforced silicon carbide matrix (SiC/SiC) composites are among the most promising candidates for long term accident-tolerant nuclear fuel cladding. A key challenge related to their deployment is lateral bowing caused by differential radiation-induced swelling under dose or temperature gradients, which could obstruct coolant flow or interfere with control rod/blade movements. Although previous modeling efforts have predicted bowing behavior in light-water reactor (LWR) environments, experimental validation remains limited, especially at prototypic LWR temperatures. This study addresses that gap by irradiating six reduced-length SiC/SiC cladding tubes (~600 mm) in the High Flux Isotope Reactor (HFIR) at ~300°C, which is representative of LWR conditions. The tubes will be housed in a sealed vessel with an inert gas gap to maintain target temperatures and prevent direct coolant contact. Arranged in three pairs, each set will receive a different radiation dose (low, medium, high), with the central pair receiving ~0.1 displacements per atom (dpa)—the expected dose for peak bowing. The experiment will determine the dose-dependent bowing behavior and validate predictive finite element models. In this work, the tubes are freely suspended from pins to allow for unconstrained bowing; however, we present a concept for introducing localized constraints to represent grid spacer effects. Post-irradiation examination will include swelling measurements and profilometry to assess bowing and compare the results with model predictions. This work aims to confirm the conditions under which maximum bowing occurs so as to improve the reliability of SiC/SiC performance models in nuclear applications.

Russell, Nick [ORNL] (ORCID:0000000296099820)↗
DOE OSTI2024

Wrought FeCrAl alloy (C26M) cladding behavior and burst under simulated loss-of-coolant accident conditions

Cladding burst experiments for FeCrAl cladding were performed in the Severe Accident Test Station facility at Oak Ridge National Laboratory. These experiments were simulated using the BISON fuel performance code to better understand the cladding plastic behavior and failure under simulated loss-of-coolant accident conditions. 3D cladding surface boundary conditions were generated using composite axial and azimuthal profiles from experiment thermocouple data. To improve the simulation analysis capabilities in BISON for cladding burst behavior, new thermal creep, plasticity, and failure stress models specific to C26M, a wrought FeCrAl alloy, were developed and implemented. Initial cladding burst results indicated a general underprediction in the failure temperature of the six cladding burst simulations versus the observed failure temperatures. Close investigation of the experiment timing versus the underlying tensile test data revealed that, compared with the tensile specimens, the cladding tubes did not experience the same long holding time at high temperatures. New tensile tests were performed at high temperatures using a temperature ramp similar to the simulated loss-of-coolant accident experiments. These new tensile curves showed an approximately 80% increase in the ultimate tensile strength of the C26M alloy, indicating that a holding time of 10 min at 700 °C and 800 °C allows annealing to change the material microstructure. Using the updated tensile properties, the burst temperatures and stresses from the simulations showed remarkable agreement with the experimental results. This study was then extended by varying the initial pressure to highlight the burst temperature difference between standard Zircaloy-4 and C26M cladding under equivalent conditions. The results show that C26M has a burst temperature that is approximately 70–130 K greater than that of Zircaloy-4. In conclusion, these modeling predictions can be further improved by collecting high-temperature tensile data for C26M beyond the temperature ranges used in this work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Test Plan for Investigation of Hydrogen Generation in SNF Canisters

This report presents a test plan to investigate radiolytic hydrogen generation in spent nuclear fuel (SNF) canisters containing Zr-based cladding materials. The initial primary contributor to the generation of radiolytic hydrogen is estimated to be the residual physisorbed water on the ZrO 2 film, post-dry out. Over the longer term the primary hydrogen source is associated with the aluminum hydroxides and water vapor. The proposed testing to be conducted in FY22 would consist of lab-scale testing on non-radioactive surrogates of oxidized ZIRLO tubing and unalloyed zirconium using a miniature steel canister (“mini-canister") designed to allow intermittent, in-situ sampling of the canister gas during irradiation. The mini-canister approach for irradiation with in-situ monitoring system was used in a recent and on-going study [McNamara and Verst, 2020a & 2020b; Verst et al., 2021] to measure radiolytic hydrogen generation from aluminum SNF cladding surrogate materials. This proposed testing will form part of the overall materials performance evaluation of the commercial SNF-in-canister system and is part of the technical bases for their continued safe dry storage

08 HYDROGEN↗
NASA NTRS2001

Development of Core Cladding Fabrication Techniques for Phase I Fission Propulsion Systems

Phase I fission propulsion systems focus on safety, timely development, and affordability. Prototype and flight units can be tested at full thrust, using resistance heaters to closely simulate heat from a fission reaction. In Phase I ground testing, one goal is to establish a reliable and affordable manufacturing technique for fabricating a flight-like core. A refractory metal (Mo) has been suggested for the core substrate, primarily due to the existence of a significant database for Mo/LJ02 fuel. The core can be fabricated by bundling Mo tubes with a bonding system that meets preliminary test goals. These criteria include materials compatibility, ability to maintain thermal and structural integrity during 10,000 hours of operation, and fabrication with existing facilities. This paper describes an effort to investigate several fabrication techniques in a cost-effective manner. First, inexpensive materials were tested at low temperatures to determine the relative effectiveness of such techniques as welding, brazing, plating, and vacuum plasma spraying (VPSing). Promising techniques were chosen for further evaluation, including thermal and structural studies, using ceramic tubing at intermediate temperatures. The most desirable technique will be tested on actual Mo tubing at anticipated operating temperatures. This work is being performed by the National Aeronautics & Space Administration (NASA) at George C. Marshall Space Flight Center (MSFC), Los Alamos National Laboratory (LANL), and Advanced Methods & Materials (AMM), Inc.

Salvail, Patrick G.↗
DOE OSTI2025

The impact of chromium coatings on Zircaloy cladding deformation behavior under reactivity-initiated accident-like mechanical loading conditions

A reactivity-initiated accident (RIA) occurs when a control rod ejection or control blade drop causes an increase in the fission rate. The injection of energy results in an increase in fuel temperature which in turn causes rapid thermal expansion of the fuel pellet. This thermal expansion may result in pellet-cladding mechanical interaction (PCMI) in which the fuel imparts a mechanical strain to the cladding. PCMI may cause the cladding to fail, and thus, the mechanical response of cladding due to PCMI must be investigated when characterizing new cladding materials. Chromium-coated Zircaloy-4 is a near-term accident-tolerant fuel cladding that exhibits improved high-temperature oxidation resistance. Modified burst testing was utilized to experimentally simulate the effects of PCMI on both uncoated and chromium-coated Zircaloy cladding samples at hot zero power conditions. Samples were coated using either cold spraying or physical vapor deposition to understand the differences in behavior that the coating application method may cause. Digital image correlation was used to analyze images of the deforming specimens to extract the in-situ strain behavior of the cladding. The uncoated specimens burst at hoop strains ranging from 8.8 % to 17.2 %. The cold-spray chromium-coated Zircaloy specimens burst at hoop strains of 7.0 % to 11.0 %. The physical vapor deposition coated tubes burst at hoop strains of 9.1 % to 11.5 %. These results indicate that the chromium coating causes a loss in the ductility of the cladding. Furthermore, the higher burst hoop strains of the physical vapor deposition-coated samples relative to the cold-spray samples indicate that the cold-spraying technique causes more of a loss in ductility than physical vapor deposition. All samples burst at higher hoop strains than those expected to occur in an RIA for fresh cladding.

Accident-tolerant fuel↗
DOE OSTI2021

Sensitivity analysis of in-pile critical heat flux experiments in TREAT for characterization of RIA power-transient effects

A reactivity-initiated accident (RIA) is one type of postulated design basis accident (DBA) that can cause a departure from nucleate boiling (DNB) event in pressurized-water reactors (PWRs). A DNB occurrence and its consequences depend on the thermophysical properties of the fuel components and coolant, characteristics of the transient energy insertion into the fuel rod, and the onset of the critical heat flux (CHF) phenomenon. To leverage the restart of the Transient Reactor Test (TREAT) Facility, an effort is currently underway to better understand the cladding-to-coolant heat transfer mechanisms and the CHF phenomenon under fast-transient irradiation conditions. This paper characterizes the impact of power transients on the thermal-hydraulic behavior of a TREAT Facility reactor heater rodlet CHF experiment to provide the priority of parameters that need to be investigated for an improved CHF model. Sobol sensitivity analysis methods and the Reactor Excursion and Leak Analysis Program (RELAP5-3D) code were used to identify key input parameters on the uncertainty in the prediction of peak outer- and inner-surface temperatures of the heater tube, as well as the time of the DNB event. A series of sensitivity analyses revealed the total energy deposition on the tube and the transient effects of power pulse had large impacts on the maximum temperatures. The CHF multiplier had the largest impact on the time occurrence of CHF. The overall results show the energy deposition rate in the tube is the most influencing factor to the manifestation of CHF and the resulting thermal-hydraulic behaviors of the tube. The multiplier for the CHF, which is interpreted as the predicted CHF value, has the largest Sobol indices for the time of the CHF in all cases, since it directly determines the occurrence of CHF. It is inferred that the uncertainties in the thermal-hydraulic behaviors of fuels increase with respect to the key parameters as the power pulse becomes broader, and an accurate estimation of the energy deposition rate is required to reduce the uncertainty in the evaluation of the integrity of fuel if the CHF is expected to occur near the peak power. Therefore, the outputs are expected to provide rigorous interpretation of ongoing in-pile CHF experiments in the TREAT Facility reactor regarding thermal-hydraulic behavior of the fuel system aiming for a new transient in-pile CHF model.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

Mechanical degradation of duplex SiC-fiber reinforced SiC matrix composite tubes under a controlled high-temperature steam environment

This paper describes results from the mechanical evaluation of unirradiated SiC fiber–reinforced SiC matrix composite tubes under a controlled high-temperature steam environment. The experiments were aimed at identifying key material degradation behavior under environments relevant to loss-of-coolant accidents of light water reactors. Mechanical tests of the SiC composite tubes at 1000 °C under steam and inert environments were conducted using a unique test capability. Further, the material tested was a duplex tube with a thick monolithic SiC layer on the outer surface. The tubes were subjected to preloading at ~100 MPa in tension before exposure to high-temperature steam with up to 75% of the preload at a constant displacement. In the presence of matrix cracks, the steam exposure caused embrittlement of the SiC composite tubes and failure at a stress level below the pretest stress. The material degradation was explained by a fiber oxidation model, which can be applied to various SiC cladding concepts. The embrittlement could be a limiting factor for using SiC cladding subjected to loss-of-coolant accident conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Fatigue Testing and Characterization of Pre-hydrided Zircaloy-4 Cladding Tubes

The solubility of hydrogen in Zircaloy-4 (Zry-4) at the cladding operating temperature is near 100 wt. ppm. Above this solubility limit, excess hydrogen precipitates as δ-hydride platelets in the cladding material. Because of the effect of the thermal gradient across the cladding thickness on the migration and precipitation of hydrogen, hydride rims are often observed at the cladding outer surface; under excessive corrosion conditions hydride blisters are possible. It is well known that the fatigue of metal alloys, especially high cycle fatigue, is sensitive to the status of surface including the microstructure, roughness, and residual stress. Thus, the question considered herein, is whether excessive hydrogen pickup modifies the microstructure such that it has a degradation effect on the fatigue performance of cladding during operation. This report describes the evaluation of fatigue performance of a pre-hydrided Zry-4 cladding. A commercial Zry-4 was polished and pre-hydrided to 800 ppm and 1300 ppm H contents. The fatigue testing was conducted under strain control at 5 Hz with fully-reversed bending by using a cyclic integrated reversible bending fatigue tester (CIRFT). Six specimens with 1300 ppm and one specimen with 800 ppm were tested. Significant variation in test results were observed. While two of the 1300 ppm specimens failed with less than 1 ×10 5 cycles (at 0.32% and 0.41%), the four other samples did not fail over the strain amplitude range of 0.25% to 0.38%. Interestingly, the fracture initiation site of the failed samples was on the outside diameter (OD) surface rather than on the inside diameter (ID) surface as is typical for the as-polished cladding. This suggested a degrading effect of the hydriding process. Subsequently, three of the unfailed specimens were then further tested at ~0.43% to observe where failure initiation occurred. Significant variation was also observed in these three specimens. One specimen failed at ~9000 cycles while the two others failed at 43000 and 1.06 ×10 5 cycles. The performance here correlated to the location of failure initiation; failure initiated on the OD in the sample that failed after 9000 cycles while it initiated on the ID in the sample that failed after 43000 and 1.06 ×10 5 cycles. Flat features at the OD initiation sites suggest a brittle hydride feature on the surface of those samples was the cause of the degradation in fatigue performance, though the overall hydrogen levels in all samples was similar. A summary of all the observations is provided below: • The un-failed specimens with 1300 ppm H were cycled to failure with a higher amplitude near 0.43%. In addition, the fatigue-treated specimen tended to have a longer fatigue at the same induced amplitude. • Fractography revealed a mixed failure mode for the pre-hydrided specimen. Particularly, the specimen with fracture initiation site (FIS) located on the outer diameter surface of tube tended to have a shorter fatigue life than that of FIS on the inner diameter surface. • Etched cross section was shown to have hydride platelets aligned with tube longitudinal axis as expected, and the density of hydrides is at the similar level as in literature data. Meanwhile, a LECO procedure was applied for hydrogen concentration measurement, which showed the measured hydrogen contents are close to the nominal value. • With the polished cladding tube as baseline, O’Donnell-Lager (O-L) analysis showed that a decrease of about 50% in reduction-of-area (RA) would be needed for the O-L fitting to the fatigue data of 1300 ppm cladding. The suggestion for the next steps is provided.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Response of a Pressurized Water Reactor Dashpot Region to Commercial Drying Cycles

The purpose of this report is to document updates to the simulation of commercial vacuum drying procedures at the Nuclear Energy Work Complex at Sandia National Laboratories. Validation of the extent of water removal in a dry spent nuclear fuel storage system based on drying procedures used at nuclear power plants is needed to close existing technical gaps. Operational conditions leading to incomplete drying may have potential impacts on the fuel, cladding, and other components in the system. A general lack of data suitable for model validation of commercial nuclear canister drying processes necessitates additional, well-designed investigations of drying process efficacy and water retention. Scaled tests that incorporate relevant physics and well-controlled boundary conditions are essential to provide insight and guidance to the simulation of prototypic systems undergoing drying processes. This report documents testing updates for the Dashpot Drying Apparatus (DDA), an apparatus constructed at a reduced scale with multiple Pressurized Water Reactor (PWR) fuel rod surrogates and a single guide tube dashpot. This apparatus is fashioned from a truncated 5×5 section of a prototypic 17×17 PWR fuel skeleton and includes the lowest segment of a single guide tube, often referred to as the dashpot region. The guide tube in this assembly is open and allows for insertion of a poison rod (neutron absorber) surrogate.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Plutonium-238 Production Program Results, Implications, and Projections from Irradiation and Examination of Initial NpO 2 Test Targets for Improved Production

An alternative target design with potential improvements, including a major increase in 238 Pu production rate and annual capacity; fewer targets to be fabricated, irradiated, and processed; and a significant replacement of a large volume of caustic-nitrate, aluminum-bearing radioactive liquid waste with a smaller volume of solid metal waste, has been conceived and evaluated using reactor physics and thermal-hydraulic analyses. The alternative target design uses pressed pellets of 237 NpO 2 , sintered to 92% to 93% of theoretical density, and stacked inside a Zircaloy-4 cladding tube. Additionally, four test targets were fabricated, irradiated, and examined. No melting or other potential problems were indicated. Projections from measured constituents indicated annual production could be increased by a factor of ~2, and the number of targets required to be fabricated, irradiated, and processed could be reduced by a factor of ~5.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Tritium Pressure Enhancement on the TPBAR Cladding by Physical Processes at the Getter

Tritium for the U.S. nuclear weapon stockpile is produced in tritium producing burnable absorber rods (TPBARs) inserted into Tennessee Valley Authoritys (TVA) light-water nuclear reactors. The rods are stainless steel tubes with a permeation barrier coating and internal components that generate and contain the tritium. The TPBAR incorporates a Ni-plated Zircoloy getter tube to capture tritium and prevent it from reaching the rod cladding and permeating into the environment. Under the conventional view of getter behavior, the tritium pressure outside the getter tube is expected to be limited to the equilibrium vapor pressure of Zr hydride at the temperature of the rod as long as the total hydrogen concentration remains below the capacity of the hydride. Since the tritium pressure is higher within the rod core, this behavior relies on the thin getters ability to hold off a differential tritium pressure. The effective tritium pressure on the cladding can also be enhanced by isotope exchange. Hydrogen ingress through the cladding from the reactor coolant creates a hydrogen pressure on the outer surface of the getter that can exchange with tritium, allowing the tritium partial pressure to increase toward this hydrogen gettering pressure. The goal of this work was to use laboratory-scale experiments to examine these mechanisms and create a model of getter behavior that describes tritium transport within the TPBAR. A third mechanism wherein the concentration at the outer surface of the getter is increased by the temperature gradient within the getter tube wall (the Soret effect) is not experimentally tested but is captured in the model. While not conclusively demonstrated by the experiments due to low pressure, high temperature, and small gap volume conditions, the model shows that when combined, the three mechanisms can explain both the magnitude and time dependence of the tritium release observed for reactor fuel assemblies with TPBARs. The model also shows how various modifications of the TPBAR design can reduce this tritium release into the environment.

07 ISOTOPE AND RADIATION SOURCES↗
DOE OSTI2024

Enhanced Stress Relaxation Behavior via Basal ⟨a⟩ Dislocation Activity in Zircaloy-4 Cladding

Herein this work evaluates the stress relaxation behavior of textured Zircaloy-4 cladding to understand how mechanical anisotropy influences pellet-cladding interactions. Uniaxial and biaxial stress relaxation tests are performed using full-tube axial tension and internal pressurization, respectively, aiming to achieve 0.25%, 1%, and 2% equivalent strains in the cladding samples at a temperature of 300°C. Internal pressure relaxation test results display enhanced stress relaxation compared to axial testing results, particularly for samples loaded beyond yield. Results of electron backscatter diffraction indicate increased deformation microstructure during loading and increased strain homogenization and recovery during relaxation for samples loaded via internal pressurization. Analysis indicates that the increased production and activity of basal ⟨a⟩ dislocations play a significant role in the enhanced relaxation measured in samples subjected to internal pressurization.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

A Standardized Analysis Process Using Digital Image Correlation to Calculate In Situ Cladding Strain from Modified Burst Tests for Fuel Performance Code Validation

Historical data collection on nuclear fuel cladding materials has focused on generating a statistically significant amount of data to assess the material and its failure behavior. Furthermore, data generated to support material model and failure criteria development were previously posttest evaluations, so a large number of tests was required to gain new understanding. A way to expedite this process is to develop techniques capable of generating large, high-fidelity data sets from a single test with lower uncertainty or quantified uncertainty. One such example of this approach is Oak Ridge National Laboratory’s use of modified burst tests (MBTs) to analyze the mechanical behavior and failure conditions of cladding during a simulated reactivity-initiated accident (RIA). Each test incorporates digital image correlation (DIC) analysis techniques that are used to assess the accumulated strain in situ, as well as eventual cladding failure. This work has been fruitful in defining strain-to-failure conditions for materials like silicon carbide (SiC) fiber–reinforced/SiC matrix composite tubes (SiC/SiC), iron-chromium-aluminum (FeCrAl) alloy tubes, and chromium-coated Zircaloy-4 tubes. However, there are numerous DIC software available, including open-source and proprietary software. The different DIC software use various algorithms to process images and calculate displacement values. Using these different software and algorithms can lead to varying results, and perhaps larger-than-expected uncertainties. In the present study, previously published MBT data encompassing a variety of test conditions were reanalyzed with two different DIC software to assess the variance in the calculated strain results. The data consisted of SiC/SiC, FeCrAl, and chromium-coated Zircaloy-4 tubes. Plots of the calculated strains during the transient revealed good agreement between the two DIC software. The average root-mean-square errors between the two software was 0.20% strain, which is slightly larger than a previously reported error value for these tests. In conclusion, this variance in results is low enough that this analysis method can be used for code validation.

Reactivity-initiated accident↗
DOE OSTI2020

Milestone 2.7: Evaluation of Techniques for the Measurement of Molecular Hydrogen Gas in Helium Matrices

Published data by Task 2 (Oxyhydroxide Layer Radiolytic Gas Generation Resolution) for Technical Considerations and Challenges for Extended (>50 yrs) Dry Storage of Aluminum Cladded Spent Nuclear Fuel (ASNF), demonstrated that radiolytic molecular hydrogen (H2) production from gamma irradiated aluminum alloy 1100 (Al-1100) coupons exhibited significant dependence on backfill gaseous environment conditions: air, due to the presence of oxygen, completely inhibited H2 production; nitrogen promoted H2 production; and argon yielded more H2 than nitrogen environments. The concern here is that helium has been proposed as the backfill gas for extended storage and is more inert than argon, which may translate into significantly more H2 production than current Task 3 argon-based models predict. However, the measurement of H2 in helium media was not possible using the previously establish gas chromatography (GC) flame ionization detector, due to similarities in thermal conductivity. This milestone was initiated to evaluate an alternative GC approach that employed a mercuric oxide (HgO) reduction gas detector (RGD). Using the HgO RGD setup, H2 was successfully calibrated in the presence of a helium carrier gas, and then subsequently measured in control and irradiated crush-tube sample vials, consistent with previous sample measurements. Overall, the HgO RGD approach was found to be sufficient for future helium environment irradiations.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗
DOE OSTI2025

Development of Large Bore Rabbit Capsules in Support of BWR Cladding Irradiations in HFIR

The High Flux Isotope Reactor (HFIR) is an ideal tool for materials irradiation testing because of its intense steady-state neutron flux. Many programs take advantage of HFIR’s central flux trap for irradiation experiments using capsules, also known as rabbits, to support advanced materials development and reactor design. The facility that makes up the HFIR flux trap has recently undergone a design change that increases the HFIR primary coolant volumetric flow rate by removing restrictions in the system. As a result, the usable cross-sectional area within the facility increased, opening the door to increase the cross-sectional area of the rabbit capsules that fill the facility. This report documents a new large-diameter rabbit housing that increases the usable volume within the rabbit capsule by 22.6%. However, challenges arise with increasing the capsule size, such as establishing a new maximum capsule operating pressure and determining the thermal-hydraulic characteristics. This report addresses those challenges with previously adopted HFIR safety methods. The rupture pressure of the rabbit housings is demonstrated while verifying that capsule swelling during and after rupture will not block coolant flow. Then, a safety factor is applied to ascertain an administrative operating pressure. Additionally, the thermal-hydraulic performance of the HFIR facility filled with large-diameter rabbit capsules is shown to not violate previously determined safety criteria. Next, heat transfer coefficients are determined for use in design calculations. Furthermore, this report gives an example of internal configurations for the new, larger rabbit capsules that use relevant boiling water reactor (BWR) cladding geometry. Finally, this report documents an example thermal design performance for a rabbit capsule containing six gauge-curved tensile tube specimens. The thermal performance gives predicted temperature distributions within the capsule and shows the expected temperature of the passive thermometers for post-irradiation temperature comparisons.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗