Here, the formation and character of gallium vacancies (V Ga ) and their complexes in near surface and bulk regions of single crystal β-Ga 2 O 3 were explored using unintentionally doped single crystals grown by the Czochralski method. As-grown and O 2 annealed (up to 1550 °C) samples were investigated using positron annihilation spectroscopy (PAS) to study the top 0.05–6 μm, and also current–voltage measurements and infrared (IR) spectroscopy, with hydrogenated samples to probe V Ga , to study the bulk. After annealing in O 2 > 1000 °C, the β-Ga 2 O 3 resistivity begins increasing, up to ~10 9 Ω cm for 1550 °C treatment, with the top 0.5 mm being many orders of magnitude more resistive. PAS measurements of the top 6 μm (S values) and very near surface 200 nm (diffusion length, L) indicate differential behavior as a function of peak annealing temperature. At least four temperature regimes of behavior are described. V Ga are present in the bulk after growth, but considerable changes occur upon annealing at a temperature ≈1000 °C, where L and S decrease simultaneously, suggesting an increasing defect concentration (L) but a decreasing defect volume (S). Annealing at a temperature ≈1400 °C increases S again, showing an increasing volume concentration of V Ga , with IR absorption showing a large signature of V Ga -2H, indicative of increased V Ga formation that was not present when annealing at a temperature ≈1000 °C. These results suggest that defect changes from annealing in oxygen are depth dependent, and that V Ga configuration may not be the same near the oxygen-exposed surface of the sample and in the bulk.
74 ATOMIC AND MOLECULAR PHYSICS↗