NASA NTRS1983

Stress Corrosion Cracking of Certain Aluminum Alloys

SC resistance of new high-strength alloys tested. Research report describes progress in continuing investigation of stress corrosion (SC) cracking of some aluminum alloys. Objective of program is comparing SC behavior of newer high-strength alloys with established SC-resistant alloy.

Hasse, K. R.↗
NASA NTRS1976

Aqueous stress-corrosion cracking of high-toughness D6AC steel

The crack growth behavior of D6AC steel as a function of stress intensity, stress and corrosion history, and test technique, under sustained load in filtered natural seawater, 3.3 per cent sodium chloride solution, and distilled water, was investigated. Reported investigations of D6AC were considered in terms of the present study with emphasis on thermal treatment, specimen configuration, fracture toughness, crack-growth rates, initiation period, and threshold. Both threshold and growth kinetics were found to be relatively insensitive to these test parameters. The apparent incubation period was dependent on technique, both detection sensitivity and precracking stress intensity level.

Gilbreath, W. P.↗
NASA NTRS1974

Stress corrosion cracking of titanium alloys

The effect of hydrogen on the properties of metals, including titanium and its alloys, was investigated. The basic theories of stress corrosion of titanium alloys are reviewed along with the literature concerned with the effect of absorbed hydrogen on the mechanical properties of metals. Finally, the basic modes of metal fracture and their importance to this study is considered. The experimental work was designed to determine the effects of hydrogen concentration on the critical strain at which plastic instability along pure shear directions occurs. The materials used were titanium alloys Ti-8Al-lMo-lV and Ti-5Al-2.5Sn.

Statler, G. R.↗
NASA NTRS1985

Environmental Degradation of Materials: Surface Chemistry Related to Stress Corrosion Cracking

Parallel experiments have been performed in order to develop a comprehensive model for stress cracking (SCC) in structural materials. The central objective is to determine the relationship between the activity and selectivity of the microstructure of structural materials to their dissolution kinetics and experimentally measured SCC kinetics. Zinc was chosen as a prototype metal system. The SCC behavior of two oriented single-crystal disks of zinc in a chromic oxide/sodium sulfate solution (Palmerton solution) were determined. It was found that: (1) the dissolution rate is strongly (hkil)-dependent and proportional to the exposure time in the aggressive environment; and (2) a specific slip system is selectively active to dissolution under applied stress and this slip line controls crack initiation and propagation. As a precursor to potential microgrvity experiments, electrophoretic mobility measurements of zinc particles were obtained in solutions of sodium sulfate (0.0033 M) with concentrations of dissolved oxygen from 2 to 8 ppm. The equilibrium distribution of exposed oriented planes as well as their correlation will determine the particle mobility.

Schwarz, J. A.↗
NASA NTRS1987

Design Criteria for Controlling Stress Corrosion Cracking

This document sets forth the criteria to be used in the selection of materials for space vehicles and associated equipment and facilities so that failure resulting from stress corrosion will be prevented. The requirements established herein apply to all metallic components proposed for use in space vehicles and other flight hardware, ground support equipment, and facilities for testing. These requirements are applicable not only to items designed and fabricated by MSFC (Marshall Space Flight Center) and its prime contractors, but also to items supplied to the prime contractor by subcontractors and vendors.

Franklin, D. B.↗
NASA NTRS1984

Influence of precracked specimen configuration and starting stress intensity on the stress corrosion cracking of 4340 steel

Experimental results are presented from a study of the effects of precracked specimen configuration and initial starting stress intensity on crack growth rate and threshold stress intensity, for both onset of cracking and crack arrest. Attention is given to AISI 4340 steel in a 3.5-percent NaCl solution, for configurations of a single edge-cracked specimen tested in cantilever bending under constant load, and a modified compact specimen bolt loaded to a constant deflection. The threshold stress intensity value determined was independent of specimen configuration, if the stress intensity value associated with the compact specimen is taken where the discontinuous break occurs in the velocity-stress intensity curve.

Lisagor, W. B.↗
NASA NTRS1980

Stress corrosion cracking in the earth

Two fundamental concepts of fracture mechanics are used to develop a theory of the earthquake mechanism which specifically predicts observed time-dependent rupture phenomena such as slow earthquakes, postseismic rupture growth and afterslip, multiple events, foreshocks, and aftershocks. The theory also predicts that there must be a nucleation stage prior to an earthquake, and suggests a physical mechanism by which one earthquake may trigger another. Investigations show that all earthquakes must be preceded by a quasi-static slip over a portion of the rupture surfaces, although it may be difficult to detect in practice, and a study of delayed multiple events characterizes the strength of some barriers in the earth as having a stress corrosion index of about 24.

Das, S.↗
NASA NTRS1980

The relative stress-corrosion-cracking susceptibility of candidate aluminum-lithium alloys for aerospace structural applications

The microstructure and tensile properties of two powder metallurgy processed aluminum-lithium alloys were determined. Strength properties of 480 MPa yield and 550 MPa ultimate tensile strength with 5% strain to fracture were attained. Very little reduction in area was observed and fracture characteristics were brittle. The magnesium bearing alloy exhibited the highest strength and ductility, but fracture was intergranular. Recrystallization and grain growth, as well as coarse grain boundary precipitation, occurred in Alloy 2. The fracture morphology of the two alloys differed. Alloy 1 fractured along a plane of maximum shear stress, while Alloy 2 fractured along a plane of maximum tensile stress. It is found that a fixed orientation relationship exists between the shear fracture plane and the rolling direction which suggests that the PM alloys are strongly textured.

Pizzo, P. P.↗
NASA NTRS1970

Stress corrosion crack inhibiting method for titanium

Addition of oxyanions to liquid solvents in excess of the number of chloride, bromide, or iodide ions present prevents cracking of titanium-aluminum alloys under exposure to aqueous and other solvent environments. The molar concentration of oxyanion is set from 10 to 100 times higher than concentration of halide ions.

Beck, T. R.↗