Fractographic principles used for analyzing failure in metals are applied to the analysis of the microstructure and fracture of polytetrafluoroethylene. This material is used as seals in cryogenic systems.
Large area (100 sq cm) polysilicon solar cells having efficiencies of up to 14.1% (100 mW/sq cm, 25 C) were fabricated and a detailed analysis was performed to identify the efficiency loss mechanisms. The 1-5 characteristics of the best cell were dominated by recombination in the quasi-neutral base due to the combination of minority carrier diffusion length and base resistivity. An analysis of the microstructural defects present in the material and their effect on the electrical properties is presented.
The crystallization of a celsian glass composition was investigated as a possible high-temperature ceramic matrix material. Heat treatments invariably resulted in crystallization of the hexaclesian phase unless a flux, such as lithia, was added or a nucleating agent used (e.g., celsian seeds). TEM analysis revealed complex microstructures. Glasses with Mo additions contained hexacelsian, mullite, and an Mo-rich glass. Li2O additions stabilized celsian but mullite and Mo-rich glass were still present.
This report presents the results of an extensive micromechanical modeling effort for woven metal matrix composites. The model is employed to predict the mechanical response of 8-harness (8H) satin weave carbon/copper (C/Cu) composites. Experimental mechanical results for this novel high thermal conductivity material were recently reported by Bednarcyk et al. along with preliminary model results. The micromechanics model developed herein is based on an embedded approach. A micromechanics model for the local (micro-scale) behavior of the woven composite, the original method of cells (Aboudi), is embedded in a global (macro-scale) micromechanics model (the three-dimensional generalized method of cells (GMC-3D) (Aboudi). This approach allows representation of true repeating unit cells for woven metal matrix composites via GMC-3D, and representation of local effects, such as matrix plasticity, yarn porosity, and imperfect fiber-matrix bonding. In addition, the equations of GMC-3D were reformulated to significantly reduce the number of unknown quantities that characterize the deformation fields at the microlevel in order to make possible the analysis of actual microstructures of woven composites. The resulting micromechanical model (WCGMC) provides an intermediate level of geometric representation, versatility, and computational efficiency with respect to previous analytical and numerical models for woven composites, but surpasses all previous modeling work by allowing the mechanical response of a woven metal matrix composite, with an elastoplastic matrix, to be examined for the first time. WCGMC is employed to examine the effects of composite microstructure, porosity, residual stresses, and imperfect fiber-matrix bonding on the predicted mechanical response of 8H satin C/Cu. The previously reported experimental results are summarized, and the model predictions are compared to monotonic and cyclic tensile and shear test data. By considering appropriate levels of porosity, residual stresses, and imperfect fiber-matrix debonding, reasonably good qualitative and quantitative correlation is achieved between model and experiment.
Single crystal superalloys have become increasingly popular for turbine blade and vane applications due to their high strength, and creep and fatigue resistance at elevated temperatures. The crystallographic orientation of a single crystal material greatly affects its material properties, including elastic modulus, shear modulus, and ductility. These directional properties, along with the type of loading and temperature, dictate an anisotropic response in the yield strength, creep resistance, creep rupture ductility, fatigue resistance, etc. A significant amount of research has been conducted to determine the material properties in the <001> orientation, yet the material properties deviating from the <001> orientation have not been assessed for all cases. Based on the desired application and design criteria, a crystal orientation is selected to yield the maximum properties. Currently, single crystal manufacturing is able to control the primary crystallographic orientation within 15 of the target orientation, which is an acceptable deviation to meet both performance and cost guidelines; the secondary orientation is rarely specified. A common experiment is the standard load-controlled tensile test, in which specimens with different orientations can be loaded to observe the material response. The deformation behavior of single-crystal materials under tension and compression is known to be a function of not only material orientation, but also of varying microdeformation (i.e. dislocation) mechanisms. The underlying dislocation motion causes deformation via slip, and affects the activation of specific slip systems based on load and orientation. The slip can be analyzed by observing the visible traces left on the surface of the specimen from the slip activity within the single crystal material. The goal of this thesis was to predict the slip systems activated in three-dimensional stress fields of a notched tensile specimen, as a function of crystal orientation, using finite element analysis without addressing microstructural deformation mechanisms that govern their activation. Out of three orientations tested, the specimen with a [110] load orientation and a [001] growth direction had the lowest maximum resolved shear stress; this specimen orientation appears to be the best design candidate for a tensile application.
Thermally sprayed coatings are being studied and developed as methods of enabling lightweight composites to be used more extensively as structural components in propulsion applications in order to reduce costs and improve efficiency through weight reductions. The primary goal of this work is the development of functionally graded material [FGM] polymer/metal matrix composite coatings to provide improved erosion/oxidation resistance to polyimide-based polymer matrix composite [PMC] substrates. The goal is to grade the coating composition from pure polyimide, similar to the PMC substrate matrix on one side, to 100 % WC-Co on the other. Both step-wise and continuous gradation of the loading of the WC-Co reinforcing phase are being investigated. Details of the coating parameter development will be presented, specifically the high velocity oxy-fuel [HVOF] combustion spraying of pure PMR-11 matrix material and layers of various composition PMR-II/WC-Co blends onto steel and PMR-15 composite substrates. Results of the HVOF process optimization, microstructural characterization, and analysis will be presented. The sprayed coatings were evaluated using standard metallographic techniques - optical and scanning electron microscopy [SEM]. An SEM + electron dispersive spectroscopy [EDS] technique has also been used to confirm retention of the PMR-II component. Results of peel/butt adhesion testing to determine adhesion will also be presented.
Thermally sprayed coatings are being studied and developed as methods of enabling lightweight composites to be used more extensively as structural components in propulsion applications in order to reduce costs and improve efficiency through weight reductions. The primary goal of this work is the development of functionally graded material [FGM] polymer/metal matrix composite coatings to provide improved erosion/oxidation resistance to polyimide-based polymer matrix composite [PMC] substrates. The goal is to grade the coating composition from pure polyimide, similar to the PMC substrate matrix on one side, to 100% WC-Co on the other. Both step-wise and continuous gradation of the loading of the WC-Co reinforcing phase are being investigated, Details of the coating parameter development will be presented, specifically the high velocity oxy-fuel [HVOF] combustion spraying of pure PMR-I1 matrix material and layers of various composition PMR-II/WC-Co blends onto steel and PMR-15 composite substrates. Results of the HVOF process optimization, microstructural characterization, and analysis will be presented. The sprayed coatings were evaluated using standard metallographic techniques - optical and scanning electron microscopy [SEMI. An SEM + electron dispersive spectroscopy [EDS] technique has also been used to confirm retention of the PMR-I1 component. Results of peel/butt adhesion testing to determine adhesion will also be presented.
A new solid lubricant coating, NASA PS400, has been developed for high temperature tribological applications. This plasma sprayed coating is a variant of the patented PS304 coating and has been formulated to provide higher density, smoother surface finish and better dimensional stability than PS304. PS400 is comprised of a nickel-molybdenum binder that provides strength, creep resistance and extreme oxidative and dimensional stability. Chromium oxide, silver and barium-calcium fluoride eutectic are added to the binder to form PS400.Tribological properties were evaluated with a pin-on-disk test rig in sliding contact to 650 C. Coating material samples were exposed to air, argon and vacuum at 760 C followed by cross section microscopic analysis to assess microstructure stability. Oil-Free microturbine engine hot section foil bearing tests were undertaken to assess PS400 s suitability for hot foil gas bearing applications. The preliminary results indicate that PS400 exhibits tribological characteristics comparable to the PS304 coating but with enhanced creep resistance and dimensional stability suitable for demanding, dynamic applications.
Gas turbine engines for military/commercial fixed-wing and rotary wing aircraft use thermal barrier coatings in the high-temperature sections of the engine for improved efficiency and power. The desire to further make improvements in gas turbine engine efficiency and high power-density is driving the research and development of thermal barrier coatings and the effort of improving their tolerance to fine foreign particulates that may be contained in the intake air. Both commercial and military aircraft engines often are required to operate over sandy regions such as in the Middle-East nations, as well as over volcanic zones. For rotorcraft gas turbine engines, the sand ingestion is adverse during take-off, hovering near ground, and landing conditions. Although, most of the rotorcraft gas turbine engines are fitted with inlet particle separators, they are not 100 percent efficient in filtering fine sand particles of size 75 microns or below. The presence of these fine solid particles in the working fluid medium has an adverse effect on the durability of turbine blade thermal barrier coatings and overall performance of the engine. Typical turbine blade damages include blade coating wear, sand glazing, Calcia-Magnesia-Alumina-Silicate (CMAS) attack, oxidation, plugged cooling holes, all of which can cause rapid performance deterioration including loss of aircraft. The objective of this research is to understand the fine particle interactions with typical ceramic coatings of turbine blades at the microstructure level. A finite-element based microstructure modeling and analysis has been performed to investigate particle-surface interactions, and restitution characteristics. Experimentally, a set of tailored thermal barrier coatings and surface treatments were down-selected through hot burner rig tests and then applied to first stage nozzle vanes of the Gas Generator Turbine of a typical rotorcraft gas turbine engine. Laser Doppler velocity measurements were performed during hot burner rig testing to determine sand particle incoming velocities and their rebound characteristics upon impact on coated material targets. Further, engine sand ingestion tests were carried out to test the CMAS tolerance of the coated nozzle vanes. The findings from this on-going collaborative research to develop the next-gen sand tolerant coatings for turbine blades are presented in this paper.
This study compares the microstructure and tensile properties of Haynes 282 fabricated using laser powder bed fusion and laser powder directed energy deposition. Both sets underwent stress-relieving, followed by hot isostatic pressing, and the standard double aging heat treatment. Tensile testing was conducted at room temperature on specimens fabricated with both technologies to evaluate and compare their tensile behaviors. Results show that the ultimate tensile and yield strengths of laser powder bed fused specimens were 18% and 57% higher, respectively than those of laser powder directed energy deposited ones, whereas the elongation to failure was similar in both. The difference in strengths is attributed to the differences in the size of ɣ' precipitates and grains, i.e., those in the LP-DED specimens being larger, whereas similar elongation to failure is attributed to the carbide debonding dominating the fracture mechanism in both batches.
Images of microstructures analyzed by transform methods. Report discusses determination of distributions of grain sizes by analysis of images of microstructures.
Introduction: The origin of diamonds in ureilitic meteorites, a major family of ultramafic achondrites, has long been debated, with various formation mechanisms inferred, including: 1) shock conversion of preexisting graphite due to a hypervelocity impact on the ureilite parent body [e.g., 1]; 2) vapor deposition during condensation of the solar nebula [e.g., 2]; or 3) static transformation in the mantle of a large planetesimal (>1000 km in diameter) [e.g., 3]. The Kenna ureilite is a 10.9 kg stone that was found in Kansas in 1972 and is dominantly composed of olivine and pigeonite (68% and 22% modal abundance, respectively), together with minor metal and carbon-rich regions. Within the carbon-rich domains researchers have identified microdiamonds up to ~10 µm in size [4]. Methods: Due to the proximity of the extremely hard microdiamonds with soft graphite and moderately hard silicates, achieving an appropriately flat surface for electron backscatter diffraction (EBSD) analysis has proven challenging. We have, therefore, employed a Hitachi ArBlade 5000 broad beam Ar ion milling system to prepare a sample with an adequately uniform surface flatness across the various minerals. The ion milling dramatically im-proved indexing of the EBSD patterns and facilitated high-resolution microstructural analysis of the carbon-rich domains. After microstructural EBSD analyses using an Oxford Symmetry detector we collected coordinated hy-perspectral cathodoluminescence (CL) analyses using a Gatan Monarc system mounted on a JEOL 7900F field emission (FE) scanning electron microscope at NASA Johnson Space Center. A focused ion beam (FIB) foil was extracted from a region of interest and analyzed using a JEOL 2500 FE scanning transmission electron microscope (STEM). In situ carbon and nitrogen isotopic analyses were collected from diamond-bearing domains using a Cameca NanoSIMS 50L at NASA JSC. Results: The carbon rich regions occur as tabular domains between polygonal olivine and pigeonite, and are composed of aggregates of micrometer-scale diamond with intermediate graphite, oxides and metal grains. Within the microdiamonds, {111} twins are abundant, many of which form ragged lamellae consistent with mechanical twinning. The microdiamond assemblages appear to pseudomorph tabular graphite habits, which together with the abundant deformation twins, support a shock transformation mechanism for microdiamond formation within the Kenna meteorite. Further supporting this observation, the diamond laths show close alignment of <111> and <110> between domains, consistent with a solid-state transformation from graphite along <0001> and <1-210>, respec-tively [5]. A FIB foil was extracted from a region with mechanical twins, and high resolution STEM analyses reveal cross-cutting veins of graphite and oriented kamacite crystals together with additional sets of {111} nano-twins formed in at least three orientations. Isotopic analyses of C and N reveal sector zoning patterns [cf. 3] that are unre-lated to the diamond substructure identified by EBSD yet consistent with hyperspectral CL images. Conclusions: These data provide new constraints on microdiamond formation within ureilites. The microdia-monds exhibit orientation variants defined by aligned <111> and <110> axes consistent with inherited crystallo-graphic orientations from transformation of a single hexagonal graphite parent crystal [5]. Crosscutting the micro-diamonds are veins of graphite and kamacite, together with additional {111} nanotwins. Taken together these data suggest that microdiamonds from ureilites formed from a solid state, diffusionless transformation from graphite, likely associated with a major shock event, which was subject to subsequent reversion either during decompression or a later deformation event. The N and C isotopic sector zoning is unrelated to diamond microstructures and likely reflects inheritance from the parent graphite crystal.
The goal of an ongoing project at NASA Glenn is to investigate the effects of the complex microstructure of a woven ceramic matrix composite and its variability on the effective properties and the durability of the material. Detailed analysis of these complex microstructures may provide clues for the material scientists who `design the material? or to structural analysts and designers who `design with the material? regarding damage initiation and damage propagation. A model material system, specifically a five-harness satin weave architecture CVI SiC/SiC composite composed of Sylramic-iBN fibers and a SiC matrix, has been analyzed. Specimens of the material were serially sectioned and polished to capture the detailed images of fiber tows, matrix and porosity. Open source analysis tools were used to isolate various constituents and finite elements models were then generated from simplified models of those images. Detailed finite element analyses were performed that examine how the variability in the local microstructure affected the macroscopic behavior as well as the local damage initiation and progression. Results indicate that the locations where damage initiated and propagated is linked to specific microstructural features.
The origin of diamonds in ureilitic meteorites, a major family of ultramafic achondrites, has long been debated, with various formation mechanisms inferred, including: 1) shock conversion of preexisting graphite due to a hypervelocity impact on the ureilite parent body; 2) vapor deposition during condensation of the solar nebula; or 3) static transformation in the mantle of a large planetesimal (>1000 km in diameter). The Kenna ureilite is a 10.9 kg stone that was found in Kansas in 1972 and is dominantly composed of olivine and pigeonite (68% and 22% modal abundance, respectively), together with minor metal and carbon-rich regions. Within the carbon-rich domains researchers have identified microdiamonds up to ~10 µm in size. Due to the proximity of the extremely hard microdiamonds with soft graphite and moderately hard silicates, achieving an appropriately flat surface for electron backscatter diffraction (EBSD) analysis has proved challenging. We have, therefore, employed a Hitachi ArBlade 5000 broad beam Ar ion milling system to prepare a sample with an adequate surface uniformity. The ion milling dramatically improved indexing of the EBSD patterns and facilitated high-resolution microstructural analysis of the carbon-rich domains. The carbon-bearing regions occur as tabular domains between polygonal olivine and pigeonite, and are composed of aggregates of micrometer-scale diamond with intermediate graphite, oxides and metal grains. Within the microdiamonds, {111} twins are abundant, many of which form ragged lamellae consistent with mechanical twinning. The microdiamond assemblages appear to pseudomorph tabular graphite habits, which together with the abundant deformation twins, supports a shock transformation mechanism for microdiamond formation within the Kenna meteorite. To compliment the EBSD microstructural analyses, coordinated laser Raman, focused ion beam/transmission electron microscopy imaging and diffraction data, and NanoSIMS N and C tomographic isotopic imaging will be collected. These data will provide further constraints on the formation of diamonds within ureilites.
Aluminum-copper-magnesium-silver (Al-Cu-Mg-Ag) alloys that were developed for thermal stability also offer attractive ambient temperature strength-toughness combinations, and therefore, can be considered for a broad range of airframe structural applications. The current study evaluated Al-Cu-Mg-Ag alloy RX226-T8 in plate gages and compared performance with sheet gage alloys of similar composition. Uniaxial tensile properties, plane strain initiation fracture toughness, and plane stress tearing resistance of RX226-T8 were examined at ambient temperature as a function of orientation and thickness location in the plate. Properties were measured near the surface and at the mid-plane of the plate. Tensile strengths were essentially isotropic, with variations in yield and ultimate tensile strengths of less than 2% as a function of orientation and through-thickness location. However, ductility varied by more than 15% with orientation. Fracture toughness was generally higher at the mid-plane and greater for the L-T orientation, although the differences were small near the surface of the plate. Metallurgical analysis indicated that the microstructure was primarily recrystallized with weak texture and was uniform through the plate with the exception of a fine-grained layer near the surface of the plate. Scanning electron microscope analysis revealed Al-Cu-Mg second phase particles which varied in composition and were primarily located on grain boundaries parallel to the rolling direction. Fractography of toughness specimens for both plate locations and orientations revealed that fracture occurred predominantly by transgranular microvoid coalescence. Introduction High-strength, low-density Al-Cu-Mg-Ag alloys were initially developed to replace conventional 2000 (Al-Cu-Mg) and 7000 (Al-Zn-Cu-Mg) series aluminum alloys for aircraft structural applications [1]. During the High Speed Civil Transport (HSCT) program, improvements in thermal stability were demonstrated for candidate aircraft wing and fuselage skin materials through the addition of silver to Al-Cu-Mg alloys based on Al 2519 chemistry [2]. Thermal stability of the resulting Al-Cu-Mg-Ag alloys, C415-T8 and C416-T8, was due to co-precipitation of the thermally stable . (AlCu) and ' (Al2Cu) strengthening phases [1-4]. The strength and toughness behavior was investigated for these alloys produced as 0.090-inch thick rolled sheet in the T8 condition and after various thermal exposures. The mechanical properties were shown to be competitive with conventional aircraft alloys, 2519-T8 and 2618-T8 [2]. During the Integral Airframe Structure (IAS) program, advanced aluminum alloys were examined for use in an integrally stiffened airframe structure where the skin and stiffeners would be machined from plate and extruded frames would be mechanically attached (see Figure 1) [5]. Advantages of integrally stiffened structure include reduced part count, and reduced assembly times compared to conventional built-up airframe structure. The near-surface properties of a thick plate are of significance for a machined integrally stiffened airframe structure since this represents the skin location. Properties measured at the mid-plane of the plate are more representative of the stiffener web. RX226 was developed to exploit strength-toughness improvements and thermal stability benefits of Al-Cu-Mg-Ag alloys in plate gages. This study evaluated the microstructure and properties of three gages of plate produced in the T8 condition.
SiC fiber-bonded ceramics (SA-Tyrannohex: SA-THX) diffusion-bonded with TiCu metallic interlayers were investigated. Thin samples of the ceramics were prepared with a focused ion beam (FIB) and the interfacial microstructure of the prepared samples was studied by transmission electron microscopy (TEM) and scanning TEM (STEM). In addition to conventional microstructure observation, for detailed analysis of reaction compounds in diffusion-bonded area, we performed STEM-EDS measurements and selected area electron diffraction (SAD) experiments. The TEM and STEM experiments revealed the diffusion-bonded area was composed of only one reaction layer, which was characterized by TiC precipitates in Cu-Si compound matrix. This reaction layer was in good contact with the SA-THX substrates, and it is concluded that the joint structure led to the excellent bonding strength.
Experimental work is reported which was directed toward obtaining interface shape control while a numerical thermal analysis program was being made operational. An experimental system was developed in which the solid-liquid interface in a directionally solidified aluminum-nickel eutectic could be made either concave to the melt or convex to the melt. This experimental system provides control over the solid-liquid interface shape and can be used to study the effect of such control on the microstructure. The SINDA thermal analysis program, obtained from Marshall Space Flight Center, was used to evaluate experimental directional solidification systems for the aluminum-nickel and the aluminum-copper eutectics. This program was applied to a three-dimensional ingot, and was used to calculate the thermal profiles in axisymmetric heat flow. The results show that solid-liquid interface shape control can be attained with physically realizable thermal configurations and the magnitudes of the required thermal inputs were indicated.
NASA Marshall Space Flight Center has developed a novel directional solidification furnace prototype for processing metals and alloys experiments in a microgravity environment. The BUNDLE (Bridgman Unidirectional Dendrite in Liquid Experiment) furnace is intended to accommodate the science requirements of Flight Definition Principle Investigators studying cellular/dendritic growth in aluminum and lead alloys at processing temperatures up to 1200 C. The furnace implements a number of innovative features to achieve high thermal gradients and quench rates in a low-power, light-weight design. These include a pyrolytic boron nitride/graphite composite heating element surrounded by layers of self-supporting refractory metal shielding, and a graphite fiber enhanced cold zone allowing high levels of heat extraction from the sample crucible. Novel to the BUNDLE design is an in-situ helium gas quench capability that ensures rapid freezing of the solidifying region (mushy zone) of the metal sample within the furnace without sample disturbance prior to quenching; this is a stringent requirement for subsequent analysis and understanding of microstructural development. The experiment hardware concept features multiple furnaces that may be "bundled" together so many samples, currently up to eight, can be processed at one time. The design of BUNDLE is flexible enough to be implemented on the Shuttle and Space Station in a number of locations (SpaceHab, Express Rack, MPESS, ISPR, etc). BUNDLE prototype furnaces have directionally solidified and quenched 1cm diameter lead - 5.8 weight percent antimony and aluminum - 4 weight percent copper alloys. Quenching of the mushy zone, as recorded by in-situ thermocouples, occurred on the order of 0.5 seconds or less, a rate within the PI's requirements. Subsequent metallographic examination revealed the solidified microstructure to be, as expected, unidirectional. Both the dendrite tips and the eutectic reaction were planar in nature indicating uniform axial heat flow. Delineation between the growing dendrites and eutectic structure with the "quenched-in" liquid was sharp, attesting to the efficacy of the helium quench. BUNDLE's conception, development, capability, and adaptability are presented (in view of Flight PI's needs and science requirements) through viewgraphs depicting actual hardware, generated thermal analysis, and micrographs prepared from BUNDLE processed, flight-like samples.