DOE OSTI2023

Analysis of Deformation and Fracture Mechanisms in the Harvested Low-Dose Baffle Former Bolt via Advanced Mechanical Tests

This report details the production of tensile specimens from in-service irradiated baffle former bolts (BFBs) and presents the results of a pilot in-situ SEM/EBSD test conducted at Oak Ridge National Laboratory’s Low Activation Materials Development and Analysis (LAMDA) facility. The SEM/EDS results confirmed that the material is AISI 316L steel, not AISI 347, and that no Nb addition was detected in several analyzed locations. EBSD analysis of the microstructure revealed in-grain misorientation gradients indicative of cold work, likely caused by material processing, and no retained ferrite was identified. During straining, dislocation channel formation was the primary deformation mechanism, with twinning also observed in favorably oriented grains at local strains as small as ~1.5%. No strain-induced phase instability was observed, likely due to the fact that the Ni and Cr content reached the upper limits for the 316L steel specification. Multiple microfracture events were observed during the tensile test. Fine strain-induced pores formed at the channel-grain boundary intersection points, while coarser microcracks were associated with non-metallic inclusions. Data analysis is ongoing, and additional tests are planned in the near future to provide more statistics and details.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Crystal Plasticity Simulation of Magnesium and Its Alloys: A Review of Recent Advances

Slip and extension twinning are the dominant deformation mechanisms in Magnesium (Mg) and its alloys. Crystal plasticity is a powerful tool to study these deformation mechanisms. Different schemes have incorporated crystal plasticity models to capture different properties, which vary from the simple homogenization Taylor model to the full-scale crystal plasticity finite element model. In the current study, a review of works available in the literature that addresses different properties of Mg and its alloys using crystal plasticity modes is presented. In addition to slip and twinning, detwinning is another deformation mechanism that is activated in Mg and its alloys. The different models that capture detwinning will also be addressed here. Finally, the recent experimental frameworks, such as in-situ neutron diffraction, 3D high energy synchrotron X-ray techniques, and digital image correlation under scanning electron microscopy (SEM-DIC), which are incorporated along crystal plasticity models to investigate the properties of Mg and its alloys, are addressed. Future research directions towards improving the deformation response of Mg and its alloys are identified, which can lead to increased deployment of the lightest structural metal in engineering applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Origin, parameters, and underlying deformation mechanisms of propagating deformation bands in irradiated 316L stainless steel

Lüders-type propagating deformation bands were observed in specimens of irradiated 316L stainless steel samples removed from Spallation Neutron Source target vessels after service. Mechanical testing with digital image correlation (DIC) and in-situ tensile testing with scanning electron microscopy electron backscatter diffraction showed that the observed Lüders-type behavior was not related to the known transformation-induced plasticity or twinning-induced plasticity behavior. Instead, the phenomenon occurs at small local strain values before a significant amount of martensite or deformation twins appear in the microstructure. Microstructural analysis and in-situ mechanical test results suggest Lüders-type band formation and propagation were related to the appearance and evolution of defect-free channels—analogous to slip bands. A modified Swift equation with a Ludwigson-like component was offered to rationalize the phenomenon and model the strain-softening processes at small strain values. Finally, the results indicate complex microstructural processes and deformation mechanisms were active at small strain values and underline the benefits of advanced mechanical test approaches such as DIC.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Visualization and validation of twin nucleation and early-stage growth in magnesium

The abrupt occurrence of twinning when Mg is deformed leads to a highly anisotropic response, making it too unreliable for structural use and too unpredictable for observation. Here, we describe an in-situ transmission electron microscopy experiment on Mg crystals with strategically designed geometries for visualization of a long-proposed but unverified twinning mechanism. Combining with atomistic simulations and topological analysis, we conclude that twin nucleation occurs through a pure-shuffle mechanism that requires prismatic-basal transformations. Also, we verified a crystal geometry dependent twin growth mechanism, that is the early-stage growth associated with instability of plasticity flow, which can be dominated either by slower movement of prismatic-basal boundary steps, or by faster glide-shuffle along the twinning plane. The fundamental understanding of twinning provides a pathway to understand deformation from a scientific standpoint and the microstructure design principles to engineer metals with enhanced behavior from a technological standpoint.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Columnar Grain-driven Plasticity and Cracking in Nanotwinned FCC Metals

The mechanisms of strengthening and plasticity in columnar-grained metals with preferentially oriented nano-sized twins have been examined traditionally by considering dislocation processes, but rarely from the perspective of grain boundary (GB) deformation. Here, the effects of GB strain accommodation on plastic deformation in four different columnar-grained nanocrystalline nanotwinned (nt) face-centered-cubic metals (Cu, Ag, Al, and Ni) were studied by large-scale molecular dynamics simulations. It is observed that in tensile deformation parallel to coherent twin boundaries (CTBs), the dislocation mechanisms in each metal are identical and associated with GB emissions of jog and threading dislocations at small and large CTB spacings, respectively. However, CTB strengthening effects are increasingly more pronounced in columnar-grained nt metals as their shear modulus increases, which is rationalized by the dependence of GB stress concentrations on twin size, metal type and strain rate. Also, while flow stresses in nt-Cu, nt-Ag, and nt-Al metals increase linearly with decreasing CTB spacing, a maximum strength limit is reached in nt-Ni below a critical CTB spacing of 6 nm. The strength limit in nt-Ni results from columnar GB cracking induced by prominent GB sliding. For columnar-grained microstructures, GB sliding is equivalent in nt-Ag and nt-Al and slightly lower in nt-Cu but markedly higher in nt-Ni. These findings underscore the importance of new GB deformation mechanisms on plasticity and fracture in columnar-grained nt metals and enrich our understanding of CTB strengthening in fcc metals synthesized in the literature.

36 MATERIALS SCIENCE↗
NASA NTRSDate not supplied

Twin nucleation and growth mechanism in Ni-based superalloys

While micro-twinning is the dominant creep deformation mechanism in Ni-based superalloys at temperatures above 700 C, many aspects of twin nucleation and growth remain unexplored. Kolbe mechanism for micro-twinning, based on thermally activated reordering, is probably the only concept currently widely accepted by the scientific community. We propose a qualitatively different mechanism for nucleation and growth of twins. The mechanism can be briefly described as follows. Penetration of a gamma prime precipitate by two 1/2(110) edge dislocations travelling on adjacent {111} glide planes triggers nucleation (at the interface of the precipitate and the matrix) and emission of Shockley partial of screw character on the glide plane of the edge dislocation, which entered the precipitate first (generating trailing high-energy anti-phase boundary (APB)). Propagation of this Shockley partial into the precipitate converts the APB into super intrinsic stacking fault (SISF). The recurring arrival of additional edge dislocations on the glide planes adjacent to the configuration described above leads to formation of super extrinsic stacking fault SESF, subsequent micro-twin formation, and growth of the twinned region. We demonstrate the proposed mechanism via molecular dynamics simulations.

Ni-superalloys↗
NASA NTRSDate not supplied

Twin nucleation and growth mechanism in Ni-based superalloys

While micro-twinning is the dominant creep deformation mechanism in Ni-based superalloys at temperatures above 700 C, many aspects of twin nucleation and growth remain unexplored. Kolbe mechanism for micro-twinning, based on thermally activated reordering, is probably the only concept currently widely accepted by the scientific community. We propose a qualitatively different mechanism for nucleation and growth of twins. The mechanism can be briefly described as follows. Penetration of a   precipitate by two 1/2(110) edge dislocations travelling on adjacent {111} glide planes triggers nucleation (at the interface of the precipitate and the matrix) and emission of Shockley partial of screw character on the glide plane of the edge dislocation, which entered the precipitate first (generating trailing high-energy anti-phase boundary (APB)). Propagation of this Shockley partial into the precipitate converts the APB into super intrinsic stacking fault (SISF). The recurring arrival of additional edge dislocations on the glide planes adjacent to the configuration described above leads to formation of super extrinsic stacking fault SESF, subsequent micro-twin formation, and growth of the twinned region. We demonstrate the proposed mechanism via molecular dynamics simulations.

Ni-based superalloys↗
DOE OSTI2024

Androgynous { 10 1 ¯ 2 } twin in zinc

Under ambient conditions, Zn is a hexagonal metal with a large c / a ratio of 1.856. Plastic deformation is predominantly accommodated by basal 〈 a 〉 slip and compression twins on the { 10 1 ¯ 2 } planes. Increasing hydrostatic pressure drastically reduces the c / a ratio of Zn and, when a critical threshold of c / a = 3 at about 10 GPa is crossed, the { 10 1 ¯ 2 } twins are predicted to change from compressive to tensile in nature. What happens at the transition point, when c / a = 3 , remains unknown. Here, we strain-cycle a textured polycrystalline sample of pure Zn at uniform hydrostatic pressures ranging between 2 and 17 GPa, over which the c / a ratio crosses the c / a = 3 compressive-tensile transition for { 10 1 ¯ 2 } twins. During deformation, the state of the sample is monitored through x-ray diffraction to extract texture and internal strain evolution. By comparing the experimental results with the predictions of an elastoviscoplastic polycrystal simulation, we confirm the androgynous nature of { 10 1 ¯ 2 } twin response at low and high pressures. When c / a = 3 , polycrystalline Zn does not display any evidence of twinning and its plastic behavior is controlled by mostly basal and pyramidal 〈 c + a 〉 slip activity, with a very small contribution of prismatic 〈 a 〉 slip. Evidence for the activity of other { 10 1 ¯ n } twinning modes, which have been suggested for Zn under high pressure, are not observed. Published by the American Physical Society 2024

Merkel, Sébastien (ORCID:000000032767581X)↗
DOE OSTI2021

Comparing the deformation mechanism in 316 L stainless steel fabricated by hybrid and additive manufacturing

This study rationalizes the relatively higher elongation with minimal strength drop of 316L stainless steel (316LSS) manufactured using the hybrid approach in comparison to a fully additive approach followed by machining. It was found that twinning was the dominant deformation mechanism in 316LSS produced by both additive and hybrid approaches. Additionally, the relatively lower fraction of twins in the as-fabricated state of hybrid approach compared to a fully additive approach resulted in delaying the onset of steady-state strain hardening rate to higher strain levels, thereby resulting in an overall increase in elongation to failure.

36 MATERIALS SCIENCE↗
NASA NTRSDate not supplied

Effect of Alloying Additions on Twinning in Ni-Based Superalloys

Micro-twinning is the dominant creep deformation mechanism in Ni-based superalloys at temperatures above 700 C. We use atomistic simulations to study two mechanisms of twin nucleation and growth that are characterized by qualitatively different rate limiting processes. In case of the mechanism proposed by Kolbe, the rate limiting process is diffusion-mediated atomic reshuffling. In case of the other mechanism, we proposed recently, the rate limiting process is nucleation of Shockley partial dislocation. We demonstrate the effects of alloying additions on functionality of these mechanisms.

Ni-based superalloys↗
DOE OSTI2022

Grain boundary slip – twin transmission in titanium

Here, using a combination of mechanical testing, scanning electron microscopy, and a unified crystal plasticity framework for discrete intragranular shear localization, we investigate intense, localized slip bands on prismatic planes and {10$\bar{1}$2} $\langle$$\bar{1}$011$\rangle$ tensile twins, and their transmission across the grain boundaries (GBs) in commercially pure titanium. The analyses show that the orientation and curvature of the GB influence the local stress fields at the GBs, and consequently, the slip/twin transmission across the boundary. In addition to host grain properties, neighboring grain properties, such as active slip systems and instances of heterogeneity like slip bands and twins, heavily affect the deformation mechanisms in each grain. Finally, the applicability of geometric factors to predict the transmission in the experimentally observed co-located pairs is discussed. The local stress field calculated by the discrete slip and twin band model is shown to be capable of determining whether a transmission has occurred in an observed co-located pair, and also the direction of the transmission.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure characterization and elastic-plastic self-consistent simulation studies of anisotropic deformation of β -tin

Uniaxial compression tests of 99.9% pure polycrystalline $β$-tin (Sn) were conducted at various strain rates (10 -3 /s, 10 -1 /s and 1/s) and temperatures (294 K and 193 K) to understand the effects of these variables on the stress–strain response, microstructure evolution, and stress relaxation behavior. Multiple Sn specimens were subjected to complex compressive loading/unloading/reloading paths at different strain rates. Specimens initially compressed at higher strain rates showed strain rate-dependent texture evolution and more pronounced relaxation upon reloading, as compared to those pre-strained at lower rates at room temperature (RT). Compression tests conducted at low temperature (193 K) revealed increased strength, similar to the enhanced strength observed when the strain rate was increased at RT. Neutron diffraction was employed to characterize the initial and final bulk textures of the RT specimens. Electron backscatter diffraction was utilized to examine the crystallographic grain orientation and morphology, thereby identifying the signatures of dislocation-mediated deformation, grain refinement, recrystallization, and twinning behaviors. Elastic-plastic self-consistent simulations were performed to investigate the deformation modes responsible for the strain rate-dependent macroscopic stress–strain response and texture evolution. Effects of crystallographic orientation on stress relaxation behavior was also examined. In conclusion, the model predictions are in reasonable agreement with experimental observations.

36 MATERIALS SCIENCE↗
NASA NTRS2024

Effects of Alloying Elements on Twinning in Ni-Based Superalloys

Micro-twinning is the major creep deformation mechanism in Ni-based superalloys at temperatures above 700 C. Recent experiments suggest that superlattice stacking faults in   phase may serve as the precursors to twin formation. Segregation of alloying elements to these precursors may have a significant effect on formation and extension of micro-twins. Using atomistic modeling we investigate and explain the effects of Cr and Nb alloying additions on these processes. Our results help to rationalize the experimentally observed puzzling effects of elemental composition of the alloy on creep resistance.

Ni-based superalloys↗
DOE OSTI2021

Interrogating the Effects of Hydrogen on the Behavior of Planar Deformation Bands in Austenitic Stainless Steel

The effects of internal hydrogen on the deformation microstructures of 304L austenitic stainless steel have been characterized using electron backscattered diffraction (EBSD), transmission Kikuchi diffraction (TKD), high-resolution scanning transmission electron microscopy (HRSTEM), and nanoprobe diffraction. Samples, both thermally precharged with hydrogen and without thermal precharging, were subjected to tensile deformation of 5 and 20 pct true strain followed by multiple microscopic interrogations. Internal hydrogen produced widespread stacking faults within the as-forged initially unstrained material. While planar deformation bands developed with tensile strain in both the hydrogen-precharged and non-precharged material, the character of these bands changed with the presence of internal hydrogen. As shown by nanobeam diffraction and HRSTEM observations, in the absence of internal hydrogen, the bands were predominantly composed of twins, whereas for samples deformed in the presence of internal hydrogen, ε -martensite became more pronounced and the density of deformation bands increased. For the 20 pct strain condition, α '-martensite was observed at the intersection of ε -martensite bands in hydrogen-precharged samples, whereas in non-precharged samples α '-martensite was only observed along grain boundaries. We hypothesize that the increased prevalence of α '-martensite is a secondary effect of increased ε -martensite and deformation band density due to internal hydrogen and is not a signature of internal hydrogen itself.

36 MATERIALS SCIENCE↗
DOE OSTI2022

In-Situ Observation of FCC→HCP Transformation-Induced Plasticity Behavior During Dynamic Deformation of CoCrNi Multi-principal Element Alloys

CoCrNi multi-principal element alloys (MPEAs) have potential as high toughness, blast resistant materials, but limited studies of their high strain rate behavior have been performed. Their high toughness has been attributed to low stacking fault energies and the activation of toughness enhancing deformation mechanisms, such as twinning- and transformation-induced plasticity (TWIP and TRIP, respectively), that may be affected by increased strain rate. This work examines a series of CoCrNi MPEAs tested with a miniaturized pressure bar, while simultaneous synchrotron x-ray diffraction and imaging are performed, and compares these results to those collected during quasi-static deformation at elevated temperatures. Here, the collected diffraction indicates that TRIP was active at elevated strain rates for the most Co-rich alloys containing 50 or 55 at. pct. Co, while TRIP behavior was suppressed at elevated strain rates in a 40 at. pct. Co alloy anticipated to experience TRIP. The suppression of TRIP in the lower Co alloy at high strain rates is attributed to adiabatic heating, consistent with suppression of TRIP as a result of elevated temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2020

< c+a > dislocations in {101 - 2} twins in Mg: A kinematic and energetic requirement

Consideration of published TEM and molecular dynamics studies of interactions between matrix dislocations and {101¯2} twin boundaries (TB) in hexagonal close packed metals inspires a hypothesis regarding the formation of dislocations with < c+a > Burgers vectors inside the twins. It was previously reported that when basal < a > dislocations from the matrix are swept by an advancing TB, they are converted into partial dislocations bounding basal I 1 stacking faults (SFs) within the twin. In the present work, we show that this dislocation configuration near TB renders it energetically favorable for a pair of partial dislocations to constrict into a dislocation within the twin. New in situ TEM observations confirm this hypothesis by revealing long < c+a > dislocation dipoles terminated by the TB at one end and by I1 SFs within the twin at the other end. Finally, the resulting near-screw < c+a > dislocation dipoles are observed to be glissile, enabling self-annihilation in some circumstances. Thus, rather than requiring a high energy dislocation pile-up to press two < a > dislocations through a TB into a single < c+a > dislocation, it is demonstrated that < c+a > dislocations naturally form, within {101¯2} twins in Mg, as TB migrates into a matrix, which inevitably contains dislocations with < a > Burgers vectors. Furthermore, these observations help to explain how the twins themselves may subsequently deform and why they may be particularly vulnerable to plastic, shear localization.

36 MATERIALS SCIENCE↗