Helium Incorporation into Scandium Fluoride, a Model Negative Thermal Expansion Material
Scandium trifluoride is a model negative thermal expansion (NTE) material. Its simple structure can be described as an A-site vacant perovskite, and it shows isotropic NTE over a very wide temperature range (up to ~1100 K), due to transverse vibrational motion of the fluoride. Like many framework NTE materials, it undergoes a phase transition at low pressures, adopting a rhombohedral (R3̅c) structure at >0.7 GPa and 300 K in commonly used nonpenetrating pressure media, such as silicone oil. High pressure X-ray diffraction data and gas uptake/release measurements indicate that, on compression in helium above ~200 K, helium is inserted into ScF 3 to form the defect perovskite He x ScF 3 . The incorporation of helium stiffens the structure and changes its phase behavior. At room temperature, complete filling of the structure with helium does not occur until >1.5 GPa. On compression, a cubic perovskite structure is maintained until ~5 GPa. As the pressure was increased to ~9.5 GPa, a further transition occurred at ~7 GPa. The first transition at ~5 GPa is likely to a tetragonal (P4/mbm) perovskite, but the detailed structure of the perovskite phase formed on compression above ~7 GPa is unclear. Cooling down from 300 to 100 K in helium at ~0.4 GPa leads to an approximate composition of He 0.1 ScF 3 . High pressure neutron diffraction measurements, in the temperature range 15–150 K show that the incorporation of helium increases the pressure at which the cubic (Pm3̅m) to rhombohedral (R3̅c) putative quantum structural phase transition occurs from close to 0 GPa to ~0.2 GPa at 0 K.