A novel approach to mitigating the potential release of radioisotopes under fire conditions - enhancing fire resiliency of radiological contamination fixatives during deactivation & decommissioning activities
Savannah River National Laboratory (SRNL), in close collaboration with the Florida International University Applied Research Center (FIU ARC), successfully executed a technology development activity on behalf of the Department of Energy, Office of Environmental Management (DOE EM). The purpose of the activity was to improve the capability of fixative technologies in immobilizing residual contamination when exposed to thermal stressors as postulated in accident scenarios in Basis for Interim Operations (BIO) documents across the DOE EM complex. The effort resulted in the test and evaluation of a down-selected, commercial-off-the-shelf (COTS) intumescent technology in a radioactive environment at the Savannah River Site (SRS) Building 235-F Plutonium Fuel Form (PuFF) Facility and highlighted the potential use of this technology as a stand-alone, fire retardant fixative. Furthermore, this activity highlighted significant shortfalls in common fixatives currently used to support decommissioning activities and brought to the forefront the need for a methodical, uniformed approach to certifying fixative technologies for operational use in Deactivation and Decommissioning (D&D) activities. An essential component of this research was to evaluate the state of industry fixatives currently in use and set the foundation for comparison to alternative technological solutions. A baseline of five (5) commonly used fixatives and decontamination gels (hereafter collectively referred to as fixatives) was conducted, and notable shortfalls and deficiencies were revealed, particularly when exposed to thermal, water, and other environmental stressors. At temperatures as low as 300 °F - 400 °F (148.89 °C – 204.44 °C), all commonly used fixatives melted from the substrates within 3-5 minutes of exposure, resulting in contaminant transport. Significant degradation in terms of mass loss, desiccation, and off-gassing occurred, and the chemical breakdown of the polymer was so complete researchers assessed there would likely have been a release of residual contamination. Additional vulnerabilities became evident when exposed to water immersion and high humidity; existing fixatives took up water, swelling and frequently delaminating from the substrate, once again increasing the likelihood of a contaminant release.