All sources NASA NTRS DOE OSTI

NASA NTRS1996

Single Transducer Ultrasonic Imaging Method that Eliminates the Effect of Plate Thickness Variation in the Image

This article describes a single transducer ultrasonic imaging method that eliminates the effect of plate thickness variation in the image. The method thus isolates ultrasonic variations due to material microstructure. The use of this method can result in significant cost savings because the ultrasonic image can be interpreted correctly without the need for machining to achieve precise thickness uniformity during nondestructive evaluations of material development. The method is based on measurement of ultrasonic velocity. Images obtained using the thickness-independent methodology are compared with conventional velocity and c-scan echo peak amplitude images for monolithic ceramic (silicon nitride), metal matrix composite and polymer matrix composite materials. It was found that the thickness-independent ultrasonic images reveal and quantify correctly areas of global microstructural (pore and fiber volume fraction) variation due to the elimination of thickness effects. The thickness-independent ultrasonic imaging method described in this article is currently being commercialized under a cooperative agreement between NASA Lewis Research Center and Sonix, Inc.

Roth, Don J.↗

NASA NTRS2001

MSFC Combustion Devices in 2001

The objectives of the project detailed in this viewgraph presentation were to reduce thrust assembly weights to create lighter engines and to increase the cycle life and/or operating temperatures. Information is given on material options (metal matrix composites and polymer matrix composites), ceramic matrix composites subscale liners, lightweight linear chambers, lightweight injector development, liquid/liquid preburner tasks, and vortex chamber tasks.

Dexter, Carol↗

NASA NTRS1998

Single-Transducer, Ultrasonic Imaging Method for High-Temperature Structural Materials Eliminates the Effect of Thickness Variation in the Image

NASA Lewis Research Center's Life Prediction Branch, in partnership with Sonix, Inc., and Cleveland State University, recently advanced the development of, refined, and commercialized an advanced nondestructive evaluation (NDE) inspection method entitled the Single Transducer Thickness-Independent Ultrasonic Imaging Method. Selected by R&D Magazine as one of the 100 most technologically significant new products of 1996, the method uses a single transducer to eliminate the superimposing effects of thickness variation in the ultrasonic images of materials. As a result, any variation seen in the image is due solely to microstructural variation. This nondestructive method precisely and accurately characterizes material gradients (pore fraction, density, or chemical) that affect the uniformity of a material's physical performance (mechanical, thermal, or electrical). Advantages of the method over conventional ultrasonic imaging include (1) elimination of machining costs (for precision thickness control) during the quality control stages of material processing and development and (2) elimination of labor costs and subjectivity involved in further image processing and image interpretation. At NASA Lewis, the method has been used primarily for accurate inspections of high temperature structural materials including monolithic ceramics, metal matrix composites, and polymer matrix composites. Data were published this year for platelike samples, and current research is focusing on applying the method to tubular components. The initial publicity regarding the development of the method generated 150 requests for further information from a wide variety of institutions and individuals including the Federal Bureau of Investigation (FBI), Lockheed Martin Corporation, Rockwell International, Hewlett Packard Company, and Procter & Gamble Company. In addition, NASA has been solicited by the 3M Company and Allison Abrasives to use this method to inspect composite materials that are manufactured by these companies.

Roth, Don J.↗

NASA NTRS2007

Design and Optimization of Composite Gyroscope Momentum Wheel Rings

Stress analysis and preliminary design/optimization procedures are presented for gyroscope momentum wheel rings composed of metallic, metal matrix composite, and polymer matrix composite materials. The design of these components involves simultaneously minimizing both true part volume and mass, while maximizing angular momentum. The stress analysis results are combined with an anisotropic failure criterion to formulate a new sizing procedure that provides considerable insight into the design of gyroscope momentum wheel ring components. Results compare the performance of two optimized metallic designs, an optimized SiC/Ti composite design, and an optimized graphite/epoxy composite design. The graphite/epoxy design appears to be far superior to the competitors considered unless a much greater premium is placed on volume efficiency compared to mass efficiency.

Bednarcyk, Brett A.↗

NASA NTRS2016

Stochastic-Strength-Based Damage Simulation of Ceramic Matrix Composite Laminates

The Finite Element Analysis-Micromechanics Analysis Code/Ceramics Analysis and Reliability Evaluation of Structures (FEAMAC/CARES) program was used to characterize and predict the progressive damage response of silicon-carbide-fiber-reinforced reaction-bonded silicon nitride matrix (SiC/RBSN) composite laminate tensile specimens. Studied were unidirectional laminates [0] (sub 8), [10] (sub 8), [45] (sub 8), and [90] (sub 8); cross-ply laminates [0 (sub 2) divided by 90 (sub 2),]s; angled-ply laminates [plus 45 (sub 2) divided by -45 (sub 2), ]s; doubled-edge-notched [0] (sub 8), laminates; and central-hole laminates. Results correlated well with the experimental data. This work was performed as a validation and benchmarking exercise of the FEAMAC/CARES program. FEAMAC/CARES simulates stochastic-based discrete-event progressive damage of ceramic matrix composite and polymer matrix composite material structures. It couples three software programs: (1) the Micromechanics Analysis Code with Generalized Method of Cells (MAC/GMC), (2) the Ceramics Analysis and Reliability Evaluation of Structures Life Prediction Program (CARES/Life), and (3) the Abaqus finite element analysis program. MAC/GMC contributes multiscale modeling capabilities and micromechanics relations to determine stresses and deformations at the microscale of the composite material repeating-unit-cell (RUC). CARES/Life contributes statistical multiaxial failure criteria that can be applied to the individual brittle-material constituents of the RUC, and Abaqus is used to model the overall composite structure. For each FEAMAC/CARES simulation trial, the stochastic nature of brittle material strength results in random, discrete damage events that incrementally progress until ultimate structural failure.

composite structures↗

DOE OSTI2020

Finite Element Modeling of the Fiber-Matrix Interface in Polymer Composites

Polymer composites are used in numerous industries due to their high specific strength and high specific stiffness. Composites have markedly different properties than both the reinforcement and the matrix. Of the several factors that govern the final properties of the composite, the interface is an important factor that influences the stress transfer between the fiber and matrix. The present study is an effort to characterize and model the fiber-matrix interface in polymer matrix composites. Finite element models were developed to study the interfacial behavior during pull-out of a single fiber in continuous fiber-reinforced polymer composites. A three-dimensional (3D) unit-cell cohesive damage model (CDM) for the fiber/matrix interface debonding was employed to investigate the effect of interface/sizing coverage on the fiber. Furthermore, a two-dimensional (2D) axisymmetric model was used to (a) analyze the sensitivity of interface stiffness, interface strength, friction coefficient, and fiber length via a parametric study; and (b) study the shear stress distribution across the fiber-interface-matrix zone. It was determined that the force required to debond a single fiber from the matrix is three times higher if there is adequate distribution of the sizing on the fiber. The parametric study indicated that cohesive strength was the most influential factor in debonding. Moreover, the stress distribution model showed the debonding mechanism of the interface. It was observed that the interface debonded first from the matrix and remained in contact with the fiber even when the fiber was completely pulled out.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Epoxy as Filler or Matrix for Polymer Composites

Epoxy is a widely used polymer because of its ease of processing, high adhesiveness, and high chemical resistance. Epoxy-based composites are commonly used in aerospace, automotive, and marine applications. The epoxy type, function, curing agent, and curing process are discussed in this chapter. Epoxy is used as either a filler or polymer matrix in composite applications. As a filler, the epoxy modification on the fiber is discussed. As a polymer matrix, the epoxy is reinforced by natural and synthetic fibers. The manufacturing process and the fabricated epoxy-based composites’ performance (e.g., mechanical and thermal properties) are investigated. The advantages and disadvantages of epoxy’s function are discussed and summarized. Epoxy modification is an effective approach to improve the composites’ performance.

Zhao, Xianhui↗

NASA NTRSDate not supplied

Latent Cure Epoxy Matrix Resins for Reliable Assembly of Thermoset Composite Structures

Polymer matrix composites are used in high performance structures because of their excellent specific strength, toughness, and stiffness. To realize their full potential, complex composite structures must be assembled with adhesive, but uncertainty in bond performance often requires manufacturers to install bolts or other crack-arrest features to ensure safety in critical applications.1 The inherent uncertainty in adhesive bonds stems from the material discontinuity at the composite-to-adhesive interfaces, which are susceptible to contamination and other causes of inter-facial weakness.2 In contrast, co-cured composites, although limited in size and complexity, result in predictable structures that may be certifiable for commercial aviation with reduced dependence on redundant load paths.1 The technology proposed here uses a stoichiometric offset of the hardener-to-epoxy ratio on the faying surfaces of epoxy compo-site laminates. Assembly of the components in a subsequent “secondary co-cure” process results in a joint with no material discontinuities (Figure 1)

Frank L. Palmieri↗

NASA NTRS2019

Materials and Processes for New Propulsion Systems with Reduced Environmental Impact

Aeronautics research at NASA Glenn Research Center includes development, characterization and modeling of high temperature, lightweight materials and fabrication processes for aircraft propulsion systems with increased efficiency and reduced emissions, fuel burn and noise. Current propulsion materials research includes Ceramic Matrix Composites and Environmental Barrier Coatings, Polymer Matrix Composites and Additive Manufacturing processes. This presentation will summarize recent progress and plans in these areas. Ceramic Matrix Composites for Turbine Components: As part of NASA's Aeronautics research, Glenn Research Center has developed Ceramic Matrix Composites for 2700 degrees Fahrenheit turbine engine applications in the next generation of ultra-efficient aircraft. In this presentation, the development of advanced fiber and matrix constituents that enabled this advancement will be reviewed, and characterization of the resulting improvements in mechanical properties and durability will be summarized. Progress toward the development and validation of models predicting the effects of the engine environment on durability of Ceramic Matrix Composites and Environmental Barrier Coatings will be summarized. Progress and plans for collaborative research with industry and other government agencies will be reviewed. Polymer Matrix Composites for Powertrain and Impact Protection: A lightweight, hybrid polymer matrix composite/steel gear concept for rotorcraft power transmission applications was evaluated at realistic speed, torque, and power conditions. Dynamic testing was performed at 5000 horsepower and 5400 revolutions per minute with no performance degradation. Test results demonstrated the potential of hybrid composite / metal gears to reduce gear weight by approximately 15 percent, enabling the implementation of multi-speed drive systems, which would otherwise have a weight penalty, for increased speed and efficiency. Results of post-test inspection and endurance tests will be presented. Separately, ballistic impact tests demonstrated improved damage tolerance in polymer matrix composites by incorporating lightweight, thermoplastic veil materials between selected composite plies during the composite fabrication process. Results of impact tests and post-test inspection will be presented. Additive Manufacturing for Electric Propulsion: Additive Manufacturing processes offer the potential to fabricate new, high power density electric motor designs with complex geometries, multi-material components and optimally designed components that would not be feasible with traditional manufacturing processes. High performance stator components using advanced 3-phase conductive coils were fabricated using direct printing with optimized silver pastes. Additional additive manufacturing methods are being used to fabricate rotors and motor housing components. Systems studies show that the higher performance and lower weight motors offer improved energy efficiency and reduced emissions. Improvements to motor performance resulting from optimized materials and component designs will be presented.

Additive Manufacturing↗

NASA NTRS1995

Thermographic imaging for high-temperature composite materials: A defect detection study

The ability of a thermographic imaging technique for detecting flat-bottom hole defects of various diameters and depths was evaluated in four composite systems (two types of ceramic matrix composites, one metal matrix composite, and one polymer matrix composite) of interest as high-temperature structural materials. The holes ranged from 1 to 13 mm in diameter and 0.1 to 2.5 mm in depth in samples approximately 2-3 mm thick. The thermographic imaging system utilized a scanning mirror optical system and infrared (IR) focusing lens in conjunction with a mercury cadmium telluride infrared detector element to obtain high resolution infrared images. High intensity flash lamps located on the same side as the infrared camera were used to heat the samples. After heating, up to 30 images were sequentially acquired at 70-150 msec intervals. Limits of detectability based on depth and diameter of the flat-bottom holes were defined for each composite material. Ultrasonic and radiographic images of the samples were obtained and compared with the thermographic images.

Roth, Don J.↗

NASA NTRS2011

Nanoparticle/Polymer Nanocomposite Bond Coat or Coating

This innovation addresses the problem of coatings (meant to reduce gas permeation) applied to polymer matrix composites spalling off in service due to incompatibility with the polymer matrix. A bond coat/coating has been created that uses chemically functionalized nanoparticles (either clay or graphene) to create a barrier film that bonds well to the matrix resin, and provides an outstanding barrier to gas permeation. There is interest in applying clay nanoparticles as a coating/bond coat to a polymer matrix composite. Often, nanoclays are chemically functionalized with an organic compound intended to facilitate dispersion of the clay in a matrix. That organic modifier generally degrades at the processing temperature of many high-temperature polymers, rendering the clay useless as a nano-additive to high-temperature polymers. However, this innovation includes the use of organic compounds compatible with hightemperature polymer matrix, and is suitable for nanoclay functionalization, the preparation of that clay into a coating/bondcoat for high-temperature polymers, the use of the clay as a coating for composites that do not have a hightemperature requirement, and a comparable approach to the preparation of graphene coatings/bond coats for polymer matrix composites.

Miller, Sandi G.↗

NASA NTRS1982

Durability of spacecraft materials

Research efforts are reviewed on the space durability of materials, including radiation effects on polymer matrix composites and films, dimensional stability of polymer matrix composites and tension-stabilized cables, and thermal control coatings. Research to date has concentrated on establishing a fundamental understanding of space environmental effects on current graphite-reinforced composites and polymer systems, and development of analytical models to explain observed changes in mechanical, physical, and optical properties. As a result of these research efforts, new experimental facilities have been developed to simulate the space environment and measure the observed property changes. Chemical and microstructural analyses have also been performed to establish damage mechanisms and the limits for accelerated testing. The implications of these results on material selection and system performance are discussed and additional research needs and opportunities in the area of tougher resin/matrix and metal/matrix composites are identified.

Darrel R. Tenney↗

NASA NTRS2018

Joint Strength Optimization and Damping Assessment of NiTi-Polymer Matrix Hybrid Composites

Approaches to optimize the adhesive joint strength between shape memory alloy ribbons and carbon fiber-reinforced epoxy composites were investigated for potential use as either an actuating structure or a dampening composite for structural applications. The interfacial bond strength between nickel-titanium (NiTi) and a polymer matrix composite (PMC) was measured by double lap shear testing as a function of NiTi surface treatment and adhesive material. The effect of NiTi surface treatment on damping was investigated using dynamic mechanical analysis. Lap shear data show that treating the surfaces of NiTi ribbons by light sandblasting and primer application increased the interfacial bond strength by 20 percent over the baseline composite structure. Lap shear data also reveal that out of three different film adhesives investigated, samples bonded with AF 191U and Hysol® 9696U display the highest adhesive joint strengths. Optical microscopy reveals that most samples failed by either cohesive failure within the adhesive or by adhesive failure at either the adhesive/PMC or NiTi/adhesive interface. Adhering NiTi to the PMC did not appear to negatively impact damping performance; however, a more thorough examination into NiTi's role on vibration damping should be investigated.

lap shear↗

DOE OSTI2020

Study on Fracture of Fiber-Reinforced Polymeric Composites Using Spiral Notch Torsion Test

Fiber-reinforced polymer-matrix composites have been widely applied in various areas due to their excellent mechanical properties. In this study, carbon fiber-reinforced polymer-matrix composites and glass fiber-reinforced polymer-matrix composites failure tests under quasi static torsion have been demonstrated by using spiral notch torsion test methodology. Three types of cylindrical specimens with different fiber orientations were prepared and tested. For both composites, after increase stage, A type exhibited limited stress variations before the sudden failure, whereas B type showed gradual failure with torque drops. Displacement contours, stress contours and energy release rates were acquired using the anisotropic elastic finite element models. Microscopic characterization exhibited that the failure of A type occurred along interfaces between fibers and matrices, whereas circular cracks in B type propagated alternatively between polymeric matrices and interfaces. Type C failure is similar to type A whereas with a curvature observed on the fracture surface.

Du, Fen↗

NASA NTRS2012

Resin Systems and Chemistry-Degradation Mechanisms and Durability in Long-Term Durability of Polymeric Matrix Composites

In choosing a polymer-matrix composite material for a particular application, a number of factors need to be weighed. Among these are mechanical requirements, fabrication method (e.g. press-molding, resin infusion, filament winding, tape layup), and use conditions. Primary among the environmental exposures encountered in aerospace structures are moisture and elevated temperatures, but certain applications may require resistance to other fluids and solvents, alkaline agents, thermal cycling, radiation, or rapid, localized heating (for example, lightning strike). In this chapter, the main classes of polymer resin systems found in aerospace composites will be discussed. Within each class, their responses to environmental factors and the associated degradation mechanisms will be reviewed.

Hinkley, Jeffrey A.↗

NASA NTRS2004

Tensile Properties of Polymeric Matrix Composites Subjected to Cryogenic Environments

Polymer matrix composites (PMC s) have seen limited use as structural materials in cryogenic environments. One reason for the limited use of PMC s in cryogenic structures is a design philosophy that typically requires a large, validated database of material properties in order to ensure a reliable and defect free structure. It is the intent of this paper to provide an initial set of mechanical properties developed from experimental data of an advanced PMC (IM7/PETI-5) exposed to cryogenic temperatures and mechanical loading. The application of this data is to assist in the materials down-select and design of cryogenic fuel tanks for future reusable space vehicles. The details of the material system, test program, and experimental methods will be outlined. Tension modulus and strength were measured at room temperature, -196 C, and -269 C on five different laminates. These properties were also tested after aging at -186 C with and without loading applied. Microcracking was observed in one laminate.

Whitley, Karen S.↗

NASA NTRS2007

Heat Rejection Systems Utilizing Composites and Heat Pipes: Design and Performance Testing

Polymer matrix composites offer the promise of reducing the mass and increasing the performance of future heat rejection systems. With lifetimes for heat rejection systems reaching a decade or more in a micrometeoroid environment, use of multiple heat pipes for fault tolerant design is compelling. The combination of polymer matrix composites and heat pipes is of particular interest for heat rejection systems operating on the lunar surface. A technology development effort is under way to study the performance of two radiator demonstration units manufactured with different polymer matrix composite face sheet resin and bonding adhesives, along with different titanium-water heat pipe designs. Common to the two radiator demonstration units is the use of high thermal conductivity fibers in the face sheets and high thermal conductivity graphite saddles within a light weight aluminum honeycomb core. Testing of the radiator demonstration units included thermal vacuum exposure and thermal vacuum exposure with a simulated heat pipe failure. Steady state performance data were obtained at different operating temperatures to identify heat transfer and thermal resistance characteristics. Heat pipe failure was simulated by removing the input power from an individual heat pipe in order to identify the diminished performance characteristics of the entire panel after a micrometeoroid strike. Freeze-thaw performance was also of interest. This paper presents a summary of the two radiator demonstration units manufactured to support this technology development effort along with the thermal performance characteristics obtained to date. Future work will also be discussed.

Jaworske, Donald A.↗

NASA NTRS1992

Tough, high performance, addition-type thermoplastic polymers

A tough, high performance polyimide is provided by reacting a triple bond conjugated with an aromatic ring in a bisethynyl compound with the active double bond in a compound containing a double bond activated toward the formation of a Diels-Adler type adduct, especially a bismaleimide, a biscitraconimide, or a benzoquinone, or mixtures thereof. Addition curing of this product produces a high linear polymeric structure and heat treating the highly linear polymeric structure produces a thermally stable aromatic addition-type thermoplastic polyimide, which finds utility in the preparation of molding compounds, adhesive compositions, and polymer matrix composites.

Pater, Ruth H.↗