Improved catalytic activity of Mo x Ni y Al z thin films as electrocatalyst for hydrogen evolution reaction in alkaline media
In this work, we report activities of Mo x Ni y X z (where X is Al, Co, Cr, Cu, Fe, W)-based electrocatalysts for hydrogen evolution reaction (HER) in a 1 M NaOH solution. Mo x Ni y X z thin film electrocatslysts were prepared by magentron sputtering at 25°C and 800°C and characterized by scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analyzer and X-ray diffraction (XRD) analysis. Here, the catalytic activity of electrocatalyst was studied by cyclic voltammetry and electrochemical impedance spectroscopy. The electrocatalyst based on Mo 80 Ni 5 Al 15 (800°C) shows the best value of the overpotential (-181 mV) for HER from all tested ternary systems. XRD analysis indicates that HER activity only Mo 80 Ni 5 Al 15 thin films prepared at 800°C contained fcc phase. Other less active composition contained only bcc phase. The results obtained from impedance spectroscopy are consistent with the results from cyclic voltammetry. The stability of the prepared catalyst was studied by chronoamperometric analysis. The results from chronoamperometry show that HER activity of Mo 80 Ni 5 Al 15 prepared at 800°C, after very slight initial activity decrease, stays constant, while activity of Ni catalyst decreased almost twice in measured time window. Since Ni is commonly used industrial catalyst, Mo 80 Ni 5 Al 15 based alloy could be more attractive catalyst material for alkaline electrolyzers.