A comparison of wrought and powder metallurgical FeCrAl claddings under simulated LWR accident transients
Iron-chromium-aluminum (FeCrAl) alloys are potential accident tolerant fuel (ATF) cladding candidates for light-water reactors but are difficult to fabricate as thin-walled tubes via conventional cast-and-wrought routes. Powder metallurgy (PM) offers a manufacturing alternative with improved compositional control, but its transient accident performance has not been directly benchmarked against wrought variants. This study evaluates the burst behavior of commercially developed PM-processed FeCrAl alloys, PM-C26M (Fe-12Cr-6Al-2Mo) and the high precipitate density FA-SMT (Fe-22Cr-5Al-3Mo), under simulated light-water reactor accident transient conditions. Burst testing was conducted using the Severe Accident Test Station with heating rates of 5 °C/s and 50 °C/s and internal pressures ranging from 25 MPa to 100 MPa. PM-C26M reproduced wrought C26M burst behavior within 7–37 °C across the stress range, indicating that PM processing does not compromise transient strength. FA-SMT exhibited markedly higher burst temperatures and reduced heating-rate sensitivity, consistent with its engineered precipitate strengthening. FA-SMT rupture exhibited axial "unzipping" rather than the lateral tearing characteristic of PM- and wrought C26M. Post-test EBSD and fractography indicate that this behavior is strongly correlated with strain-gated intergranular void nucleation associated with the dense precipitate architecture of FA-SMT, a response absent in the comparatively clean PM-C26M matrix and consistent with rupture morphologies reported for oxide-dispersion strengthened (ODS) FeCrAl of similar base-matrix chemistry to PM-C26M. These findings highlight the potential of powder metallurgy as a viable fabrication route for ATF claddings from an accident performance standpoint.