Temperature dependent interfacial microstructure in HIP-bonded Al6061/Zr joints

Pressing (HIP) at 450 °C and 560 °C under 103 MPa for 90 minutes to evaluate interfacial diffusion and microstructural evolution. Sound metallurgical bonding was achieved at both temperatures, with Zr serving as an effective diffusion barrier. Microstructural analysis revealed the the formation of a (Al,Si)3Zr intermetallic layer at the Al/Zr interface, whose thickness increased from ~100 nm at 450 °C to ~2100 nm at 560 °C, consistent with temperature-driven diffusion kinetics. The thin and continuous reaction layer observed at 450 °C indicates controlled interdiffusion and minimal reaction zone growth, favorable for maintaining interface stability and ductility. At 560 °C, enhanced atomic mobility led to pronounced intermetallic development, confirming diffusion-controlled growth behavior. These results provide valuable insights for optimizing Al/Zr interface design and diffusion barrier performance in advanced structural and energy systems.

Al/Zr interface↗

DOE OSTI2025

Micro-tensile testing of neutron-irradiated Al/Zr and Zr/U-Mo diffusion bonds

This study focuses on micro-tensile testing of neutron-irradiated Al/Zr and Zr/U-Mo diffusion bonds, which are integral to the structure and performance of nuclear fuel plates used in the fuel being developed for U.S. high-power research reactors. During fabrication, two distinct diffusion bonds occur—one at the Zr/U-10Mo interface via roll bonding, and the Zr/Al interface via hot isostatic pressing at 833 K. This work utilizes micro-tensile testing specimens approximately 7 × 7 × 18 μm 3 , which are sufficiently large to encompass the identified diffusion zones to evaluate the failure strength and identify the failure location. For the Zr/Al interface, all failures occurred in the bulk aluminum. The average yield strength, ultimate strength, and strain at failure for the two parent samples were: 125 ± 10 MPa, 139 ± 24 MPa, 156 ± 21 MPa, 185 ± 14 MPa, 37.9 ± 5.6 %, and 29.7 ± 3.4 %, respectively. For specimens across the Zr/U-Mo interface, failures occurred either in the bulk Zr or U-Mo, with no failures observed in the diffusion region. For specimens that failed in the bulk Zr the failure strength and strain for the two parent samples were 570 MPa, 710 ± 131 MPa, and 43.3 %, 27.3 ± 6.6 % respectively. The specimens that failed in the bulk U-Mo had failure strengths and strains of 596 ± 32 MPa, 548 ± 124 MPa, and 2.2 ± 1.3 %, 1.5 ± 0.6 % respectively. In conclusion, these findings support the development of accurate thermo-mechanical models for irradiated fuel performance by identifying the mechanical limits and failure locations within the bonded regions.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗