Control of interfaces in Al-C fibre composites

The interface of Al-C fiber composite was modified by coating a silver layer on the surface of carbon fibres prior to making composites, in an attempt to improve the wettability between molten aluminum and carbon fibers during infiltration. An electroless plating technique was adopted and perfected to provide a homogeneous silver coating on the carbon fiber surface. Al-C fiber composites were prepared using a liquid infiltration technique in a vacuum. It was found that silver coating promoted the wetting between aluminum and carbon fibers, particularly with polyacrylonitrile-base carbon fibers. However, due to rapid dissolution of silver in molten aluminum, it was believed that the improved infiltration was not due to the wetting behavior between molten aluminum and silver. The cleaning of the fiber surface and the preservation of the cleaned carbon surface with silver coating was considered to be the prime reason for the improved wettability. Interfacial reactions between aluminum and carbon fibers were observed. Amorphous carbon was found to react more with aluminum than graphitic carbon. This is believed to be because of the inertness of the graphitic basal planes.

Warrier, S. G.↗

A review of rapid solidification studies of intermetallic compounds

A review of rapid solidification studies of high-temperature ordered intermetallic compounds is presented. Emphasis is on the nickel - and iron- aluminides which are of potential interest as structural materials. The nickel-base aluminides which have been rapidly solidified exhibit changes in grain size, compositional segregation, and degree of long range order (as reflected in APB size and distribution) which markedly affect mechanical properties. Some experiments indicate the formation of a metastable L1(2) phase in rapidly solidified Fe-(Ni,Mn)-Al-C alloys, while other work observes only a metastable fcc phase in the same composition range. The metastable phases and/or microstructures in both nickel and iron aluminides are destroyed by annealing at temperatures above 750 K, with subsequent degradation of mechanical properties. Rapid solidification studies of several other intermetallic compounds are briefly noted.

Koch, C. C.↗

Chemical interactions in the aluminum-carbon and aluminum-silicon carbide systems

XPS was used to investigate the influence of O2 and H2O on the formation of aluminum carbide at Al-C and Al-SiC interfaces. It was determined that dosing the interfaces with H2O catalyzed the formation of aluminum carbide in both systems. This result is consistent with the oxidation model of carbide formation (developed to understand the kinetics of aluminum carbide formation at graphite-aluminum interfaces). These results imply that the formation of aluminum carbide in graphite- and SiC-reinforced metal-matrix composites, which severely degrades the composite mechanical properties by degrading the fiber and interface strength is catalyzed.

Maruyama, Benji↗