Observations of Atmospheric Corrosion Testing on Heated Austenitic Stainless Steel Surfaces: Exploring the Role of Inert Dust Particulates and Seawater

Relevant atmospheric corrosion laboratory testing environments were developed to explore the influence of inert dust and seawater on the corrosion susceptibility of stainless steel in spent nuclear fuel dry storage conditions. Measurements from dust collected on in-service dry storage canisters were applied to develop exposure conditions. Three atmospheric exposure conditions, two static and one cyclic, were examined with three different surface coverages: co-deposited large dust and seawater, co-deposited small dust and seawater, and solely seawater. Stainless steel coupons representative of spent nuclear fuel dry storage canister material were subjected to the various corrosion environments, with the results from exposures up to 1 year presented here. Post exposure, corrosion damage was analyzed using optical microscopy, scanning electron microscopy, and energy dispersive X-ray spectroscopy. Initial observations are presented herein, and potential implications with respect to the influence of inert dust particles on corrosion susceptibility are summarized. In general, the co-deposition of dust and salt resulted in larger pits and exhibited mixed modes of corrosion that were not observed in the no-dust conditions (i.e., crevicing, filiform, and pits within pits). The presence of the inert dust may influence brine spreading and/or act as crevice formers, leading to enhanced corrosion. This study highlights the significance of incorporating dust particulate(s) beyond the deliquescent chemistries to fully evaluate atmospheric corrosion severity.

Sea salt↗
DOE OSTI2020

Revealing the growth kinetics of atmospheric corrosion pitting in aluminum via in situ microtomography

Abstract Understanding the mechanistic relationship between the environment, microstructure, and local kinetics of atmospheric corrosion damage remains a central challenge. To address this challenge, this study used laboratory-based X-ray tomography to directly observe attack in-operando over an extended period, enabling insights into the evolving growth kinetics and morphology of individual pits over months of exposure. Damage progression associated with nine pits in a 99.9% pure aluminum wire exposed to chloride salts in humid air was characterized. Most pits grew at a nominally linear rate up until pit death, which occurred within 12–24 h of nucleation. Exceptions to this were observed, with three pits exhibiting bimodal growth kinetics and growing for 40 or more hours. This was explained by secondary droplets that formed near the pits, increasing the cathode area. A corrosion-driven drying mechanism likely contributed to pit death in both cases. Pits first grew into the material followed by lateral expansion.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Evaluation of Applied Stress on Atmospheric Corrosion and Pitting Characteristics in 304L Stainless Steel

For this study, the effects of applied stress, ranging from tensile to compressive, on the atmospheric pitting corrosion behavior of 304L stainless steel (SS304L) were analyzed through accelerated atmospheric laboratory exposures and microelectrochemical cell analysis. After exposing the lateral surface of a SS304L four-point bend specimen to artificial seawater at 50°C and 35% relative humidity for 50 d, pitting characteristics were determined using optical profilometry and scanning electron microscopy. The SS304L microstructure was analyzed using electron backscatter diffraction. Additionally, localized electrochemical measurements were performed on a similar, unexposed, SS304L four-point bend bar to determine the effects of applied stress on corrosion susceptibility. Under the applied loads and the environment tested, the observed pitting characteristics showed no correlation with the applied stress (from 250 MPa to -250 MPa). Pitting depth, surface area, roundness, and distribution were found to be independent of location on the sample or applied stress. The lack of correlation between pitting statistics and applied stress was more likely due to the aggressive exposure environment, with a sea salt loading of 4 g/m 2 chloride. The pitting characteristics observed were instead governed by the available cathode current and salt distribution, which are a function of sea salt loading, as well as pre-existing underlying microstructure. In microelectrochemical cell experiments performed in Cl - environments comparable to the atmospheric exposure and in environments containing orders of magnitude lower Cl - concentrations, effects of the applied stress on corrosion susceptibility were only apparent in open-circuit potential in low Cl - concentration solutions. Cl - concentration governed the current density and transpassive dissolution potential.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Marine Atmospheric Corrosion of Additively Manufactured Stainless Steels

Additively manufactured (AM) stainless steels exhibit numerous microstructural differences compared to their wrought counterparts, such as Cr enriched dislocation cell structures. The influence these unique features have on a SSs corrosion resistance are still under investigation with most current works limited to laboratory experiments. The work herein shows the first documented study of AM 304L and 316L exposed to a severe marine environment on the eastern coast of Florida with comparisons made to wrought counterparts. Coupons were exposed for 21 months and resulted in significant pitting corrosion to initiate after 1 month of exposure for all conditions. At all times, the AM coupons exhibited lower average and maximum pit depths than their wrought counterparts. After 21 months, pits on average were 4 μm deep for AM 316L specimen and 8 μm deep for wrought specimen. Pits on the wrought samples tended to be nearly hemispherical and polished with some pits showing crystallographic attack while pits on AM coupons exhibited preferential attack at melt pool boundaries and the cellular microstructure.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The evolution of pit morphology and growth kinetics in aluminum during atmospheric corrosion

Abstract Assessing the lifetimes of alloys in humid, corrosive environments requires growth kinetic information regarding individual instances of damage, e.g. pit growth rates. Corrosion rates measured at the continuum scale using mass change convolute the rate of pit nucleation and growth, providing limited information on local kinetics. The current study used in-situ X-ray computed tomography to measure growth rates of individual pits in aluminum over 100 h of exposure in a humid, chloride environment. While pits grew at relatively constant rates over the first hours after nucleation, significant growth-rate nonlinearities subsequently occurred. These were linked to both droplet spreading, which altered the cathode size, and changes in the mode of pit growth. Pit morphology appeared to influence the dominant growth mode and the duration of pit growth. Post-mortem serial sectioning revealed pits preferentially attacked grain-boundary triple junctions and dislocation boundaries.

Noell, Philip J. (ORCID:0000000346998999)↗